There are two main reasons that impair the health of working people at work. One of them is occupational accident and the other is occupational disease. It is possible to suffer an occupational disease due to various reasons during working in the workplace or to be exposed to substances harmful to human health. It is known that with the measures taken, occupational accidents are significantly reduced and occupational diseases are completely prevented. In this study, it is aimed to reveal statistical data about occupational accidents and occupational diseases that people working at workplaces are exposed to. In the research, the sectoral comparison of occupational accidents and diseases and their distribution by years, the distribution of injuries according to the location of occupational accidents and the distribution of occupational accidents according to work hours were investigated. The data in the study covers the years 2000-2018. According to the data obtained, it has been determined that the sector in which occupational accidents result in the highest number of deaths is the construction sector. In general, it was determined that the number of work accidents showed an increasing trend until 2019, but this number decreased by 2% and fatal work accidents by 6% in 2019. In the accidents resulting in injury, it has been determined that the hands, arms and face parts of the employees are damaged the most, and the occupational accidents are more common in the working hours before lunch and especially in the first working hour. According to the total duration of the study, the number of occupational accidents was determined in the group working between 1 month and 1 year at most. There are more occupational accidents in enterprises with 1-49 workers compared to other groups., Çalışan insanların iş yerlerinde sağlığını bozan iki temel neden vardır. Bunlardan bir tanesi iş kazası diğeri ise meslek hastalığıdır. İşyerlerinde çalışma esnasında çeşitli sebeplerden dolayı iş kazasına uğramak ya da insan sağlığına zararlı maddelere maruz kalmaktan dolayı meslek hastalığına yakalanmak mümkün olabilmektedir. Alınan önlemlerle iş kazasının önemli ölçüde azaltıldığı, meslek hastalığının ise tamamen önlendiği bilinmektedir. Bu çalışmada iş yerlerinde çalışan insanların maruz kaldıkları iş kazası ve meslek hastalığı ile ilgili istatistiksel verilerin ortaya konulması amaçlanmıştır. Araştırmada iş kazası ve meslek hastalığının sektör karşılaştırılması ve yıllara göre dağılımı, iş kazalarında yaranın yerine göre dağılımı ve iş kazalarının iş saatlerine göre dağılımı araştırılmıştır. Çalışmadaki veriler 2000-2018 yıllarını kapsamaktadır. Elde edilen verilere göre iş kazalarının en fazla ölümle neticelendiği sektörün inşaat sektörü olduğu belirlenmiştir. Genel olarak iş kazası sayısının 2019 yılına kadar artan bir eğilim gösterdiği ancak bu sayının 2019 yılında %2 ve ölümlü iş kazasının ise %6 oranında azaldığı tespit edilmiştir. Yaralanma ile neticelenen kazalarda ise çalışanların en fazla el, kol ve yüz kısımlarından zarar gördüğü, iş kazalarının öğle yemeği öncesi çalışma saatlerinde ve özellikle ilk iş saatinde daha fazla olduğu belirlenmiştir. Çalışma toplam süreye göre ise iş kazası sayısı en fazla 1ay ile 1 yıl arasında çalışan grupta tespit edilmiştir. 1-49 arasında çalışan işçisi olan işletmelerde diğer gruplara göre daha fazla iş kazası olmaktadır

In this study, the effects of perlite use on fire resistance in wood plastic composite production were investigated. Scots pine wood flour, polypropylene and perlite using certain proportions of wood plastic composite materials were produced by flat-presses method. In the production of wood plastic composites, 5%, 10%, 15% and 20% perlite was used in the mixture. Test samples were obtained from the produced wood plastic composite boards in accordance with the relevant standards. Horizontal and vertical combustion rate and Limited Oxygen Index tests were performed to determine the fire resistance properties. Horizontal combustion rate (ASTM D 635), vertical combustion rate (UL-94) and LOI test (ASTM 2863-09 standards) were carried out. As a result, according to both the horizontal-vertical combustion rate and LOI data, It has been determined that perlite improves the fire resistance due to the increase in the usage rate. In the production of wood plastic composite, the most positive effect on fire resistance was determined at a 20% perlite usage rate. It was concluded that this effect increased with the use of MAPP., Bu çalışmada odun plastik kompozit üretiminde perlit kullanımının yanma dayanımı üzerine etkileri araştırılmıştır. Sarıçam odun unu, polipropilen ve perlit belirli oranlarda kullanılarak odun plastik kompozit malzemeler doğrudan pres yöntemi ile üretilmiştir. Üretilen odun plastik kompozitlerin üretiminde karışımın %5, %10, %15 ve %20 oranlarında perlit kullanılmıştır. Üretilen odun plastik kompozit levhalardan ilgili standartlara uygun olarak test numuneleri elde edilmiştir. Yanma dayanım özelliklerinin belirlenmesinde yatay ve dikey yanma hızı ve Limited Oksijen Index testleri yapılmıştır. Yatay yanma hızı ASTM D 635, dikey yanma hızı (UL 94) ve LOI testi ASTM 2863-09 standartlarına uygun olarak yapılmıştır. Sonuçta hem yatay ve dikey yanma hızı hem de LOI ile ilgili verilere göre perlit kullanım oranının artmasına bağlı olarak yanma dayanımını iyileştirdiği belirlenmiştir. Odun plastik malzeme üretiminde yanma dayanımı için en olumlu etki %20 perlit kullanım oranında tespit edilmiştir. MAPP kullanımı ile bu etkinin arttığı sonucuna ulaşılmıştır.

