Search

The electronic structure of the new diluted magnetic semiconductor Ba$_{1-x}$K$_{x}$(Zn$_{1-y}$Mn$_{y}$)$_{2}$As$_{2}$ ($x=0.30$, $y=0.15$) in single crystal form has been investigated by angle-resolved photoemission spectroscopy (ARPES). %High density of states of nondispersive bands composed of the Zn $3d$ orbitals are observed with ultraviolet incident light. Measurements with soft x-rays clarify the host valence-band electronic structure primarily composed of the As $4p$ states. Two hole pockets around the $\Gamma$ point, a hole corrugated cylinder surrounding the $\Gamma$ and Z points, and an electron pocket around the Z point are observed, and explain the metallic transport of Ba$_{1-x}$K$_{x}$(Zn$_{1-y}$Mn$_{y}$)$_{2}$As$_{2}$. This is contrasted with Ga$_{1-x}$Mn$_{x}$As (GaMnAs), where it is located above the As $4p$ valence-band maximum (VBM) and no Fermi surfaces have been clearly identified. Resonance soft x-ray ARPES measurements reveal a nondispersive (Kondo resonance-like) Mn $3d$ impurity band near the Fermi level, as in the case of GaMnAs. However, the impurity band is located well below the VBM, unlike the impurity band in GaMnAs, which is located around and above the VBM. We conclude that, while the strong hybridization between the Mn $3d$ and the As $4p$ orbitals plays an important role in creating the impurity band and inducing high temperature ferromagnetism in both systems, the metallic transport may predominantly occur in the host valence band in Ba$_{1-x}$K$_{x}$(Zn$_{1-y}$Mn$_{y}$)$_{2}$As$_{2}$ and in the impurity band in GaMnAs.

We have investigated the electronic and magnetic properties of Co-doped Pr0.8Ca0.2MnO3 thin films using various spectroscopic techniques. X-ray absorption and hard x-ray photoemission spectroscopy revealed that the substituted Co ions are in the divalent state, resulting in hole doping on the Mn atoms. Studies of element-selective magnetic properties by x-ray magnetic circular dichroism found a large orbital magnetic moment for the Co ions. These spectroscopic studies reveal that the substituted Co ions play several roles of hole doping for Mn, ferromagnetic superexchange coupling between the Co2+ and Mn4+ ions, and orbital magnetism of the Co2+ ions. Competition among these complex interactions produces the unique electronic and magnetic behaviors including enhanced coercivity of the Co-doped Pr0.8Ca0.2MnO3., Comment: 7 pages and 6 figures

We have studied the electronic structure of Ba(Fe$_{1-x}$Mn$_{x}$)$_{2}$As$_{2}$ ($x$=0.08), which fails to become a superconductor in spite of the formal hole doping like Ba$_{1-x}$K$_{x}$Fe$_{2}$As$_{2}$, by photoemission spectroscopy and X-ray absorption spectroscopy (XAS). With decreasing temperature, a transition from the paramagnetic phase to the antiferromagnetic phase was clearly observed by angle-resolved photoemission spectroscopy. XAS results indicated that the substituted Mn atoms form a strongly hybridized ground state. Resonance-photoemission spectra at the Mn $L_{3}$ edge revealed that the Mn 3d partial density of states is distributed over a wide energy range of 2-13 eV below the Fermi level ($E_F$), with little contribution around $E_F$. This indicates that the dopant Mn 3$d$ states are localized in spite of the strong Mn 3d-As $4p$ hybridization and split into the occupied and unoccupied parts due to the on-site Coulomb and exchange interaction. The absence of superconductivity in Ba(Fe$_{1-x}$Mn$_{x}$)$_{2}$As$_{2}$ can thus be ascribed both to the absence of carrier doping in the FeAs plane, and to the strong stabilizaiton of the antiferromagnetic order by the Mn impurities.

We report the detailed electronic structure of a hole-doped delafossite oxide CuCr_{1-x}Mg_{x}O_{2} (0 <= x <= 0.03) studied by photoemission spectroscopy (PES), soft x-ray absorption spectroscopy (XAS), and band-structure calculations within the local-density approximation +U (LDA+U) scheme. Cr/Cu 3p-3d resonant PES reveals that the near-Fermi-level leading structure has primarily the Cr 3d character with a minor contribution from the Cu 3d through Cu 3d-O 2p-Cr 3d hybridization, having good agreement with the band-structure calculations. This indicates that a doped hole will have primarily the Cr 3d character. Cr 2p PES and L-edge XAS spectra exhibit typical Cr^{3+} features for all x, while the Cu L-edge XAS spectra exhibited a systematic change with x. This indicates now that the Cu valence is monovalent at x=0 and the doped hole should have Cu 3d character. Nevertheless, we surprisingly observed two types of charge-transfer satellites that should be attributed to Cu^{+} (3d^{10}) and Cu^{2+} (3d^{9}) like initial states in Cu 2p-3d resonant PES spectrum for at x=0, while Cu 2p PES spectra with no doubt shows the Cu^{+} character even for the lightly doped samples. We propose that these contradictory results can be understood by introducing no only the Cu 4s state, but also finite Cu 3d,4s-Cr 3d charge transfer via O 2p states in the ground-state electronic configuration., Comment: 9 pages, 9 figures, revised version accepted for publication in Phys. Rev. B