Organic-inorganic hybrid materials overcome drawbacks associated with alginate hydrogels. In this work, covalently coupled silica-alginate hybrids were prepared by Schiff base formation and sol-gel reaction using alginate dialdehyde (ADA), (3- Aminopropyl) triethoxysilane (APTES), and APTES/tetraethylorthosilicate (TEOS) precursors. The influence of the polysaccharide/inorganic ratio, the nature of the inorganic precursor and the ionic crosslinking ability are studied. Prepared hybrids were characterized by FT-IR, 13C and 29Si -NMR spectroscopies, SEM, and rheology. For ADA/APTES hybrids, at higher ADA content, Schiff base formation is predominant, but at lower ADA content, the sol-gel reaction is prevalent. However, the progress of the sol-gel reactions for ADA/(APTES+TEOS), is favored with higher ADA compositions. Introducing a posterior ionic crosslinking treatment was possible, increasing the moduli in ADA/(APTES+TEOS) hybrids from 86207Pa for 1.5 ADA/Si to 362171Pa for 1.5 ADA/Si-Ca. In-situ ADA-Silica hybrid hydrogels containing both ionic and covalent crosslinking can be successfully synthesized with the proposed method., Instituto Politécnico Nacional, México (IPN-SIP 20196660 and IPN-SIP 20201294), AEI/FEDER,UE (DPI2017-90147-R), CONACYT scholarship.

The search of suitable combinations of stem cells, biomaterials and scaffolds manufacturing methods have become a major focus of research for bone engineering. The aim of this study was to test the potential of dental pulp stem cells to attach, proliferate, mineralize and differentiate on 3D printed polycaprolactone (PCL) scaffolds. A 100% pure Mw: 84,500 +- 1000 PCL was selected. 5 x 10 x 5 mm3 parallelepiped scaffolds were designed as a wood-pilled structure composed of 20 layers of 250 microm in height, in a non-alternate order ([0,0,0,90,90,90º]). 3D printing was made at 170 ºC. Swine dental pulp stem cells (DPSCs) were extracted from lower lateral incisors of swine and cultivated until the cells reached 80% confluence. The third passage was used for seeding on the scaffolds. Phenotype of cells was determined by flow Cytometry. Live and dead, Alamar blue™, von Kossa and alizarin red staining assays were performed. Scaffolds with 290 + 30 micron strand diameter, 938 x 80 micron pores in the axial direction and 689 x 13 micron pores in the lateral direction were manufactured. Together, cell viability tests, von Kossa and Alizarin red staining indicate the ability of the printed scaffolds to support DPSCs attachment, proliferation and enable differentiation followed by mineralization. The selected material-processing technique-cell line (PCL-3D printing-DPSCs) triplet can be though to be used for further modelling and preclinical experiments in bone engineering studies., Grant PAPIIT IA207420, UNAM, México and AEI/FEDER, UE (DPI2017-90147-R) Spain.

Additive manufacturing (AM) techniques are becoming the approaches of choice for the construction of scaffolds in tissue engineering. However, the development of 3D printing in this field brings unique challenges, which must be accounted for in the design of experiments. The common printing process parameters must be considered as important factors in the design and quality of final 3D-printed products. In this work, we study the influence of some parameters in the design and fabrication of PCL scaffolds, such as the number and orientation of layers, but also others of &ldquo, hidden&rdquo, importance, such as the cooling down rate while printing, or the position of the starting point in each layer. These factors can have an important impact oin the final porosity and mechanical performance of the scaffolds. A pure polycaprolactone filament was used. Three different configurations were selected for the design of the internal structure of the scaffolds: a solid one with alternate layers (solid) (0&deg, 90&deg, ), a porous one with 30% infill and alternate layers (ALT) (0&deg, ) and a non-alternated configuration consisting in printing three piled layers before changing the orientation (n-ALT) (0&deg, 0&deg, ). The nozzle temperature was set to 172 &deg, C for printing and the build plate to 40 &deg, C. Strand diameters of 361 &plusmn, 26 &micro, m for room temperature cooling down and of 290 &plusmn, 30 &micro, m for forced cooling down, were obtained. A compression elastic modulus of 2.12 &plusmn, 0.31 MPa for n-ALT and 8.58 &plusmn, 0.14 MPa for ALT scaffolds were obtained. The cooling down rate has been observed as an important parameter for the final characteristics of the scaffold.

