Search

In this study, indium tin oxide nanowires (ITO NWs) with high density and crystallinity were synthesized by chemical vapor deposition (CVD) via a vapor–liquid–solid (VLS) route; the NWs were decorated with 1 at% and 3 at% silver nanoparticles on the surface by a unique electrochemical method. The ITO NWs possessed great morphologies with lengths of 5~10 μm and an average diameter of 58.1 nm. Characterization was conducted through transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS), X-ray diffraction (XRD) and X-ray photoelectron spectroscope (XPS) to identify the structure and composition of the ITO NWs. The room temperature photoluminescence (PL) studies show that the ITO NWs were of visible light-emitting properties, and there were a large number of oxygen vacancies on the surface. The successful modification of Ag was confirmed by TEM, XRD and XPS. PL analysis reveals that there was an extra Ag signal at around 1.895 eV, indicating the potential application of Ag-ITO NWs as nanoscale optical materials. Electrical measurements show that more Ag nanoparticles on the surface of ITO NWs contributed to higher resistivity, demonstrating the change in the electron transmission channel of the Ag-ITO NWs. ITO NWs and Ag-ITO NWs are expected to enhance the performance of electronic and optoelectronic devices. [ABSTRACT FROM AUTHOR]

Indium oxide (In2O3) is a widely used n-type semiconductor for detection of pollutant gases; however, its gas selectivity and sensitivity have been suboptimal in previous studies. In this work, zinc-doped indium oxide nanowires with appropriate morphologies and high crystallinity were synthesized using chemical vapor deposition (CVD). An accurate method for electrical measurement was attained using a single nanowire microdevice, showing that electrical resistivity increased after doping with zinc. This is attributed to the lower valence of the dopant, which acts as an acceptor, leading to the decrease in electrical conductivity. X-ray photoelectron spectroscopy (XPS) analysis confirms the increased oxygen vacancies due to doping a suitable number of atoms, which altered oxygen adsorption on the nanowires and contributed to improved gas sensing performance. The sensing performance was evaluated using reducing gases, including carbon monoxide, acetone, and ethanol. Overall, the response of the doped nanowires was found to be higher than that of undoped nanowires at a low concentration (5 ppm) and low operating temperatures. At 300 °C, the gas sensing response of zinc-doped In2O3 nanowires was 13 times higher than that of undoped In2O3 nanowires. The study concludes that higher zinc doping concentration in In2O3 nanowires improves gas sensing properties by increasing oxygen vacancies after doping and enhancing gas molecule adsorption. With better response to reducing gases, zinc-doped In2O3 nanowires will be applicable in environmental detection and life science. [ABSTRACT FROM AUTHOR]

Owing to its unique and variable lattice structure and stoichiometric ratio, tungsten oxide is suitable for material modification; for example, doping is expected to improve its catalytic properties. However, most of the doping experiments are conducted by hydrothermal or multi-step synthesis, which is not only time-consuming but also prone to solvent contamination, having little room for mass production. Here, without a catalyst, we report the formation of high-crystallinity manganese-doped and potassium-doped tungsten oxide nanowires through chemical vapor deposition (CVD) with interesting characterization, photocatalytic, and gas sensing properties. The structure and composition of the nanowires were characterized by transmission electron microscopy (TEM) and energy-dispersive spectroscopy (EDS), respectively, while the morphology and chemical valence were characterized by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS), respectively. Electrical measurements showed that the single nanowires doped with manganese and potassium had resistivities of 1.81 × 0−5 Ω·m and 1.93 × 10−5 Ω·m, respectively. The doping contributed to the phase transition from monoclinic to metastable hexagonal for the tungsten oxide nanowires, the structure of which is known for its hexagonal electron channels. The hexagonal structure provided efficient charge transfer and enhanced the catalytic efficiency of the tungsten oxide nanowires, resulting in a catalytic efficiency of 98.5% for the manganese-doped tungsten oxide nanowires and 97.73% for the potassium-doped tungsten oxide nanowires after four hours of degradation of methylene blue. Additionally, the gas sensing response for 20 ppm of ethanol showed a positive dependence of doping with the manganese-doped and potassium-doped responses being 14.4% and 29.7%, respectively, higher than the pure response at 250 °C. The manganese-doped and potassium-doped tungsten oxide nanowires are attractive candidates in gas sensing, photocatalytic, and energy storage applications, including water splitting, photochromism, and rechargeable batteries. [ABSTRACT FROM AUTHOR]

