Search

Recent experiments have revealed that accelerated tungsten (W) nanostructure growth occurs during the exposure to helium (He) plasmas with an additional W deposition, and mm-thick large-scale fiberform nanostructures (LFNs) are formed when certain condition is satisfied. In order to reveal whether accelerated growth occurs in fusion device, it is important to understand the annealing process in addition to the growth process. In this study, we will perform thermal treatment of W LFNs. Detailed observation reveals that the LFNs shrink at a faster rate than that of conventional fuzz, though it takes longer time to fully be reintegrated to the surface because the thickness is orders of magnitude greater.

We have developed a compact divertor plasma simulator (CDPS) that can produce steady-state deuterium and/or helium plasmas with densities above ∼ 1018 m−3 for Plasma-Wall Interaction (PWI) studies of neutron-irradiated materials. The maximum particle flux is about 1022 m−2s−1. The CDPS was installed and is being operated in the radiation-controlled area of the International Research Center for Nuclear Materials Science, Institute for Materials Research, Tohoku University. We are able to control sample temperature within uncertainty of 5 °C during plasma exposure by adjusting the cooling air flow rate to the sample holder. The CDPS has a sample-carrier system, which makes it possible to transfer a plasma-irradiated sample from the sample holder to an infrared heater for analysis using thermal desorption spectroscopy (TDS) without exposing it to the air. This avoids the oxidation of the sample and minimizes the time between the end of plasma exposure and TDS analysis. An ITER-like tungsten (W) sample (A.L.M.T. Corp.), which has been irradiated by neutrons to 0.06 dpa in a fission reactor, was exposed to a deuterium plasma in the CDPS. The experimental results clearly show that the total deuterium retention in the neutron-irradiated W sample increases significantly in comparison with a pristine W, as demonstrated by broadening of the TDS spectrum at high temperatures., source:https://doi.org/10.1585/pfr.12.1405040, identifier:0000-0001-7826-0046

This overview presents recent results regarding hydrogen isotope absorption and emission dynamics in neutron-irradiated tungsten (W) using our recently developed Compact Diverter Plasma Simulator (CDPS), a linear plasma device in a radiation-controlled area. Neutron irradiation to 0.016 - 0.06 displacement per atom resulted in a significant increase in deuterium (D) retention due to trapping effects of radiation-induced defects. We analyzed the dependency of D retention on the D plasma fluence by exposing neutron-irradiated pure W to D plasma at 563 K over a range of D fluence values. The total retention was revealed to be proportional to the square root of D fluence, indicating that the implanted D atoms first occupy the defects caused by neutron-irradiation near the surface and then the defects located in deeper regions. We further investigated the effects of post-plasma annealing on D emission; neutron-irradiated pure W was exposed to D plasma at 573 K and was then annealed at the same temperature for 30 hours. Approximately 10% of the absorbed D was released by annealing, suggesting that a heat treatment of the plasma-facing component of a fusion reactor at moderately elevated temperatures could contribute to the removal of accumulated hydrogen isotopes. The experimental results obtained in this study were only available by investigating neutron-irradiated specimens with the CDPS system, which will be essential for future studies of material behavior and plasma-wall interactions in the fusion reactor environment., source:https://doi.org/10.1585/pfr.15.1505081