HA-based hybrid hydrogels were successfully developed. The polysaccharide (HA) chains were chemically modified and hybridized via amidation of their carboxylic groups with aminosilane molecules. HA-polysaccharide chains were crosslinked by a 3D siloxane organic-inorganic matrix via sol-gel. The novel inorganic crosslinking network (PDMS-SiO2) provided to sodium hyaluronate (HA) strong chemical bonds, giving restriction to their natural hydrophilicity and stiffness to its structure (improved rheological properties). It was observed that synthesis conditions such as starting HA concentration solution and temperature determined gelling times, efficiency in the polysaccharide chemical modification and in crosslinking hydrolysis-condensation reactions, resulting in the siloxane organic-inorganic matrix. Drying processes influenced crosslinking in HA hybrid hydrogels, either by enhancing polycondensation reactions or inhibiting them. Room temperature-drying produced more densified hybrid structures. Freeze-drying increased porosity and surface hydroxyl groups (-OH) resulting in more Q3 structural units. 60 °C-drying boosted polycondensation of monodendate structural units, enhancing the formation of hybrid D-Q bonds.

Two series of segmented polyurethanes were obtained and their mechanical and thermal properties as well as their biodegradability and cytotoxicity were evaluated. The chemical nature of the polyurethanes was varied by using either 1,4 butanediol (poly-ester-urethanes, PEUs) or l-lysine ethyl ester dihydrochloride (poly-ester-urea-urethanes, PEUUs) as chain extenders. Results showed that varying the hard segment influenced the thermal and mechanical properties of the obtained polymers. PEUs showed strain and hardness values of about 10&ndash, 20 MPa and 10&ndash, 65 MPa, respectively. These values were higher than the obtained values for the PEUUs due to the phase segregation and the higher crystallinity observed for the polyester-urethanes (PEUs), phase segregation was also observed and analyzed by XRD and DSC. Moreover, both series of polymers showed hydrolytic degradation when they were submerged in PBS until 90 days with 20% of weight loss. In vitro tests using a Human Osteoblastic cell line (Hob) showed an average of 80% of cell viability and good adhesion for both series of polymers.

Compounds having the general formula MFO·4H2O where M = Ca or Sr and FO = a folate anion were prepared and their structure and physico-chemical properties were determined by elemental and thermal TGA, DSC analysis, FTIR, and EDAX spectroscopies and DRX. The results indicate that the two compounds form stable structures where folic acid acts as a self-bridging ligand via two bidentate carboxylate groups. Moreover the two compounds showed a low toxicity in vitro response as h-osteoblast cell viability was not negatively affected by the presence of folate derivatives within the range of 0.063-0.5 mg ml-1. The results also indicate that the folate derivatives that are formed overcome the toxic effects related to free Sr2+ ions. The range of maximum cell viability corresponding with a concentration of SrFO falls within the in vitro physiologically active range for strontium while within the same range the strontium derivative showed a potential osteogenic activity as indicated by the overexpression of ALP activity.

Emulsion-templated (polyHIPE) scaffolds for bone tissue engineering were produced by photopolymerisation of a mixture of trimethylolpropane tris(3-mercaptopropionate) and dipentaerythritol penta-/hexaacrylate in the presence of hydroxyapatite (HA) or strontium-modified hydroxyapatite (SrHA) nanoparticles. Porous and permeable polyHIPE materials were produced regardless of the type or incorporation level of the bioceramic, although higher loadings resulted in a larger average pore diameter. Inclusion of HA and SrHA into the scaffolds was confirmed by EDX-SEM, FTIR and XPS and quantified by thermogravimetry. Addition of HA to polyHIPE scaffolds significantly enhanced compressive strength (148–216 kPa) without affecting compressive modulus (2.34–2.58 MPa). The resulting materials were evaluated in vitro as scaffolds for the 3D culture of MG63 osteoblastic cells vs. a commercial 3D cell culture scaffold (Alvetex®). Cells were able to migrate throughout all scaffolds, achieving a high density by the end of the culture period (21 days). The presence of HA and in particular SrHA gave greatly enhanced cell proliferation, as determined by staining of histological sections and total protein assay (Bradford). Furthermore, Von Kossa and Alizarin Red staining demonstrated significant mineralisation from inclusion of bioceramics, even at the earliest time point (day 7). Production of alkaline phosphatase (ALP), an early osteogenic marker, was used to investigate the influence of HA and SrHA on cell function. ALP levels were significantly reduced on HA- and SrHA-modified scaffolds by day 7, which agrees with the observed early onset of mineralisation in the presence of the bioceramics. The presented data support our conclusions that HA and SrHA enhance osteoblastic cell proliferation on polyHIPE scaffolds and promote early mineralisation.

