Dynamic surface modification of suspended graphene at high temperatures was directly observed with in situ scanning transmission electron microscopy (STEM) measurements. The suspended graphene devices were prepared on a SiN membrane substrate with a hole so that STEM observations could be conducted during Joule heating. Current-voltage characteristics of suspended graphene devices inside the STEM chamber were measured while monitoring and controlling the temperature of graphene by estimating the electrical power of the devices. During the in situ STEM observation at high temperatures, residual hydrocarbon adsorbents that had remained on graphene effectively evaporated creating large, atomically clean graphene areas. At other places, dynamic changes in the shape, position, and orientation of adsorbents could be directly observed. The temperature of the suspended graphene sample was estimated to reach up to 2000 K during the experiment, making graphene an efficient high-temperature micrometer-sized electron-transparent hot plate for future experiments in microscopes.

Transparent conducting electrodes (TCEs) have attracted considerable attention towards the development of flexible optoelectronic devices. In this study, mixed-dimensional TCEs are fabricated based on the two-dimensional graphene and one-dimensional electrospun metal fiber that can address the shortcomings of each electrode. In comparison with other TCEs, the Ag fiber/graphene hybrid electrodes exhibited a highly stable morphology (67% lower peak-to-valley ratio), low sheet resistance (approximately 11 Ω/sq), high transmittance (approximately 94%), high oxidation stability with excellent flexibility, and outstanding chemical stability. The multiple functionalities of the transparent and flexible hybrid structure highlight its potential for applications in emerging electronics and highly stable optoelectronics.

With a growing interest in two-dimensional transition metal dichalcogenide (TMD), etching the structure of TMD for further application is a challenge due to its thermal stability by a high melting point. Here, we report on diverse etched structures in MoS2 flakes based on the catalytic oxidation using a Co catalyst. After impregnated with a Co precursor, MoS2 flakes were oxidized in air by induction heating to obtain an etched structure. As a result, microscopic observation revealed that diverse etched structures in the shape of a channel and a pit were created in the MoS2 flakes. Especially, the catalytic etching by CoO nanoparticles produced two types of channels which have an angle of 120° and 150°, respectively. Also, a pit with a depth of approximately 3 nm was found on the oxidized surface of MoS2 flakes. Our results open a new perspective to control the edge site of TMD flakes including S element as well as MoS2 flakes.

We report improved conductance by reducing the work function via incorporation of hydrogen into VO2 nanowires. The VO2 nanowires were prepared using the chemical vapor deposition method with V2O5 powder on silicon substrates at 850 °C. Hydrogenation was carried out using the high-pressure hydrogenation method. Raman spectroscopy confirmed that the incorporated hydrogen atoms resulted in a change in the lattice constant of the VO2 nanowires (NWs). To quantitatively measure the work function of the nanowires, Kelvin probe force microscopy (KPFM) was employed at ambient conditions. We found that the work function decreased with increasing H2 pressure, which also resulted in increased conductance. This is associated with hydrogen diffused into the VO2 that acts as a donor to elevate the Fermi level, which was also confirmed by KPFM. From these results, tuning of the reversible electrical properties of VO2 NWs, including the conductance and work function, can be achieved by incorporating hydrogen at relatively moderate temperatures.

In this study, high-performance few-layered ReS2 field-effect transistors (FETs), fabricated with hexagonal boron nitride (h-BN) as top/bottom dual gate dielectrics, are presented. The performance of h-BN dual gated ReS2 FET having a trade-off of performance parameters is optimized using a compact model from analytical choice maps, which consists of three regions with different electrical characteristics. The bottom h-BN dielectric has almost no defects and provides a physical distance between the traps in the SiO2 and the carriers in the ReS2 channel. Using a compact analyzing model and structural advantages, an excellent and optimized performance is introduced consisting of h-BN dual-gated ReS2 with a high mobility of 46.1 cm2 V−1 s−1, a high current on/off ratio of ≈106, a subthreshold swing of 2.7 V dec−1, and a low effective interface trap density (Nt,eff) of 7.85 × 1010 cm−2 eV−1 at a small operating voltage (2 channel through Y-function method as a function of constant top gate bias.

