Search

CNPq - Conselho Nacional de Desenvolvimento Científico e Tecnológico FAPESP - Fundação de Amparo à Pesquisa do Estado de São Paulo The effects of tooth brushing could affect the long-term esthetic outcome of composite restorations. This study evaluated the effect of two different emission spectrum light-curing units on the surface roughness, roughness profile, topography and microhardness of bulk-fill composites after in vitro toothbrushing. Valo (multiple-peak) and Demi Ultra (single-peak) curing lights were each used for 10s to polymerize three bulk-fill resin composites: Filtek Bulk Fill Posterior Restorative (FBF), Tetric EvoCeram Bulk Fill (TET) and Surefil SDR Flow (SDR). After 30,000 reciprocal strokes in a toothbrushing machine, the roughness profile, surface roughness, surface morphology, and microhardness were examined. Representative SEM images were also obtained. When light-cured with the Demi Ultra, SDR showed the most loss in volume compared to the other composites and higher volume loss compared to when was light-cured with Valo. The highest surface roughness and roughness profile values were found in SDR after toothbrushing, for both light-curing units tested. FBF always had the greatest microhardness values. Light-curing TET with Valo resulted in higher microhardness compared to when using the Demi Ultra. Confocal and SEM images show that toothbrushing resulted in smoother surfaces for FBF and TET. All composites exhibited surface volume loss after toothbrushing. The loss in volume of SDR depended on the light-curing unit used. Toothbrushing can alter the surface roughness and superficial aspect of some bulk-fill composites. The choice of light-curing unit did not affect the roughness profile, but, depending on the composite, it affected the microhardness

Orientadores: Andreia Bolzan de Paula, Regina Maria Puppin Rontani Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba Resumo: O objetivo neste estudo foi avaliar o potencial inibitório do crescimento bacteriano, a área de desmineralização e a resistência da união ao cisalhamento (RU) bráquete-esmalte, colados com compósito contendo metacrilato de triclosan (MT). Para avaliar a atividade antimicrobiana foram confeccionadas amostras de compósito com MT (CMT) e sem MT (SMT) (n=4). Cepas de Streptococcus mutans foram reativadas por 24 horas e ajustadas à densidade óptica de 1.0 (DO550nm) e diluídas em BHI suplementado com 1% de sacarose. Biofilmes foram estaticamente formados sobre a superfície dos materiais durante 24 horas. Em seguida, as amostras foram lavadas e os biofilmes formados sonicados em solução salina. As células dispersas foram diluídas serialmente e cultivadas em Mitis Salivarius Agar. Após 48 horas de incubação, as células foram contabilizadas. Quatro experimentos independentes foram realizados em quadruplicada. Os dados foram submetidos ao teste t de Student com significância de 5%. Para avaliar a desmineralização ao redor dos bráquetes, 20 blocos de esmalte bovino (6mmx4mm) foram distribuídos em dois grupos (n=10) de acordo com o material para colagem (CMT e SMT). Após a colagem dos bráquetes, os blocos de esmalte foram submetidos ao desafio cariogênico com biofilme de S. mutans por 24 horas. A dureza Knoop do esmalte foi mensurada com microdurômetro usando carga de 50 gf durante 5 segundos. Trinta penetrações foram feitas em cada amostra, em 5 regiões, 6 profundidades diferentes e os valores submetidos à análise de variância de três fatores para medidas repetidas (?=0,05). Para avaliar a RU, 60 dentes bovinos foram distribuídos em três grupos (n=20) de acordo com os materiais para colagem (CMT, SMT e Transbond XT). Os bráquetes metálicos foram colados no esmalte e fotoativados com aparelho Bluephase. As amostras foram armazenadas em água destilada a 37oC por 24 horas e submetidas a 1500 ciclos térmicos. A RU foi avaliada em máquina de ensaio com velocidade de 0,5 mm/min até ocorrer falha. Os dados foram submetidos à análise de variância de um fator e ao teste de Tukey (?=0,05). O Índice de Remanescente do Adesivo (IRA) foi avaliado e os valores submetidos ao teste de Mann-Whitney. O compósito CMT apresentou menor acúmulo de biofilme quando comparado ao SMT, em todos os experimentos realizados. Não foram encontradas diferenças significativas nos valores da dureza do esmalte ao redor dos bráquetes colados com os compósitos SMT e CMT. Maiores valores de RU foram obtidos pelo grupo Transbond XT (18,38 ± 5,74). Não foram encontradas diferenças estáticas entre os grupos SMT (12,16 ± 4,74) e CMT (10,22 ± 3,80). Pode-se concluir que o compósito CMT foi efetivo na inibição do crescimento de S. mutans; porém, não reduziu a desmineralização do esmalte ao redor dos bráquetes. A incorporação do antimicrobiano no compósito não causou influência negativa nos valores de RU Abstract: The aim of this study was to evaluate the effect on the inhibition of bacterial growth, reduction enamel demineralization around orthodontic brackets and shear bond strength (SBS) of bracket bonding on enamel, using a composite resin modified by the addition of triclosan methacrylate (MT). To evaluate the antimicrobial effect, composite samples were prepared with MT (CMT) and without MT (SMT) (n = 4). Overnight-Incubated Streptococcus mutans culture was adjusted to 1.0 optical density (OD550nm) and diluted in BHI with 1% sucrose. Biofilms were grown for 24 hours on the samples. All the samples were washed in saline solution to remove loosely adherent cells, the viable cells in the solution were quantified. Twelve dilutions were made from this initial suspension in MSA. The petri dishes were incubated for 48 hours. After incubation the colonies were counting. Four independent experiments were performed in quadruplicate. The data were analyzed using Student's t-test. To evaluate enamel demineralization around orthodontic brackets, 20 bovine enamel blocks (6mmx4mm) were divided into two groups (CMT e SMT). Brackets were bonding in the blocks, then the specimens were exposed to a cariogenic challenge using Streptococcus mutans for 24 hours. A microhardness tester with a Knoop diamond under a 50-g load for 5 seconds was used for the microhardness analysis. Thirty indentations were made in a half block, in five positions and six different depths and values subjected to analysis of variance of three factors for repeated measures (? = 0.05). ANOVA and Tukey post-hoc test were used. For the SBS test, 60 bovine teeth were divided into three groups in accordance with the materials (CMT, SMT and Transbond XT). The brackets were positioned at the buccal surface and cured for 20 seconds by a Bluephase light curing unit. The groups were thermocycled 1500 times and then were tested. The SBS was determined with a universal testing machine. After brackets failure, the Adhesive Remnant Index (ARI) score was verified. The data were analyzed using ANOVA one way, Tukey post-hoc test and Mann-Whitney test. The CMT composite exhibited an inhibitory effect on S. mutans growth when compared to SMT in all experiments. No significant differences were found in the microhardness around the bracket, the MT was not efficient in the reducing enamel demineralization. Transbond XT (18.38 ± 5.74) had a significant difference when compared with SMT (12, 16 ± 4.74) and CMT (10.22 ± 3.80). The MT was effective to inhibit of S. mutans grown, however it was not effective to prevent the enamel demineralization around the brackets. The incorporation of the antimicrobial in the composite did not influence negatively on the SBS on enamel Mestrado Materiais Dentários Mestre em Materiais Dentários CAPES