With the continuous advancement of high-tech industries, how to properly handle pollutants has become urgent. Photocatalysis is a solution that may effectively degrade pollutants into harmless molecules. In this study, we synthesized single crystalline Zn2SnO4 (ZTO) nanowires through chemical vapor deposition and selective etching. The chemical bath redox method was used to modify the ZTO nanowires with Ag nanoparticles to explore the photocatalytic properties of the nanoheterostructures. The combination of the materials here is rare. Optical measurements by photoluminescence (PL) and UV–Vis show that the PL spectrum of ZTO nanowires was mainly in the visible light region and attributed to oxygen vacancies. The luminescence intensity of the nanowires was significantly reduced after modification, demonstrating that the heterojunction could effectively reduce the electron-hole pair recombination. The reduction increased with the increase in Ag decoration. The conversion from the UV–Vis absorption spectrum to the Tauc Plot shows that the band gap of the nanowire was 4.05 eV. With 10 ppm methylene blue (MB) as the degradation solution, ZTO nanowires exhibit excellent photodegradation efficiency. Reusability and stability in photodegradation of the nanowires were demonstrated. Photocatalytic efficiency increases with the number of Ag nanoparticles. The main reaction mechanism was confirmed by photocatalytic inhibitors. This study enriches our understanding of ZTO-based nanostructures and facilitates their applications in water splitting, sewage treatment and air purification. [ABSTRACT FROM AUTHOR]

High quality single-crystalline NiSi2, Ni2Si and Ni31Si12 nanowire arrays coated with amorphous silicon dioxide were synthesized in high quantity by a nickel transport chemical vapor deposition (CVD) method. The morphological changes with various reaction temperatures, ambient pressures and reaction times, were observed and studied. At 750 °C and 850 °C, cone-shaped nanowire arrays were formed, composed of dense and oriented Ni31Si12 and Ni2Si nanowires with lengths of over 60 μm. The growth mechanisms of the nickel silicide nanowires have been proposed and identified with microscopy studies. Field emission measurements show that the as-grown NiSi2, Ni2Si and Ni31Si12 nanowires were of remarkable field enhancement factors, 2532, 4822 and 4099, respectively, and magnetic property measurements show ferromagnetic characteristics for the Ni2Si and Ni31Si12 nanowires, demonstrating promising potential applications for field emitters, magnetic storage, and biological cell separation. [ABSTRACT FROM AUTHOR]

Single-crystalline iron silicide nanowires were synthesized via an original approach, pre-deposition method (PDM), with significantly improved morphologies and physical characteristics as compared with those fabricated by conventional chemical vapor deposition. In the pre-deposition method, combining rapid thermal annealing (RTA) and chemical vapor deposition (CVD), iron silicide nanowires grew from the heterogeneous nucleation sites on the surface of the thin film without a catalyst or Al2O3 template. The morphology of the nanowires has been considerably improved in terms of alignment and aspect ratio. HRTEM analysis confirms that the nanowires were β-FeSi2 with a crystal direction of [111]. Physical property measurements indicate that compared with CVD β-FeSi2 nanowires, β-FeSi2 nanowires synthesized by the PDM performed better in both the field emission and magnetic properties. Magnetic property measurements show that the coercive field of PDM nanowires increased from 249 Oe to 900 Oe. Field emission studies reveal that the average β value of the CVD β-FeSi2 nanowires was 1060, while that of the PDM nanowires became 1892. Notably, with a furnace, few researchers can successfully synthesize nanowires of β-FeSi2, which is one of the most fascinating silicides for its important applications. [ABSTRACT FROM AUTHOR]

In this study, indium oxide nanowires of high-density were synthesized by chemical vapor deposition (CVD) through a vapor–liquid–solid (VLS) mechanism without carrier gas. The indium oxide nanowires possess great morphology with an aspect ratio of over 400 and an average diameter of 50 nm; the length of the nanowires could be over 30 μm, confirmed by field-emission scanning electron microscopy (SEM). Characterization was conducted with X-ray diffraction (XRD), transmission electron microscopy (TEM), photoluminescence spectrum (PL). High-resolution TEM studies confirm that the grown nanowires were single crystalline c-In2O3 nanowires of body-centered cubic structures. The room temperature PL spectrum shows a strong peak around 2.22 eV, originating from the defects in the crystal structure. The electrical resistivity of a single indium oxide nanowire was measured to be 1.0 × 10−4 Ω⋅cm, relatively low as compared with previous works, which may result from the abundant oxygen vacancies in the nanowires, acting as unintentional doping. [ABSTRACT FROM AUTHOR]

