Search

Functional poly(methyl methacrylate) core-shell microspheres were prepared by dispersion polymerization. An appropriate selection of experimental parameters and in particular of the initiator and stabilizer amount and of the medium solvency power allowed a monodisperse sample as large as 600 nm to be prepared. To this purpose, low initiator concentration, high steric stabilizer amount and a low solvency power medium were employed. The microspheres present a core-shell structure in which the outer shell is constituted by the steric stabilizer which affords carboxylic groups able to interact with basic proteins, such as trypsin, whose adsorption is essentially driven by the carboxylic group density in the microsphere shell. Finally, fluorescent microspheres were prepared for biodistribution studies and shown to be readily taken up by the cells both in vitro and in vivo. These results suggest that these microspheres are promising delivery systems for the development of novel protein-based vaccines.

Not available

Non disponibile

Not available

Partly deuterated hydroxy-terminated poly(styrene d8-r-methyl methacrylate) statistical copolymers with different molecular weights were grafted to a silicon substrate. Then, fully hydrogenated hydroxy-terminated poly(styrene-r-methyl methacrylate) statistical copolymers were spun over the pregrafted substrate and let to react at 250 °C following the time evolution of the brush thickness and composition. Over time, the grafting density of the deuterated polymers decreases, whereas the grafting density of the hydrogenated polymers increases thus indicating the simultaneous occurrence of grafting and degrafting reactions. Moreover, keeping constant the grafting time, the total grafting density decreases as the molecular weight of the hydrogenated polymers increases, until a limiting value is reached when the molecular weight of the incoming polymer is equal to the one of the preformed brush. The overall picture of the experimental data, further supported by hybrid-particle field coarse-grained simulations, suggests that the reactivity of the system is related to the degree of stretching of the brush layer induced by the entering of additional polymer chains. This new vision of the grafting to mechanism implies that the self-limiting nature of this process derives from a mechanochemical control of the reaction rather than from diffusion/penetration effects.

The orientation of block copolymer (BCP) features in thin films can be obtained by spin-coating a BCP solution on a substrate surface functionalized by a polymer brush layer of the appropriate random copolymer (RCP). Although this approach is well established, little work reporting the amount and distribution of residual solvent in the polymer film after the spin-coating process is available. Moreover, no information can be found on the effect of trapped solvent on the interface between the BCP film and RCP brush. In this work, systems consisting of poly(styrene)-b-poly(methyl methacrylate) thin films deposited on poly(styrene-r-methyl methacrylate) brush layers are investigated by combining neutron reflectivity (NR) experiments with simulation techniques. An increase in the amount of trapped solvent is observed by NR as the BCP film thickness increases accompanied by a significant decrease of the interpenetration length between the BCP and RCP, thus suggesting that the interpenetration between grafted chains and block copolymer chains is hampered by the solvent. Hybrid particle-field molecular dynamics simulations of the analyzed system confirm the experimental observations and demonstrate a clear correlation between the interpenetration length and the amount of trapped solvent.

Nanosized PTFE-based core-shell particles can be prepared by emulsifier-free seed emulsion polymerization technique starting from spherical or rod-like PTFE seeds of different size. The shell can be constituted by the relatively high Tg polystyrene and polymethylmethacrylate as well as by low Tg polyacrylic copolymers. Peculiar thermal behavior of the PTFE component is observed due to the high degree of PTFE compartmentalization. A very precise control over the particle size can be exerted by properly adjusting the ratio between the monomers and the PTFE seed. Samples with uniformity ratios suited to build 2D and 3D colloidal crystals are easily prepared. 2D colloidal crystal of spheres leads to very small 2D nanostructuration, useful for the preparation of masks with a combination of nanosphere lithography and reactive ion etching. 3D colloidal crystals were also obtained featuring excellent opal quality.