Therapeutic agents, such as drugs and cells, play an essential role in virtually every treatment of injury, illness, or disease. However, the conventional practices of drug delivery often result in undesirable side effects caused by drug overdose and off-target delivery. In the case of cell delivery, the survival rate of the transplanted cells is extremely low and difficulties with the administration route of cells remain a problem. Recently, magnetically actuated microrobots have started offering unique opportunities in targeted therapeutic delivery due to their tiny size and ability to access hard-to-reach lesions in a minimally invasive manner; considerable advances in this regard have been made over the past decade. Here, recent progress in magnetically actuated microrobots, developed for targeted drug/cell delivery, is presented, with a focus on their design features and mechanisms for controlled therapeutic release. Additionally, the practical challenges faced by the microrobots, and future research directions toward the swift bench-to-bedside translation of the microrobots are addressed.

This study aims to quantify the stresses of sonographers using two different ultrasound devices, one of conventional and one of ergonomic design. A total of 20 obstetricians and gynecologists participated in this study, and two types of tasks (scanning and positioning) were evaluated while using the two different devices. To quantify workload, four dependent variables (muscle activity, estimated grip force, subjective comfort rating, and task time) were measured. The muscular activity required while using the conventional device was 14.4% MVC (Maximum voluntary contraction) for the scanning task, which was significantly higher than that of the ergonomic device. The subjective comfort rating for the conventional design was lower than that of the ergonomic design. For the positioning task, the ergonomic device (33.2% MVC) resulted in significantly higher muscle activity in the extensor digitorum (ED) and flexor digitorum superficialis (FDS) than the conventional design (22.2% MVC), whereas the deltoid muscle showed significantly lower activity than in users of conventional design (4.5% MVC). Ergonomically-designed ultrasound devices improve ease of moving and the probe's supporters, reduce physical load and increase ease of use for sonographers. Our results may be used as guidelines for usability testing of ultrasound devices.

We construct a theoretical framework to understand the crack density of bloodstains by modeling whole blood as a suspension of binary size colloid particles. Our analysis based upon theories of soft capillarity and porous flows explains the observed increase of the crack density with increase of blood viscosity and decrease of environmental humidity. The results have direct implications on forensic science and medical diagnosis.

Irradiation of MoS

To extract the confined waveguided light in organic light-emitting diodes (OLEDs), inserting a low refractive index (RI) periodic structure between the anode and organic layer has been widely investigated as a promising technology. However, the periodic-structure-based light extraction applied inside devices has been shown to severely distort spectrum and affect EL characteristics. In this study, a simple light extraction technology using periodic low-RI nanodot array (NDA) as internal light extraction layer has been demonstrated. The NDA was fabricated simply via laser interference lithography (LIL). The structural parameters of periodic pattern, distance, and height were easily controlled by the LIL process. From computational analysis using finite-difference time-domain (FDTD) method, the NDA with 300 nm pitch and 0.3 coverage ratio per unit cell with 60 nm height showed the highest enhancement with spectral-distortion-minimized characteristics. Through both computational and experimental systematic analysis on the structural parameters of low-RI NDA-embedded OLEDs, highly efficient OLEDs have been fabricated. Finally, as representative indicators, hexagonal and rectangular positioned NDA-embedded OLEDs showed highly improved external quantum efficiencies of 2.44 (+29.55%) and 2.77 (+57.38%), respectively. Furthermore, the disadvantage originating from the nanoscale surface roughness on the transparent conductive oxide was minimized.

Light extraction in organic light-emitting diodes (OLEDs) was improved by applying SnO

Transition-metal dichalcogenide (TMD) materials with two-dimensional layered structures and stable surfaces are well suited for transparent and flexible device applications. In order to completely utilize the advantages of thickness control and fabrication of various heterostructure stacks, we proposed a transfer method of TMD field-effect transistors (FETs) and TMD complementary metal-oxide-semiconductor (CMOS) circuits from a Si/SiO2 substrate to a flexible substrate. We compared the characteristics of transferred MoS2 and WSe2 FETs with those of the corresponding devices transferred after channel passivation with an Al2O3 layer on a flexible substrate. Al2O3 passivation further stabilized the transfer of the entire device with electrodes. A CMOS circuit with MoS2 and WSe2 materials could be successfully transferred to a polyethylene terephthalate substrate after the channel passivation. This implies that TMD circuits can be easily fabricated on polymer substrates, which makes them suitable for use in semiconductor processes, for various applications.