The aim of this work is to evaluate the potential of cryogels to be used as scaffolds in tissue engineering. Scaffolds based on the α-tricalcium phosphate reinforced PDMAEMA (Poly(dimethyl aminoethyl methacrylate))/PHEMA (poly(hydroxyethyl methacrylate)) system were prepared and human trabecular bone-derived cells (HTBs) and bone marrow derived-mesenchymal stem cells (BM-MSCs) cultured on them. Several features, such as porosity, pore shape, molecular weight between crosslinks and mesh size, are studied. The most suitable PDMAEMA/PHEMA ratio for cell proliferation has been assessed and the viability, adhesion, proliferation and expression of osteoblastic biochemical markers are evaluated. The PDMAEMA/PHEMA ratio influences the scaffolds porosity. Values between 53% ± 5.7% for a greater content in PHEMA and 75% ± 5.5% for a greater content in PDMAEMA have been obtained. The polymer ratio also modifies the pore shape. A greater content in PDMAEMA leads also to bigger network mesh size. Each of the compositions were non-cytotoxic, the seeded cells remained viable for both BM-MSCs and HTBs. Thus, and based on the structural analysis, specimens with a greater content in PDMAEMA seem to provide a better structural environment for their use as scaffolds for tissue engineering. The α-tricalcium phosphate incorporation into the composition seems to favor the expression of the osteogenic phenotype., We acknowledge support by the CSIC Open Access Publication Initiative through its Unit of Information Resources for Research (URICI)

The purpose of this work is to study the dissolution mechanism of SiO2-based bioactive hybrid materials containing both CaO and P2O5 in their structures and to determine the influence of apatite crystallization over the surface features of the hybrids during degradation. Hybrid materials were synthesized using sol–gel method. Tetraethoxysilane (TEOS), hydroxyl terminated polydimethylsiloxane (PDMS), Ca(NO3)2·4H2O, and triethyl phosphate (TEP) were used as reactants. The degradation and bioactivity of the hybrid materials were tested by soaking the specimens into simulated body fluid (SBF). Raman spectroscopy, tensiometry and N2 adsorption/desorption curves were used to measure the changes during the degradation experiments. Several mathematical approaches have been taken to analyze the results. The growth of an apatite layer on the surface of SiO2-modified PDMS-P2O5-CaO hybrid materials occurs together with degradation of the silica-based matrix. The dissolution kinetics depends upon the composition of the material. It varies from a surface-driven mechanism in the case of low-P2O5 samples to a degradation path which fits into a Weibull type kinetic model, typical of matrix dissolution processes in materials enriched in P2O5. During degradation, the surface parameters, fractal constant and anisotropy of the pores were determined. The slight increase of the fractal constant in low-containing P2O5 materials suggests the formation of a homogeneous silica-like layer in the first stage of degradation, which also works as anchoring nucleus for subsequent apatite formation. In all the cases, the degradation leads to ink-bottle shaped pores, increasing their volume as degradation occurs, but keeping their neck shape., This work was supported by SIP-IPN 20150064 Project (Mexico), DGICYT Project, MAT2014-51918-C2-1-R (Spain), Fundación General CSIC (Programa ComFuturo) (A. Tamayo). DA Sánchez – Téllez also acknowledges CONACYT for the scholarship given.

Protein-surface interaction may determine the success or failure of an implanted device. Not much attention have been paid to the specific surface parametes of hydroxyapatite (OHAp) that modulates and determines the formation and potential activity of the layer of proteins that is first formed when the material get in contact with the host tissue. the influence of specific surface area (SSA), crystallite size (CS) and particle size (PS) of OHAp on the adsorption of proteins relevant for bone regeneration is evaluated in this article. OHAp have been prepared by a wet chemical reaction of Ca(OH)(2) with H(3) PO(4) . One set of reactions included poly acrylic acid in the reactant solution to modify the properties of the powder. Fibrinogen (Fg) Fraction I, type I: from Human plasma, (67% Protein), and Fibronectin (Fn) from Human plasma were selected to perform the adsorption experiments. The analysis of protein adsorption was carried out by UV/Vis spectrometry. A lower SSA and a different aspect ratio are obtained when the acrylic acid is included in the reaction badge. The deconvolution of the amide I band on the Raman spectra of free and adsorbed proteins reveals that the interaction apatite-protein happens through the carboxylate groups of the proteins. The combined analysis of CS, SSA and PS should be considered on the design of OHAp materials intended to interact with proteins.