Potentially viable therapeutic approaches for Duchenne muscular dystrophy (DMD) are now within reach. Indeed, clinical trials are currently under way. Two crucial aspects still need to be addressed: maximizing therapeutic efficacy and identifying appropriate and sensible outcome measures. Nevertheless, the end point of these trials remains painful muscle biopsy to show and quantify protein restoration in treated boys. In this study we show that PMMA/N-isopropil-acrylamide+ (NIPAM) nanoparticles (ZM2) bind and convey antisense oligoribonucleotides (AONs) very efficiently. Systemic injection of the ZM2-AON complex restored dystrophin protein synthesis in both skeletal and cardiac muscles of mdx mice, allowing protein localization in up to 40% of muscle fibers. The mdx exon 23 skipping level was up to 20%, as measured by the RealTime assay, and dystrophin restoration was confirmed by both reverse transcription-PCR and western blotting. Furthermore, we verified that dystrophin restoration also occurs in the smooth muscle cells of the dorsal skin arrector pili, an easily accessible histological structure, in ZM2-AON-treated mdx mice, with respect to untreated animals. This finding reveals arrector pili smooth muscle to be an appealing biomarker candidate and a novel low-invasive treatment end point. Furthermore, this marker would also be suitable for subsequent monitoring of the therapeutic effects in DMD patients. In addition, we demonstrate herein the expression of other sarcolemma proteins such as alpha-, beta-, gamma- and delta-sarcoglycans in the human skin arrector pili smooth muscle, thereby showing the potential of this muscle as a biomarker for other muscular dystrophies currently or soon to be the object of clinical trials.

For subsets of Duchenne muscular dystrophy (DMD) mutations, antisense oligoribonucleotide (AON)-mediated exon skipping has proven to be efficacious in restoring the expression of dystrophin protein. In the mdx murine model systemic delivery of AON, recognizing the splice donor of dystrophin exon 23, has shown proof of concept. Here, we show that using cationic polymethylmethacrylate (PMMA) (marked as T1) nanoparticles loaded with a low dose of 2′-O-methyl-phosphorothioate (2′OMePS) AON delivered by weekly intraperitoneal (IP) injection (0.9 mg/kg/week), could restore dystrophin expression in body-wide striated muscles. Delivery of an identical dose of naked AON did not result in detectable dystrophin expression. Transcription, western, and immunohistochemical analysis showed increased levels of dystrophin transcript and protein, and correct localization at the sarcolemma. This study shows that T1 nanoparticles have the capacity to bind and convoy AONs in body-wide muscle tissues and to reduce the dose required for dystrophin rescue. By immunofluorescence and electron microscopy studies, we highlighted the diffusion pathways of this compound. This nonviral approach may valuably improve the therapeutic usage of AONs in DMD as well as the delivery of RNA molecules with many implications in both basic research and medicine.

Binary homopolymer blends of two hydroxyl-terminated polystyrene (PS-OH) and polymethylmethacrylate (PMMA-OH) homopolymers (Mn similar to 16000 g mol(-1)) were grafted on SiO2 substrates by high-temperature (T > 150 degrees C), short-time (t < 600 s) thermal treatments. The resulting brush layer was tested to screen preferential interactions of the SiO2 substrate with the different symmetric and asymmetric PS-b-PMMA block copolymers deposited on top of the grafted molecules. By properly adjusting the blend composition and the processing parameters, an efficient surface neutralization path was identified, enabling the formation, in the block copolymer film, of homogeneous textures of lamellae or cylinders perpendicularly oriented with respect to the substrate. A critical interplay between the phase segregation of the homopolymer blends and their grafting process on the SiO2 was observed. In fact, the polar SiO2 is preferential for the PMMA-rich phase that forms a homogeneous layer on the substrate, while the PS-rich phase is located at the polymer-air interface. During the thermal treatment, phase segregation and grafting proceed simultaneously. Complete wetting of the PS rich phase on the PMMA rich phase leads to the formation of a PS/PMMA bilayer. In this case, the progressive diffusion of PS chains toward the polymer-SiO2 interface during the thermal treatment allows tuning of the brush layer composition.