Underwater sensors that detect the distance and direction of acoustic sources are critical for surveillance monitoring and target detection in the water. Here, we propose an axial vector sensor that utilizes a small (~1 cm3) compressive-type piezoelectric accelerometer using piezoelectric single crystals. Initially, finite element analysis (FEA) was used to optimize the structure that comprised piezoelectric Pb(Mb1/3Nb2/3)O3-28%PbTiO3 single crystals on a tungsten seismic mass. The receiving voltage sensitivity (RVS) was enhanced through geometric optimization of the thickness and sensing area of the piezoelectric material and the seismic mass. The estimated maximum RVS of the optimized vector sensor was &minus, 212 dB. FEA simulations and practical measurements were used to verify the directivity of the vector sensor design, which exhibited a dipole pattern. The dipole beam pattern was used to obtain cardioid patterns using the simulated and measured results for comparison. The results clearly showed the feasibility of using the proposed piezoelectric single-crystal accelerometer for a compressive-type vector sensor.

Single-walled carbon nanotube (SWCNT) is generally used as a networked structure in the fabrication of a field-effect transistor (FET) since it is known that one-third of SWCNT is electrically metallic and the remains are semiconducting. In this case, the presence of metallic paths by metallic SWCNT (m-SWCNT) becomes a significant technical barrier which hinders the networks from achieving a semiconducting behavior, resulting in a low on/off ratio. Here, we report on an easy method of controlling the on/off ratio of a FET where semiconducting SWCNT (s-SWCNT) and m-SWCNT constitute networks between source and drain electrodes. A FET with SWCNT networks was simply sonicated under water to control the on/off ratio and network density. As a result, the FET having an almost metallic behavior due to the metallic paths by m-SWCNT exhibited a p-type semiconducting behavior. The on/off ratio ranged from 1 to 9.0 × 104 along sonication time. In addition, theoretical calculations based on Monte-Carlo method and circuit simulation were performed to understand and explain the phenomenon of a change in the on/off ratio and network density by sonication. On the basis of experimental and theoretical results, we found that metallic paths contributed to a high off-state current which leads to a low on/off ratio and that sonication formed sparse SWCNT networks where metallic paths of m-SWCNT were removed, resulting in a high on/off ratio. This method can open a chance to save the device which has been considered as a failed one due to a metallic behavior by a high network density leading to a low on/off ratio.

Organic light-emitting diodes (OLEDs) with an enhanced outcoupling efficiency and a suppressed efficiency roll-off were fabricated by inserting a nanosize pixel-defining layer (nPDL) that defines the OLED emission region as an array of nanoholes. The outcoupling efficiency of the nano-arrayed OLEDs was increased through the reduced surface plasmon polariton loss caused by the wavy diffraction grating at the metal–organic interface, and their efficiency roll-off was suppressed through the diffusive exciton outside the exciton-formation zone. As a result, the nano-arrayed OLEDs exhibited enhancements of 148.7% in the power efficiency and 137.0% in the external quantum efficiency at 1000 cd m−2 compared with a reference device. Furthermore, the critical current density (J0) where the external quantum efficiency decreased to half of its initial value was improved by a factor of 2.5.

In this study, we designed a smooth, highly flexible, mechanically robust poly(vinyl-butyral) (PVB)/silver nanowire (AgNW) composite transparent conducting electrode (TCE) integrated with a random nanocone (RNC) to enhance the light extraction of flexible organic light-emitting diodes (OLEDs). The RNC was fabricated by reactive-ion etching (RIE) on AgNW embedded in PVB. As the etching time increased, the size of the RNC became larger. The sheet resistance and transmittance of PVB/AgNW with the RNC was 21.7 Ω/sq and ~87%, respectively. For the PVB/AgNW, the change in sheet resistance was only 2.6% when a 2,000-bend test was performed. The maximum external quantum efficiency was 28.3% when RNC 700 s was used as a green phosphorescent OLED. In addition, for current efficiency and power efficiency, RNC 700 s increased 1.4 times over RNC 0 s. RNC is free of viewing-angle-dependent color and brightness distortion. PVB/AgNW and RNC are practical ways to overcome the brittleness of conventional indium tin oxide and improve the efficiency of flexible OLEDs. Finally, this product is expected to be applied to various flexible optical devices.