Aim of study: In this study, it is aimed to make the wood material hydrophobic and magnetic by creating a smart biomimetic artificial form for lignocellulosic surfaces.Material and methods: Ferrous sulfate heptahydrate (FeSO4·7H2O), Manganese (II) chloride (MnCl2.4H2O), Ethyl alcohol (EtOH), Sodium hydroxide (NaOH), and Potassium nitrate (KNO3) having implemented on the wood to the synthesis of the intelligent biomimetic surface. Hydrophobisation had supplied by Octadecyltrichlorosilane (OTS, 95%). Fourier-transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), Scanning electron microscopy (SEM), and Energy dispersive x-ray (EDX) having used for the characterization step. Water contact angle (WCA) had used for hydrophobicity. Finally, the UV-Vis spectrometer device had used to determine the magnetic properties.Main results: According to the characterizations, the smart biomimetic artificial form having been synthesized on a wood surface successfully. The water contact angle of the new surface having determined as θγ 125 °. It showed absorption properties in the wavelength range of 200-800 nm.Highlights: As a smart biomimetic artificial design has produced as a result of this study improves the resistance of wood to water and sunshine, this could be significantly diminished maintenance costs in many fields from living areas to the maritime industry., Çalışmanın amacı: Bu çalışmada, lignoselülozik yüzeyler için akıllı biyomimetik yapay form oluşturup ahşap malzemenin hidrofobik ve manyetik özellik kazanması amaçlanmıştır.Materyal ve yöntem: Akıllı biyomimetik yapay yüzeyin oluşturulması için Demirli sülfat heptahidrat (FeSO4·7H2O), Manganez (II) klorür (MnCl2.4H2O), Etil alkol (EtOH), Sodyum hidroksit (NaOH) ve Potasyum nitrat (KNO3) kullanılarak masif yüzeye hidrotermal olarak uygulanmıştır. Hidrofobizasyon Oktadesiltriklorosilan (OTS, %95) kullanılarak sağlanmıştır. Modifikasyon çalışmalarını karakterize etmek için Fourier dönüşümü kızılötesi spektroskopisi (FTIR), X-ışını kırınımı (XRD), Taramalı elektron Mikroskopisi (SEM) ve Enerji dağıtıcı x-ışını (EDX) analizleri yapılmıştır. Hidrofobiklik özelliğinin belirlenmesi için su temas açısı (WCA) ve son olarak manyetik özelliklerini belirlemek için UV-Vis spektrometre cihazı kullanılmıştır.Temel sonuçlar: Yapılan karakterizasyon çalışmaları ahşap yüzeyde akıllı biyomimetik yapay form başarılı bir şekilde oluşturulduğunu göstermektedir. Yeni yüzeyin su temas açısı θγ 125° olarak belirlenmiştir. 200-800 nm dalga boyu aralığında absorbsiyon özellik göstermiştir.Araştırma vurguları: Bu çalışma sonucunda üretilen akıllı biyomimetik yapay form ahşabın suya ve güneş ışığına olan dayanımını artırdığı için yaşam alanlarından denizcilik sektörüne kadar birçok alandaki bakım maliyetlerini önemli ölçüde azaltabilir.Anahtar Kelimeler

Aim of study: In this study, a ZnO-based smart artificial nano biomimetic form is created on the wooden surface with the hydrothermal approach to increase the resistance of the wood against moisture and water and provide a more hygienic surface.Material and methods: Zinc borate, Zinc oxide, Sodium hydroxide and Hydrochloric acid were hydrothermally applied to the massive surface to synthesize the ZnO-based nano biomimetic structure on the lignocellulosic surface. The hydrophobization step was achieved using 1H,1H,2H,2H- Perfluorodecyltriethoxysilane. In the characterization step; XRD, EDX, SEM and TGA analyzes were done. WCA analysis was performed to determine the hydrophobicity feature.Main results: ZnO-based nano biomimetic smart surface form with photo catalyst feature created on the wooden surface has provided a water contact angle of θγ 145°.Highlights: Synthesized ZnO-based nano biomimetic smart surface form has given the wooden material a hydrophobic structure. Thanks to the new feature gained by functionalizing the lignocellulosic surface, it is predicted to be preferred in all areas where hygiene is desired., Çalışmanın amacı: Bu çalışmada, hidrotermal yaklaşımla ahşap yüzeyde ZnO esaslı akıllı yapay nano biyomimetik form oluşturularak ahşabın neme ve suya karşı olan direncinin artırarak daha hijyenik bir yüzeye sahip olmasını sağlamaktır.Materyal ve yöntem: ZnO esaslı nano biyomimetik yapının lignoselülozik yüzeyde sentezlenmesi için Çinko borat, Çinko oksit, Sodyum hidroksit ve Hidroklorik asit masif yüzeye hidrotermal olarak uygulanmıştır. Hidrofobizasyon aşamasında 1H,1H,2H,2H-Perfluorodecyltriethoxysilan kullanılarak sağlanmıştır. In the characterization step; XRD, SEM, EDX and TGA analyzes were performed. WCA analysis was performed to determine the hydrophobicity property.Temel sonuçlar: Ahşap yüzeyde oluşturulan foto katalizör özellikli ZnO esaslı nano biyomimetik akıllı yüzey formu θγ 145°’lik su temas açısı sağlanmıştır.Araştırma vurguları: Sentezlenen ZnO esaslı nano biyomimetik akıllı yüzey formu ahşap malzemeye hidrofobik bir yapı kazandırmıştır. Lignoselülozik yüzeyin fonksiyonlandılmasıyla kazandırılan yeni özellik sayesinde hijyen istenen her türlü alanda tercih sebebi olması öngörülmektedir.

