Search

Abstract Low cycle fatigue (LCF) behavior of CP-Ti along transverse direction under symmetrical strain and stress-controlled modes was compared systematically. For the strain-controlled tests, tension-compression asymmetry (TCA) has little effect on LCF behavior due to the negligible compressive mean stress. For the stress-controlled tests, TCA is detrimental to LCF resistance. The microstructure evolution during cycling deformation was characterized by EBSD and TEM to identify different deformation mechanisms. It was found that strain cycling deformation was dominated by dislocation slip and exhibited the transition from planar slip to wavy slip with the increase of strain amplitude. For the stress-controlled tests, tensile twinning together with dislocation slip accommodated the increased ratcheting deformation. The strain-life curve under stress-controlled tests is lower than that at strain-controlled tests due to the heterogeneous plastic deformation caused by ratcheting deformation. In order to obtain a unified fatigue life prediction model for different control modes, a novel effective strain range related model was proposed by introducing the TCA factor into the original Manson–Coffin relation. Furthermore, the application of this effective strain range related model was extended to the condition of asymmetrical stress cycling by correcting fatigue ductility coefficient and exponent. [ABSTRACT FROM AUTHOR]

Abstract In order to understand the effects of cyclic asymmetry and control mode on low cycle fatigue (LCF) behavior of CP-Ti along rolling direction (RD), symmetrical strain and stress-controlled fatigue tests were conducted in this paper. LCF behavior of CP-Ti along RD under different control modes was systematically compared from the aspects of cyclic response, microstructure evolution and fatigue life with the technique of electron backscatter diffraction (EBSD) and scanning electron microscope (SEM). It was found that cyclic softening resulted by dislocation slip dominates strain-controlled fatigue. On the contrary, cyclic hardening dominates stress-controlled fatigue at high stress amplitude, leading to a higher cyclic stress-strain curve. Owing to asymmetrical hysteresis loop, compressive ratcheting strain is accumulated in stress-controlled LCF test despite of the fully reversed stress cycling. EBSD results show there is a transition of deformation mechanism from dislocation slip to dislocation slip and twinning dominated cyclic deformation with the increase of compressive ratcheting strain. Meanwhile, GOS analysis and SEM observation indicate that the appearance of massive twins results in the heterogeneous plastic deformation and micro-cracks are favorable to be initiated in the twin abundant area. Besides, compressive ratcheting strain has significant effects on fatigue crack growth as the fracture surface presents the serious abrasion of cleavage facets and fatigue striations. Finally, strain-life curves under different control modes are identical, indicating that fatigue life along RD is insensitive to compressive ratcheting strain under the interaction of these factors. [ABSTRACT FROM AUTHOR]

• For CP-Ti, the threshold value for ratcheting strain accumulation of the axial stress amplitude is closer to 287 MPa. • Rate Surface Ratio is proposed to represent the difference in velocity during ratcheting accumulation. • The brand-new KBM-PH model with mean stress correction is the best overall among all models. Asymmetrical multiaxial fatigue tests were performed. A new quantification parameter is proposed to represent the difference in velocity during ratcheting accumulation. Although the stress–strain response under asymmetric loading is similar to that under symmetric loading, substantial deteriorations of life are observed. The threshold value for ratcheting strain accumulation of axial stress amplitude is closer to 287 MPa. The brand-new stress parameters-based KBM-PH model with mean stress correction is the best overall among a series of models based on strain and stress parameters with or without mean strain and stress corrections with the best accuracy and ease of use. [ABSTRACT FROM AUTHOR]