The development of dental materials needs to be supported with sound evidence. This in vitro study aimed to measure the fracture toughness of a short fibre-reinforced composite (sFRC), at differing thicknesses. In this study, 2 mm, 3 mm and 4 mm depths of sFRC were prepared. Using ISO4049, each preparation was tested to failure. A total of 60 samples were tested: 10 samples for each combination of sFRC and depth. Fractured samples were viewed, and outcomes were analysed. EXF showed greater toughness than EXP, with a mean of 2.49 (95%CI: 2.25, 2.73) MPa.m1/2 compared to a mean of 2.13 (95%CI: 1.95, 2.31) MPa.m1/2, (F(1,54) = 21.28; p < 0.001). This difference was particularly pronounced at 2 mm depths where the mean (95%CI) values were 2.72 (2.49, 2.95) for EXF and 1.90 (1.78, 2.02) for EXP (Interaction F(2,54) = 7.93; p < 0.001). Both materials performed similarly at the depths of 3 mm and 4 mm. The results for both materials were within the accepted fracture toughness values of dentine of 1.79–3.08 MPa.m1/2. Analysis showed crack deflection and bridging fibre behaviour. The optimal thickness at the cavity base for EXF was 2 mm and for EXP 4 mm. Crack deflection and bridging behaviour indicated that restorations incorporating sFRCs are not prone to catastrophic failure and confirmed that sFRCs have similar fracture toughness to dentine. sFRCs could be a suitable biomimetic material to replace dentine. [ABSTRACT FROM AUTHOR]

This study evaluated the properties of 3D-printed Onyx–fiberglass composites. These composites were 3D-printed with zero, one, two, three, and four layers of fiberglass. Ten samples of each configuration were printed for the tensile and flexural tests. The average tensile strength of the Onyx specimens was calculated to be 44.79 MPa, which increased linearly by approximately 20–25 MPa with each additional fiberglass layer. The elastic moduli calculated from the micromechanics models were compared with the experimental values obtained from the tensile tests. The experimental elastic modulus increased more significantly than the model prediction when more fiberglass layers were added. The flexural modulus of Onyx was 17.6 GPa, which increased with each additional fiberglass layer. This quantitative analysis of composites fabricated using 3D printing highlights their potential for commercialization and industrial applications. [ABSTRACT FROM AUTHOR]

This article deals with the possibility of using 3D-printed models as an input for the production of a mould for cast iron castings. This new progressive process is significantly faster (with sufficient accuracy) compared to the current way of making models for moulds. The need to create a wooden model is removed by this process. The quality of this wooden model was highly dependent on the experience and qualifications of the worker. This article describes the manufacturing process of the model and mould in detail. The key dimensions of the final parts are compared with the model and, thus, the accuracy of the chosen procedure is verified. A 3D-printing technology known as Multi Jet Fusion (MJF) was used to produce the model. The material used for the production of the model is polyamide PA12 with 40% glass fibre filling. This material has sufficient structural and strength properties to be used for the given application. Taking into account the dimensions of the part and the printing space of the printer, it was necessary to structurally modify and divide the part. The inlet cone of a turbine is used as an example This cone is produced from grey cast iron as standard. [ABSTRACT FROM AUTHOR]

In recent years, wind energy has begun to receive a significant amount of attention as clean energy is utilised and demanded in large quantities, resulting in a sharp increase in the use of wind turbines. The demand for wind turbines has gradually risen due to the clean and recyclable nature of wind energy. The current blade life of wind turbines in China is about 20 years, which means that the disposal of obsolete used blades can become a difficult problem in the future. Therefore, this study is of great significance to explore the regeneration performance of the blades after recycling and disposal. In this paper, wind turbine blades were mechanically recycled into recycled macrofibres, which were added to concrete as a reinforcing material to make wind impeller fibre concrete (WIC), and the three proportion ratios of 1%, 1.5%, and 2% were explored to compare the performance. The performance of WIC was also evaluated and its performance was compared to that of glass fibre concrete (GC). In addition, the material physical properties of second-generation recycled aggregate concrete (RAC) based on WIC were explored. The strength and peak strain variations and their causal mechanisms were analysed both macroscopically and microscopically by means of the classical mechanical tests (compression and bending tests), SEM, and XRD. The results show that the compressive strength of WIC was negatively correlated with the fibre content and increased by 6.04–18.12% compared to that of ordinary concrete (OG), with a maximum of 19.25 MPa; the flexural strength was positively correlated with the fibre content, with an increase of 5.37–18.5%. The microstructural analysis confirmed the macroscopic results and the intrinsic model better validated the experimental results. [ABSTRACT FROM AUTHOR]

Traditional rock wool fibres are susceptible to crystallization and pulverization. To mitigate this, glass fibres were produced from iron ore waste (IOW). When the ratio of Fe2+ and Fe3+ is 1:3 and the Al2O3 content is 10 wt.%, increasing the FexOy content enhances the thermal stability.At an FexOy content of 17–19% and an Al2O3 content of 10–13%, the glass transition temperature (Tg) peaked. Increasing the FexOy content from 10% to 20% enhanced the stability of Si-O and Al-O bonds and increased bridged oxygen, stabilizing the structure. Here, Fe2+ balances structural charges, while Fe3+ replaces some Al atoms in the network. When the Al2O3 content is 10–13% and the FexOy content is 17–19%, the thermal stability of the IOW rock glass reaches its optimal level. At 20% FexOy content, the structure becomes three-dimensional and cyclic, increasing polymerization. Consequently, incorporating FexOy alongside a 10% Al2O3 content improves thermal stability, supporting the development of high-stability rock wool from IOW. This approach also enhances the refractory properties of rock wool fibres within the FexOy-Al2O3-SiO2-MgO-CaO system. [ABSTRACT FROM AUTHOR]

This study examines the process of using injection moulding to join two different materials to manufacture bi-component moulded products with improved performance characteristics. The two-component process, which combines the advantages of two different technologies—the high efficiency of the injection moulding process and the excellent mechanical properties of long glass fibre composites produced by resin transfer moulding (RTM) technology—offers a particular advantage and improved applicability of the prepared lightweight products in both the automotive and aerospace sectors. The composite studied here consists of Elium® thermoplastic resin (30%) reinforced with unwoven glass fibre fabric (70%) using the RTM process. The Elium® composite sample is consequently used as an insert overmoulded with polybutylene terephthalate (PBT) homopolymer reinforced with 20% w/w of short glass fibre through injection moulding. The influence of different mould temperatures and surface treatments on the adhesion between the materials used is investigated by evaluating the mechanical performance using tensile shear strength tests. It was found that while an increase in mould temperature from 40 °C to 120 °C resulted in a doubling of the initial average bond strength between untreated Elium® RTM inserts and overmoulded PBT parts (0.9 MPa), sandblasting the inserts ensured a further tripling of the bond strength of the composites to a value of 5.4 MPa. [ABSTRACT FROM AUTHOR]

In this article, an L-shaped three-dimensional (3D) braided piezoelectric composite energy harvester (BPCEH) is established, which consists of an elastic layer composed of a 3D braided composite, flanked by upper and lower layers of piezoelectric material and two tuning mass blocks. Glass fiber and epoxy resin are used to produce a 3D braided composite. This L-shaped 3D BPCEH is mechanically designable and can be adapted to different work requirements by varying the braided angle of the 3D braided composite layer. The material parameters of 3D braided composites are predicted for different braided angles by means of a representative volume element (RVE). Electro-mechanical coupled vibration equations for the L-shaped 3D BPCEH are established. The impact of braided angles on voltage and power output is discussed in this article. Simulations using finite element method are conducted to analyze the voltage and power output responses at various braided angles. In addition, the effects of the mass of mass block B and the length of the beam on the output performance of the L-shaped 3D BPCEH are analyzed. [ABSTRACT FROM AUTHOR]