Bu çalışmanın amacı, ahşap yüzeyde hidrotermal metod kullanılarak nono boyutta fonksiyonlandırma yapmak ve böylelikle, yüzeyin çevre şartlarına karşı akıllı bir yönelim sergilemesini sağlamaktır. Lignoselülozik yüzeyde iki aşamalı oluşturulan fonksiyonlandırma sürecinin ilk kısmında Demirli sülfat heptahidrat (FeSO4·7H2O), Krom (II) klorür (CrCl2), Sodyum hidroksit (NaOH), Etil alkol (EtOH), ve Potasyum nitrat (KNO3) kimyasalları kullanılarak öncelikle anti-UV özellikli bir yüzey elde edilmiştir. Ikinci basamak olan Hidrofobizasyon kısmında ise Oktadesiltriklorosilan (OTS,%95) kullanılmıştır. Yapılan modifikasyon uygulamalarının karakterizasyonunda Fourier dönüşümü kızılötesi spektroskopisi (FTIR), Taramalı elektron mikroskopisi (SEM), X-ışını kırınımı (XRD) ve Enerji dağıtıcı x-ışını (EDX) enstrümental analizleri kullanılmıştır. Fonksiyonlanan yeni yüzeyin su temas açısı (WCA) ölçümleri yapılarak hidrofobisitesi belirlenmiştir. Anti-UV özellikliği ise UV-Vis spektrometresi tespit edilmiştir. Yapılan karakterizasyon çalışmaları sonucunda, hidrotermal olarak yapılan nano fonksiyonlandırmanın başarılı olduğu kanıtlanmıştır. Yeni yüzeyin su temas açısı θγ 128° olarak ölçülmüştür. Dalga boyu aralığının 200-800 nm olduğu alanda anti-UV özellik sergilemiştir. Fonksiyonlandırma sonrası yüzey değişim parametreleri ISO 4287 standardına göre yapılmıştır. Renk değişim oranları ise ISO 2469 (2014) standartlarına uygun olarak belirlenmiştir., The aim of this study is to make nono-dimensional functionalization on the wooden surface by using hydrothermal method and thus to ensure that the surface exhibits a smart orientation towards environmental conditions. Ferrous sulfate heptahydrate (FeSO4·7H2O), Chromium (II) chloride (CrCl2), Sodium hydroxide (NaOH), Ethyl alcohol (EtOH) and Potassium nitrate (KNO3) chemicals were used in the first part of the two-stage functionalization process on the lignocellulosic surface. Thus, a surface with anti-UV property was obtained. Octadecyltrichlorosilane (OTS, 95%) was used in the second step, Hydrophobization. Fourier transform infrared spectroscopy (FTIR), Scanning electron microscopy (SEM), X-ray diffraction (XRD) and Energy diffuser x-ray (EDX) instrumental analyzes were used to characterize the modification applications. Hydrophobicity was determined by measuring the water contact angle (WCA) of the new functional surface. Its anti-UV feature was determined by UV-Vis spectrometry. As a result of the characterization studies, hydrothermal nano functioning has been proved to be successful. The water contact angle of the new surface was measured as θγ 128 °. It has anti-UV properties in the area where the wavelength range is 200-800 nm. It has anti-UV properties in the area where the wavelength range is 200-800 nm. After functioning, surface change parameters were made according to ISO 4287 standard. Color change rates are determined in accordance with ISO 2469 (2014) standards.

Bu çalışmanın amacı, genellikle yüzey temizliği için kullanılan ultrasonik banyonun ceviz kaplamaların kurutma süresi, yüzey pürüzlülüğü, rengi ve yoğunluğu üzerine olan etkilerinin incelenmesidir. Bu amaçla, özdeş boyutlarda hazırlanan kaplama örnekleri sabit frekansta (40 kHz) üç farklı süre ve sıcaklıkta ayarlı ultrasonik banyo ile ön işleme tabi tutulmuştur. Uygulanan bu üç farklı ultrasonik ön işlem sonrası ceviz kaplamaların yapılarında meydana gelen değişimlerin, kuruma süresine, yoğunluk (g/cm3) değerlerine, ISO 4287 standardına göre yüzey pürüzlülüğü parametrelerine ve ISO 2469 (2014) standartlarına uygun olarak renk parametrelerine olan etkileri incelenmiştir. Elde edilen sonuçlara göre; ceviz kaplama numunelerinin ultrasonik yıkama da en az etkileneceği optimum şartlar; 25°C’de 15 dakika olarak tespit edilmiştir., The aim of this study is to investigate the effects of ultrasonic bath, which is generally used for surface cleaning, on drying time, surface roughness, color and density of walnut veneers. For this purpose, coating samples prepared in identical sizes were pretreated with an ultrasonic bath set at three different times and temperatures at fixed frequency (40 kHz). After these three different ultrasonic pretreatments applied, the effects of changes in the structure of walnut coatings on drying time, density (g/cm3) values, surface roughness parameters according to ISO 4287 standard and color parameters in accordance with ISO 2469 (2014) standards were examined. According to the results obtained; optimum conditions in which walnut veneer samples will be least affected by ultrasonic washing; It was determined as 15 minutes at 25°C.

