Abstract: The effect of corona pre-treatment on the performance of Al2O3 and SiO2 gas barrier layers applied by atomic layer deposition onto polymer-coated paperboards was studied. Both polyethylene and polylactide coated paperboards were corona treated prior to ALD. Corona treatment increased surface energies of the paperboard substrates, and this effect was still observed after several days. Al2O3 and SiO2 films were grown on top of the polymer coatings at temperature of 100°C using the atomic layer deposition (ALD) technique. For SiO2 depositions a new precursor, bis(diethylamido) silane, was used. The positive effect of the corona pre-treatment on the barrier properties of the polymer-coated paperboards with the ALD-grown layers was more significant with polyethylene coated paperboard and with thin deposited layers (shorter ALD process). SiO2 performed similarly to Al2O3 with the PE coated board when it comes to the oxygen barrier, while the performance of SiO2 with the biopolymer-coated board was more moderate. The effect of corona pre-treatment was negligible or even negative with the biopolymer-coated board. The ALD film growth and the effect of corona treatment on different substrates require further investigation. [Copyright &y& Elsevier]

Abstract: Atomic layer deposition (ALD), electron beam evaporation, magnetron sputtering and a sol–gel method were used to deposit thin aluminum oxide coatings onto two different fiber-based packaging materials of commercial board grades coated with synthetic and biodegradable polymers. Significant decreases in both the water vapor and oxygen permeation rates were observed. With each technique the barrier performance was improved. However, among the techniques tested ALD was found to be most suitable. Our results moreover revealed that biodegradable polylactic acid-coated paperboard with a 25-nm thick layer of aluminum oxide grown by ALD on top of it showed promising barrier characteristics against water vapor and oxygen. [Copyright &y& Elsevier]

Abstract: Thin aluminum oxide coatings have been deposited at a low temperature of 80°C on various uncoated papers, polymer-coated papers and boards and plain polymer films using the atomic layer deposition (ALD) technique. The work demonstrates that such ALD-grown Al2O3 coatings efficiently enhance the gas-diffusion barrier performance of the studied porous and non-porous materials towards oxygen, water vapor and aromas. [Copyright &y& Elsevier]