Search

The novel quinary fatty acid eutectic (CA-LA-MA-PA-SA) of capric acid, lauric acid, myristic acid, palmitic acid and stearic acid was successfully prepared with the mass ratio of 61.09/24.61/8.13/4.01/2.16. Thereafter, the innovative Ag-coated polyurethane (PU) fibers membranes with different concentrations of Ag, which were selected as a supporting material to adsorb the CA-LA-MA-PA-SA eutectics, were successfully fabricated through electrospinning followed by magnetron sputter. The energy dispersive X-ray confirmed that Ag nanoclusters were successfully deposited on the surface of PU fibers as a result of sputter coating. The observations of atomic force microscope indicated that the surface roughness of the PU fibers significantly increased with increase in coating time. The scanning electron microscope images demonstrated that the CA-LA-MA-PA-SA eutectics were uniformly distributed into the three-dimensional porous structures of uncoated and Ag-coated PU fibers membranes. Furthermore, the differential scanning calorimeter curves suggested that the CA-LA-MA-PA-SA/PU/Ag composites phase change materials (PCMs) possessed melting enthalpies about 110 kJ/kg and melting temperature around 17 °C. The absorption ratios of the CA-LA-MA-PA-SA eutectic in composite PCMs was approximately at 73.74%–83.18%. The investigation on thermal performance indicated that we achieved higher melting and freezing rates of the CA-LA-MA-PA-SA/PU/Ag composites PCMs by increasing coating time. In addition to this, after depositing Ag nanoparticles the melting and freezing times of composites PCMs were shortened to about 21%–65%. [ABSTRACT FROM AUTHOR]

In the present work, a novel PAN-based form-stable composite phase change materials with the methyl stearate (MES) encapsulated in the supporting matrices of polyacrylonitrile (PAN) nanofibers were fabricated through electrospunning for the storage and retrieval of thermal energy. Influences of graphene oxide (GO) addition on the chemical properties, structural morphologies, mechanical properties, thermal energy storage properties, thermal stability, and thermal energy storage/retrieval rates of electrospun MES/PAN/GO phase change composite nanofibers were systematically investigated by FT-IR, FE-SEM, tensile testing, DSC, TG, and measurement of melting/freezing times, respectively. The results revealed that the incorporation of GO effectively enhanced the mechanical properties, thermal stability, as well as heat storage and release rates of the phase change composite nanofibers. The averaged tensile strength of electrospun MES/PAN/GO phase change composite nanofibers increased significantly by 573 % with 10 mass% loading of GO, while elongation at break had a maximum 107 % increment when adding 3 mass% of GO. The DSC results indicated that the electrospun PAN-based phase change composite nanofibers with various GO loadings had suitable phase transition temperatures with the latent heat ranging from about 92 to 109 kJ kg and exhibited good thermal reliability in terms of DSC measurements during 50 melting-freezing cycles. Moreover, the melting and freezing time were significantly decreased about 44 and 43 % for the MES/PAN/GO5, as well as 59 and 64 % for the MES/PAN/GO10 after introducing the GO into the composite nanofibers systems. [ABSTRACT FROM AUTHOR]

Abstract: The ultrafine composite fibers based on the composites of binary fatty acid eutectics and polyethylene terephthalate (PET) with varied fatty acid eutectics/PET mass ratios (50/100, 70/100, 100/100 and 120/100) were fabricated using the technique of electrospinning as form-stable phase change materials (PCMs). The five binary fatty acid eutectics including LA–MA, LA–PA, MA–PA, MA–SA and PA–SA were prepared according to Schrader equation, and then were selected as an innovative type of solid–liquid PCMs. The results characterized by differential scanning calorimeter (DSC) indicated that the prepared binary fatty acid eutectics with low phase transition temperatures and high heat enthalpies for climatic requirements were more suitable for applications in building energy storage. The structural morphologies, thermal energy storage and thermal stability properties of the ultrafine composite fibers were investigated by scanning electron microscope (SEM), DSC and thermogravimetric analysis (TGA), respectively. SEM images revealed that the electrospun binary fatty acid eutectics/PET ultrafine composite fibers possessed the wrinkled surfaces morphologies compared with the neat PET fibers with cylindrical shape and smooth surfaces; the grooves or ridges on the corrugated surface of the ultrafine composite fibers became more and more prominent with increasing fatty acid eutectics amount in the composite fibers. The fibers with the low mass ratio maintained good structural morphologies while the quality became worse when the mass ratio is too high (more than 100/100). DSC measurements suggested that the heat enthalpies of melting and crystallization of the ultrafine composite fibers increased gradually with increasing fatty acid eutectics amounts, but their phase transition temperatures had almost no obvious variation as relative to the corresponding fatty acid eutectics. Meanwhile, the characteristic temperatures and heat enthalpies of the ultrafine composite fibers varied with the different types of binary fatty acid eutectics. TGA results indicated that the degradation of electrospun binary fatty acid eutectics/PET ultrafine composite fibers with representative mass ratio of 100/100 had two steps and corresponded respectively to the degradations of binary fatty acid eutectics and PET polymer chains; and the charred residue at 700°C of the composite fibers was lower than that of the neat PET fibers. It could be envisioned that the electrospun binary fatty acid eutectics/PET composite fibers would be extensively used for latent heat storage in the field of building energy conservation. [Copyright &y& Elsevier]