Bu çalışmanın amacı, çeşitli biyokütle atıklarının ahşap esaslı kompozit yapı malzeme üretimine doğrudan kazanımlarının sağlanmasıdır. Böylelikle mobilya sektörünün milli kaynaklarımız olan ormanlarımız üzerindeki yükün azaltılması amaçlanmıştır. Ek olarak masif ürünler yerine alternatifleri olan ahşap esaslı kompozit türlerinin zenginleştirilmesi hedeflenmiştir. Bu amaçla; muz kabuğu başta olmak üzere, gliserin, mısır nişastası, biber sapı (100 mesh) ve kızılçam odun unu (60 mesh) kullanılarak hazırlanan 16 farklı biyoplastik numunesi üretilmiştir. Daha sonra, hazırlanan bu örneklerin asidik ve bazik ortamdaki çözünmeleri incelenmiştir ve ASTM D 792 standartlarına uygun olarak yoğunluk değerleri tespit edilmiştir. Elde edilen sonuçlara göre; asidik ortamdaki en düşük ve en yüksek çözünme değerleri % 6.7 ve % 61.9 olup sırasıyla G14O8 ve G7O2 numunelerine aittir. Bazik ortamda ise sırasıyla, % 14.3 ile G7O8 ve % 35.7 çözünme değeri ile G7B1 numunesi belirlenmiştir. Üretilen biyoplastik kompozitler arasında yoğunluğu en yüksek olan 2.29 g/cm3 değeri ile G7O8 numunesi, en düşük ise 1.03 g/cm3 ile G7B7 ve G14B7 numunelerinin olduğu tespit edilmiştir., The aim of this study is to provide the direct recovery of various biomass wastes to the production of wood based composite materials. Thus, it is aimed to reduce the burden on our forests, which are the national resources of the furniture sector. In addition, it is aimed to enrich wood-based composite types with alternatives instead of massive products. For this purpose; 16 different bioplastic specimens were produced using banana peel, glycerin, corn starch, pepper stalk (100 mesh) and pine wood flour (60 mesh). Then, the dissolution of these samples in acidic and basic medium were examined and density values were determined in accordance with ASTM D 792 standards. According to the results obtained; The lowest and highest dissolution values in the acidic medium were 6.7% and 61.9%, respectively, belonging to G14O8 and G7O2 samples. In the basic medium, respectively, G7O8 with 14.3 % and G7B1 sample with 35.7% dissolution value were determined. Among the produced bioplastic composites, G7O8 sample had the highest density of 2.29 g/cm3 and G7B7 and G14B7 samples had the lowest value of 1.03 g/cm3.

Bu çalışmanın amacı, petrol türevi ambalajların insansağlığına ve çevreye verdiği zararı en aza indirebilmek için farklı biyokütlelerden elde edilennişasta esaslı çevre dostu alternatif akıllı biyoplastik ve odun biyokompozitambalaj malzemelerinin üretilmesidir. Bu amaçla, üretilen numunelerin sudakiçözünme (%), su alma (%), ASTM D 792 standartlarına göre yoğunluk (g/cm3) ve ISO 4287 standardına göre yüzeypürüzlülüğü değerleri belirlenmiştir. Elde edilen sonuçlara göre; en yüksek veen düşük suda çözünme değerleri sırasıyla % 100 ile D numunesi ve % 8,01 ile Fnumuneleridir. Suda alma (%) değerleri, en yüksek % 242 ile B numunesi en düşükise % 108 değeri ile E numunesi ölçülmüştür. En düzgün yüzeye Ra, Rzve Rmax değerleri ile sırasıyla, 3.53, 18.8 ve 25.1 µm olarak Anumunesi ölçülür iken, yüzey pürüzlülüğünün en fazla olduğu numune ise 10.4,43.8 ve 55.0 µm değerleri ile D numunesinin olduğu belirlenmiştir., The aim of this study is to produce eco-friendly alternativebioplastic and wood biocomposite packaging materials based on starch, derivedfrom different biomasses, in order to minimize the damage caused by petroleumderivative packages to human health and the environment. For this purpose, solubilityin water (%), water absorption (%), density according to ASTM D 792 (g/cm3)and surface roughness values according to ISO 4287 standard were determined. Accordingto the results obtained; the highest and lowest water solubility values aresample D with 100 % and sample F with8.01 %, respectively. The highest and lowest water absorption (%) capacity withvalue of % 242 as sample B and as 108 % with the sample E were measuredrespectively. The most uniform surface was obtained by the values Ra, Rz andRmax, as 3.53, 18.8 and 25.1 µm for sample A while the highest surfaceroughness with respectively as 10.4, 43.8 and 55.0 µm values for sample D wasdetermined.

In this study, the effects of aging on surfaceroughness were investigated by applying aging process on beech wood veneers. Samplesprepared from beech veneers were first subjected to aging after airconditioning in the air conditioning cabinet. Surface roughness values of thesamples were measured by Marsurf M300 according to ISO 4287 standards. Ra, Rzand Rmax values of the test samples were determined. According to the dataobtained, it was determined that the surface roughness values increased withthe increase in aging process time, Buçalışmada, kayın odunu kaplamaları üzerinde yaşlandırma işlemi uygulanarak,yaşlandırmanın yüzey pürüzlülüğü üzerine etkileri araştırılmıştır. Kayınkaplamalardan hazırlanan numuneler öncelikle iklimlendirme kabininde klimatizeedildikten sonra yaşlandırma işlemine maruz bırakılmıştır. Yaşlandırma işlemiuygulanan numunelerin yüzey pürüzlülük değerleri ISO 4287 standartlarına göreMarsurf M300 cihazı ile ölçülmüştür. Test örneklerinin Ra, Rz ve Rmax değerleribelirlenmiştir. Elde edilen verilere göre yaşlandırma işlem süresinin artmasıile yüzey pürüzlülük değerlerinin arttığı belirlenmiştir.