The complex air environment makes it urgent to build good and safe indoor environments, and the study and application of new materials have become the focus of current research. In this study, we tested and analyzed the structural parameters and filtration performances of the four most commonly used new filter materials in the current market. The results showed that all four new filter materials showed a trend of first increasing and then decreasing their filtration efficiency with an increase in filtration velocity. The filtration efficiency of the materials was as follows: PTFE > glass fiber > nanomaterial > electret. The filtration efficiency of all materials reached its maximum when the filtration velocity was 0.2 m/s. The filtration efficiency of the PTFE for PM10, PM2.5, and PM1.0 was higher than that of the other three materials, with values of 0.87% to 24.93%, 1.21% to 18.69%, and 0.56% to 16.03%, respectively. PTFE was more effective in capturing particles smaller than 1.0 μm. Within the testing velocity range, the resistance of the filter materials was as follows: glass fiber > PTFE > electret > nanomaterial, and the resistance of the four materials showed a good fitting effect. It is also necessary to match the resistance with the filtration efficiency during use, as well as to study the effectiveness of filter materials in blocking microorganisms and absorbing toxic gases. Overall, PTFE showed the best comprehensive performance, as well as providing data support for the selection of related materials or the synthesis and research of filter materials in the future. [ABSTRACT FROM AUTHOR]

Short glass fibers are generally used in posterior dental restorations to enhance the mechanical properties and improve the material microstructure. Two resin-based composites (S0 and SF) were formulated and characterized to investigate the influence of zirconium in their characteristics and properties. The organic part of the investigated materials was the same (BisGMA, TEGDMA, and a photochemical polymerization system), and in the inorganic part, besides quart, glassA, and hydroxylapatite with Zn, sample S0 contained strontium glass with zirconium and sample SF contained fiber powder of chopped zirconium. The samples were characterized by the degree of conversion (DC), mechanical properties, water sorption (WS), scanning electron microscopy (SEM), atomic force microscopy (AFM) before and after the WS test, and antimicrobial properties. The results obtained were subjected to one-way ANOVA and Tukey's statistical tests. Both samples had a high DC. Regarding the mechanical properties, both samples were very similar, except DTS, which was higher for the composite without fibers. After 14 days, the WS value of the SF sample was lower than that of the S0 sample. Water caused significant changes in the topography of the SF sample, but thanks to its antimicrobial properties and the diffusion phenomenon, SF had a more pronounced antimicrobial effect. This study shows that the addition of appropriate amounts of Sr-Zr-glass powder gives the material in which it is added similar properties to material containing chopped zirconium glass fiber powder. According to the antimicrobial test results, resin composites containing experimental zirconia fillings can be considered in future in vitro clinical studies for posterior reconstructions with significantly improved mechanical properties. [ABSTRACT FROM AUTHOR]

Standard glass fiber filter media were chemically modified with suitably chosen surface-active agents. The aim of these modifications was to improve the three fundamental filtration performance characteristics, namely, to increase the separation efficiency, reduce the differential pressure (∆P) and increase the dirt holding capacity (DHC). The increase in separation efficiency was considered quantitatively in terms of changes in the work of adhesion between the contaminant and the modified media substrate derived from the contact angle measurements. The experimental confirmation of this behavior was demonstrated by an improved separation efficiency especially for particles in the smaller size ranges, well below the mean porosity of the original substrate. In addition, the effect of different surface modifications, especially those of the opposite ends of the surface energy values, has clearly manifested itself in the experimental results of separation efficiency derived from the multipass evaluations. Collectively, the obtained contact angle (surface energy) and separation efficiency results are strongly indicative of a wide range of filtration performance enhancements that can be achieved through suitably chosen surface-active modification of standard substrate materials. [ABSTRACT FROM AUTHOR]

Various modifications of standard glass fiber filtration media using electrospun PA66 nanofibers are described. PA66 were selected because they were readily available from commercial sources. Other polymers, such as PP, PET and PBT, could also be used. The first set of samples was prepared by mixing the nanofibers at two, three and five weight percent with glass fibers, and the second by laying the same proportion of the nanofibers directly onto the downstream side of the substrate. The aim of these modifications was to improve the three most basic functionalities of filter media, the separation efficiency, the differential pressure (ΔP) and the dirt holding capacity (DHC). The modified media samples were evaluated with the standard textile characterization techniques and filtration performance evaluation procedures. The results showed differences in the several tens of percentage points achieved with the two modification methods. Moreover, additional differences in performance were observed depending on the percentage of nanofibers admixed to the substrate. These differences were most apparent in the filtration efficiency and the DHC, both by several percentage points, with no apparent effect on the ∆P. The results strongly suggest that the preparation of new filter media by incorporating nanofibers directly into the matrix can result in significant improvements in filtration performance characteristics. [ABSTRACT FROM AUTHOR]

This study experimentally investigates the influence of metal chips and glass fibers on the mode I fracture toughness, energy absorption, and tensile strength of polymer concretes (PCs) manufactured by waste aggregates. A substantial portion of the materials employed in manufacturing and enhancing the tested polymer concrete are sourced from waste material. To achieve this, semi-circular bend (SCB) samples were fabricated, both with and without a central crack, to analyze the strength and fracture behavior of the composite specimens. The specimens incorporated varying weight percentages comprising 50 wt% coarse mineral aggregate, 25 wt% fine mineral aggregate, and 25 wt% epoxy resin. Metal chips and glass fibers were introduced at 2, 4, and 8 wt% of the PC material to enhance its mechanical response. Subsequently, the specimens underwent 3-point bending tests to obtain tensile strength, mode I fracture toughness, and energy absorption up to failure. The findings revealed that adding 4% brass chips along with 4% glass fibers significantly enhanced energy absorption (by a factor of 3.8). However, using 4% glass fibers alone improved it even more (by a factor of 10.5). According to the results, glass fibers have a greater impact than brass chips. Introducing 8% glass fibers enhanced the fracture energy by 92%. However, in unfilled samples, aggregate fracture and separation hindered crack propagation, and filled samples presented added barriers, resulting in multiple-site cracking. [ABSTRACT FROM AUTHOR]

It is vital to maximize the safety of outdoor constructions, airplanes, and space vehicles by protecting against the impact of airborne debris from increasing winds due to climate change, or from bird strikes or micrometeoroids. In a widely-used compression-molded short glass fiber polyester bulk-molded compound (SGFRP-BMC) with 55% wt. CaCO3 filler, the center of the mother panel has lower impact strength than the outer sections with solidification texture angles and short glass fiber (SGF) orientations being random from 0 to 90 degrees. Therefore, a new double-step process of: (1) reducing commercial fiber length without change in molding equipment; followed by a (2) 0.86 MGy dose of homogeneous low-voltage electron beam irradiation (HLEBI) to both sides of the finished samples requiring no chemicals or additives, which is shown to increase the Charpy impact value (auc) about 50% from 6.26 to 9.59 kJm−2 at median-accumulative probability of fracture, Pf = 0.500. Shortening the SGFs results in higher fiber spacing density, Sf, as the thermal compressive stress site proliferation by action of the CTE difference between the matrix and SGF while the composite cools and shrinks. To boost impact strength further, HLEBI provides additional nano-compressive stresses by generating dangling bonds (DBs) creating repulsive forces while increasing SGF/matrix adhesion. Increased internal cracking apparently occurs, raising the auc. [ABSTRACT FROM AUTHOR]

