The development of construction materials with the integration of phase change materials (PCMs) has been a topic of wide interest in the scientific community, especially in recent years, due to its positive impact on temperature regulation inside buildings. However, little is known about the behavior of materials doped with PCMs when exposed to accidental or severe environments. Currently, a large area of the planet experiences seasonal freeze–thaw effects, which impact the durability and performance of construction materials. Accordingly, the main objective of this study was to evaluate the damage caused by cyclic freeze–thaw actions on the behavior of a cement mortar, including a PEG-based form-stable PCM. An experimental methodology was developed based on the physical and mechanical characterization of mortars under normal operating conditions and after being subjected to freeze–thaw cycles. The results indicated that, under normal exposure conditions, the incorporation of aggregate functionalized with PCM led to a decrease in the mortar’s water absorption capacity, compressive strength, and adhesion. However, its applicability has not been compromised. Exposure to freeze–thaw cycles caused a loss of mass in the specimens and a decrease in the compressive strength and adhesion capability of the mortar.

This research study focused on the effect of adding boric acid to epoxy resin in order to obtain a composite material with improved properties and performance. To this end, a fine powder of boric acid (H3BO3) was introduced into epoxy resin in different amounts, i.e., 0.5 g, 1.0 g, and 1.5 g. As the matrix of the epoxy composites, styrene-modified epoxy resin based on bisphenol A (BPA) (Epidian 53) was used. It was cross-linked with two types of curing agents, i.e., an amine (ET) and a polyamide (PAC). The mechanical properties of the obtained epoxy composites (in terms of compressive strength, compressive modulus, and compressive strain) were determined at room temperature in order to assess the effect of the addition of boron acid and of the type of curing agent employed to cure the epoxy on these characteristics. Calorimetric measurements were made to highlight any changes in the glass transition temperature (Tg) as a result of the addition of boric acid to epoxy resin. Finally, flammability tests were performed on both Epidian 53/PAC and Epidian 53/ET epoxy composites to analyze their fire behavior and consequently establish the effectiveness of the selected additive as a flame retardant.

The aim of this research was a comparative analysis of selected mechanical properties of epoxy compounds that were modified with metallic fillers and aged in aqueous environments. The tested epoxy compounds consisted of three components: styrene modified epoxy resin based on Bisphenol A, triethylenetetramine curing agent (resin/curing agent ratio of 100:10) and two types of metallic fillers in the form of particles: aluminum alloy (EN AW-2024–AlCu4Mg1) and tin-phosphor bronze (CuSn10P). Samples were subjected to ageing in 4 water environments: low-, medium- and high-mineralized natural water and in a sugar-containing solution for 1, 2 and 3 months. The epoxy samples were subjected to compressive strength tests in accordance with the ISO 604:2002 standard. It was observed that, among others, the compositions seasoned in low-mineralized water usually achieved the highest average compressive strength. As for filler type, using the bronze filler (CuSn10P) usually achieved the highest average compressive strength results.

The widespread use of synthetic plastics, as well as the waste produced at the end of their life cycle, poses serious environmental issues. In this context, bio-based plastics, i.e., natural polymers produced from renewable resources, represent a promising alternative to petroleum-based materials. One potential source of biopolymers is waste from the food industry, the use of which also provides a sustainable and eco-friendly solution to waste management. Thus, the aim of this work concerns the extraction of polysaccharide fractions from lemon, tomato and fennel waste. Characterizing the chemical–physical and thermodynamic properties of these polysaccharides is an essential step in evaluating their potential applications. Hence, the solubility of the extracted polysaccharides in different solvents, including water and organic solvents, was determined since it is an important parameter that determines their properties and applications. Also, acid-base titration was carried out, along with thermoanalytical tests through differential scanning calorimetry. Finally, the electrospinning of waste polysaccharides was investigated to explore the feasibility of obtaining polysaccharide-based membranes. Indeed, electrospun fibers are a promising structure/system via which it is possible to apply waste polysaccharides in packaging or well-being applications. Thanks to processing feasibility, it is possible to electrospin waste polysaccharides by combining them with different materials to obtain porous 3D membranes made of nanosized fibers.

The construction industry is responsible for high energetic consumption, especially associated with buildings’ heating and cooling needs. This issue has attracted the attention of the scientific community, governments and authorities from all over the world, especially in the European Union, motivated by recent international conflicts which forced the countries to rethink their energy policies. Over the years, energy consumption has been based on non-renewable energy sources such as natural gas, oil and coal. Nowadays, it is urgent to implement solutions that aim to minimize these high energetic consumptions and act based on clean and renewable energy sources. In recent years, phase change materials (PCM) have become an area of high interest and development, since they allow to minimize the energy consumption in buildings, based in solar energy, due to their thermal storage capacity. The main objective of this work consists of a perspective of the evolution of the development and application of thermal storage technology through the incorporation of PCM in the construction sector, focusing on the last 10 years of research, showing the most recent developments of its application in construction materials, such as mortars, concrete, incorporation in porous aggregates, naturally based materials, carbon-based materials, boards, blocks and solar thermal systems.