We report improved conductance by reducing the work function via incorporation of hydrogen into VO2 nanowires. The VO2 nanowires were prepared using the chemical vapor deposition method with V2O5 powder on silicon substrates at 850 °C. Hydrogenation was carried out using the high-pressure hydrogenation method. Raman spectroscopy confirmed that the incorporated hydrogen atoms resulted in a change in the lattice constant of the VO2 nanowires (NWs). To quantitatively measure the work function of the nanowires, Kelvin probe force microscopy (KPFM) was employed at ambient conditions. We found that the work function decreased with increasing H2 pressure, which also resulted in increased conductance. This is associated with hydrogen diffused into the VO2 that acts as a donor to elevate the Fermi level, which was also confirmed by KPFM. From these results, tuning of the reversible electrical properties of VO2 NWs, including the conductance and work function, can be achieved by incorporating hydrogen at relatively moderate temperatures.

Electrospun metal fiber is a promising flexible transparent electrode owing to its extremely long length and facile fabrication process. However, metal-fiber electrodes have problems with chemical and thermal stability and nonuniform emission in organic light-emitting diode (OLED) at low luminance. In this study, we proposed a Ag fiber/IZO composite electrode with high stability. Ag fiber/IZO composite electrodes exhibited chemical and thermal stability. In addition, it was demonstrated that the OLED with the Ag fiber/IZO composite electrode operated stably, and the uniform emission of the OLED with metal-fiber electrodes improved by using highly conductive IZO film.

This work was financially supported by the Korea Institute of Energy Technology Evaluation and Planning (KETEP) (Grant No. 20143030011850), and funded by the Ministry of Trade, Industry and Energy (MOTIE). I. Kim acknowledges KUUC (KIST-UNIST-Ulsan Center for Convergent Materials) for partial financial support.

In this work, graphene field effect transistors (FETs) were fabricated on a trench structure made by carbonized poly(methylmethacrylate) to modify the graphene surface. The trench-structured devices showed different characteristics depending on the channel orientation and the pitch size of the trenches as well as channel area in the FETs. Periodic corrugations and barriers of suspended graphene on the trench structure were measured by atomic force microscopy and electrostatic force microscopy. Regular barriers of 160 mV were observed for the trench structure with graphene. To confirm the transfer mechanism in the FETs depending on the channel orientation, the ratio of experimental mobility (3.6-3.74) was extracted from the current-voltage characteristics using equivalent circuit simulation. It is shown that the number of barriers increases as the pitch size decreases because the number of corrugations increases from different trench pitches. The noise for the 140 nm pitch trench is 1 order of magnitude higher than that for the 200 nm pitch trench.

Plasmacytoid dendritic cells (pDCs) are unique bone-marrow-derived cells that produce large amounts of type I interferon in response to microbial stimulation. Furthermore, pDCs also promote T cell tolerance in sterile-inflammation conditions. However, the immunomodulatory role of aortic pDCs in atherosclerosis has been poorly understood. Here, we identified functional mouse and human pDCs in the aortic intima and showed that selective, inducible pDC depletion in mice exacerbates atherosclerosis. Aortic pDCs expressed CCR9 and indoleamine 2,3-dioxygenase 1 (IDO-1), an enzyme involved in driving the generation of regulatory T cells (Tregs). As a consequence, loss of pDCs resulted in decreased numbers of Tregs and reduced IL-10 levels in the aorta. Moreover, antigen presentation by pDCs expanded antigen-specific Tregs in the atherosclerotic aorta. Notably, Tregs ablation affected pDC homeostasis in diseased aorta. Accordingly, pDCs in human atherosclerotic aortas colocalized with Tregs. Collectively, we identified a mechanism of atheroprotection mediated by tolerogenic aortic pDCs.

In this study, random nanoscale rods (RNRs) with a double refractive index were fabricated via spin coating, dry etching, and sputtering, which are processes that are extensively applied in industry. With regard to optical properties, the RNRs with a double refractive index (RNRsD) exhibited a total transmittance that was >90% in the visible range and an optical haze in the range of 42%-50% at a wavelength of 520 nm. Organic light-emitting diodes (OLEDs) with RNRsD, where SiO2 was deposited on the RNRs via radiofrequency sputtering, exhibited an enhancement of 34.5% in the external quantum efficiency compared with OLEDs with the bare substrate. Furthermore, the color variation of the OLEDs with the optimal RNRsD with respect to a change in the viewing angle was improved from color coordinates of Δ(x, y) = (0.032, 0.034) to Δ(x, y) = (0.014, 0.014). Therefore, the proposed film can be used as a scattering layer for enhancing the light extraction and viewing angle of OLEDs by reducing the substrate mode light loss and changing the direction of light. In addition to using a low-temperature fabrication process that does not employ a photomask and a lithographic template, the proposed method is applicable to flexible devices because it uses a polymer and a thin inorganic film.