Though hydroxyapatite has the ability to promote bone growing, devices based on OHAp are mechanically weak and need to be reinforced for load bearing applications or in the manufacturing of scaffolds for bone regeneration. Graphite (Gr) could provide appropriate reinforcement properties to OHAp without being deleterious for the biocompatibility of the system. This paper describes an accelerated synthesis of the OHAp with ultrasonic agitation in the presence of functionalized graphite (GO). The toxicity of the Graphite and the GO-OHAp system is evaluated. GO-OHAp was produced by a wet chemical reaction involving CaCl2 and Na2HPO4. The calcium salt solution was added first and the solution sonicated for 1 hour, before repeating the operation with the phosphate solution. Biocompatibility was tested by using a primary cell culture of HOB (ECCAC). The disappearance of the maximum at 2q = 26.32º corresponding to the d002 plane of graphite and the appearance of the maximum at 2q = 13.2º in the XRD patterns is related with an expansion of the grapheme sheets from 0.34 nm to 0.59 nm and it has been used to assess the graphite oxidation. The OHAP on GO growing has been confirmed by the appearance of a broad peak centred at 2q = 31.5º and a sharpened peak at 2q = 26.0º characteristic of low crystalline apatites. Although the employed graphite can be considered biocompatible, cellular viability is significantly improved by the presence of apatite.

This paper focuses on the preparation of siloxane-polyurethane hybrid materials using a sol-gel method. The global aim of the project is to tailor mechanical properties, degradability rate, bioactivity and biocompatibility to design scaffolds for musculoskeletal applications. A series of seven hybrid materials were synthesized with varying the proportion of polydimethylsiloxane (PDMS), and Polyurethane (PU). The organic part ratios (by weight) employed were (% PDMS:% PU) 30:0, 35:5, 20:10, 15:15, 10:20, 5:25, and 0:30. The organic part was reacted with constant 70 % TEOS to obtain the hybrid materials. A sol-gel process was selected for the synthesis of the hybrids. The characterization of materials was carried out by the fourier-infrared spectroscopy (FT-IR), x-ray diffraction (XRD), thermogravimetric analysis (TGA), scanning electronic microscopy (SEM) and proton nuclear magnetic resonance (1H-NMR) techniques in order to analyze the structure, microstructure and chemical composition of the hybrid materials. Gelification time depends on the proportion of PU used. When no PU is employed, the gel time is 8 hours but it rises up to 18 days for 30 % of polyurethane. Materials range from opaque to translucent but with a greater fragility for greater amounts of polyurethane. No differences in the bonding of materials could be appreciated.

The manufacturing of a composite made of a synthetic bioactive ceramic, pseudowollastonite (psW), and a bioresorbable copolymer ethylmethacrylate–vinylpyrrolidone (EMA/VP) is presented in this article. psW porous blocks were produced by dipping an open porous polyurethane foam in a psW containing slurry. A 40/60 wt % EMA/VP monomers mixture was poured on the blocks, and free radical polymerization initiated by azobis(isobutyronitrile) at 50°C. Disks of 1 mm height were obtained by cutting the composite with a diamond saw, and bioresorption and bioactivity of the specimens were tested by immersion of the disks into SBF. A ceramic/polymer weight ratio of 72/28, greater than the usually achievable ratio by polymeric solidification of slurries of monomers charged with a powdered solid component, has been obtained. The system is bioactive and does not change the pH of the medium during the degradation test. © 2006 Wiley Periodicals, Inc. J Biomed Mater Res 80A:, 2007

