Search

Alkaline-earth metal oxide aerogels prepared by sol–gel method followed by autoclave drying are nanocrystalline mesoporous materials with high reactivity. Bulk solid-state reaction of MgO aerogels with CF2Cl2 takes place after a long induction period, during which the active sites are accumulated on the surface of the nanoparticles. It was found that vanadium addition has a promoting effect on this reaction accelerating the process of the active sites formation. A method for characterization of electron-acceptor sites by electron spin resonance spectroscopy using perylene as the spin probe was developed. A good correlation was observed between the rate of the CF2Cl2 destructive sorption and the concentration of weak electron-acceptor sites. Simplified models of such sites were suggested. The acid sites on the modified MgO surface were supposed to be originated from separation of the charged fragments resulting in the surface polarization. Uncompensated oxygen substitution for chlorine and/or fluorine ions leads to appearance of Lewis acid sites while HCl/HF chemisorption results in Bronsted acid sites formation.

Calcium aluminates (CA) with a mayenite structure have attracted a growing interest during the last decades. The present paper reports the preparation of vanadia-mayenite composites performed via an impregnation of pure CA with ammonium vanadate solution. The properties of the prepared materials were explored by a low-temperature nitrogen adsorption/desorption technique, X-ray diffraction analysis, transmission electron microscopy, and spin probe method. As revealed, the addition of vanadium significantly affects the textural properties and the porous structure of mayenite. The blockage of micropores by vanadium species is supposed. The spin probe electron paramagnetic resonance technique based on the adsorption of 1,3,5-trinitrobenzene, phenothiazine, and diphenylamine has been applied to study the active sites on the surface of the composite samples. The results demonstrated an increase in the concentration of weak electron-acceptor sites when the vanadium loading was 10 wt%. X-ray diffraction analysis and transmission electron microscopy studies showed that the composites consist of few phases including mayenite, CaO, and calcium vanadates. [ABSTRACT FROM AUTHOR]

С/Al2O3 and C/MgO carbon-mineral composites were synthesized by propane decomposition over Al2O3 at 600–650 °C and MgO carbonization in 1,3-butadiene at 600 °C. The synthesized carbon-mineral composites were studied by EPR, XRD and transmission electron microscopy. It was found that a mosaic structure of carbon clusters was formed on the internal surface of the oxides and gradually grew until it covered its whole surface. A method for synthesis of graphene materials by using MgO as a template followed by its dissolution in hydrochloric acid was suggested. A maximum was observed on the dependence of the graphene surface area on the carbon concentration in the composites. The highest specific surface area of the synthesized graphene about 1800–1900 m2/g was observed for the samples obtained from C-MgO composites containing 8–10 wt.% C. [ABSTRACT FROM AUTHOR]

A study is carried out on the reaction between CF2Cl with nanoscale MgO at 325 degree Celsius and higher temperature. The reaction results in the formation of MgFe2 as a predominant solid product, with CCl4, and CO2 formed as the main gaseous products when excess of halocarbons is used.

The HRTEM study indicates that the composition of the mineral constituent in the carbon-mineral materials was not changed by the carbon deposition. A singular balanced Lorentzian line owing to carbon deposits has been observed in the ESR range of the carbon-mineral materials.

Transformation of nanocrystalline Mg(OH)2 to MgO under dynamic vacuum in a temperature range of 570-770 K is studied by TGA-GCMS, FTIR, HREM, XRD, helium pycnometry, and nitrogen adsorption at 77 K. A new phenomenon of decrease of the interlayer distance in MgO crystallites with increase of the nanoparticle size was observed.

Alkaline-earth metal oxide aerogels prepared by sol-gel method followed by autoclave drying are nanocrystalline mesoporous materials with high reactivity. Bulk solid-state reaction of MgO aerogels with CF2Cl2 takes place after a long induction period, during which the active sites are accumulated on the surface of the nanoparticles. It was found that vanadium addition has a promoting effect on this reaction accelerating the process of the active sites formation. A method for characterization of electron-acceptor sites by electron spin resonance spectroscopy using perylene as the spin probe was developed. A good correlation was observed between the rate of the CF2Cl2 destructive sorption and the concentration of weak electron-acceptor sites. Simplified models of such sites were suggested. The acid sites on the modified MgO surface were supposed to be originated from separation of the charged fragments resulting in the surface polarization. Uncompensated oxygen substitution for chlorine and/or fluorine ions leads to appearance of Lewis acid sites while HCl/HF chemisorption results in Bronsted acid sites formation. [ABSTRACT FROM AUTHOR]