Search

AgBiSe2 is a promising thermoelectric (TE) candidate because of its intrinsically low thermal conductivity (κ = 0.4–0.5 W K−1 m−1 at ∼770 K) and optimal n-type carrier concentration (5.85 × 1018 cm−3 at 300 K). However, its TE figure of merit (ZT) is still low (0.3 at ∼770 K). Therefore, it is necessary to further improve its ZT. In this work, the solid solutions (AgBiSe2)1−x(Ag2Te)x (x = 0–0.125) have been designed through simple alloying Ag2Te inspired by the entropy engineering concept, and the TE performance has been further regulated. The analyses show that the exothermic effects related to α/β and β/γ phase transitions weaken, and the transition temperature of β/γ decreases as the Ag2Te content increases, which indicates the stabilization of the cubic γ-phase at high temperatures. Aside from that, the power factor (PF) enhances from 2.91 μW/cm K2 (x = 0) to 3.49 μW/cm K2 (x = 0.075), and at the same time, the lattice thermal conductivity reduces from 0.3 W K−1 m−1 to 0.1 W K−1 m−1 at ∼760 K. This directly improves the TE performance with the highest ZT value of 1.0, which is almost double that of the pristine AgBiSe2. The result suggests that the entropy engineering is a very effective screening method in thermoelectrics. [ABSTRACT FROM AUTHOR]

In this paper we reported the thermoelectric (TE) properties in nanostructured homologous series alloys GamSbnTe1.5(m+n) over the temperature range of 318–482 K and observed the maximum TE figure of merit (ZT) value of 0.98 for the alloy with m:n=1:10 at 482 K, which is approximately 0.24 higher than that of undoped Sb2Te3 at the corresponding temperature. This improvement is mainly attributed to the substantial reduction in lattice thermal conductivity due to the phonon scattering caused partly by the nanograins (<30 nm) and amorphous structure conceived in the matrix and partly by the lattice distortion resulted from an occupation of some Ga atoms in the Sb sites and a certain amount of Ga2Te3 precipitation. If in comparison with the TE properties for Ga directly doped Bi–Sb–Te solid solutions, we conclude that these Bi-free nanostructured homologous series alloys GamSbnTe1.5(m+n) with proper compositions are of great potentiality for the improvement of TE performance. [ABSTRACT FROM AUTHOR]

In this paper we reported the thermoelectric (TE) properties in nanostructured homologous series alloys GamSbnTe1.5(m+n) over the temperature range of 318–482 K and observed the maximum TE figure of merit (ZT) value of 0.98 for the alloy with m:n=1:10 at 482 K, which is approximately 0.24 higher than that of undoped Sb2Te3 at the corresponding temperature. This improvement is mainly attributed to the substantial reduction in lattice thermal conductivity due to the phonon scattering caused partly by the nanograins (<30 nm) and amorphous structure conceived in the matrix and partly by the lattice distortion resulted from an occupation of some Ga atoms in the Sb sites and a certain amount of Ga2Te3 precipitation. If in comparison with the TE properties for Ga directly doped Bi–Sb–Te solid solutions, we conclude that these Bi-free nanostructured homologous series alloys GamSbnTe1.5(m+n) with proper compositions are of great potentiality for the improvement of TE performance. [ABSTRACT FROM AUTHOR]

In this work we have observed the beneficial effect from the solid solution formation on the thermoelectric performance of (Cu 2(1 − x ) Sb 2 x Te)(Ga 2 Te 3 ) 3 upon Sb substitution for Cu. This substitution allows the different occupations of Sb in the crystal lattice, i.e. Sb at Cu sites with x ≤ 0.05 and at Ga sides with x ≥ 0.05, which has resulted in the Pisarenko relation does not exactly capture the measured Seebeck coefficient under assumed effective masses m *. The reduction of the lattice thermal conductivity ( κ L ) has been quantified within the temperature range from room temperature to 723 K. Over the entire composition range, the κ L value is reduced by 33% and 25% at temperature 723 K and 580 K, respectively. This observation is in a good agreement with the theoretical calculation based on the Callaway model used in the solid solutions. Along with the increasing of the mobility and electrical conductivity, the thermoelectric performance has been improved with the highest ZT value of 0.58 at 723 K, which is about double the value of intrinsic (Cu 2 Te)(Ga 2 Te 3 ) 3 . [ABSTRACT FROM AUTHOR]

In this work, we have observed the enhancement of carrier concentration in α-In2Se3 at a specific S content. This enhancement results from avoiding the annihilation of defects, such as VIn and interstitial Ini acting as donors, via the rearrangement of both the cationic and anionic disorders. Therefore, there is a remarkable improvement in electrical conductivity ( σ). For example, the sample α-In2S0.05Se2.95 perpendicular to the pressing direction ( C┴) gives the highest σ value of 5.56 × 103 Ω−1 m−1 at 923 K, while the virgin α-In2Se3 gives only 9.17 × 102 Ω−1 m−1. In addition, there are dual effects on the lattice thermal conductivity ( κL) resulting from the stabilization of the lattice structure caused by the rearrangement of defect disorder and the lattice distortion from the formation of defect SSe. Therefore, the lattice contribution ( κL) in S-incorporated α-In2Se3 remains relatively high at high temperatures. As a consequence, we have improved the thermoelectric performance, achieving a ZT value of 0.67 for α-In2S0.05Se2.95 at 923 K, which is about 2.8 times that of virgin α-In2Se3 ( ZT = 0.24 at C┴). [ABSTRACT FROM AUTHOR]