Influence of Fe x O y and Al 2 O 3 Contents on the Thermal Stability of Iron Ore-Waste Fibers: Key Mechanisms and Control.

Traditional rock wool fibres are susceptible to crystallization and pulverization. To mitigate this, glass fibres were produced from iron ore waste (IOW). When the ratio of Fe2+ and Fe3+ is 1:3 and the Al2O3 content is 10 wt.%, increasing the FexOy content enhances the thermal stability.At an FexOy content of 17–19% and an Al2O3 content of 10–13%, the glass transition temperature (Tg) peaked. Increasing the FexOy content from 10% to 20% enhanced the stability of Si-O and Al-O bonds and increased bridged oxygen, stabilizing the structure. Here, Fe2+ balances structural charges, while Fe3+ replaces some Al atoms in the network. When the Al2O3 content is 10–13% and the FexOy content is 17–19%, the thermal stability of the IOW rock glass reaches its optimal level. At 20% FexOy content, the structure becomes three-dimensional and cyclic, increasing polymerization. Consequently, incorporating FexOy alongside a 10% Al2O3 content improves thermal stability, supporting the development of high-stability rock wool from IOW. This approach also enhances the refractory properties of rock wool fibres within the FexOy-Al2O3-SiO2-MgO-CaO system. [ABSTRACT FROM AUTHOR]