Considering the different structural strength requirements of different parts of fiberglass yachts, carbon fiber/glass fiber hybrid reinforcement can be applied to the skins of sandwich panels in special areas. This paper designs and prepares 12 foam sandwich panel samples composed of pure carbon fiber, a carbon fiber/glass fiber hybrid, pure glass fiber skin, and PVC and SAN foam sandwich, with reference to the layup structure of the outer panel of a fiberglass yacht. Through a comparative analysis of low-speed impact experiments, edge compression experiments, and short beam three-point bending experiments, we seek the optimal carbon fiber/glass fiber hybrid layup design scheme for local structures to guide production. The results show that a reasonable hybrid carbon fiber layup in fiberglass skin can effectively reduce the low-speed impact damage of the sandwich structure, reduce edge compression damage, and improve the bending and compression resistance of sandwich structure. The impact resistance, compression resistance, and shear resistance of the SAN sandwich structure are stronger than the PVC sandwich structure. The carbon fiber/glass fiber hybrid SAN foam sandwich structure can be used for the local structural reinforcement of special parts such as the bow, side, and main deck of fiberglass yachts. [ABSTRACT FROM AUTHOR]

In this paper, the glass-fiber-fabric-reinforced resin-based absorbing composites were prepared, and their microwave-absorbing properties were studied via simulation and experiment. The simulation results show that the absorption bandwidth of the absorbing material can cover the X\C\S band, respectively, at different thicknesses. The minimum reflection loss (RL) of the composite with a thickness of 2.2 mm is −27.4 dB at 5.95 GHz. However, the experiment results are quite different from those of the simulation. The metallographic results indicate that it is the change of the mass fraction of the absorbents in the composites after curing that causes the difference. According to the metallographic results, three shape approximation methods were proposed to calculate the real mass ratio of the absorbents in the composites, namely, parallelogram approximation, bows approximation, and elliptical approximation. Meanwhile, the structural parameter K f was introduced to optimize the calculation results. The electromagnetic parameters of the material based on the calculation results were measured, and the results show that the simulation results obtained via bow approximation have a better coincidence to the experiment results, and the mass ratio of the absorbent raises by around 9.95%, which lays a foundation for the subsequent design of microwave-absorbing composites. [ABSTRACT FROM AUTHOR]

The problem of the growing amount of waste polymer materials currently affects virtually every area of the global economy. New actions taken by the E.U. and member states could lead to a reduction in the burden on the natural environment, as well as the reuse of thermoplastic waste. The aim of this study was to analyze the possibility of reusing post-industrial waste (recycled polypropylene—rPP) in order to produce mixtures with original polypropylene (PP) and glass fibers. The research undertaken is characterized by a high level of innovation and was carried out on an industrial scale from industrial waste. The primary goal of the analyses was to determine changes in the properties of the polymer mixtures depending on the amount of recycled polymers. For this purpose, four types of mixtures were prepared, characterized by different degrees of filling with recycled material obtained from big-bag packaging (the filling levels were 0 wt.%, 20 wt.%, 30 wt.%, and 70 wt.%). A detailed analysis of the physical properties of the obtained mixtures was carried out to determine changes in the densities depending on the amount of rPP material. In addition, changes in the MFIs (melt flow indexes), characterizing viscosity changes, were analyzed depending on the amount of secondary raw material used. An analysis of the mechanical properties was also carried out based on static tensile testing, the impact strength (the Charpy method), and the Rockwell hardness test (the M method). The analysis of the thermal changes was performed using the DSC method. The results showed that the composites made of virgin polypropylene (PP GF30) and those made from re-granulates and glass fibers (rPP GF30) are characterized by similar mechanical properties and significantly different processing properties, determined by MFI. This means that the addition of re-granulates significantly affects the processability of the obtained materials, while the addition of glass fibers maintains the basic mechanical properties. [ABSTRACT FROM AUTHOR]

To address the issues of insufficient strength and poor precision in polystyrene forming parts during the selective laser sintering process, a ternary composite of polystyrene/glass fiber/hollow glass microbeads was prepared through co-modification by incorporating glass fiber and hollow glass microbeads into polystyrene using a mechanical mixing method. The bending strength and dimensional accuracy of the sintered composites were investigated by conducting an orthogonal test and analysis of variance to study the effects of laser power, scanning speed, scanning spacing, and delamination thickness. The process parameters were optimized and selected to determine the optimal combination. The results demonstrated that when considering bending strength and Z-dimensional accuracy as evaluation criteria for terpolymer sintered parts, the optimum process parameters are as follows: laser power of 24 W, scanning speed of 1600 mm/s, scanning spacing of 0.24 mm, and delamination thickness of 0.22 mm. Under these optimal process parameters, the bending strength of sintered parts reaches 6.12 MPa with a relative error in the Z-dimension of only 0.87%. The bending strength of pure polystyrene sintered parts is enhanced by 15.69% under the same conditions, while the relative error in the Z-dimension is reduced by 63.45%. It improves the forming strength and precision of polystyrene in the selective laser sintering process and achieves the effect of enhancement and modification, which provides a reference and a new direction for exploring polystyrene-based high-performance composites and expands the application scope of selective laser sintering technology. [ABSTRACT FROM AUTHOR]

A total of 66 sets of pullout specimens were prepared to investigate the bonding properties of basalt fiber-reinforced polymer reinforcement (hereinafter referred to as BFRP) with seawater sand concrete (hereinafter referred to as SSC). The volume dosages of mono-doped glass fibers and mono-doped polypropylene fibers were 0.1%, 0.2%, and 0.3%; the total volume dosage was set to be constant at 0.3%; and the doping ratios of the hybrid fibers were 1:2, 1:1, and 2:1. The effect on the bonding performance of BFRP reinforcement with SSC was studied on the condition of the diameter D of the BFRP reinforcement being 12 mm; the bond length of SSC being 3D, 5D, and 7D; and the surface characteristics of the reinforcement being sandblasted and threaded. The research showed that due to internal cracks in the matrix, salt crystals in the pores, chloride salts with high brittleness and expansion, as well as sulfate corrosion products such as "Frederick salts" in SSC, the concrete became brittle, resulting in more brittle splitting failures during the pullout test. Doped fibers can increase the ductility effect of concrete, but the bonding effect between the threaded fiber reinforcement and the SSC was not as good as that of the sandblasting group. When the bond length was 5D, the bonding effect between the BFRP reinforcement and SSC was the best, and the bonding performance of the experimental group with doped fibers was better than that of the threaded group. Finally, by combining the ascending segment of the Malvar model with the descending segment of the improved BPE model, a constitutive relationship model suitable for the bond–slip curve between BFRP reinforcement and SSC was fitted, which laid a theoretical foundation for future research on SSC. [ABSTRACT FROM AUTHOR]