Waste management is an area of significant global concern. The reuse of waste materials (such as: plastics, glass, wood, etc.) in concrete manufacturing has been studied for potential cost savings, improvements in quality, and reduction of environmental impact leading to sustainability. This study examines the performance of concrete containing recycled polyethylene terephthalate (PET) waste in granular form to replace the fine aggregate. A series of concrete specimens for Grade 32 concrete mix were cast using PET granules as partial replacement to fine aggregates in the mixture (0%, 10%, 30%, and 50% replacement by volume of fine aggregate). Important properties such as workability (slump), density, compressive strength, elastic modulus, tensile strength, flexural strength, and crack mouth opening displacement (CMOD) were evaluated together with the microstructural observations. The experimental results indicated that volumetric replacement of fine aggregates with 10% recycled PET granules positively impacted the characteristics of the concrete. The findings further revealed an improvement in the ductility of concrete with recycled PET granules content, albeit the effect was more pronounced with the concrete containing 10% PET granules. The experimental results for the mechanical properties were compared against available Australian and American design guidelines and a strong linear relationship is observed. Lastly, the findings of this study on mechanical properties revealed an optimum performance relative to those reported in the available literature, particularly for the concrete with 10% of fine aggregate replaced by PET granules.

The aim of this work was to study the valorization of argan seed pulp, a waste material obtained from argan oil extraction, for the biosynthesis of polyhydroxybutyrate (PHB). A new species that showed the metabolic capacity for the conversion of argan waste into the bio-based polymer was isolated from an argan crop located in Teroudant, a southwestern region of Morocco, where the arid soil is exploited for goat grazing. The PHB accumulation efficiency of this new species was compared to the previously identified species 1B belonging to the genus Sphingomonas, and results were reported as dry cell weight residual biomass and PHB final yield measured. Temperature, incubation time, pH, NaCl concentration, nitrogen sources, residue concentrations, and culture medium volumes were analyzed with the aim of obtaining a maximum accumulation of PHB. UV-visible spectrophotometry and FTIR analysis confirmed that PHB was present in the material extracted from the bacterial culture. The results of this wide investigation indicated that the new isolated species 2D1 had a higher efficiency in PHB production compared to the previously identified strain 1B, which was isolated from a contaminated argan soil in Teroudant. PHB final yield of the two bacterial species, i.e., the new isolated and 1B, cultivated under optimal culture conditions, in 500 mL MSM enriched with 3% argan waste, were 21.40% (5.91 ± 0.16 g/L) and 8.16% (1.92 ± 0.23 g/L), respectively. For the new isolated strain, the result of the UV-visible spectrum indicates the absorbance at 248 nm, while the FTIR spectrum showed peaks at 1726 cm−1 and 1270 cm−1: these characteristic peaks indicated the presence of PHB in the extract. The data from the species 1B UV-visible and FTIR spectra were previously reported and were used in this study for a correlation analysis. Furthermore, additional peaks, uncharacteristic of standard PHB, suggest the presence of impurities (e.g., cell debris, solvent residues, biomass residues) that persisted after extraction. Therefore, a further enhancement of the sample purification during extraction is recommended for more accuracy in the chemical characterization. If 470,000 tons of argan fruit waste can be produced annually, and 3% of waste is consumed in 500 mL culture by 2D1 to produce 5.91 g/L (21.40%) of the bio-based polymer PHB, it can be estimated that the amount of putative PHB that can be extracted annually from the total argan fruit waste is about 2300 tons.