In this study,artificial aging with iron acetate ((CH3COO)2Fe) solutionwas applied to Fir wood and it was aimed to investigate effects of aging time,sanding number and cross section directions on surface roughness and colorchanges. The surfaceroughness parameter values ​​were measured according to ISO 4287 standard andcolor measurement analyzes was performed according to ISO 2469 standard. Accordingto the obtained data, the smoothest surfaces in the radial and tangentialsections were observed in the samples exposed to iron acetate for 15 minutes,respectively, which were sanded with sanders 150 and 80, respectively., Bu çalışmada, Göknar odununa demir asetat ((CH3COO)2Fe)çözeltisi ile yapay yaşlandırma işlemi uygulanmış ve yaşlandırma işlemine maruzbırakılma süresi, zımpara numarası ve kesit yönlerinin yüzey pürüzlülüğü verenk değişimleri üzerine olan etkilerinin araştırılması amaçlanmıştır. Yüzeypürüzlülük parametre değerleri ISO 4287 standardına, renk ölçüm analizleri ISO 2469 standardına göregerçekleştirilmiştir. Elde edilen verilere göre, radyal ve teğet kesitlerdekien düzgün yüzeyler sırasıyla 150 ve 80 numaralı zımparalar ile zımpara işlemiuygulanan 15 dakika demir asetata maruz bırakılan numunelerde gözlemlenmiştir.

Bu çalışmada amaç, polipropilen esaslı odun plastik kompozit (OPK) malzeme üretiminde kullanılan sepiolit mineralinin termal özellikler ve ısı iletkenliği üzerine etkisinin araştırılması olacaktır. Çift vidalı ekstruder ile odun unu, polipropilen ve sepiolit minerali karışımından elde edilen peletler, öğütülmüş ve presleme işlemi yapılarak OPK levhalar üretilmiştir. Üretilen levhaların ısı iletkenliği özelliklerinin (ASTM C 1113-09) yanı sıra Termogravimetrik Analiz (TGA) ve Diferansiyel Taramalı Kalorimetri (DSC) gibi termal özellikleri belirlenmiştir. OPK malzemelerde yangın geciktirici olarak kullanılan sepiolit mineralinin eklenme miktarının artması ile termal ve ısı iletkenliği özelliklerinin geliştiği, kristalizasyon derecesinin ise azaldığı belirlenmiştir., The aim of this study is to investigate the effect of sepiolite mineral used in the production of polypropylene based wood plastic composite (OPK) materials on thermal properties and thermal conductivity. The pellets obtained from the mixture of wood flour, polypropylene and sepiolite minerals with double-screw extruder were milled and pressed to produce OPK boards. Thermal properties such as Thermogravimetric Analysis (TGA) and Differential Scanning Calorimetry (DSC) as well as the thermal conductivity properties of the produced boards (ASTM C 1113-09) have been determined. It has been determined that the addition of the sepiolite mineral used as fire retardant in OPK materials increases the thermal and thermal conductivity properties, while the crystallization degree decreases.

Bu çalışmanın amacı belirli sıcaklık ve sürelerdeısıl işlem uygulanmış orta yoğunluklu lif levhalara (MDF) uygulanan yaşlanmatestinin yüzey pürüzlülüğü üzerine etkilerini araştırmak olacaktır. MDFlevhalara 150, 170 ve 190 oC derece 15, 30 ve 45 dakika ısıl işlemuygulanmıştır. Daha sonra levhalara 30gün yaşlandırma testi uygulanmıştır. Yaşlandırma testi sıcaklık ve bağıl nemebağlı olarak UV yaşlandırma kabininde yapılmıştır. Yüzey pürüzlülüğüparametrelerinin yaşlandırma testinin süresi artıkça belirli oranlarda arttığıbelirlenmiştir. 30 gün yaşlandırma testi uygulanan 190 oC ve 45dakika ısıl işlem uygulanmış test numuneleri yüzey pürüzlülüğü en çok olumsuzetkilenen örnekler olmuştur., The purpose of thisstudy will be to investigate the effects of aging test on the hardness andsurface roughness of the Medium Density Fiberboards (MDF) subjected to heattreatment for a certain temperature and time. MDF boards were heat treated at150, 170 and 190 oC for 15, 30 and 45 minutes, respectively. Then,the boards were subjected to a 30-day aging test. The aging test was carriedout in a UV aging cabinet depending on temperature and relative humidity. Ithas been determined that the surface roughness parameters increase over time inthe aging test. The test samples subjected to the 30-day aging test at 190 oCand the heat treatment for 45 minutes were the most adversely affected samplesof surface roughness

