Search

A novel design of high-voltage compatible polarimeter for spin-resolved hard X-ray photoelectron spectroscopy (Spin-HAXPES) went into operation at beamline BL09XU of SPring-8 in Hyogo, Japan. The detector is based on the well-established principle of electron diffraction from a W(001) single-crystal at a scattering energy of 103.5 eV. It's special feature is that it can be operated at a high negative bias potential up to 10 kV, necessary to access the HAXPES range. The polarimeter is operated behind a large hemispherical analyzer (Scienta R-4000). It was optimized for high transmission of the transfer optics. A delay-line detector (20 mm dia.) is positioned at the exit plane of the analyzer enabling conventional multichannel intensity spectroscopy simultaneously with single-channel spin analysis. The performance of the combined setup is demonstrated by the spin-resolved data for the valence-region of a FeCo functional layer of a tunneling device, buried beneath 3 nm of oxidic material. The well-structured spin polarization spectrum validates Spin-HAXPES in the valence energy range as powerful method for bulk electronic structure analysis. The spin polarization spectrum exhibits a rich structure, originating from clearly discernible transitions in the majority and minority partial spin spectra. [ABSTRACT FROM AUTHOR]

The tunnel magnetoresistance ratio (TMR) of fully epitaxial magnetic tunnel junctions with an off- stoichiometric Co2MnSi Heusler alloy has been shown to exhibit a systematic dependence on Mn content, reaching 1135% at 4.2 K for Co2Mn1.29Si. In this paper, we explain the behaviorof the observed TMR ratio using ab initio calculations and hard x-ray photoelectron spectroscopy (HAXPES). For the Mn-deficient samples, we show that the the drop of the TMR is caused by Co antisite atoms, which impose extra states into the minority-spin band gap. On the other hand, Mn-excess composition shows nearly half-metallic behavior. This result can be intuitively understood since both Co2MnSi and Mn2CoSi are theoretically predicted to be half-metallic ferromagnets. [ABSTRACT FROM AUTHOR]

This work reports on hard x-ray photoelectron spectroscopy (HAXPES) of CoFeB based tunnel junctions. Aim is to explain the role of the boron diffusion for the observed improvement of the tunneling magnetoresistance ratio with increasing annealing temperature. The high bulk sensitivity of HAXPES was used as a nondestructive technique to analyze CoFeB–MgO–CoFeB magnetic tunnel junctions. The investigated samples were processed at different annealing temperatures from 523 to 923 K. Hard x-ray core level spectroscopy reveals an enforced diffusion of boron from the CoFeB into the adjacent Ta layer with increasing annealing temperature. The dependence of the tunneling magnetoresistance on the annealing temperature is explained by the combined effects of an improved crystalline structure together with a change in the spin polarization at the Fermi energy caused by the removal of boron from the CoFeB layer and Ta diffusion at high annealing temperature. [ABSTRACT FROM AUTHOR]

This work reports on the electronic and crystalline structure and the mechanical, magnetic, and transport properties of the polycrystalline Heusler compound Co2MnGe. The crystalline structure was examined in detail by extended x-ray absorption fine-structure spectroscopy and anomalous x-ray diffraction. The compound exhibits a well-ordered L21 structure as is typical for Heusler compounds with 2:1:1 stoichiometry. The low-temperature magnetic moment agrees well with the Slater-Pauling rule and indicates a half-metallic ferromagnetic state of the compound, as is predicted by ab initio calculations. Transport measurements and hard x-ray photoelectron spectroscopy were performed to explain the electronic structure of the compound. The obtained valence band spectra exhibit small energy shifts that are the result of the photoexcitation process, whereas electron-electron correlation in the ground state is negligible. The vibration and mechanical properties of the compound were calculated. The observed hardness values are consistent to a covalent-like bonding of Co2MnGe. [ABSTRACT FROM AUTHOR]

Mn2NiGa is reported to be a shape memory material with a martensite-austenite phase transition. Temperature dependent measurements of the transport and magnetic properties reveal the martensitic transition close to room temperature with a thermal hysteresis of about 27 K. The electronic structure of the valence band in both phases was studied by hard x-ray photoelectron spectroscopy. The results clearly indicate that strong changes in the electronic structure appear at the phase transition. [ABSTRACT FROM AUTHOR]