Light extraction in organic light-emitting diodes (OLEDs) was improved by applying SnO x nanocones grown via thermal annealing in a low-O2 atmosphere. SnO x was easily fabricated through thermal processing after Sn deposition. The diameter of the SnO x nanocones was controlled by changing the deposition thickness of Sn. The SnO x nanocones induced strong Mie scattering, which reduced the total internal reflection in the glass substrate. Consequently, the OLED with SnO x nanocones exhibited a 23% increase in the external quantum efficiency compared with a reference device.

We demonstrated light extraction improvement by applying a scattering layer of Ag nanoparticles physically synthesized through a low-temperature annealing process to flexible organic light-emitting diodes (OLEDs). In general, increasing the size of Ag nanoparticles is preferred to increase light scattering, but a high-temperature annealing process (∼400 °C) is required to produce them. However, flexible substrates generally cannot withstand high-temperature processes. In this study, we formed Ag nanoparticles at a low temperature of ∼200 °C by inserting a poly(3,4-ethylenedioxythiophene) polystyrene sulfonate buffer layer, thus promoting Ag dewetting. As a result, the scattering layer of enlarged Ag nanoparticles formed at low temperatures increased the external quantum efficiency by 24% in a flexible OLED compared to a reference device.

We investigated a low-temperature mask-free process for preparing random nanoscale rods (RNRs) as a scattering layer. The process involves spin coating and dry etching, which are already widely applied in industry. Our film exhibited 17–33% optical haze at 520 nm wavelength and 95% total transmittance in the visible range. Therefore, this film can be used as a scattering layer for improving viewing angle characteristics and decreasing substrate mode loss in organic light-emitting diodes (OLEDs). Specifically, we focussed on varying the height and density of the RNRs to control the optical characteristics. As a result, the OLEDs with RNRs revealed a variation in colour coordinates of Δ(x, y) = (0.007, 0.014) for a change in the viewing angle, which was superior to those without the RNRs that displayed a variation of Δ(x, y) = (0.020, 0.034) in CIE 1931. Moreover, the OLEDs with RNRs exhibited 31% enhanced external quantum efficiency compared to those of the OLEDs with the bare substrate. The flexibility of the polymer used for the RNRs and the plasma treatment suggests that the RNRs can be applied to flexible OLED displays and lighting systems.

We report on p-type and n-type thermoelectric (TE) materials made of single-walled carbon nanotube (SWCNT) networks incorporated into the cellulose fiber structure of a common packaging paper. This leads the paper to possess both mechanical flexibility from the cellulose fibers as a supporting matrix and the high electrical conductivity originating from the SWCNTs. Thermoelectric power of up to ±50 μV K−1 was successfully obtained as well, depending on their electronic type. Further, to demonstrate its thermoelectric voltage (VTEP) and generating power, a couple of thermoelectric modules composed of both p-type and n-type composite layers were assembled in series. The produced VTEP shows a quasi-linearity with respect to the number of p–n couples and the temperature difference ΔT. Our testing module enables the provision of VTEP and power generation as large as ≈16.8 mV and ≈75.5 nW upon inducing a 50 K temperature difference. The feasibility of commercial TE modules consisting of 10, 100 and 1000 p–n SWCNT couples was numerically calculated, taking into account our experimental results.

With the advances in the separation and purification of carbon nanotubes (CNTs), the use of highly pure metallic or semiconducting CNTs has practical merit in electronics applications. When highly pure CNTs are applied in various fields, CNT networks are preferred to individual CNTs. In such cases, the presence of an electrical path becomes crucial in the network. In this study, we report on the electrical percolation thresholds of semiconducting single-walled carbon nanotube (s-SWCNT) networks, and their electrical characteristics in field-effect transistors (FET). Using the Monte Carlo method, s-SWCNT networks were randomly generated in the channels defined by the source-drain electrodes of the FET. On the basis of percolation theory, the percolation thresholds of s-SWCNT networks were obtained at different channel lengths (2, 6, and 10 μm) by generating random s-SWCNT networks 100 times. The network density corresponding to the electrical percolation threshold was theoretically gained at each channel length. As a result, the network densities at the percolation thresholds for the channel lengths of 2, 6, and 10 μm were 6.8, 9.0, and 9.9 tube μm(-2), respectively. In addition, SPICE calculations were performed for each s-SWCNT network, constituting an electrical path between the source and the drain electrodes of the FET. In all channel lengths, the on/off ratio of the s-SWCNT networks was enhanced with increasing network density. Finally, we found a power law relationship between the on/off ratio of the s-SWCNT networks and the network density at the percolation threshold.