The use of fibre-reinforced polymer materials (FRPs) for the retrofitting of reinforced concrete (RC) structures has become very popular. However, the main concern for the exploitation of FRPs is their premature debonding failure modes. This paper presents two different universal models for calculating flexed RC elements strengthened with externally bonded and near-surface mounted FRP reinforcements, which were derived by coupling principles of the fracture mechanics of solids and generally accepted assumptions. The first model allows a complete analysis of the behaviour, development, and propagation of rupture of the joint. The main advantages of the proposed model, compared to existing ones, are that it does not require additional bond shear tests to identify missing factors, and it is versatile and suitable for both externally bonded reinforcements (EBR) and near surface mounted (NSM) strengthening techniques. In addition, the concrete–FRP connection is divided into zones and the current phase and length of each zone are determined, allowing for more detailed analysis of the connection at different load stages. The proposed computational model and its derivation focus on the performance of the joint between the two cracks and the distribution of the shear stresses in that joint. The second one requires fewer computations and can be fully exploited when the joint is treated as a unit, without division. The results of the calculations have been validated using the experimental database of 77 RC beams and strengthened with externally bonded and near-surface mounted carbon fibre reinforced polymer (CFRP) and glass fibre reinforced polymer (GFRP) sheets, plates, strips, and bars taken from 13 different studies. Both the prestress force and the initial stress state before strengthening were evaluated. [ABSTRACT FROM AUTHOR]

To address the weight, cost, and sustainability associated with fibreglass application in structural composites, plant fibres serve as an alternative to reduce and replace the usage of glass fibres. However, there remains a gap in the comprehensive research on plant fibre composites, particularly in their durability for viable structural applications. This research investigates the fatigue and impact properties of pultruded kenaf/glass-reinforced hybrid polyester composites tailored for structural applications. Utilising kenaf fibres in mat form, unidirectional E-glass fibre direct roving yarns, and unsaturated polyester resin as key constituents, pultruded kenaf/glass hybrid profiles were fabricated. The study reveals that pultruded WK/UG alternate specimens exhibit commendable fatigue properties (18,630 cycles at 60% ultimate tensile strength, UTS) and fracture energy (261.3 kJ/m2), showcasing promise for moderate load structural applications. Notably, the pultruded 3 WK/UG/3WK variant emerges as a viable contender for low-load structural tasks recorded satisfactory fatigue properties (10,730 cycles at 60% UTS) and fracture energy (167.09 kJ/m2). Fatigue failure modes indicate that the stress applied is evenly distributed. Ductile failures and delaminations during impact test can be attributed to damping and energy absorbing properties of kenaf fibres. Moreover, incorporating kenaf as a hybrid alternative demonstrates substantial reductions in cost (35.7–50%) and weight (9.6–19.1%). This research establishes a foundation for advancing sustainable and efficient structural materials and highlights the significant role of materials design in shaping the future of engineering applications. [ABSTRACT FROM AUTHOR]

Due to the high interest in the use of glass/epoxy laminates in aerospace applications, aviation, and as cryogenic tanks, it is crucial to understand the behavior of composites under challenging environmental conditions. Polymer composites are exposed to low temperatures, including cryogenic temperatures, which can lead to the initiation of microdamage. This paper investigates damage initiation/accumulation and its influence on the properties of cross-ply woven glass fiber epoxy composites at low temperatures compared to room temperature conditions. To evaluate the influence of a low-temperature environment on the mechanical performance of glass fiber reinforced epoxy composite (GFRP) laminates, three types of test campaigns were carried out: quasi-static tensile tests and stepwise increasing loading/unloading cyclic tensile tests at room temperature and in a low-temperature environment (−50 °C). We demonstrated that the initial stiffness of the laminates increased at low temperatures. On the other hand, there were no observed changes in the type or mechanism of developed damage in the two test conditions. However, the reduction in stiffness due to the accumulated damage was more significant for the laminates tested at low temperatures (~17% vs. ~11%). Exceptions were noted in a few formulations where the extent of damage at low temperatures was insignificant (<1%) compared to that at room temperature. Since some of the studied laminates exhibited a relatively minor decrease in stiffness (~2–3%), we can also conclude that the formulation of matrix material plays an important role in delaying the initiation and formation of damage. [ABSTRACT FROM AUTHOR]

This paper focuses on the development of thin-walled panels with specific properties for applications such as water-tight structures. The authors propose the use of textile-reinforced concrete (TRC) as a composite material and highlight its advantages, which include high tensile strength, improved crack resistance, and design flexibility. The study presents a novel approach which combines TRC with reactive powder concrete (RPC) as a matrix and a lightweight aggregate. RPC, known for its brittle behaviour, is reinforced with glass fibres and a textile fabric to increase its flexural strength. The research includes a comprehensive analysis of the physical and mechanical properties of both the unreinforced RPC matrix and the TRC composite. In particular, the lightweight aggregate RPC matrix has a porosity of 41%, and its mechanical properties, such as flexural and compressive strength, are discussed. The TRC composites, produced in thicknesses ranging from 1 mm to 4 mm, are subjected to flexural tests to evaluate their behaviour under load. The thicker elements show typical damage phases, while the thinner elements show greater flexibility and elasticity. SEM observations confirm good adhesion between the glass fibres and the RPC matrix. Water permeability tests show that the TRC composite, despite its highly porous structure, achieves a water permeability two orders of magnitude higher than that of a reference material, highlighting the roles of both the porous aggregate and the matrix hydration. The paper concludes with a proof of concept—a canoe called the PKanoe, which is constructed from the developed TRC composite. The design of the canoe is supported by numerical analysis to ensure its optimal shape and structural integrity under load. The research contributes to the exploration of innovative materials for sustainable civil engineering applications and addresses both structural and environmental considerations. [ABSTRACT FROM AUTHOR]

Thin-walled and thick-walled microcellular moldings were obtained by MuCell® technology with nitrogen as a supercritical fluid. 2 mm thick polyamide 6 (PA6) with 30% wt. glass fiber (GF) samples were cut from automotive industrial elements, while 4 mm, 6 mm, and 8.4 mm thick moldings of PA6.6 with 30% wt. GF were molded into a dumbbell shape. The internal structure was investigated by scanning electron microscopy (SEM) and X-ray computed microtomography (micro-CT) and compared by numerical simulations for microcellular moldings using Moldex3D® 2022 software. Young's modulus, and tensile and impact strength were investigated. Weak mechanical properties of 2 mm thick samples and excellent results for thick-walled moldings were explained. SEM pictures, micro-CT, and simulation graphs revealed the tendency to decrease the cell size diameter together with increasing sample thickness from 2 mm up to 8.4 mm. [ABSTRACT FROM AUTHOR]

Composites are materials that are widely used in industry, including yachting, railway and aviation. The properties of these materials can be modified by changing the type of reinforcement, the type of matrix, as well as the use of additives in the form of fillers and nanofillers that improve their mechanical or specific parameters. Due to the fact that these materials are often used for important structures, computational models using FEM tools may not be sufficient to determine the actual strength parameters, and what is more, to check them during operation. When designing structures made of composite materials, it is necessary to use high safety factors due to their behavior under several different types of loads, which is still difficult to determine precisely. This situation makes these structures much heavier and characterized by much higher strength properties than those that would actually be needed. In this article, the Kolmogorov-Sinai (K-S) metric entropy was used to determine the transition from the elastic to the viscoelastic state in GFRP (glass fiber reinforced polymer) composite materials without and with the addition of nanoaluminum, during a static tensile test. Additionally, the acoustic emission method was used during the research. This signal was further processed, and graphs were made of the number of events and the amplitude as a function of time. The obtained values were plotted on tensile graphs. The influence of the nano-filler on these parameters was also analyzed. The presented results show that it is possible to determine additional parameters affecting the strength of the structure for any composite materials. [ABSTRACT FROM AUTHOR]