Bu çalışmada, yaşam alanlarında geniş bir kullanıma sahip ceviz kaplamalarının maruz kalabilecekleri asidik ve bazik temizleme ürünlerine karşı yüzeylerinde meydana gelebilecek renk ve morfolojik değişikliklerin incelenmesi amaçlanmıştır. Farklı pH değerlerinde hazırlanan hidroklorik asit (HCI) ve sodyum hidroksit (NaOH) çözeltilerinin ceviz ahşap kaplama levhalarının yüzey pürüzlülüğü ve renk özellikleri üzerine olan etkileri araştırılmıştır. Ceviz kaplama levhaları 10 dakika süreyle asidik pH (1.5, 3.0, 5.0) ve bazik pH (8.0, 11.0 ve 13.5) çözeltilere maruz bırakılmıştır. Levhaların yüzey pürüzlülük ölçümleri ISO 4287, renk ölçüm analizleri ISO 2469 standardına göre gerçekleştirilmiştir. Elde edilen verilere göre, hem asidik hem de bazik ortam da pH değeri düştükçe kaplama levhaların yüzey pürüzlülük parametrelerine (Ra, Rz ve Rmax) ait değerlerin azaldığı belirlenmiştir. Renk ölçümlerinde ise asidik ve bazik ortamda pH değeri düştükçe sarılık derecesinin arttığı belirlenmiştir. Beyazlık ve parlaklık derecesi asidik ortamda etkilenmez iken, bazik ortamda pH değeri yükseldikçe beyazlık ve parlaklık derecelerinde artma olduğu tespit edilmiştir., This study aimed to examine the walnut coating which has a wide range of applications in the living spaces may be exposed to acidic and basic cleaning products that may occur the color and morphological changes. The effects of hydrochloric acid (HCl) and sodium hydroxide (NaOH) solutions prepared at different pH values on the surface roughness and color properties of walnut wood veneer sheets were investigated. The walnut veneer boards were exposed to acidic pH (1.5, 3.0, 5.0) and basic pH (8.0, 11.0 and 13.5) solutions for 10 min. Surface roughness measurements of boards were performed according to ISO 4287, color measurement analyzes according to ISO 2469 standard. According to the obtained results, the values of surface roughness parameters (Ra, Rz and Rmax) of the walnut veneer boards decreased as the pH value was decreased in both acidic and basic media. In color measurements, it was determined that the degree of yellowness increases as the pH value decreases in acidic and basic medium. While the whiteness and brightness levels were not affected in the acidic medium, it was found that the whiteness and brightness were increased in the basic medium as the pH value increased.

Buçalışmanın amacı yüksek yoğunluklu lif levha üretiminde kullanılan yanmayıgeciktirici etkiye sahip muskovit mineralinin yüzey pürüzlülüğü üzerineetkisini araştırmak olacaktır. Muskovit minerali tam kuru lif ağırlığına göre%3, 6, 9, 12 ve 15 oranlarında üre formaldehit tutkalı (%10) ile muameleedilmiş %50 okaliptüs ve %50 akçaağaç lifleri arasına homojen bir şekilde ilaveedilmiş ve karıştırılmıştır. Karışım sıcakpreskullanılarak8 mm kalınlığındayüksek yoğunluklu lif levhalar (HDF) üretilmiştir. Elde edilen levhaların yüzeypürüzlülüğü parametreleri Marsurf M300 cihazı ile ölçülmüştür ve yüzeypürüzlülüğü parametre (Ra, Rz, ve Rmax) değerleri ISO 4287 standardına göre belirlenmiştir.Elde edilen sonuçlara göre levha üretiminde muskovit mineralinin kullanımoranın artması ile yüzey pürüzlülüğünün de arttığı belirlenmiştir. En yüksekyüzey pürüzlülük değerleri %15 muskovit ilave edilmiş numunelerde tespit edilmiştir., Bu çalışmanın amacı yüksek yoğunluklu lif levha üretiminde kullanılan yanmayı geciktirici etkiye sahip muskovit mineralinin yüzey pürüzlülüğü üzerine etkisini araştırmak olacaktır. Muskovit minerali tam kuru lif ağırlığına göre %3, 6, 9, 12 ve 15 oranlarında üre formaldehit tutkalı (%10) ile muamele edilmiş %50 okaliptüs ve %50 akçaağaç lifleri arasına homojen bir şekilde ilave edilmiş ve karıştırılmıştır. Karışım sıcakpreskullanılarak8 mm kalınlığında yüksek yoğunluklu lif levhalar (HDF) üretilmiştir. Elde edilen levhaların yüzey pürüzlülüğü parametreleri Marsurf M300 cihazı ile ölçülmüştür ve yüzey pürüzlülüğü parametre (Ra, Rz, ve Rmax) değerleri ISO 4287 standardına göre belirlenmiştir. Elde edilen sonuçlara göre levha üretiminde muskovit mineralinin kullanım oranın artması ile yüzey pürüzlülüğünün de arttığı belirlenmiştir. En yüksek yüzey pürüzlülük değerleri %15 muskovit ilave edilmiş numunelerde tespit edilmiştir.

Buaraştırma; ortaokul 8. Sınıf matematik dersinde Kareköklü İfadeler konusununöğretiminde kavram haritası destekli eğitiminin geleneksel öğretim yönteminekıyasla öğrenci başarısına ve matematiğe yönelik tutumlarına etkisinibelirlemek amacıyla yapılmıştır. Çalışmanın örneklemini 26’sı kontrol, 27’sideney grubunda olmak üzere toplam 53 öğrenci oluşturmaktadır. Ön-test son-testkontrol gruplu yarı deneysel desen kullanılan bu çalışmada elde edilen verilerSPSS istatistik paket programında ilişkili t-testi ve ilişkisiz t-testikullanılarak analiz edilmiştir. Araştırma sonucunda; “Kareköklü İfadeler”konusunu kavram haritası destekli öğretimle işlemenin, öğrencilerin akademikbaşarısını ve matematiğe yönelik tutumlarını arttırdığı sonucuna ulaşılmıştır.

