Search

The aim of the present study was to determine the effect of a variety of abnormal fibres on the mechanical properties of paper made from Norway spruce, Picea abies (L.) Karst. Fibres representing abnormality were obtained from trees treated by irrigation and fertilisation. Moreover, fibres from compression wood and its accompanying opposite wood were isolated. The effect of dislocations on paper quality was studied on four mixtures (20, 40, 60 and 80% fibres with induced dislocations) of untreated/compressed fibres. Two more groups consisting of control untreated samples and samples with 100%-induced dislocations were also included in the test. The mechanical properties of the paper were tested and the results were compared to those of control samples. Abnormal fibres reduced the desired mechanical properties of the final paper concerning tensile strength, modulus of elasticity and tear-tensile index. Irrespective of the type of treatment, all morphological changes introduced in fibre cell walls appear to directly affect changes in the mechanical properties of the paper. Control samples had a tear index of 25 compared to 10 mN m2 g-1 of samples containing 100% dislocations. It is obvious that 20% of dislocations, an amount that is expected to be induced in pulp under mechanical processing and transport, will contribute to a decrease in tear index with an average of 3 mN m2 g-1, i.e., 10% of the total value.

Wood “cell-wall deformation” is a comprehensive term describing any physical dislocation in the wall caused by mechanical forces. The development and effect of fibre dislocations on wood fibres, and their ultimate impact on the mechanical properties of paper remain rather obscure and controversial. Dislocations are difficult to quantify through a lack of defined measurable features, and research is aggravated by the inherent difficulties of applying statistical tools. A direct approach for studying the effect of dislocations on the mechanical properties of paper was used in this study. Dislocations in fibre cell walls were introduced by exposing whole wood fibres in mature and juvenile wood samples to compression stress. Sapwood samples of Norway spruce (Picea abies Karst.) were loaded by compression to their ultimate strength using an Alwetron-50 universal testing machine. Failure of samples conditioned to a moisture content of 9–15% always occurred in an oblique (relative to the fibre axis) plane and all fibres in the plane were deformed. When samples were loaded in a wet condition (i.e., moisture content close to the fibre saturation point), failure occurred at one end of the samples, resulting in highly disorganised fibres. Pulp and paper from the compressed fibres were produced and the mechanical properties of the paper were tested. Results of the mechanical tests were compared statistically to results derived from paper made from matched non-compressed control samples. Morphological features of fibres and dislocations after compression failure were characterised using microscopy (scanning electron microscopy, polarised light) on the whole wood and macerated fibres before and after paper testing. The above experimental approach showed that paper made from control samples had significantly better mechanical properties than paper made from samples loaded by compression under dry or wet conditions. At a tensile index of 90 N m/g, the tear index was measured as 23.6 mN m2/g for controls, while the corresponding values for compressed wet wood samples was 12.6 and 16.3 mN m2/g for samples at 9–15% moisture content. Paper made from juvenile wood also showed lower mechanical properties compared to controls. The results prove the negative effect of dislocations on the mechanical properties of paper in the worst case scenario and are of practical importance.

In this work the application of polyelectrolyte complexes (PEC) to different pulps, to improve the strength of papers produced from them, is compared with conventional pulp beating. The pulps chosen for the investigation were a fully bleached chemical hardwood pulp (HBK), a fully bleached chemical softwood pulp (SBK), and a peroxide-bleached chemi-thermomechanical pulp (BCTMP). The polyelectrolytes used were a polyamideamine epichlorohydrine condensate (PAE), traditionally used as a wet-strength additive, and carboxymethylcellulose. Since the complexes prepared from these chemicals bear an anionic charge, they can only be used after fibre pre-treatment with the cationic PAE. Results indicate that the addition of 2% PAE and 2% PEC can improve all the measured tensile strength properties of the sheets as much as is commonly achieved by mechanically beating the pulps. In fact, for the chemical pulps, PEC addition at the chosen level produced better results than did traditional beating, since the improved tensile index and tensile energy absorption could be achieved without any significant deterioration in the light scattering coefficient of the papers produced. However, with the BCTMP a significant decrease in light scattering could be detected, especially following the addition of PEC. Adding the chemicals (especially the PEC) increased the sheet density, so chemical treatment left the bending stiffness of the sheets unaffected. However, based on the results, it was suggested that a combination of unbeaten HBK and BCTMP treated with PAE and PEC should be used as the fibre components of a typical fine paper furnish.