Permanent deformation, or rutting, is one of several critical distresses in flexible pavements. This paper introduced a novel experimental method, a penetration test, for asphalt mixtures to quantify the effects of glass fibre geogrids embedded in asphalt under repeated loading. It was found that the evolution of permanent deformation (εp) and its strain rate have three clearly identifiable stages. It was also observed that the presence of the geogrid increased the flow number and the number of cycles to failure significantly compared to control samples. Some of the current εp fitting models were found to be valid for deformation prediction under penetration. In addition, a new simple FN calculation method was also proposed based on strain rate and it showed consistent results. In particular, geogrid type "Grid10", which has smaller aperture size (12.7 mm) had slightly better reinforcement performance regarding the rutting resistance due to its larger contact area. Overall, the test and data analysis method presented in this study could be an important reference for future investigations on geosynthetic-reinforced pavement materials. [ABSTRACT FROM AUTHOR]

This study presents the effect of the addition of 0.4 wt.% carbon black (CB) to polyamide 66 (PA66) containing 30 wt.% short glass fibers (GFs) on the behavior of composite thermal crystallization. Composites were studied by differential scanning calorimetry analysis (DSC) at different cooling rates using wide-angle X-ray scattering (WAXS) and scanning electron microscopy (SEM). This thermal crystallization study highlights the nucleation effect of GFs that promote PA66 crystallization by significantly increasing crystallization kinetics and rates. The activation energies (Eas) calculated by model-free (FWO; KAS) and model-fitting (Kissinger method and C–R method) approaches showed that the combination of both GF and CB decreases the activation energy with respect to neat PA66, meaning that the presence of both additives facilitates crystallization. The Coats–Redfern and Criado methods showed that the crystallization of neat PA66 and related composites follows the second-order reaction, i.e., the decelerated reaction, evidencing compatibility between GFs and the matrix. [ABSTRACT FROM AUTHOR]

Many researchers use fiber to improve the cracking resistance of asphalt mixtures, but research concerning the effects of fiber on fracture behavior is limited. The fracture behavior of asphalt mixtures with various fiber types (basalt fiber, glass fiber, and polyester fiber) and contents (0.1%, 0.2%, 0.3%, 0.4%, and 0.5%) has been studied using the indirect tensile asphalt cracking test (IDEAL-CT) in conjunction with digital image correlation (DIC) technology. The evaluation indexes used in the test included crack initiation energy (Gif), crack energy (Gf), splitting tensile strength (RT), cracking tolerance index (CTindex), and the real-time tensile strain (Exx) obtained using digital image correlation technology. The results showed that despite the fiber type, the increase of fiber content resulted in first, an increase, and then, a decrease of the cracking resistance of asphalt mixtures, indicating the presence of optimum fiber content—specifically, 0.4%, 0.3%, and 0.3% for basalt fiber, glass fiber, and polyester fiber, respectively. The development of real-time tensile strain, obtained based on digital image correlation technology, could be divided into two stages: slow-growth stage and rapid-expansion stage. In addition, asphalt mixture with basalt fiber presented the best cracking resistance at both the slow-growth and rapid-expansion stages. This research is helpful in understanding the effects of fiber type and content on the fracture behavior of asphalt mixtures and has certain reference significance for the application of fiber in asphalt mixtures. [ABSTRACT FROM AUTHOR]

Poor interlaminar fracture toughness has been a major issue in glass fiber-reinforced epoxy resin (GF/EP) laminate composites. In this paper, soft carboxy-terminated nitrile (CTBN) rubber particles and rigid nano-SiO2 are used to toughen the epoxy resin (EP) matrix to improve the interlayer properties of GF/EP laminate composites. The effects of adding two toughening agents on the mechanical and interlayer properties of GF/EP laminates were studied. The results showed that adding the two kinds of particles improved the mechanical properties of the epoxy matrix. When the additional amount of flexible CTBN rubber particles was 8 wt%, and the rigid nano-SiO2 was 0.5 wt%, the fracture toughness of the matrix resin was increased by 215.8%, and the tensile strength was only decreased by 2.3% compared with the pure epoxy resin. On this basis, the effects of two kinds of particles on the interlayer properties of GF/EP composites were studied. Compared with the unmodified GF/EP laminates, the interlayer shear strength and mode I interlayer fracture toughness is significantly improved by a toughening agent, and the energy release rate GIC of interlayer shear strength and interlayer fracture toughness is increased by 109.2%, and 86.8%, respectively. The flexible CTBN rubber particles and rigid nano-SiO2 improve the interfacial adhesion between GF and EP. The cavitation of the two particles and the plastic deformation of the matrix is the toughening mechanism of the interlayer properties of the composite. Such excellent interlaminar mechanical properties make it possible for GF/EP laminates to be widely used as engineering materials in various industries (e.g., aerospace, hydrogen energy, marine). [ABSTRACT FROM AUTHOR]

Standard Digital Volume Correlation (DVC) approaches enable quantitative analyses of specimen deformation to be performed by measuring displacement fields between discrete states. Such frameworks are thus limited by the number of scans (due to acquisition duration). Considering only one projection per loading step, Projection-based Digital Volume Correlation (P-DVC) allows 4D (i.e., space and time) full-field measurements to be carried out over entire loading histories. The sought displacement field is decomposed over a basis of separated variables, namely, temporal and spatial modes. In the present work, the spatial modes are constructed via scan-wise DVC, and only the temporal amplitudes are sought via P-DVC. The proposed method is applied to a glass fiber mat reinforced polymer specimen containing a machined notch, subjected to in situ cyclic tension and imaged via X-ray Computed Tomography. The P-DVC enhanced DVC method employed herein enables for the quantification of damage growth over the entire loading history up to failure. [ABSTRACT FROM AUTHOR]

It is undeniable that mechanical properties, such as the stiffness or residual strength of fibre-reinforced thermoplastics, are adversely affected by fatigue damage caused by cyclic loading. In order to quantify and predict this damage influence, a calculation approach was developed in the past for the subgroup of short-fibre-reinforced thermoplastics. In order to test and expand the applicability of this approach to the field of long-fibre-reinforced thermoplastics, the decrease in mechanical properties is investigated experimentally in this paper using PP LGF30, propylene reinforced with long glass fibres, as an example. The paper describes both the fatigue behaviour and the residual strength of the material after fatigue damage. A decrease in the residual strength of up to about 35% could be recorded. The paper also presents a modelling approach that predicts the orientation-dependent fatigue strength of the material, and furthermore allows for the calculation of its residual strength as a function of fatigue damage. The novelty of the contribution lies in the continuous modelling of fatigue behaviour for arbitrary oriented samples of long-fibre-reinforced thermoplastics and also in the prediction of its residual strength depending on previously induced fatigue damage. [ABSTRACT FROM AUTHOR]

To improve heat dissipation capability and enhance mechanical properties, a series of silica aerogel (SA) and modified glass fiber (GF)-filled SBR composites were prepared. It was found that the addition of SA successfully reduced the thermal conductivity of SBR by 35%, owing to the heat shield of the nanoscale porous structure of SA. Moreover, the addition of modified glass fiber (MGF) yielded a significant increase in the tensile and tear strength of SBR/SA composite rubber of 37% and 15%, respectively. This enhancement was more pronounced than the improvement observed with unmodified GF, and was attributed to the improved dispersion of fillers and crosslinking density of the SBR matrix. Rheological analysis revealed that the addition of SA and MGF weakened the ω dependence. This was due to the partial relaxation of immobilized rubber chains and limited relaxation of rubber chains adsorbed on the MGF. Furthermore, the strain amplification effect of MGF was stronger than that of GF, leading to a more pronounced reinforcing effect. [ABSTRACT FROM AUTHOR]