This paper reports on an easy process of fabricating conductive carbon nanotube (CNT) paper by recycling waste paper. In the absence of a dispersion agent, we just mixed and ground multi-walled carbon nanotubes (MWCNT) and shredded A4 paper together in water. CNT paper was obtained after filtering and rolling the mixture of MWCNT and waste paper. The thickness of the CNT paper was controllable by using different volumes of the mixture in the fabrication. Scanning electron microscope images showed that MWCNT was evenly stuck to the surface of the cellulose. Raman spectra indicated that the structure of a sidewall of MWCNT was influenced by cellulose through the mixing process. In addition, the thermal stability of CNT paper was enhanced in proportion to the amount of MWCNT used. The presence of MWCNT also contributed to the enhancement in the elastic properties of CNT paper. Depending on the amount of MWCNT and the thickness of CNT paper, the sheet resistance of CNT paper varied from 49.1 to 3365.6 Ω sq−1. This CNT paper can be utilized in the fields of electronic devices and energy storage devices, leading to easy mass-production at low cost.

Charge carrier transport in multilayer van der Waals (vdW) materials, which comprise multiple conducting layers, is well described using Thomas-Fermi charge screening (λTF ) and interlayer resistance (Rint ). When both effects occur in carrier transport, a channel centroid migrates along the c-axis according to a vertical electrostatic force, causing redistribution of the conduction centroid in a multilayer system, unlike a conventional bulk material. Thus far, numerous unique properties of vdW materials are discovered, but direct evidence for distinctive charge transport behavior in 2D layered materials is not demonstrated. Herein, the distinctive electron conduction features are reported in a multilayer rhenium disulfide (ReS2 ), which provides decoupled vdW interaction between adjacent layers and much high interlayer resistivity in comparison with other transition-metal dichalcogenides materials. The existence of two plateaus in its transconductance curve clearly reveals the relocation of conduction paths with respect to the top and bottom surfaces, which is rationalized by a theoretical resistor network model by accounting of λTF and Rint coupling. The effective tunneling distance probed via low-frequency noise spectroscopy further supports the shift of electron conduction channel along the thickness of ReS2 .

In adipose tissue, agonists of the β3-adrenergic receptor (ADRB3) regulate lipolysis, lipid oxidation, and thermogenesis. The deficiency in the thermogenesis induced by neuroblast differentiation-associated protein AHNAK in white adipose tissue (WAT) of mice fed a high-fat diet suggests that AHNAK may stimulate energy expenditure via development of beige fat. Here, we report that AHNAK deficiency promoted browning and thermogenic gene expression in WAT but not in brown adipose tissue of mice stimulated with the ADRB3 agonist CL-316243. Consistent with the increased thermogenesis, Ahnak−/− mice exhibited an increase in energy expenditure, accompanied by elevated mitochondrial biogenesis in WAT depots in response to CL-316243. Additionally, AHNAK-deficient WAT contained more eosinophils and higher levels of type 2 cytokines (IL-4/IL-13) to promote browning of WAT in response to CL-316243. This was associated with enhanced sympathetic tone in the WAT via upregulation of adrb3 and tyrosine hydroxylase (TH) in response to β-adrenergic activation. CL-316243 activated PKA signalling and enhanced lipolysis, as evidenced by increased phosphorylation of hormone-sensitive lipase and release of free glycerol in Ahnak−/− mice compared to wild-type mice. Overall, these findings suggest an important role of AHNAK in the regulation of thermogenesis and lipolysis in WAT via β-adrenergic signalling.