Polyhydroxybutyrate (PHB) is a biodegradable bio-based polymer synthesized by microorganisms under unfavorable conditions from agro-industrial residues as a source of carbon. These aspects make the bio-based polymer attractive for the mass production of biodegradable plastics, and a definitive replacement for petroleum-based plastics. The aim of this work was to characterize the putative PHB-producing bacterium 1B isolated from the argan soil, to identify the polymer produced, and quantify the PHB production using argan seeds waste. DNA extraction, PCR, and Sanger sequencing were conducted for the molecular identification of strain 1B; the residual biomass and the PHB quantification were measured and compared in the presence of simple sugars and pretreated argan seeds waste. The 1B growth and PHB synthesis were optimized by selecting physical and nutritional parameters: temperature, incubation time, pH, NaCl concentration, and nitrogen sources concentrations. A preliminary characterization of the bio-based polymer extracted was conducted by UV-Visible spectrophotometry and FTIR analysis. The strain 1B was identified as belonging to the genus Sphingomonas. The PHB final yield was higher in a growth culture enriched with argan waste (3.06%) than with simple sugars. The selected conditions for the bacterial optimal growth incremented the PHB final yield to 6.13%, while the increase in the argan residue concentration from 1 to 3% in a larger culture volume led to the PHB final yield of 8.16%. UV-Visible spectrophotometry of the extracted sample reported a remarkable peak at 248 nm, as well as FTIR spectra analysis, showed peaks at 1728 and 1282 wavenumber/cm. Both preliminary characterizations demonstrated that the extracted sample is the bio-based polymer polyhydroxybutyrate. The results reported in this work reveal how the costless available argan seeds can be used for polyhydroxybutyrate production using a novel Sphingomonas species.

The aim of this work was to investigate selected biological and toxicity properties of cured epoxy resin-based compounds based on a bisphenol A epoxy resin, cold-cured by a polyamide and containing two types of metal powders (aluminum and copper). This study involved cytotoxicity analysis, pH measurements, absorbance measurements and sterilization. The cytotoxicity analysis was conducted to determine the harmful degree of the cured epoxy resin. Aimed at identifying toxic agents in cured compounds, the cytotoxicity analysis involved absorbance measurements in an entire wavelength range. Cytotoxicity and absorbance results demonstrated that the extracts of all the tested resin samples had no cytotoxic effects on the cells of living organisms. The absorbance values obtained over the entire wavelength range did not point to the formation of aggregations, which proved that no toxic agents harmful to living organisms were extracted from the resin samples. Based on the results obtained, it can be concluded that all tested compounds, based on epoxy resins, which are also used as adhesives in various applications, are essentially safe materials when using such formulations in a cured state.

This paper presents the results of an experimental study of adhesive joint strength with consideration of the inaccuracy of the hardener dosage, in the context of evaluating the degradation of joints when used either at ambient or elevated temperatures. The butt joint strength characteristics were assessed for two types of adhesives—rigid and flexible—and two curing scenarios—with and without heat curing. An excess hardener was shown to be significantly more unfavourable than its deficiency, which can ultimately be considered as a recommendation for forming epoxy adhesive joint assemblies. In order to fully understand the relationship between the analysed mechanical properties of the material and the influence of component ratio excesses and heating, a process of fitting basic mathematical models to the obtained experimental data was also performed.

The growing interest in piezoresistive sensors has favored the development of numerous approaches and materials for their fabrication. Within this framework, carbon nanotubes (CNTs) are often employed. However, CNTs are a heterogeneous material with different morphological characteristics in terms of length and diameter, and, so far, experimental studies have not usually considered the effect of these parameters on the final sensor performances. Here, we observe how, by simply changing the CNTs length in a solvent-free mechanochemistry fabrication method, different porous 3D elastomeric nanocomposites with different electrical and mechanical properties can be obtained. In particular, the use of longer carbon nanotubes allows the synthesis of porous nanocomposites with better mechanical stability and conductivity, and with a nine-times-lower limit of detection (namely 0.2 Pa) when used as a piezoresistive sensor. Moreover, the material prepared with longer carbon nanotubes evidenced a faster recovery of its shape and electrical properties during press/release cycles, thus allowing faster response at different pressures. These results provide evidence as to how CNTs length can be a key aspect in obtaining piezoresistive sensors with better properties.

The aim of this work is to assess the influence of different commercial diluents on some mechanical properties of two bisphenolic epoxy compounds, cold-cured by a polyamide curing agent, to be employed as epoxy structural adhesives for building and industrial applications. The diluents under analysis were epoxy, bituminous, nitro, acrylic and extraction. The choice of these products was made on the basis of their wide commercial availability as diluents for epoxies used as adhesives and in different industrial and construction applications. The diluents were all added in small proportions, i.e., from 1 to 10 g per 100 g of epoxy resin. The cold-cured epoxy compounds were subjected to compressive (according to ISO 604) and static tensile (according to ISO 527-1) tests. The same mechanical tests were performed on both unmodified epoxy resins, for comparison purposes. On the basis of the obtained results, it was concluded that the influence of the presence of a diluent, and of its amount, on the mechanical properties of epoxy compounds depends on the type of resin and of diluent, as well as on the mechanical characteristics analyzed.

As any other natural or industrial material, polymers can experience some kind of degradation during their service life, resulting in minor to severe changes in their properties [...]