ÖzetÇalışmanın amacı: Bu çalışmanın amacı, yüzeykaplamasına eklenen amonyum polifosfat (APP) ve borik asidin (BA) yanma direnciüzerine etkisini belirlemek olacaktır.Çalışmaalanı: Ahşap esaslı levhalarda, yanmazlıközelliğinin geciktirilmesini sağlamakMateryalve Yöntem:Yüzey kaplama karışımı kalsit, tutkal, yanmayı geciktirici kimyasallar ve sukarışımından oluşmaktadır. Karışım içindeki tutkal (%10), BA ve APP (%1, %3 ve%5) oranı, kalsitin tam kuru ağırlığına göre belirlenmiştir. Yüzeyi 0.25 mmkalınlıktaki karışım ile kaplanmış MDF test örneklerinin yanma testleri ASTM E69 standartlarına göre yapılmıştır. Örneklerin ağırlık kaybı miktarları dijitalterazi ile belirlenirken, sıcaklık, O2,CO ve NOdeğerleri Testo 340 M gaz analizörü ile ölçülmüştür. Her test için 30 saniyearalıklar ile 20 ölçüm yapılmıştır.Sonuçlar: Elde edilen sonuçlara göre; kalsit ilekaplamanın yanı sıra yanmayı geciktirici (FR) kimyasal eklenmesi yanmadirencini artırmıştır. En düşük ağırlık kaybı APP %5 ile muamele edilmişörneklerde bulunmuştur.Araştırma vurguları: Ahşap esaslılevhaların yüzeylerinin kaplanması ve bu kaplama içerisine FR kimyasalı vemineral eklenmesi yanma özelliklerini geciktirmektedir, Aim of study: The purpose of this study weredetermined the effect of ammonium polyphosphate (APP) and boric acid (BA) assurface coating materials on combustion resistance of MDF panels. Area of study: To ensure the retardation ofcombustion properties of wood based panelsMaterial and Methods: Surface coating mixture consists ofcalcite, glue, fire retardant (FR) and water. The amount of glue (10%), APP andBA (1%, 3% and 5%) in the mixture was determined by the oven dry weight ofcalcite. Combustion tests of Medium Density Fiberboard (MDF) test specimenscoated with 0.25 mm thickness of this mixture were carried out according toASTM E 69 standards. Temperature, O2, CO and NO contents of sampleswere measured with Testo 340 M gas analyzer while weight loss was measured withdigital scales. For each test, 20 measurements were recorded at intervals of 30seconds.Main results: According to the obtained results,besides calcite coating, the increase of FR addition rate increased theresistance of combustion. It was found that the weight loss of the samplestreated with APP 5% was the lowest (66,7%).Research highlights: The coating of the surfaces ofwood-based boards and the addition of FR chemistry and mineral to this coatingdelays the burning properties

MDF levhaların yüzeyleri kalsit, yanmayı geciktirici (FR) vetutkal karışımı ile kaplanmıştır. Daha sonra yanma dayanımı özellikleriaraştırılmıştır. Kalsitin tam kuru ağırlığına oranla, karışıma %1, %3 ve %5 oranlarındayanmayı geciktirici olarak bilinen boraks ve muskovit ilave edilmiştir. Yanmakarakteristiklerinin belirlenebilmesi için, numunelerin yanma testleri ASTM E69 standardına göre yapılmıştır. Test örneklerinin, ağırlık kaybı, sıcaklık,O2, CO ve NO gaz miktarları ölçülmüştür. Ölçümler her 30 saniyede birkaydedilmiştir. Boraks %5 kimyasalı, ağırlık kaybı (%74.5) ve O2 miktarı (%20.5) üzerine en olumlu etkiyi yaparken,muskovit %5 kimyasalı ise sıcaklık (289 oC) ve NO miktarı (342 ppm) üzerinedaha fazla etki etmiştir. Yüzey kaplamasında kullanılan boraks ve muskovit,ilave edilme oranına bağlı olarak yanma performansı üzerine olumlu etkiyapmışlardır., In this study, the surfaces of MDF were coated with amixture of calcite, fire retardant (FR) and glue. Then the properties of MDFboards combustion resistance were investigated. Borax and muscovite, known asflame retardants, were added to the mixture at 1%, 3% and 5% relative to theoven dry weight of calcite. The burning tests of the samples were carried out accordingto ASTM E 69 standard so that the combustion characteristics could bedetermined. The weight loss, temperature, O2, CO and NO gas emissionsquantities of the test samples were measured. The measurements were recordedevery 30 seconds. Borax had the most positive effect on weight loss (74.5%) andO2 amount (20.5%), while muscovite 5% chemistry had a greater effect ontemperature (289 oC) and NO amount (342 ppm). Borax and muscovite used insurface coating have been positively influenced on burning performancedepending on addition rate.

Buçalışmanın amacı orta yoğunluklulevhanın (MDF) yüzey pürüzlülüğü üzerine ısıl işlemin etkisini araştırmaktır.Ticari olarak üretilen MDF levhalar 170 oC 190 oC ve 210 oCde kurutma fırınında ısıl işlem uygulanmıştır. Isıl işlemin her bir sıcaklıkparametresi için 15, 30 ve 45 dakika belirlenmiştir. Levhaların yüzeypürüzlülüğü testleri ISO 4287’ ye göre ölçülmüştür. Test örneklerinin ortalamapürüzlülük (Ra), on nokta pürüzlülük ortalama değeri (Rz)ve en büyük pürüzlülük değeri (Rmax) Marsurf M300 cihazı ile iğnetaramalı yöntem ile ölçülmüştür. Sıcaklık ve sürenin artması ile MDFlevhalarının yüzey pürüzlülüğünün iyileştiği tespit edilmiştir. 210 oCve 45 dakika ısıl işlem görmüş levhalar Ra 3.57, Rz 23.28ve Rmax 27.28 μm değerleri ile en pürüzsüz yüzeye sahip olduklarısaptandı. Sonuçlar, sıcaklığın ve sürenin artması ile MDF levhaların yüzeypürüzlülüğünün olumlu etkilendiğini ortaya çıkarmıştır., The objective of this study was to investigate the effects of heattreatment on the surface roughness of medium density fiberboard (MDF) panelswith 8 mm thickness. Commercially manufactured MDF panels were applied withheat treatment at 170, 190, and 210 oC with 15, 30 and 45 minute inthe oven, respectively. The surface roughness of the panels was measured inaccordance with ISO 4287. The average roughness (Ra), ten pointaverage roughness value (Rz) and maximum surface roughness (Rmax)were measured by using Marsurf M300 test device with the stylus method. MDFboards with increasing temperature and time have been found to improve thesurface roughness. Samples applied heat treatment with 45 min at 210 oChad the smoothest surface with Ra 3.57, Rz 23.28 and Rmax27.28 μm,respectively. Results revealed that the surface quality of the MDF panelsimproved with increasing heat treatment and duration.