The practical applicability of electronic devices is largely determined by the reliability of field effect transistors (FETs), necessitating constant searches for new and better-performing semiconductors. We investigated the stress-induced degradation of MoS2 multilayer FETs, revealing a steady decrease of drain current by 56% from the initial value after 30 min. The drain current recovers to the initial state when the transistor is completely turned off, indicating the roles of soft-traps in the apparent degradation. The noise current power spectrum follows the model of carrier number fluctuation–correlated mobility fluctuation (CNF–CMF) regardless of stress time. However, the reduction of the drain current was well fitted to the increase of the trap density based on the CNF–CMF model, attributing the presence of the soft-type traps of dielectric oxides to the degradation of the MoS2 FETs.

Fabrication of junction-free Ag fiber electrodes for flexible organic light-emitting diodes (OLEDs) is demonstrated. The junction-free Ag fiber electrodes are fabricated by electrospun polymer fibers used as an etch mask and wet etching of Ag thin film. This process facilitates surface roughness control, which is important in transparent electrodes based on metal wires to prevent electrical instability of the OLEDs. The transmittance and resistance of Ag fiber electrodes can be independently adjusted by controlling spinning time and Ag deposition thickness. The Ag fiber electrode shows a transmittance of 91.8% (at 550 nm) at a sheet resistance of 22.3 Ω □-1 , leading to the highest OLED efficiency. In addition, Ag fiber electrodes exhibit excellent mechanical durability, as shown by measuring the change in resistance under repeatable mechanical bending and various bending radii. The OLEDs with Ag fiber electrodes on a flexible substrate are successfully fabricated, and the OLEDs show an enhancement of EQE (≈19%) compared to commercial indium tin oxide electrodes.

In this work, an easy method to etch monolayer graphene is shown by catalytic oxidation in the presence of ZnO nanoparticles (NPs). The catalytic etching of monolayer graphene, which was transferred to the channel of field-effect transistors (FETs), was performed at low temperature by heating the FETs several times under an inert gas atmosphere (ZnO + C → Zn + CO or CO2). As the etching process proceeded, diverse etched structures in the shape of nano-channels and pits were observed under microscopic observation. To confirm the evolution of etching, current–voltage characteristics of monolayer graphene were measured after every step of etching by catalytic oxidation. As a result, the conductance of monolayer graphene decreased with the development of etched structures. This decrease in conductance was analyzed by percolation theory in a honeycomb structure. Finally, well-patterned graphene was obtained by oxidizing graphene under air in the presence of NPs, where Al was deposited on graphene as a mask for designed patterns. This method can substitute graphene etching via carbon hydrogenation using H2 at high temperature.

We investigated the induction heating effect on device characteristics of flexible molybdenum disulfide (MoS2) field-effect transistors (FETs). A polyimide film was employed as a flexible substrate, and poly(3,4-ethylenedioxythiophene):polystyrene sulfonate was coated on the flexible substrate as a bottom gate. After the annealing process on the flexible MoS2 FETs by induction heating, the field effect mobility was enhanced from 2.13 to 5.58 cm2/V·s with the slight increase of the on-off ratio from 5.17 × 102 to 1.98 × 103. Moreover, the low field mobility was almost unchanged from 7.75 to 7.33 cm2/V·s, indicating that the induction heating mainly contributed to the enhancement of the device performances by contact improvement between electrodes and MoS2. With the simple model of the diode and resistor connected in series, it was confirmed that the Schottky diode disappeared with contact enhancement. Our findings can contribute to the contact improvement with minimum damage when low dimensional nanomateri...

To develop the advanced electronic devices, the surface/interface of each component must be carefully considered. Here, we investigate the electrical properties of metal-semiconductor nanoscale junction using conductive atomic force microscopy (C-AFM). Single-crystalline CdS, CdSe, and ZnO one-dimensional nanostructures are synthesized via chemical vapor transport, and individual nanobelts (or nanowires) are used to fabricate nanojunction electrodes. The current-voltage (I -V) curves are obtained by placing a C-AFM metal (PtIr) tip as a movable contact on the nanobelt (or nanowire), and often exhibit a resistive switching behavior that is rationalized by the Schottky (high resistance state) and ohmic (low resistance state) contacts between the metal and semiconductor. We obtain the Schottky barrier height and the ideality factor through fitting analysis of the I-V curves. The present nanojunction devices exhibit a lower Schottky barrier height and a higher ideality factor than those of the bulk materials, which is consistent with the findings of previous works on nanostructures. It is shown that C-AFM is a powerful tool for characterization of the Schottky contact of conducting channels between semiconductor nanostructures and metal electrodes.