Starting from two low-cost, low-environmental-impact polymers belonging to the Polyethylene Glycol (PEG) family, i.e., PEG 800 and PEG 1000, two form-stable phase change materials were produced. The two PEGs differ in molecular weight and, as a consequence, the melting and crystallization range of temperatures. The PCMs were obtained, including the PEG, in a liquid state, inside the pores of Lecce Stone flakes, obtained as waste pieces from its processing. A simple and inexpensive impregnation process was selected to produce the PCMs, thus adopting low-environmental-impact materials and cheap processes, and respecting circular economy principles. The two PCMs, the first composed of PEG 800, namely LS/PEG800, and the second composed of a 50/50%wt. mix of the different LS/PEGs, i.e., LS/PEG800_LS/PEG1000, were added as aggregates to four types of mortars, based on aerial and hydraulic lime, gypsum, and cement. The obtained mortars were characterized in their fresh state to assess their workability, and in a solid state after a proper cure to determine their characteristic Latent Heat Thermal Energy Storage (LHTES) properties and mechanical properties in both flexural and compressive modes, taking the mortars not containing any PCM as the reference. The results revealed that, with the proper selection of mortar formulations, it was possible to achieve suitable workability and adequate mechanical characteristics. The selection of a PEG with a low range of phase change temperatures, such as PEG 800, allows one to obtain mortars characterized by a melting/crystallization range that can be considered appropriate in applications characterized by cold climates. The production of a mixed PCM, composed of both PEGs, led to mortars displaying a large interval of melting/crystallization temperatures, which could be suitable in both warm and cold climates.

The aim of this experimental investigation was to produce a form-stable phase change material (PCM) able to reduce the need for nonrenewable energy resources required for the heating/cooling of buildings located in regions characterized by different climatic conditions. The innovative PCM must also be sustainable and must be produced according to the principles of the circular economy. To achieve such ambitious goals, a form-stable, sustainable PCM was produced through vacuum impregnation. The form-stable PCM was produced starting from a low-toxicity, low-flammability polyethylene glycol of medium molecular weight (PEG 800), which was included in porous stone granules obtained as waste products of the cutting/processing of local (Lecce) stone. The thermal properties and thermal stability of PEG 800 and of its PCM-composite were evaluated by employing differential scanning calorimetry (DSC) and thermo-gravimetric analysis (TGA). The appropriate parameters to perform the impregnation procedure were identified through rheological and calorimetric analyses. A simple leakage test was performed to assess if the PEG polymer can leak from the stone flakes. Finally, the new PCM was added as an aggregate in aerial-lime-based mortars, and the mortar’s properties were analyzed in fresh (workability) and hardened (flexural and compressive strength and thermal characteristics) states for potential applications, particularly in ancient buildings.

During their useful life, polymers are subject to degradation processes due to exposure to specific environmental conditions over long times. These processes generally lead to changes, almost always irreversible, of properties and performances of polymers, changes which would be useful to be able to predict in advance. To meet this need, numerous investigations have been focused on the possibility to predict the long-term performance of polymers, if exposed to specific environments, by the so called “accelerated aging” tests. In such procedures, the long-term behavior of polymeric materials is typically predicted by subjecting them to cycles of radiations, temperatures, vapor condensation, and other external agents, at levels well above those found in true conditions in order to accelerate the degradation of polymers: this can produce effects that substantially deviate from those observable under natural exposure. Even following the standard codes, different environmental parameters are often used in the diverse studies, making it difficult to compare different investigations. The correlation of results from accelerated procedures with data collected after natural exposure is still a debated matter. Furthermore, since the environmental conditions are a function of the season and the geographical position, and are also characteristic of the type of exposure area, the environmental parameters to be used in accelerated aging tests should also consider these variables. These and other issues concerning accelerated aging tests applied to polymers are analyzed in the present work. However, bearing in mind the limitations of these practices, they can find useful applications for rating the durability of polymeric materials.

The environmental issues caused by the impacts of synthetic plastics use and derived wastes are arising the attention to bio-based plastics, natural polymers produced from renewable resources, including agricultural, industrial, and domestic wastes. Bio-based plastics represent a potential alternative to petroleum-based materials, due to the insufficient availability of fossil resources in the future and the affordable low cost of renewable ones that might be consumed for the biopolymer synthesis. Among the polyhydroxyalkanoates (PHA), the polyhydroxybutyrate (PHB) biopolymer has been synthesized and characterized with great interest due to its wide range of industrial applications. Currently, a wide number of bacterial species from soil, activated sludge, wastewater, industrial wastes, and compost have been identified as PHB producers. This work has the purpose of isolating and characterizing PHB-producing bacteria from the agricultural soil samples of Argania spinosa in the south region of Morocco where the plant species is endemic and preserved. During this research, four heat-resistant bacterial strains have been isolated. Among them, two species have been identified as endospore forming bacteria following the Schaffer-Fulton staining method with Malachite green and the Methylene blue method. Black intracellular granules have been appreciated in microscopy at 100× for both strains after staining with Sudan black B. The morphological and biochemical analyses of the isolates, including sugar fermentation and antibiotic susceptibility tests, preliminarily identified the strains 1B and 2D1 belonging to the genus Serratia and Proteus, respectively.

