Search

Zn 0.95− x Co 0.05 Cu x O (ZCCO, where x = 0, 0.005, 0.01 and 0.015) thin films were deposited on Si (1 0 0) substrates by pulsed laser deposition technique. Crystal structures, surface morphologies, chemical compositions, bonding states and chemical valences of the corresponding elements for ZCCO films were characterized by X-ray diffraction (XRD), field emission scanning electron microscope (FESEM) and X-ray photoelectron spectroscopy (XPS). XRD and FESEM results indicate that crystallite sizes of the highly (0 0 2)-oriented ZCCO films slightly decrease with increasing Cu content. When the Cu content increases from 0 to 0.015, Zn 2 p 3/2 , Co 2 p , Cu 2 p 3/2 and O 1 s peaks of the ZCCO film shift towards higher or lower binding energy regions, and the reasons for these chemical shifts are investigated by fitting the corresponding XPS narrow-scan spectra. Both in-plane and out-of-plane magnetization-magnetic field hysteresis loops of the ZCCO films reveal that all the films have room temperature ferromagnetisms (RTFMs). The conceivable origin of the RTFM is ascribed to the combined effects of the local structural disorder resulted from (Co 2+ , Cu 2+ , Cu 1+ )-cations which substitute Zn 2+ ions in the ZnO matrices, ferromagnetic coupling between coupled dopant atoms caused by Co 2+ (3 d 7 4 s 0 ) and Cu 2+ (3 d 9 4 s 0 ) spin states, and exchange interactions between the unpaired electron spins originating from lattice defects induced by Cu doping in the Zn 0.95 Co 0.05 O matrices.

Ba0.9Sr0.1TiO3 (BST) thin films were deposited on fused quartz and Pt/TiN/Si3N4/Si substrates by radio frequency magnetron sputtering technique. Microstructure and chemical bonding states of the BST films annealed at 700 °C were characterized by field emission scanning electron microscopy, X-ray photoelectron spectroscopy, glancing angle X-ray diffraction and Raman spectrum. Optical constants including refractive indices, extinction coefficients and bandgap energies of the as-deposited BST film and the BST films annealed at 650, 700 and 750 °C, respectively, were determined from transmittance spectra by envelope method and Tauc relation. Dielectric constant and remnant polarization for the BST films increase with increasing annealing temperature. Leakage current density-applied voltage (J–V) data indicate that the dominant conduction mechanism for all the BST capacitors is the interface-controlled Schottky emission under the conditions of 14 V

Bi1−x Ce x FeO3 (x = 0, 0.05, 0.1, 0.15 and 0.20) (BCFO) thin films were deposited on Pt/TiN/Si3N4/Si substrates by sol–gel technique. Crystal structures, surface chemical compositions and bonding states of BCFO films were investigated by X-ray diffraction and X-ray photoelectron spectroscopy (XPS), respectively. Compared to BiFeO3 (BFO) counterparts, the fitted XPS narrow-scan spectra of Bi 4f7/2, Bi 4f5/2, Fe 2p3/2, Fe 2p1/2 and O 1s peaks for Bi0.8Ce0.2FeO3 film shift towards higher binding energy regions by amounts of 0.33, 0.29, 0.43, 0.58 and 0.49 eV, respectively. Dielectric constants and loss tangents of the BCFO (x = 0, 0.1 and 0.2) film capacitors are 159, 131, 116, 0.048, 0.041 and 0.035 at 1 MHz, respectively. Bi0.8Ce0.2FeO3 film has a higher remnant polarization (P r = 2.04 μC/cm2) than that of the BFO (P r = 1.08 μC/cm2) at 388 kV/cm. Leakage current density of the Bi0.8Ce0.2FeO3 capacitor is 1.47 × 10−4 A/cm2 at 388 kV/cm, which is about two orders of magnitude lower than that of the BFO counterpart. Furthermore, Ce cations are feasibly substituted for Bi3+ in the Bi0.8Ce0.2FeO3 matrix, possibly resulting in the enhanced ferroelectric properties for the decreased grain sizes and the reduced oxygen vacancies.

Ba0.65Sr0.35TiO3 (BST) thin films were deposited on Pt/Ti/SiO2/Si substrates by radio frequency magnetron sputtering technique. X-ray photoelectron spectroscopy (XPS) depth profiling data show that each element component of the BST film possesses a uniform distribution from the outermost surface to subsurface, but obvious Ti-rich is present to BST/Pt interface because Ti4+ cations are partially reduced to form amorphous oxides such as TiOx (x

Sol-gel-derived (Ba0.65,Sr0.35)TiO3 (BST) thin films were etched in CF4∕Ar and CF4∕Ar∕O2 plasmas using magnetically enhanced reactive ion etching technology. Experimental results show that adding appropriate O2 to CF4∕Ar can better the etching effects of BST films for the increase of etching rate and decrease of etched residues. The maximum etching rate is 8.47nm∕min when CF4∕Ar∕O2 gas-mixing ratio is equal to 9∕36∕5. X-ray photoelectron spectroscopy (XPS) data confirm accumulation of reaction products on the etched surface due to low volatility of reaction products such as Ba and Sr fluorides, and these residues could be removed by annealing treatment. The exact peak positions and chemical shifts of the interested elements were deduced by fitting XPS narrow-scan spectra with symmetrical Gaussian-Lorentzian product function for Ba 3d, Sr 3d, and O 1s peaks, meanwhile asymmetrical Gaussian-Lorentzian sum function was used to fit Ti 2p doublet to adjust the multiple splitting and/or shake-up process of tran...