In this work, we report a novel and efficient silicidation method to synthesize higher manganese silicide (HMS) nanowires with interesting characterization and physical properties. High density silicon nanowire arrays fabricated by chemical etching reacted with MnCl2 precursor through a unique double tube chemical vapor deposition (CVD) system, where we could enhance the vapor pressure of the precursor and provide stable Mn vapor with a sealing effect. It is crucial that the method enables the efficient formation of high quality higher manganese silicide nanowires without a change in morphology and aspect ratio during the process. X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were utilized to characterize the HMS nanowires. High-resolution TEM studies confirm that the HMS nanowires were single crystalline Mn27Si47 nanowires of Nowotny Chimney Ladder crystal structures. Magnetic property measurements show that the Mn27Si47 nanowire arrays were ferromagnetic at room temperature with a Curie temperature of over 300 K, highly depending on the relationship between the direction of the applied electric field and the axial direction of the standing nanowire arrays. Field emission measurements indicate that the 20 μm long nanowires possessed a field enhancement factor of 3307. The excellent physical properties of the HMS nanowires (NWs) make them attractive choices for applications in spintronic devices and field emitters. [ABSTRACT FROM AUTHOR]

Manipulation of electron beam irradiation using TEM determines the selective region with a particular size and depth to conduct the subsequent process for nanopore formation. • Recording the effect of e-beam irradiation on Mo 5 O 14 nanowires by in situ TEM. • Manipulating e-beam to define the anticipated region and the size of nanoporosity. • Atom removal and crystallinity degradation resulting in structural transformation. • The formation of nanopores due to the numerous broken bonds in crystalline Mo 5 O 14. • Revealing the mechanism of selective nanopore formation in nanoscale modification. The Mo 5 O 14 -type structure is representative of the MoO-based catalyst in the selective oxidation process. Single-crystalline Mo 5 O 14 nanowires can be synthesized in a controlled manner by chemical vapor deposition (CVD). A nanowire catalyst with a porous structure combines the advantages of both nanoparticles and nanowires, leading to a substantial increase in the specific surface area. Therefore, we aim to manipulate the e-beam irradiation process on Mo 5 O 14 nanowires to induce the nanoporous structures in selected regions. In situ transmission electron microscopy (TEM) enabled us to visualize the structural transformation through gradual e-beam irradiation. The e-beam irradiation process removes oxygen atoms and renders the internal structure unstable. After the irradiated region is exposed to air, atoms tend to escape to decrease the internal energy. This results in the formation of nanopores because of the irradiation effect. By nanoscale modification method, the irradiated region is controlled by the electron beam size, which determines the nanopore distribution in the selected region. The study is beneficial for increasing the surface area of Mo 5 O 14 -type catalysts with variable nanopore densities and for modifying nanomaterials using a convenient method. [ABSTRACT FROM AUTHOR]

In this paper, we report the synthesis of iron silicide and β-iron disilicide nanowires with chemical vapor deposition; remarkably, the latter has drawn much attention but has seldom been achieved. We also propose the formation mechanisms for the two phases. To investigate the effects of the growth parameters on compositions and morphologies of the iron silicide nanowires, we changed and studied the reaction time, substrate temperature, position of samples, and pressure. The reaction concentration was found to be altered by all of the parameters; thus, we observed different nanowires in terms of morphologies and compositions with scanning electron microscopy. To confirm the growth direction and crystal structure of the nanowires, we conducted x-ray diffraction and high-resolution transmission electron microscopy studies. With the potential of being utilized as circuit elements in electronic devices for Schottky barriers, ohmic contacts, and interconnection among silicon-based transistors, the silicide work at nanoscale is beneficial for nanoelectronics. Understanding the effects of these growth parameters facilitates the control of nanowire growth with better quality. [ABSTRACT FROM AUTHOR]