Bisphosphonates (BPs) may play an important role in minimizing osteolysis. In this work two new bisphosphonates pertaining to second and third generations respectively, have been synthesized and incorporated onto a chemically enriched hydroxyapatite. BP synthesis has been performed by adding H3PO3, PCl3 and methanesulfonic acid over 4-aminophenyl acetic acid (APBP) and 1-H-indole-3-acetic acid (IBP) respectively at 65°C in a N2 atmosphere. These compounds bear a primary amine group bonded to an aromatic ring, and a secondary amine group within a heterocyclic ring respectively. A chemically enriched hydroxyapatite with a chemical content corresponding to a 50% fluorided hydroxyapatite has been synthesized. Ceramic bodies manufactured by uniaxial pressure followed by cold isostatic press have a 97% density and submicron grain size. The BP was adsorbed onto the surface by immersion in a stirred solution at 37°C for 48 hours. A 10-fold decrease of the surface energy was observed for bodies modified with the APBP whereas only a 25 % decrease is obtained for bodies loaded with the bisphosphonate loaded with the IBP.

Iron is a vital element of cellular function within the body. High concentrations of iron can be found in the kidneys and the circulatory system. In bones and teeth it is present as a trace element. The use of iron-based compounds in combination with hydroxyapatite offers a new alternative for prosthetic devices. This work investigates the synthesis and processing of iron containing apatites as a possible new type of ceramic for biomedical devices. Stoichiometric and calcium deficient iron containing apatites were synthesized by a wet chemical reaction with di-ammonium-hydrogen-phosphate, calcium nitrate and a ferrous iron nitrate solution. A secondary phase of tri-calcium-phosphate (TCP) was observed after heat treatment of iron containing, calcium deficient, hydroxyapatite. The apatite structure was maintained after heat treatment of stoichiometric apatite, synthesized in the presence of iron. Sintering in air produced oxidation of Fe2+ to Fe3+, resulting in the formation of hematite as a secondary phase. The introduction of iron into the synthesis of hydroxyapatite causes: (i) an increase of the a-lattice parameter after synthesis and heat treatment in air; (ii) an increase in the c-lattice parameter after sintering in air.

The development of synthetic apatites that replicate the features and properties of the contained in natural tissues will help to diminish the misfit between artificial implants and natural hostesses but the structure of these compounds is still under discussion. The variability in Ca/P ratio of calcium deficient apatites has been explained through different models: surface adsorption, lattice substitution and intercrystalline mixtures of hydroxyapatite and octacalcium phosphate. This work investigates which of the models mentioned suits better in a range of samples. Hydroxyapatites obtained by precipitation, by hydrolysis of dicalcium phosphate and calcined samples with Ca/P ratio between 1.50 and 1.77 and specific surface area between 7 and 108 m2/g have been analysed. OCP and surface adsorption models suit better for great SSA particles and low Ca/P ratio while for smaller SSA particles the lattice substitution model is more accurate. SSA also plays the main role when the capacity to absorb substances is studied though their chemistry can not be explained solely in terms of surface reactivity.

Hydroxyapatite has been frequently described as an osteoconductive but not osteoinductive material based on failure to observe bone formation in nonbony sites. Bisphosphonates (BPs) are stable pyrophosphate analogs, that enhance the proliferation, differentiation and bone forming activity of osteoblasts and are potent inhibitors of bone resorption. In this paper, the modification of a calcium hydroxyfluor carbonate apatite with sodium alendronate and (4-(aminomethyl)benzene)bisphosphonic acid is described. The surface modification is carried out by refluxing the apatite in a bisphosphonate acetone solution. Modified particles are characterized by thermal analysis, ATR-IR spectroscopy and contact angle between other techniques. A weight loss between 150 and 500ºC can be observed for the modified apatites. IR spectra show the appearance of bisphosphonate bands on modified powders. The surface energy of the modified apatite is reduced up to a 74% from the total apatite value after the alendronate surface modification with a decrease of 58% of the polar component main responsible of the cellular interaction of biomaterials., Financial support through research project MAT2002-04147-C02-02, CICYT (Spain) is acknowledged. LMRL has been supported by CAM regional government (Spain) through the program to incorporate doctors to the Madrid research system.

Modification of hydroxyapatite surfaces can improve the properties of biomedical devices. The objective of this work was to encapsulate hydroxyapatite particles with a fluorapatite layer. A suspension of hydroxyapatite microspheres was prepared in a solution at different pH and treated with ammonium fluoride. pH, calcium, and fluoride were monitored in real time and particles subjected to fluoride analysis. After addition of fluoride, it was found that more material is released from the particle surface at low pH conditions, but leads to a high fluoride uptake from solution. Low solution fluoride levels produce a fluorapatite layer, but higher fluoride levels produce calcium fluoride.