The effects of aging exposures to three non-saline aqueous environments on the compressive mechanical properties of a calcium carbonate-filled bisphenolic epoxy adhesive, cold-cured with the addition of two curing agents suitable for the cure at ambient temperature (i.e., Mannich base and triethylenetetramine), were assessed. The amount of the added filler (CaCO3) varied from 1 to 3 g per 100 g of resin; the immersion times in each of the selected medium varied from 1 to 10 months. It was found that the mechanical properties measured in compression mode on cylindrical specimens of unfilled and CaCO3-loaded epoxy were scarcely influenced by the kind of curing agent employed; only the compressive modulus was limitedly affected by this parameter. Referring to the behavior when aged in water, the CaCO3-filled epoxies displayed noticeable growths in modulus, small reductions in strength, and limited variations in strain, with a certain influence of the exposure time, especially when comparing the properties at the lowest time with those at medium–long times. On the basis of the results of statistical MANOVA analysis, it can be concluded that among the compositional factors (i.e., the type of curing agent employed to cure the epoxy compounds and the micro-filler content), only the amount of CaCO3 filler significantly affects the compressive modulus.

The degradation of polymeric components is of considerable interest to the nuclear industry and its regulatory bodies. The objective of this work was the development of a methodology to determine the useful life—based on the storage temperature—of acrylonitrile O-rings used as mechanical sealing elements to prevent leakages in nuclear equipment. To this aim, a reliability-based approach that allows prediction of the use-suitability of different storage scenarios (that involve different storage times and temperatures) considering the further required in-service performance, is presented. Thus, experimental measurements of Shore A hardness have been correlated with storage variables (temperature and storage time). The storage (and its associated hardening) was proved to have a direct effect on in-service durability, reducing this by up to 60.40%. Based on this model, the in-service performance was predicted; after the first three years of operation the increase in probability of failure (POF) was practically insignificant. Nevertheless, from this point on, and especially, from 5 years of operation, the POF increased from 10% to 20% at approximately 6 years (for new and stored). From the study, it was verified that for any of the analysis scenarios, the limit established criterion was above that of the storage time premise considered in usual nuclear industry practices. The novelty of this work is that from a non-destructive test, like a Shore A hardness measurement, the useful life and reliability of O-rings can be estimated and be, accordingly, a decision tool that allows for improvement in the management of maintenance of safety-related equipment. Finally, it was proved that the storage strategies of our nuclear power plants are successful, perfectly meeting the expectations of suitability and functionality of the components when they are installed after storage.

An experimental nano-filled coating, based on a fluorine resin containing SiO2 nano-particles, was applied on calcareous stones, representative of materials used in buildings and monuments of the Mediterranean basin; for comparison purposes, two commercial products were applied on the same substrates. The efficacy of the protective treatments was assessed by analyzing different characteristics of the three experimental/commercial products, i.e., color changes and permeability to water vapor to evaluate the treatments’ harmlessness; capillary water absorption and water stone contact angle to evaluate the protection against water ingress; oleophobicity of the treated surfaces and the behavior under staining by acrylic blue-colored spray paint and felt-tip marker to verify the anti-graffiti action. Finally, the properties of the treated stone surfaces were analyzed also after the application of pancreatin, used to simulate bird excreta (guano). The protective coatings were found to promote graffiti removal, reducing also the detrimental effects due to simulated guano. The experimental nano-filled product, in addition, was able to provide outstanding performance but using smaller amounts of product in comparison to commercial systems.

Academic and industrial efforts around the world are continuously engaged to develop new smart materials that can provide efficient alternatives to conventional construction materials and improve the energy-efficiency in buildings or are able to upgrade, repair, and protect existing infrastructures [...]