In this study, the coefficients of thermal expansion of solid wood and laminated wood materials preparedfrom beech (Fagus orientalis L.), poplar (Populus x euramericana I-214) and eucalyptus (Eucalyptus grandisW. Hill ex Maiden) species were determined. The experiments were made on the sapwood and heartwood ofsolid wood material, separately. Laminated wood materials were produced from 3 mm thickness rotary peeledveneer using UF (urea-formaldehyde) and PF (phenol-formaldehyde) adhesive. The tests were performedbetween -10 and +40 ºC temperature interval. In tangential direction, the lowest coefficient of thermal expansionwas measured on the poplar heartwood (1.88x10–5 ºC–1) and the highest coefficient of thermal expansion wasmeasured on the laminated wood made from eucalyptus used PF (4.66x10–5 ºC–1). The results showed thatlaminated materials produced from poplar wood has higher coefficient of thermal expansion than solid poplarwood. The differences between solid and laminated wood from the beech and eucalyptus weren’t statisticallysignificant., Bu çalışmada, kayın (Fagus orientalis L.), kavak (Populus x euramericana I-214) ve okaliptüs(Eucalyptus grandis W. Hill ex Maiden) odunlarından hazırlanan masif ağaç malzeme ve lamine ağaçmalzemelerin teğet yönde ve liflere paralel yönde ısıl genleşme katsayıları belirlenmiştir. Denemeler masif ağaçmalzemelerde öz ve diri odundan elde edilen, lamine malzemelerde 3 mm kalınlıktaki soyma kaplamalarla ÜF(üre-formaldehit) ve FF (fenol-formaldehit) tutkalları kullanılarak üretilen lamine ağaç malzemeden elde edilendeneme örnekleri üzerinde ve -10 ile +40 °C sıcaklık aralığında yapılmıştır. Teğet yönde en düşük termikgenleşme katsayısı kavak öz odununda (1.88x10–5 ºC–1) ve en yüksek FF ile üretilmiş okaliptüs lamine ağaçmalzemede ölçülmüştür (4.66x10–5 ºC–1). Sonuçlar, teğet yönde kavak odunundan üretilen lamine malzemeninmasif ağaç malzemeden daha yüksek termik genleşme katsayısına sahip olduğunu, kayın ve okaliptüste ise masifağaç malzeme ile lamine ağaç malzeme arasındaki farkların istatistiksel olarak önemsiz olduğunu göstermiştir.

The aim of this study is to determine the effects of certain fire retardant chemicals on mold resistance of laminate flooring. As a source of fiber for high density fiberboard (HDF) panels were used a mixture of %50 yellow pine and beech fibers. HDF panels were produced in 6,5 mm thickness by adding fire retardant chemical materials into fiber. In proportion to complete dry fiber essence fire retardant chemicals borax (BX), boric acid (BA), ammonium polyphosphate (APP) and alpha-x (AX) in pulverized form were added in the ratios of 3%, 6%, and 9%. Afterwards, surfaces of produced HDF boards were coated with overlay, decor and balance sheets and then laminated floorings boards were produced.Mold resistance of produced laminate flooring was explored. In the test, Aspergillus niger and Aureobasidium pullulans mold were used. To detect mold resistance, the test was made according to ASTM D4445–10. It was determined that 3%, 6%, and 9% additions of fire retardant (FR) chemicals enhanced mold resistance of laminat flooring. As a result, it was ascertained that type of chemical, Bu çalışmanın amacı laminat parkede kullanılan yanmayı geciktirici bazı kimyasal maddelerin küf mantarı üzerine etkilerini belirlemektir. Yüksek yoğunlukta lif levhalar (HDF) için lif kaynağı olarak %50 kayın ve %50 sarıçam kullanılmıştır. Liflerin arasına yanmayı geciktirici kimyasal maddeler eklenerek 6,5 mm kalınlıkta HDF levhalar üretilmiştir. Boraks, borik asit, amonyum polifosfat ve alfa-x yanmayı geciktirici kimyasalları tam kuru lif miktarına oranla %3, %6 ve %9 oranlarında pulverize şekilde eklenmiştir. Daha sonra elde edilen HDF levhaların üzeri overlay, dekor ve balans kâğıtları ile kaplanmış ve laminat parke levhaları üretilmiştir.Üretilen laminat parkenin küf mantarı direnci araştırılmıştır. Küf mantarı olarak Aspergillus niger and Aureobasidium pullulans mantarları kullanılmıştır. Küf mantarı direncini belirlemek için testler ASTM D 4445–10 standardına göre yapılmıştır. Laminat parkede yanmayı geciktirici kimyasal maddelerin %3, %6 ve %9 oranlarında eklenmesi küf mantarı direncini artırdığı belirlenmiştir. Sonuç olarak, yanmayı geciktirici kimyasal maddelerin türü ve konsantrasyon oranı üretilen laminat parkede küf mantarı direnci üzerine etkili olmuştur.