An ultra-wideband electromagnetic (EM) absorber is proposed. The proposed absorber consists of two thin metasurfaces, four dielectric layers, a glass fiber reinforced polymer (GFRP), and a carbon fiber reinforced polymer (CFRP) which works as a conductive reflector. The thin metasurfaces are accomplished with 1-bit pixelated patterns and optimized by a genetic algorithm. Composite materials of GFRP and CFRP are incorporated to improve the durability of the proposed absorber. From the full-wave simulation, more than 90% absorption rate bandwidth is computed from 2.2 to 18 GHz such that the fractional bandwidth is about 156% for the incidence angles from 0° to 30°. Absorptivity is measured using the Naval Research Laboratory (NRL) arch method in an EM anechoic environment. It was shown that the measured results correlated with the simulated results. In addition, the proposed absorber underwent high temperature and humidity tests under military environment test conditions in order to investigate its durability. [ABSTRACT FROM AUTHOR]

The present work studies the response to hygrothermal ageing of natural fibre composites (NFCs) against synthetic fibre composites when using three different types of polymers as matrices. For ageing, coupons were fully immersed in distilled water at 23, 40, and 60 °C for a total ageing period of 56 days. Flax fibre-reinforced composites, using two recyclable polymer systems: (i) a bio-based recyclable epoxy and (ii) an acrylic-based liquid thermoplastic resin, were tested against conventional glass fibre-reinforced composites employing a synthetic (petroleum-based) epoxy. Different fibre/polymer matrix material combinations were tested to evaluate the effects of hygrothermal ageing degradation on the reinforcement, matrix, and fibre/matrix interface. The hygrothermal ageing response of unaged and aged composite coupons was assessed in terms of flexural and viscoelastic performance, physicochemical properties, and microscopy (SEM—Scanning Electron Microscopy). [ABSTRACT FROM AUTHOR]

As an important energy conversion component in electromagnetic-forming technology, the coil is subjected to great internal stress and is easy to break. The geometric structure and winding process of the forming coil draw on the research results of pulsed magnets. However, the two use conditions are different. It is very important to clarify the force difference between the two for the design of the forming coil. In this paper, the numerical model of an aluminum alloy (AA1060-O) is established, and the difference in force between the pulse magnet and forming coil with the same size in time and space under different working conditions is analyzed. A two-dimensional fully coupled finite element model consisting of circuit, magnetic field, and solid mechanics is established and used to determine the key parts of the coil force. It is found that the von Mises stress of the forming coil is greater than that of the pulsed magnet under the same circuit parameters and geometric structure. In the electromagnetic forming of the tube, the glass fiber is subjected to a large stress. In addition, the stress of glass fiber under the condition of tube necking is about 2 times that of pulsed magnet. When the voltage is increased, the failure of the middle part of the glass fiber causes the coil to break. In the electromagnetic forming of the sheet, the coil skeleton is subjected to large stress, and its upper end failure causes the coil to break. Therefore, new design ideas for forming coils under different working conditions are proposed. [ABSTRACT FROM AUTHOR]

This paper presents new photocatalysts obtained by treating carbon spheres (CS) and TiO2 in a microwave reactor at a pressure of 20 atm and a temperature of up to 300 °C for 15 min and then depositing TiO2/CS composites on glass fibre cloths. Such highly CO2-adsorbing photocatalysts showed photoactivity in the simultaneous water-splitting process, generating H2, reducing CO2 to CO and CH4, and reducing N2 to NH3. In addition, calculations of the hydrogen balance involved in all reactions were performed. Adding 1 g of carbon spheres per 1 g of TiO2 maintained the high selectivity of nitrogen fixation at 95.87–99.5%, which was continuously removed from the gas phase into the water as NH4+ ions. [ABSTRACT FROM AUTHOR]

The use of fibres applied to concrete in order to improve its properties is widely known. Nowadays, research is not only focused on improving mechanical properties but also on the environmental implications. The aim of this research was a mechanical and environmental comparison between different types of fibres. For this purpose, commercial fibres of three materials were used: low carbon steel, modified polyolefins, and glass fibre. In order to improve the sustainability of the sector, we also analysed and compared the performance of using a waste product, such as fibres from machining operations on lathes. For the evaluation of the mechanical properties, compression and flexural tests were carried out. The results show that the use of low carbon steel fibres increases the flexural strength by 4.8%. At the environmental level, and in particular for impact categories such as the Global Warming Potential (GWP), lathe waste fibres prove to be the most suitable. For instance, compared to glass fibres, CO2 emissions are reduced by 14.39%. This is equivalent to a total of 38 kg CO2 emissions per m3 of reinforced concrete. In addition to avoiding the consumption of 482 MJ/m3 of fossil fuels, the results of the research indicate the feasibility of using waste fibres as a substitute for commercial fibres, contributing to an improved environmental balance without losing mechanical performance. [ABSTRACT FROM AUTHOR]

Glass fibers are widely used in cement-based precast products, given the reinforcing requirements for toughness and strength. However, inferior alkali resistance hinders the effectiveness of glass fibers in reinforcing cement-based materials. In this paper, nanoparticle coatings were applied on the surface of alkali-resistant glass fiber (ARGF) as a protective layer via the in situ chemical reaction of oleic acid (OA) and potassium permanganate (PP). The morphology and constituents of the as-prepared ARGFs were examined using scanning electron microscopy (SEM) and obtaining X-ray photoelectron spectroscopy (XPS) measurements. Mass loss and strength retention were investigated to characterize alkali resistance of modified ARGFs. Results showed that ARGFs could be optimally coated by a layer of MnO2-based nanoparticles consisting of approximately 70% MnO2, 18% MnO, and 12% MnSiO3, when modified with an optimum OA to PP ratio of 10 for 24 h. The dissolution of ARGFs matrix in 4% and 10% NaOH solutions were distinctly delayed to 28 d, as a consequence of the introduction of the MnO2-based nanoparticle layer, compared with nontreated ARGF occurring at 3 d in 4% NaOH solution. For the optimally modified ARGFs, the mass loss was controlled to 1.76% and 2.91% after 90 d of corrosion in 4% and 10% NaOH solutions, and the retention of tensile strength was increased by approximately 25%. With respect to the increment in alkali-resistant performance, the modified ARGFs can be promising candidates for wide applications in alkaline cement-based products. [ABSTRACT FROM AUTHOR]

Composite sandwich structures are extensively used in aircraft applications. Aircraft components are required to be robust and lightweight. Sandwich structures made of carbon-fiber-reinforced polymer as the facing sheets and milled-glass-fiber-reinforced rigid polyurethane foam with a different glass fiber content as the core structure were prepared. The influence of glass fiber content in the foam on the sandwich structure's mechanical properties was investigated. Flexural and compression tests were performed to assess the mechanical properties of the sandwich structures. Visual inspection and an optical microscope were used to observe the morphology of the polyurethane composite foams at different contents. From the flexural test, the force, facing stress and core shear stress improved with the increase in the milled fiber loading with the maximum increase at 10 wt.% loading and then a drop. Meanwhile, the compression modulus and strength increased up to 20 wt.% loadings and then dropped subsequently. The increase in the polyurethane composite foam's compression strength shifted the bending load's failure type from facing crack failure into core shear failure. The loadings range of 8–10 wt.% showed a transitional of the bending loading failure type. The density of the foams increased with the increase in milled glass fiber loading. At 10 wt.% loading, the density increased by 20%, and it increased by 47% at 30 wt.% loading. At 30 wt% loading, the optical microscope images of the foam showed wall thinning and broken walls that were responsible for the drop in the mechanical properties of the sandwich. [ABSTRACT FROM AUTHOR]