The purpose of this study was to assess the effects of different aqueous environments (i.e., demineralised, distilled and spring water) on the mechanical properties of a cold-cured bisphenolic epoxy resin modified with the addition of calcium carbonate filler, typically employed as structural adhesive. The parameters selected for the analysis have been; the kind of curing agent employed to cure the epoxy resin at ambient temperature (i.e., Mannich base and triethylenetetramine); the load of calcium carbonate added to liquid epoxy (i.e., from 1 to 3 g per 100 g of resin) and; the duration of the exposure to the different aging conditions (i.e., from 1 to 10 months). Cylindrical specimens of calcium carbonate-modified epoxy systems were tested in compression mode, before and after each of the aging regimes. The effect of the selected curing agents is very small, and they are both suitable for a cure at ambient temperature, on the unfilled epoxy on compressive maximum strength and strain at break; the choice of the hardener affects instead the compressive modulus. The CaCO3 amount was demonstrated to have a significant effect on the mechanical characteristics of un-aged epoxy systems, leading to growth in compressive modulus and maximum strength with reductions in strain at break. Generally speaking, the aging time noticeably affects the compressive properties of calcium carbonate-modified epoxies while almost negligible is the kind of water employed in each exposure regime. Notwithstanding the adverse effects of an aqueous environment on compressive mechanical properties of CaCO3-filled epoxies, these systems keep compressive modulus and maximum strength greater than, and close to, respectively, the same characteristics measured on unaged unfilled control epoxies, demonstrating the positive effect of the addition of this kind of filler to epoxy-based structural adhesives, especially with the addition of 2 and 3 g of CaCO3 per 100 g resin. The results obtained in this study demonstrated that it is possible to contrast the detrimental effects observed in cold-cured epoxy-based structural adhesives due to their aging in water upon the addition of limited amounts (particularly at 2 and 3 g per 100 g resin) of a cheap CaCO3 filler.

Cyclodextrins (CDs) are oligosaccharides, comprising 6 (α), 7 (β), or 8 (γ) glucose residues, used to prepare oil-in-water emulsions and improve oil stability towards degradation. In this research, the aptitude of α-, β-, and γ-CDs to form complexes with a supercritical CO2 extracted lycopene-rich tomato oil (TO) was comparatively assessed. TO/CD emulsions and the resulting freeze-dried powders were characterized by microscopy, Fourier transform infrared-attenuated total reflection (FTIR-ATR), and differential scanning calorimetry (DSC), as well as for their antioxidant activity. Furthermore, carotenoid stability was monitored for 90 days at 25 and 4 °C. Confocal and SEM microscopy revealed morphological differences among samples. α- and β-CDs spontaneously associated into microcrystals assembling in thin spherical shells (cyclodextrinosomes, Ø ≈ 27 µm) at the oil/water interface. Much smaller (Ø ≈ 9 µm) aggregates were occasionally observed with γ-CDs, but most TO droplets appeared “naked”. FTIR and DSC spectra indicated that most CDs did not participate in TO complex formation, nevertheless structurally different interfacial complexes were formed. The trolox equivalent antioxidant capacity (TEAC) activity of emulsions and powders highlighted better performances of α- and β-CDs as hydrophobic antioxidants-dispersing agents across aqueous media. Regardless of CDs type, low temperature slowed down carotenoid degradation in all samples, except all-[E]-lycopene, which does not appear efficiently protected by any CD type in the long storage period.

In this study, poly(lactic-co-glycolic acid) microspheres (PLGA MS)for controlled protein release by double emulsion-solvent evaporation were produced and characterized for their morphological and technological features. MS autocatalytic degradation was described by a mathematical model based on a Michaelis and Menten-like chemical balance. Here, for the first time MS degradation was correlated to the advancement of MS degradation front with respect to the degraded radius, derived from mass loss experiments. The model can satisfactorily describe the kinetics of advancement of the degradation front experimentally derived for all MS formulations, especially when produced at higher PLGA concentrations.

This paper aims at reviewing the works published in the last five years (2016–2020) on polymer nanocomposites based on epoxy resins. The different nanofillers successfully added to epoxies to enhance some of their characteristics, in relation to the nature and the feature of each nanofiller, are illustrated. The organic–inorganic hybrid nanostructured epoxies are also introduced and their strong potential in many applications has been highlighted. The different methods and routes employed for the production of nanofilled/nanostructured epoxies are described. A discussion of the main properties and final performance, which comprise durability, of epoxy nanocomposites, depending on chemical nature, shape, and size of nanoparticles and on their distribution, is presented. It is also shown why an efficient uniform dispersion of the nanofillers in the epoxy matrix, along with strong interfacial interactions with the polymeric network, will guarantee the success of the application for which the nanocomposite is proposed. The mechanisms yielding to the improved properties in comparison to the neat polymer are illustrated. The most important applications in which these new materials can better exploit their uniqueness are finally presented, also evidencing the aspects that limit a wider diffusion.

