Search

This study reports the use of an inorganic corrosion inhibitor to mitigate dissolved CO2-induced corrosion. Using electrochemical techniques (polarization curves, open circuit potential, polarization resistance, and electrochemical impedance), the effect of adding Nd3+ ions on the corrosion resistance of X52 steel immersed in CO2-saturated brine at 20 °C and 60 °C was evaluated. The polarization curves showed that the Icorr values tend to decrease with increasing Nd3+ ion concentration, up to the optimal inhibition concentration, and that the corrosion potential increases at nobler values. Open circuit potential measurements showed a large increase in potential values immediately after the addition of the Nd3+ ions. Similarly, polarization resistance measurements showed similar trends. It was observed that regardless of temperature, Nd3+ ions can reduce the corrosion rate by more than 97% at doses as low as 0.001 M. Electrochemical impedance measurements confirmed the formation of a protective layer on the steel surface, which caused an increase in the magnitude of the impedance module and phase angle, which indicates an increase in the resistance to charge transfer and capacitive properties of the metallic surface. The characterization of the metallic surface showed that the protective layer was formed by Nd carbonates, whose formation was due to a CO2 capture process. [ABSTRACT FROM AUTHOR]

This study reports the use of an inorganic corrosion inhibitor to mitigate dissolved CO2-induced corrosion. Using electrochemical techniques (polarization curves, open circuit potential, polarization resistance, and electrochemical impedance), the effect of adding Nd3+ ions on the corrosion resistance of X52 steel immersed in CO2-saturated brine at 20 °C and 60 °C was evaluated. The polarization curves showed that the Icorr values tend to decrease with increasing Nd3+ ion concentration, up to the optimal inhibition concentration, and that the corrosion potential increases at nobler values. Open circuit potential measurements showed a large increase in potential values immediately after the addition of the Nd3+ ions. Similarly, polarization resistance measurements showed similar trends. It was observed that regardless of temperature, Nd3+ ions can reduce the corrosion rate by more than 97% at doses as low as 0.001 M. Electrochemical impedance measurements confirmed the formation of a protective layer on the steel surface, which caused an increase in the magnitude of the impedance module and phase angle, which indicates an increase in the resistance to charge transfer and capacitive properties of the metallic surface. The characterization of the metallic surface showed that the protective layer was formed by Nd carbonates, whose formation was due to a CO2 capture process.

This work focuses on the application of an orthogonal array design to the optimization of the facile direct carbonization reaction for the synthesis of neodymium carbonate nanoparticles, were the product particles are prepared based on the direct precipitation of their ingredients. To optimize the method the influences of the major operating conditions on the dimensions of the neodymium carbonate particles were quantitatively evaluated through the analysis of variance (ANOVA). It was observed that the crystalls of the carbonate salt can be synthesized by controlling neodymium concentration and flow rate, as well as reactor temperature. Based on the results of ANOVA, 0.03 M, 2.5 mL min −1 and 30 °C are the optimum values for the above-mentioend parameters and controlling the parameters at these values yields nanoparticles with the sizes of about of 31 ± 2 nm. The product of this former stage was next used as the feed for a thermal decomposition procedure which yielding neodymium oxide nanoparticles. The products were studied through X-ray diffraction (XRD), SEM, TEM, FT-IR and thermal analysis techniques. In addition, the photocatalytic activity of dyspersium carbonate and dyspersium oxide nanoparticles were investigated using degradation of methyl orange (MO) under ultraviolet light. [ABSTRACT FROM AUTHOR]