Fiber-reinforced silica aerogel blankets (FRABs) are an important high-temperature thermal insulation material for industry applications that have emerged in recent years. In order to better understand the performance evolution of FRABs at high temperatures, the effect of heat treatment at different temperatures on the performance of FRABs as well as their base material, hydrophobic silica aerogel powder and glass wool, was investigated. The property evolution of the hydrophobic silica aerogel powder showed two stages with an increase in thermal treatment temperatures. The skeleton structure of the aerogel remained unchanged, but the residual organic chemicals, such as hydrophobic groups, were decomposed when the heat treatment temperature was lower than 400 °C. Above 400 °C, the skeleton began to shrink with the increase in temperature, which led to an increase in thermal conductivity. The structure and room-temperature thermal conductivity of the glass wool blanket were less affected by a heat treatment temperature under 600 °C. Therefore, the performance degradation of FRABs at high temperatures is mainly due to the change in the aerogel powder. The insulation performance of the glass wool and FRAB at high temperatures was studied using a heating table which was designed to simulate working conditions. The energy savings of using FRABs instead of glass fiber were calculated and are discussed here. [ABSTRACT FROM AUTHOR]

The milling of polymer composites is a process that ensures dimensional and shape accuracy and appropriate surface quality. The shaping of thin-walled elements is a challenge owing to their deformation. This article presents the results of milling polymer composites made of glass and carbon fibers saturated with epoxy resin. The milling of each material was conducted using different tools (tools with polycrystalline diamond inserts, physically coated carbide inserts with titanium nitride and uncoated carbide inserts) to show differences in feed force and deformation after the machining of individual thin-walled samples. In addition, the study used recurrence analysis to determine the most appropriate quantifications sensitive to changes occurring in milling different materials with the use of different tools. The study showed that the highest forces occurred in milling thin-walled carbon-fiber-reinforced plastics using uncoated tools and the highest feeds per revolution and cutting speeds. The use of a high feed per revolution (0.8 mm/rev) in carbon-fiber-reinforced plastics machining by uncoated tools resulted in a maximum feed force of 1185 N. A cutting speed of 400 m/min resulted in a force of 754 N. The largest permanent deformation occurred in the milling of glass-fiber-reinforced composite samples with uncoated tools. The permanent deformation value of this material was 0.88 mm. Low feed per revolution (0.1 mm/rev) resulted in permanent deformations of less than 0.30 mm for both types of materials. A change in feed per revolution had the most significant effect on the deformations of thin-walled polymer composites. The analysis of forces and deformation made it possible to conclude that high feed per revolution were not recommended in composite milling. In addition to the analysis of machining thin-walled composites, the novelty of this study was also the use of recurrence methods. Recurrence methods were used to determine the most appropriate quantifications. Determinism, averaged diagonal length and entropy have been shown to be suitable quantifications for determining the type of machined material and the tools used. [ABSTRACT FROM AUTHOR]

With the development of the automotive industry, a large amount of waste rubber is produced every year. The application and development of recycled rubber concrete (RRC) can effectively reduce 'black pollution' caused by waste rubber. However, the addition of recycled rubber particles can lead to a decrease in the compressive behavior of concrete. Previous research has demonstrated that by preventing crack growth, fiber addition can increase the strength and ductility of concrete. In this work, a total of 28 RRC mixes are designed, and the compressive behavior of RRC reinforced by steel fibers (SFs) and glass fibers (GFs) is investigated. The workability of fresh RRC can be negatively impacted by an increase in both fiber contents, with the GF content having a more notable effect. With the addition of fibers, the maximum increase rates for the compressive strength, elastic modulus, strain at peak stress, and compressive toughness were 27%, 8%, 45%, and 152%, respectively. A constitutive model is concurrently put forward to forecast the stress–strain curves of RRC with various fiber contents. These findings indicate that the maximum improvement in compressive behavior is achieved when the GF content was 0.4% and the SF content was 1.2%. The proposed constitutive model can be used to predict the stress–strain curve of hybrid fiber-reinforced recycled rubber concrete (HFRRRC). [ABSTRACT FROM AUTHOR]

Polyamide 6 (PA6) thermoplastic composites have higher recyclability potential when compared to conventional thermoset composites. A disruptive liquid molding manufacturing technology named Thermoplastic Resin Transfer Molding (T-RTM) can be used for processing composites due to the low viscosity of the monomers and additives. In this process, polymerization, crystallization and shrinkage occur almost at the same time. If these phenomena are not controlled, they can compromise the reproducibility and homogeneity of the parts. This work studied the influence of packing pressure, as a process variable, throughout the filling and polymerization stages. To assess the process reproducibility and parts' homogeneity, physical, thermal and mechanical properties were analyzed in different areas of neat PA6 and composite parts. This study showed that a two-stage packing pressure can be successfully used to increase parts' homogeneity and process reproducibility. The use of 3.5 bar packing pressure during the polymerization stage resulted in mechanical properties with lower standard deviations, indicating a higher degree of homogeneity of the manufactured parts and higher process reproducibility. These results will be used for establishing the actual state of the technology and will be a base for future process optimization. [ABSTRACT FROM AUTHOR]

The proposed study combines sprayed glass fiber-reinforced mortar and basalt textile-reinforcement to harness the favorable properties of each component to obtain a composite material that can be used for strengthening of existing structures. This includes crack resistance and a bridging effect of glass fiber-reinforced mortar and the strength provided by the basalt mesh. In terms of weight, mortars containing two different glass fiber ratios (3.5% and 5%) were designed, and tensile and flexural tests were conducted on these mortar configurations. Moreover, the tensile and flexural tests were performed on the composite configurations containing one, two, and three layers of basalt fiber textile reinforcement in addition to 3.5% glass fiber. Maximum stress, cracked and uncracked modulus of elasticity, failure mode, and average tensile stress curve results were compared to determine each system's mechanical parameters. When the glass fiber content increased from 3.5% to 5%, the composite system without basalt textiles' tensile behavior slightly improved. The increase in tensile strength of composite configurations with one, two, and three layers of basalt textile reinforcement was 28%, 21%, and 49%, respectively. As the number of basalt textile reinforcements increased, the slope of the hardening part of the curve after cracking clearly increased. Parallel to the tensile tests, four-point bending tests showed that the composite's flexural strength and deformation capacities increase as the number of basalt textile reinforcement layers increase from one to two. [ABSTRACT FROM AUTHOR]

In order to study the influence of vinyl acetate–ethylene copolymerization emulsions on the bonding performance of fiber and mortar, mortar materials with different polymer contents were prepared. The optimal mix ratio of the matrix was obtained using a pull-out test with a 0° inclination angle. On this basis, polypropylene fibers and alkali-resistant glass fibers were set at different burial depths (6 mm, 12 mm, and 18 mm) and different burial angles (0°, 30°, 45°, and 60°). The load–displacement curves of two types of fibers pulled out from the polymer mortar were obtained. The test results show that polymer contents of 3% and 5% increase the peak pull-out loads of glass fibers and polypropylene fibers by 16.28% and 30.72% and 7.41% and 27.11%, respectively. When the polymer content is 7%, the peak pull-out load decreases by 1.31% and 24.26%, especially for polypropylene fiber, which significantly weakens the bonding performance between the matrix and the fiber. The pull-out load of glass fibers and polypropylene fibers increases with the increase in the buried depth, and both show tensile failure at 18 mm. As the embedding angle increases, the pull-out load of polypropylene fibers decreases continuously, while the glass fiber shows a higher pull-out load at 30°. [ABSTRACT FROM AUTHOR]