Increasing concerns about climate change and global warming bring about technical steps for the development of several energy-efficient technologies. Since the building sector is one of the largest energy users for cooling and heating necessities, the incorporation of a proper energy-efficient material into the building envelopes could be an interesting solution for saving energy. Phase change material (PCM)-based thermal energy storage (TES) seems suitable to provide efficient energy redistribution. This is possible because the PCM is able to store and release its latent heat during the phase change processes that occurs according to the environmental temperature. The purpose of this paper was the characterization of the thermal properties of a composite PCM (i.e., Lecce stone/poly-ethylene glycol, previously developed) incorporated into mortar compositions based on different binders (i.e., hydraulic lime and cement). The study was carried out using an experimental set up through which it was possible to simulate the different seasons of the years. It was observed that the addition of PCM in mortars leads to a decrease of the maximum temperatures and increase of the minimum temperatures. Furthermore, the results shown a reduction of the heating and cooling needs, thus confirming the capability of this material to save energy.

Different hybrid epoxy formulations were produced and cold-cured, monitoring the properties development during low temperature curing and aging. All systems were based on silane functionalized bis-phenol A (DGEBA) resins (Part A), cured at ambient temperature with two amine hardeners (Part B). The different components of the formulations were selected on their potential capability to bring about enhancements in the glass transition temperature. The durability of the produced hybrids was probed in comparison to the corresponding neat epoxies by monitoring changes in glass transition temperature (Tg) and flexural mechanical properties after exposure to different levels of humidity and immersion in water and at temperatures slightly higher than the local ambient temperature, in order to simulate the conditions encountered during summer seasons in very humid environments. The thermal degradation resistance of the hybrid systems was also evaluated by thermogravimetric analysis.

The curing reaction of a commercial cold-curing structural epoxy resin, specifically formulated for civil engineering applications, was analyzed by thermal analysis as a function of the curing time and the sample thickness. Original and remarkable results regarding the effects of curing time on the glass transition temperature and on the residual heat of reaction of the cold-cured epoxy were obtained. The influence of the sample thickness on the curing reaction of the cold-cured resin was also deeply investigated. A highly exothermal reaction, based on a self-activated frontal polymerization reaction, was supposed and verified trough a suitable temperature signal acquisition system, specifically realized for this measurement. This is one of the first studies carried out on the curing behavior of these peculiar cold-cured epoxy resins as a function of curing time and thickness.

This work is aimed to present an innovative technology for the reinforcement of beams for urban furniture, produced by in-mold extrusion of plastics from solid urban waste. This material, which is usually referred to as “recycled plastic lumber”, is characterized by very poor mechanical properties, which results in high deflections under flexural loads, particularly under creep conditions. The Prowaste project, founded by the EACI (European Agency for Competitiveness and Innovation) in the framework of the Eco-Innovation measure, was finalized to develop an innovative technology for selective reinforcement of recycled plastic lumber. Selective reinforcement was carried out by the addition of pultruded glass rods in specific positions with respect to the cross section of the beam, which allowed optimizing the reinforcing efficiency. The reinforcement of the plastic lumber beams with pultruded rods was tested at industrial scale plant, at Solteco SL (Alfaro, Spain). The beams obtained, characterized by low cost and weight, were commercialized by the Spanish company. The present paper presents the most relevant results of the Prowaste project. Initially, an evaluation of the different materials candidates for the reinforcement of recycled plastic lumber is presented. Plastic lumber beams produced in the industrial plant were characterized in terms of flexural properties. The results obtained are interpreted by means of beam theory, which allows for extrapolation of the characteristic features of beams produced by different reinforcing elements. Finally, a theoretical comparison with other approaches which can be used for the reinforcement of plastic lumber is presented, highlighting that, among others, the Prowaste concept maximizes the stiffening efficiency, allowing to significantly reduce the weight of the components.

Eco-sustainable, low toxic and low flammable poly-ethylene glycol (PEG) was forced into flakes of the porous Lecce stone (LS), collected as stone cutting wastes, employing a very simple cheap method, to produce a “form-stable” phase change material (PCM). The experimental PCM was included in mortars based on different binders (hydraulic lime, gypsum and cement) in two compositions. The main thermal and mechanical characteristics of the produced mortars were evaluated in order to assess the effects due to the incorporation of the PEG-based PCM. The mortars containing the PEG-based PCM were found to be suitable as thermal energy storage systems, still displaying the characteristics melting and crystallization peaks of PEG polymer, even if the related enthalpies measured on the mortars were appreciably reduced respect to pure PEG. The general reduction in mechanical properties (in flexural and compressive mode) measured on all the mortars, brought about by the presence of PEG-based PCM, was overcome by producing mortars possessing a greater amount of binder. The proposed LS/PEG composite can be considered, therefore, as a promising PCM system for the different mortars analyzed, provided that an optimal composition is identified for each binder.