Hydroxy-fluorapatites (OH-FAps) occur biologically in teeth and form the basis for application as biomaterials. This work aims to synthesize a series of fluoride substituted calcium hydroxyapatites (OHAps) to determine how fluoride influences the synthesis and the resulting characteristics of solid solutions. OH-FAPs powders were synthesized with a chemical composition of Ca(10)(PO(4))(6)(OH)(2-x) F(x), with x=0.0, 0.4, 0.8, 1.2, 1.6 and 2.0. The synthesis of partially substituted OHAp yields materials with lower crystallinity and higher specific surface area than OHAp or fluorapatite (FAp). The smallest crystal size of 263A, occurs at less than 50% hydroxyl substitution with fluoride at x=0.4, and the highest surface area of 132m(2)/g occurs at x=0.8. Reaction kinetics occur faster at higher fluoride content, producing the expected Ca/P ratio of 1.67 only for x=2.0. X-ray and IR studies show that OH-FAPs are homogeneous solid solutions instead of mixtures of OHAp and FAp. The presence of a high fluoride concentration increases the driving force for crystal growth during the calcination process.

X-ray diffraction (XRD) patterns of hydroxyfluorapatites with a nominal composition of Ca10(PO4)6(OH)2-xFx, where x = 0.0, 0.4, 0.8, 1.2, 1.6, and 2.0, were collected and analyzed using the Rietveld method. A multiphase Rietveld analysis performed on calcined samples reveals a range of Ca/P ratios from 1.56 for the sample with x = 0.4 to 1.67 for the sample with x = 2.0 on the synthesized powders. Calcined apatites exhibit a decrease in the lattice parameter a, a greater crystallite size, lower distortion in the phosphate tetrahedra, and greater stability of the apatite structure for higher fluoride contents.

The layering of fluorapatite on hydroxyapatite bodies provides a means of decreasing the solubility of hydroxyapatite, providing fluoride for possible stimulation of bone formation and delaying the release of calcium and phosphate from the more soluble hydroxyapatite. The purpose of this work was to encapsulate hydroxyapatite particles with fluorapatite spanning a thickness more than several crystallites deep. A three-step procedure was employed. Hydroxyapatite powder was immersed in an electrolyte solution until an equilibrium was established between the solid and the dissolved calcium at pH 4.67 and 37 °C. Equilibrium was determined by measurement of dissolved calcium with a calcium-specific ion-specific electrode. A 5×10−2 M ammonium fluoride added to the suspension resulted in a rapid decrease of both calcium and fluoride in the solution. Analysis with X-ray diffraction indicated that a fluoride rich layer containing calcium fluoride deposited onto the particle surface. Scanning electron microscopy revealed submicron spherical precipitate clusters on the hydroxyapatite particles. These clusters transformed to fluorapatite by soaking in a 0.1 M K2HPO4 solution at pH 8 and 70 °C. A total time of 10 h was necessary for complete transformation of CaF_2 into fluorapatite.

The growing necessity of biomaterials has increased the interest in calcium phosphates, particularly apatites. Small differences in stoichiometry, crystallinity, morphology, etc. could contribute to the different clinical behaviors observed, so perfect control of the synthesis parameters and their influence in the characteristics of the samples is a must. In the present work, a crystallization set able to produce massive and reproducible quantities of different calcium phosphates is presented. Apatites with different stoichiometries and morphologies are prepared, and the effects of varying synthesis conditions are analyzed. Temperatures in the range 25−37 °C are necessary to obtain apatites with crystal sizes in the range of adult human bone. Longer reaction times produce increased Ca/P ratios. Aging of the precipitated powder can lead to the incorporation of minor quantities of carbonate. It is possible to force the incorporation of carbonate ions into the apatitic structure without introducing monovalen...

Composite biomaterials with good mechanical response and a partially biodegradable character were prepared by the free radical polymerization of mixtures of α-Al 2 O 3 , low-molecular-weight but crystalline poly(L-lactic acid) (PLLA), and methyl methacrylate (MMA). Cylindrical specimens prepared with different composition were characterized by thermogravimetry, calorimetry, 1 H-NMR spectroscopy, and x-ray diffraction (XRD). The in vitro biodegradative process was studied in different media, following variations of the pH, gravimetric weight loss of the specimens, and crystalline domain change by XRD after immersion in pure water and buffered solutions at pH 4.0 and pH 8.0 for 90 days. Formation of a relatively porous structure with good cohesion after the biodegradative treatment (confirmed by SEM) was observed. These systems can be considered for applications in orthopedic surgery as filling biomaterials and even as control drug-delivery systems.