Light-transmitting concrete as a building material already exists in many forms, but its light properties and the possibilities of using it to improve the lighting of interior spaces have not been investigated in detail yet. This paper focuses on the illumination of interior spaces using constructions made of light-transmitting concrete, which will allow light to pass between individual spaces. The experimental measurements carried out are divided into two typical situations using reduced room models. The first part of the paper focuses on the illumination of the room through the penetration of daylight through the ceiling made of light-transmitting concrete. The second part of the paper investigates the transmission of artificial light from one room to another through a non-load-bearing dividing structure composed of unified slabs of light-transmitting concrete. For the experiments, several models and samples were created for comparison. The first step of the experiment was to create slabs of light-transmitting concrete. While there are many options to produce such a slab, the best option is to use high-performance concrete with glass-fiber reinforcement, which improves the load transfer properties, and plastic optical fibers for light transmission. By adding optical fibers, we can achieve the transmission of light between any two spaces. For both of the experiments, we used reduced-scale models of rooms. Slabs with dimensions of 250 × 250 × 20 mm and 250 × 250 × 30 mm were used in three versions: concrete slabs with optical fibers, concrete slabs with air holes and solid slabs. The experiment measured and compared the level of illumination at several points in the model as it passed through each of the three different slabs. Based on the results of these experiments, it was concluded that the interior level of illumination of any space can be improved by using light-transmitting concrete, especially those without access to natural light. The experiment also assessed the strength properties of the slabs in relation to their intended use and compares them with the properties of stone slabs used as cladding. [ABSTRACT FROM AUTHOR]

Glass fiber reinforced polymer (GFRP) is the main composite material used in wind turbine blades. In recent years, zero-carbon energy sources such as wind power have been widely used to reduce carbon emissions, resulting in a large amount of waste GFRP, and causing serious environmental problems. To explore efficient ways to recycle waste GFRP, this study explores the impact of adding GFRP powder (nominal maximum particle size ≤ 0.075 mm) on the high and low temperature properties of asphalt mastic. Samples of GFRP asphalt mastics were prepared with filler-asphalt mass ratios of 0.01:1, 0.1:1, 0.8:1, and 1:1, as well as two control samples of limestone filler asphalt mastics with filler-asphalt mass ratios of 0.8:1 and 1:1. The study analyzed the effect of GFRP on the asphalt mastic's performance using temperature sweep, MSCR, and BBR tests. Results showed that the presence of GFRP improved the high-temperature resistance and recovery of asphalt mastic but led to decreased low-temperature crack resistance. The results suggest that GFRP has the potential to be used as a filler in asphalt mastic, with a recommended filler-asphalt mass ratio range of less than 0.8:1 for optimal low-temperature performance. However, further research is necessary to determine the optimal content of GFRP in asphalt mastic and to study its impact on other road performance metrics. [ABSTRACT FROM AUTHOR]

In this study, carbon nanotubes (CNTs) were grown under the same conditions as those of carbon fibers and glass fibers, and a comparative analysis was performed to confirm the potential of glass fibers with grown CNTs as electromagnetic interference (EMI) shielding materials. The CNTs were grown directly on the two fiber surfaces by a chemical vapor deposition process, with the aid of Ni particles loaded on them via a Ni-P plating process followed by heat treatment. The morphology and structural characteristics of the carbon and glass fibers with grown CNTs were analyzed using scanning electron microscopy–energy dispersive X-ray spectroscopy (SEM–EDS), X-ray diffraction (XRD), and X-ray photoelectron spectrometry (XPS), and the EMI shielding efficiency (EMI SE) of the directly grown CNT/carbon and glass fiber-reinforced epoxy matrix composites was determined using a vector-network analyzer. As the plating time increased, a plating layer serving as a catalyst formed on the fiber surface, confirming the growth of numerous nanowire-shaped CNTs. The average EMI SET values of the carbon fiber-reinforced plastic (CFRP) and glass fiber-reinforced plastic (GFRP) with grown CNTs maximized at approximately 81 and 40 dB, respectively. Carbon fibers with grown CNTs exhibited a significantly higher EMI SET value than the glass fiber-based sample, but the latter showed a higher EMI SET increase rate. This indicates that low-cost, high-quality EMI-shielding materials can be developed through the growth of CNTs on the surface of glass fibers. [ABSTRACT FROM AUTHOR]

An investigation of fluoroindate glass and fiber co-doped with Yb3+/Er3+ ions as a potential temperature sensor was assessed using the fluorescence intensity ratio (FIR) technique. Analysis of thermally coupled levels (TCLs—2H11/2 and 4S3/2), non-thermally coupled levels (non-TCLs—4F7/2 and 4F9/2), and their combination were examined. Additionally, the luminescent stability of the samples under constant NIR excitation using different density power at three different temperatures was carried out. The obtained values of absolute sensitivity (0.003 K−1—glass, 0.0019 K−1—glass fiber 2H11/2 → 4S3/2 transition) and relative sensitivity (2.05% K−1—glass, 1.64% K−1—glass fiber 4F7/2 → 4F9/2 transition), as well as high repeatability of the signal, indicate that this material could be used in temperature sensing applications. [ABSTRACT FROM AUTHOR]

In the case of concrete sustainability, two main ways are generally discussed: (1) the reduction of natural raw materials and (2) the reduction of emissions related to concrete production. Following the second point, there have not yet been reported clear results. This problem is not given enough attention in present publications. This study brings a general view of this issue and a basic comparison with common concrete and traditional reinforcement. This case study deals with the life cycle analysis of a concrete slab made of recycled aggregate concrete with a fine recycled aggregate. The concrete slab was designed according to the limit states of load-bearing capacity and serviceability, which is based on the experimental verification of recycled aggregate concrete properties. Two different reinforcements are compared: (1) ordinary reinforcement by steel bars and (2) glass fibers. Furthermore, scenarios vary due to the slab thickness and reinforcement percentage. The results show the positive environmental impact of replacing natural sand with a fine recycled aggregate. The reduction of climate change potential can be almost 40% in some cases. [ABSTRACT FROM AUTHOR]

Based on the stiffness theory of wave spring, this paper proposes the wave springs made of glass fiber reinforced plastic (GFRP) and investigates the effect of the number of periods on the GFRP wave springs' stiffness and frequency response characteristics. First of all, five different periods of composite wave springs which have identical outside dimensions are designed. Afterwards, the load-displacement curves of the GFRP wave springs are obtained using a combination of experimental and finite element analysis (FEA). Finally, the frequency response characteristics of the GFRP wave springs are measured using a force hammer excitation, and the experiment results of a GFRP wave spring are compared with a metal helical spring. The results show that the stiffness of the GFRP wave spring decreases from 34.84 N/mm to 20.59 N/mm with the increase in the number of periods. As the number of periods increases, the vibration attenuation increases from 16.32 dB to 69.17 dB. The stiffness of the GFRP wave spring is increased by 90.30% and the weight is reduced by 26.78%. The vibration isolation interval and vibration attenuation amplitude of the GFRP wave spring are higher than the metal helical spring. [ABSTRACT FROM AUTHOR]