Se describe el caso de una niña de 4 años 3 meses de edad, con parálisis cerebral discinética con tendencia espástica causada por citomegalovirus con síndrome convulsivo, quien fue referida a la Clínica Integral del Niño de la Facultad de odontología de la Universidad Nacional Mayor de San Marcos (UNMSM) para su tratamiento. La paciente fue evaluada de manera integral con procedimientos odontológicos no convencionales sin sedación consciente, teniendo en cuenta la edad y el nivel de colaboración que presentaba, además de trabajar con un equipo multidisciplinario médico- odontológico. Se destaca el hecho que la paciente redujo significativamente la frecuencia de convulsiones luego del tratamiento odontológico, finalmente se resalta la importancia de integrar al odontólogo en el equipo multidisciplinario que trabaja con estos pacientes.

El propósito de esta investigación consistió en evaluar los efectos de dos colutorios orales (un colutorio con fluoruro de sodio al 0,05% y un colutorio de agua con sal al 5%) sobre la placa bacteriana y el pH salival en una población de soldados del ejercito. La muestra estuvo conformada por tres grupos: un grupo uso un colutorio de fluoruro de sodio al 0,05%, otro uso un colutorio de agua con sal y un tercer grupo control utiltzó agua destilada durante 40 días. Las características de la población permitió controlar importantes variables intervinientes tales como la dieta, higiene bucal de los soldados, momentos de higiene y cumplimiento del protocolo señalado. Se usó un pHmetro calibrado y el índice simplificado de Green y Vermillon, para medir el pH salival y el índice de placa bacteriana respectivamente. Se utilizó el análisis de varianza, la prueba F y la prueba T de student para muestras apareadas y establecer diferencias. Los resultados del trabajo de investigación indicaron que tanto el colutorio con fluoruro de sodio al 0,05% como e1 colutorio con agua con sal al 5% se comportan de manera similar sobre la placa bacteriana, disminuyéndola al cabo de 40 días; mientras que ninguno de los colutorios fue capaz de alterar el pH salival de forma significativa.