Composite materials are very promising biomaterials for hard tissue augmentation. The approach assayed in this work involves the manufacturing of a composite made of a bioactive ceramic, natural wollastonite (W) and a nanostructured copolymer of ethylmethacrylate (EMA) and vinylpyrrolidone (VP) to yield a bioresorbable and biocompatible VP–EMA copolymer. A bulk polymerization was induced thermally at 508C, using 1 wt % azobis(isobutyronitrile) (AIBN) as free-radical initiator. Structural characterization, compressive strength, flexural strength (FS), degradation, bioactivity, and biocompatibility were evaluated in specimens with a 60/40 VP/EMA ratio and ceramic content in the range 0–60%. A good integration between phases was achieved. Greater compression and FS, in comparison with the pure copolymer specimens was obtained only when the ceramic load got up to 60% of the total weight. The soaking in NaCl solution resulted in the initial swelling of the specimens tested. The maximum swelling was reached after 2–3 h of immersion and it was significantly greater for lower ceramic loads. This result makes the polymer component the main responsible for the interactions with the media. After soaking in SBF, microdomains segregation can be observed in the polymer component that can be related with a dramatic difference in the reactivity of both monomers in free radical polymerization, whereas the formation of an apatite-like layer on the W surfaces can be observed. Biocompatibility in vitro studies showed the absence of cytotoxicity of all formulations. The cells were able to adhere on the polystyrene negative control and on specimens containing 60 wt % wollastonite forming a monolayer and showing a normal morphology. However, a low cellular growth was observed. 2008 Wiley Periodicals, Inc. J Biomed Mater Res 88A: 53–64, 2009

Bisphosphonates (BP) are drugs currently administered orally to treat diseases characterised by an excessive bone resorption. Alternative and more efficient delivery routes and more potent compounds are being investigated. Three implantable delivery systems, which allow the controlled release of therapeutic agents from the device core, are examined in this paper. (4- (aminomethyl) benzene) bisphosphonic acid (ABBP) was incorporated on Ca8.8Na0.8(PO4)4.8(CO3)1.2(OH)0.4F1.6 particles by refluxing the powder in a 60 mmol suspension in acetone at 60ºC for 5 hours. 4-aminophenyl acetic bisphosphonate monosodium salt (APBP) and 1- H-indole-3-acetic bisphosphonate monosodium (IBP) were loaded on Ca10(PO4)6(OH)1F1 ceramic bodies by stirring the ceramic bodies in 0.04M BP solutions. Injectable acrylic cements based on self-curing formulations of methyl methacrylate (MMA) and vitamin E were loaded with APBP and IBP. The incorporation of ABBP was confirmed by MAS-NMR spectroscopy. Modified powder shows two different phosphorous environments, the first one at 2.91 ppm can be assigned to the apatite base and the second one at 18.0 ppm has to be attributed to the phosphonic group of the ABBP. The IBP addition on ceramic surfaces did not decrease the number of osteoclast colonies and appeared to improve the performance of the HA as a surface for osteoblast culture. A therapeutic dosage of APBP and IBP can be achieved from acrylic cements that showed lack of toxicity and an increased cellular activity and proliferation, Financial support from CICYT, Spain (MAT2004-01654) and NoE EXPERTISSUES (UE contract Nº: 500283-2) is acknowledged. Mar Fernández and Luis M. Rodríguez Lorenzo are supported by the Ramón y Cajal Programme, MEC-Spain