We demonstrate the fabrication of shallow Si nanopillar structures at a submicron scale which provides broadband antireflection for crystalline Si (c-Si) solar cells in the wavelength range of 350 nm–1100 nm. The Si random nanopillars were made by reactive ion etch (RIE) processing with thermally dewetted Sn metals as an etch mask. The diameters and coverages of the Si nanopillars were adjusted in a wide range of the nanoscale to microscale by varying the nominal thickness of the Sn metals and subsequent annealing temperatures. The height of the nanopillars was controlled by the RIE process time. The optimal size of the nanopillars, which are 340 nm in diameter and 150 nm in height, leads to the lowest average reflectance of 3.6%. We showed that the power conversion efficiency of the c-Si solar cells could be enhanced with the incorporation of optimally designed Si random nanopillars from 13.3% to 14.0%. The fabrication scheme of the Si nanostructures we propose in this study would be a cost-effective and promising light trapping technique for efficient c-Si solar cells.

Advanced secondary (rechargeable) batteries require high energy density and high structural stability anodes and cathodes. High volumetric energy density is particularly desirable for micro-electronic devices and portable applications, however it can impact almost any application. In current commercial lithium-ion batteries, carbon-based anodes are dominant; however, their capacity and structural stability are not ideal due to the low theoretical capacity (372 mAh g‒1) and intrinsically fragile structure of carbon. Silicon is a very attractive anode material because of its huge theoretical capacity (~4,200 mAh g‒1). Nevertheless, the solid electrolyte interphase (SEI) formation on Si surface is generally unstable due to the large volume change during lithiation-delithiation (400%), which leads to substantial capacity decay with cycling. Here we present an anode design consisting of closed-end Si nanotubes coated with carbon on both sides (C@Si@C). This sandwich-like structure with double-sided carbon coatings provides both good electrical conductivity and effective protection of electrochemically active Si, leading to a stable SEI. Because the C@Si@C nanotube array was fabricated onto a three-dimensional (3D) scaffold, the anode exhibits a considerable energy density. Our results show this nanotube array exhibits a capacity of about 2,200 mAh g-1, and a nearly constant Coulombic efficiency of about 98% over 60 cycles. Correspondingly, the volumetric energy density (~750 mAh cm–3) considerably exceeds the volumetric energy density of commercial graphite anodes (~300 mAh cm–3). Through a series of control experiments, we find the C@Si@C nanotube array gives much better capacity and structure stability compared to the Si nanotubes without carbon coatings, the ZnO@C@Si@C nanorods, a Si thin film on Ni foam, and C@Si and Si@C nanotubes. In-situ SEM observations on lithiation-delithiation shows a stable structure evolution of the sandwich nanotube. Through stress and plastic strain modeling, while the plastic strain in the nanotubes increases gently, the one in the nanorods increases dramatically. Since the plastic strain amplitude in the nanorods is significantly higher than that in the nanotubes, in terms of a low-cycle fatigue mechanism of Si during lithiation-delithiation, it is expected that the nanorods would fail with significantly fewer lithiation-delithiation cycles compared to the nanotubes. Our findings show this design of sandwich-structured nanotube array is effective for fabricating anodes with both stable structure retention and high energy density. We believe this strategy is quite general can find application for a large variety of other anode and cathode designs.

In the present study, we demonstrate the effect of vacancy evolution on high-pure metallic single-walled carbon nanotube (m-SWCNT) networks by observing the electrical characteristics of the networks on the field-effect transistor (FET). By catalytic oxidation using Co catalyst, vacancy evolution was gradually realized in high-pure m-SWCNT formed as networks between source-drain electrodes of FET. The evolution of vacancy defects in the m-SWCNT networks gradually proceeded by heating FET several times at 250 °C in air. Atomic force microscopic images showed the presence of the Co catalyst nanoparticles, which were evenly formed in the m-SWCNT networks between the electrodes of FET. Vacancy evolution was confirmed by monitoring the D- and G-bands in the Raman spectra measured from the networks after every step of the catalytic oxidation. With vacancy evolution in the networks, the D-band gradually increased, and the transconductance of m-SWCNT networks drastically decreased. In addition, the metallic behaviour of the m-SWCNT networks was converted into a semiconducting one with an on/off ratio of 2.7.