The construction industry is responsible for consuming large amounts of energy. The development of new materials with the purpose of increasing the thermal efficiency of buildings is, therefore, becoming, imperative. Thus, during the last decades, integration of Phase Change Materials (PCMs) into buildings has gained interest. Such materials can reduce the temperature variations, leading to an improvement in human comfort and decreasing at the same time the energy consumption of buildings, due to their capability to absorb and release energy from/in the environment. In the present paper, recent experimental studies dealing with mortars or concrete-containing PCMs, used as passive building systems, have been examined. This review is mainly aimed at providing information on the currently investigated materials and the employed methodologies for their manufacture, as well as at summarizing the results achieved so far on this subject.

The development of improved cold-cured resins, to be used as either adhesives or matrices for FRP (fiber reinforced polymer) composites employed in the construction industry, has become the focus of several academic and industrial research projects. It is expected that the use of nano-structured organic–inorganic hybrid materials could represent a realistic alternative to commercial epoxy-based resins due to their superior properties, especially in terms of higher durability against: moisture, temperatures, harsh environments, and fire. In this context, organic–inorganic epoxy hybrids were synthesized by a modified sol–gel method without the addition of water. The experimental formulations were prepared starting from a mixture of a silane-functionalized epoxy resin, alkoxysilane components and a deep eutectic solvent (DES) based on a blend of choline chloride and urea. The latter was added in two different loads in order to analyze in depth its effect as a promoter for an effective dispersion of silica nano-phases, formed through hydrolysis and condensation reactions, into the cross-linked epoxy network. The produced formulations were cold-cured for different time spans in the presence of two hardeners, both suitable for a curing process at ambient temperature. In this first part of a wider experimental program, several analyses were carried out on the liquid (rheological and calorimetric) and cold-cured (calorimetric, thermogravimetric, dynamic-mechanical, flexural mechanical, and morphological) systems to evaluate and quantify the improvement in properties brought about by the presence of two different phases (organic and inorganic) in the same epoxy-based hybrid system.

An innovative photopolymerizable microgel modified UV-cured acrylic-silica hybrid formulation was developed and characterized for possible use as protective coating for different substrates. A deep investigation, aiming at providing a strong scientific basis for the production of organic-inorganic (O-I) hybrids exhibiting phase co-continuity, was firstly carried out. The O-I hybrid first proposed in this study was obtained from organic precursors with a high siloxane content, which are mixed with tetraethoxysilane (TEOS) in such a way to produce co-continuous silica nanodomains dispersed within the crosslinked organic phase, as a result of the sol-gel process. The first part of the research deals with the selection and optimization of suitable systems through appropriate chemical modifications, in order to ensure that curing reactions can be carried out at room temperature and in the presence of UV radiation. Firstly, the silica domains are formed, followed by crosslinking reactions of the acrylic groups in the oligomer via a free radical polymerization. The crosslinking reaction was controlled with the use of a suitable photoinitiator. Most of the experimental work was devoted to understanding the morphology of the hybrid system, both in uncured and cured states, and to assess its final thermal and optical properties, using different experiential techniques.

In materials research, the development of polymer nanocomposites (PN) is rapidly emerging as a multidisciplinary research field with results that could broaden the applications of polymers to many different industries. PN are polymer matrices (thermoplastics, thermosets or elastomers) that have been reinforced with small quantities of nano-sized particles, preferably characterized by high aspect ratios, such as layered silicates and carbon nanotubes. Thermal analysis (TA) is a useful tool to investigate a wide variety of properties of polymers and it can be also applied to PN in order to gain further insight into their structure. This review illustrates the versatile applications of TA methods in the emerging field of polymer nanomaterial research, presenting some examples of applications of differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), dynamic mechanical thermal analysis (DMTA) and thermal mechanical analysis (TMA) for the characterization of nanocomposite materials.

The use of fiber reinforced polymer (FRP) composites for the rehabilitation of buildings or other infrastructure is increasingly becoming an effective and popular solution, being able to overcome some of the drawbacks experienced with traditional interventions and/or traditional materials. The knowledge of long-term performance and of durability behavior of FRP, in terms of their degradation/aging causes and mechanisms taking place in common as well as in harsh environmental conditions, still represents a critical issue for a safe and advantageous implementation of such advanced materials. The research of new and better performing materials in such fields is somewhat limited by practical and economical constrains and, as a matter of fact, is confined to an academic argument.