En este trabajo se presenta el estudio de la biocompatibilidad in vitro, empleando cultivos celulares de fibroblastos embrionarios humanos, de tres sistemas acrílicos de liberación controlada de bisfosfonatos (BFs). Estos sistemas, basados en metacrilato de metilo (MMA), metacrilato de vitamina E (MVE) y trietilenglicol dimetacrilato (TEGDMA), han sido diseñados para su aplicación en el tratamiento de enfermedades caracterizadas por una elevada resorción osteoclástica. En su preparación se ha empleado un BP comercializado (alendronato; ALN) y dos de nueva síntesis, pertenecientes a la segunda y tercera generaciones, el ácido 1-hidroxi-2-[4-aminofenil]etano-1,1-difosfónico (APBP) y el ácido 1-hidroxi-2-[3-indolil]etano-1,1-difosfónico (IBP), respectivamente. La citotoxicidad de MVE ha sido notablemente inferior a la medida para TEGDMA. La citotoxicidad de APBP e IBP se ha comparado con la de ALN, obteniéndose unos valores para la concentración IC50, de15,56, 9,86 y 6,25 mmol/l para APBP, ALN e IBP, respectivamente. Los niveles de citotoxicidad liberada han sido superiores para la formulación portadora de ALN, situándose a continuación los cementos cargados con IBP y APBP. Cuando los cultivos se han establecido sobre la superficie de las formulaciones, se han detectado unos niveles de proliferación celular y adhesión superiores para los sistemas de liberación de IBP y APBP, siendo además inferior en estos casos la mortalidad celular. This paper reports the in vitro biocompatibility study, using human embryonic fibroblast cultures, of three acrylic systems for controlled release of bisphosphonates (BFs). These systems, that are based on methyl methacrylate (MMA), vitamin E methacrylate (MVE) and triethyleneglycol dimethacrylate (TEGDMA), have been designed for its application in the treatment of pathologies characterized by a high osteoclastic resorption. A commercial BP (alendronate; ALN) and two novel BPs, belonging to the second and third generations, 1-hydroxy-2-[4-aminophenyl]ethane-1,1-diphosphonic acid (APBP) and 1-hydroxy-2-[3-indolyl]ethane-1,1-diphosphonic acid (IBP), respectively, have been used in their preparation. The cytotoxicity of MVE has been notably lower than that measured for TEGDMA. Cytotoxicity of APBP and IBP was evaluated along with that of ALN, and the following values of the IC50, concentration were obtained for APBP, ALN and IBP respectively: 15.56, 9.86 and 6.25 mmol/l. The cytotoxicity levels obtained from the extracts of the cured systems were higher for the formulation containing ALN, followed by the cements loaded with IBP and APBP. When the cultures were seeded directly on the formulations surface, higher levels of cellular proliferation and adhesion were obtained for the systems containing IBP and APBP, the cellular mortality being also inferior in these cases.

Fluoride substitution within hydroxyapatite is an important occurrence for biological apatites and is a promising approach for the chemical modification of synthetic hydroxyapatite. Limited information on the influence of fluoride substitution for hydroxyl groups on the mechanical properties has provided the rationale for this study. Hydroxyfluorapatites with 0%, 20%, 40%, 60%, 80% and 100% replacement of hydroxyl groups with fluoride ions were assessed for hardness, elastic modulus, fracture toughness and brittleness using microindentation of sintered pellets. The production of samples with a similar grain size and density allowed the influence of fluoride on mechanical properties to be determined. It was found that the hardness remains unaffected until 80% replacement of hydroxyl groups with fluoride, after which the hardness rapidly increases. The elastic modulus increases linearly with fluoride content. Fracture toughness is improved with fluoride incorporation into the lattice and reaches a peak of 1.8 for a 95% dense sintered pellet with a 60% fluoride replacement, followed by a rapid decrease at higher fluoride concentrations. The brittleness index is lowered to a minimum at 60%, after which a rapid increase occurs. High fluoride levels are unfavourable from a mechanical perspective, are not recommended for biomaterials, and can lead to a higher incidence of fracture where sodium fluoride, for treatment of osteoporosis, may produce a highly fluoridated hydroxyapatite.

The growing necessity of biomaterials has increased the interest in calcium phosphates, particularly apatites. Small differences in stoichiometry, crystallinity, morphology, etc. could contribute to the different clinical behaviors observed, so perfect control of the synthesis parameters and their influence in the characteristics of the samples is a must. In the present work, a crystallization set able to produce massive and reproducible quantities of different calcium phosphates is presented. Apatites with different stoichiometries and morphologies are prepared, and the effects of varying synthesis conditions are analyzed. Temperatures in the range 25−37 °C are necessary to obtain apatites with crystal sizes in the range of adult human bone. Longer reaction times produce increased Ca/P ratios. Aging of the precipitated powder can lead to the incorporation of minor quantities of carbonate. It is possible to force the incorporation of carbonate ions into the apatitic structure without introducing monovalen...