The influence of Ga content on the melting temperature, wettability, microstructure, and mechanical properties of low-silver 12AgCuZnSn-2In-0.15Pr cadmium-free filler metal was investigated systematically by means of differential thermal analysis, X-ray diffractometer, scanning electron microscopy, energy-dispersive spectrometer, etc. The results showed that the addition of the Ga element reduced the solidus and liquidus temperatures of the novel low-silver filler metals, and effectively increased the spreading area of the filler metal on the copper and 304 stainless steel substrates. Furthermore, an appropriate amount of Ga element significantly optimized the interface morphology and improved the mechanical properties of the brazed joints. When the Ga content was 1wt.%, the shear strength of the brazed joints reached a peak value of 448 MPa, and the corresponding fracture morphology showed typical ductile characteristics with obvious dimples.

The flame brazing of H62 brass using a novel, low-silver Cu-P brazing filler metal was investigated in this study. The effect of the addition of a trace amount of Sn on the microstructure and properties of Cu-7P-1Ag filler metals was analyzed by means of X-ray diffractometer, scanning electron microscopy and energy dispersive spectrometer. The addition of trace Sn led to a decrease in the solidus and liquidus temperatures of Cu-7P-1Ag filler metals. Meanwhile, the spreading performance of the filler metals on a H62 brass substrate was improved. The microstructure of the low-silver, Cu-P brazing filler metal was mainly composed of α-Ag solid solution, α-Cu solid solution and Cu3P; an increase of Sn content led to the transformation of the microstructure of the joints from a block to a lamellar structure. When the Sn content was 0.5 wt. %, the shear strength of the joint at room temperature reached 348 MPa, and the fracture morphologies changed from a cleavage to a quasi-cleavage structure.

Ag-based and Cu-based brazing filler metals, which are the most widely used brazing materials in industrial manufacturing, have excellent gap-filling properties and can braze almost all the metallic materials and their alloys, except for the low-melting-point metals such as Al and Mg. Therefore, Ag-based and Cu-based brazing filler metals have attracted great attention. In this review, three series of typical Ag-based filler metals: the Ag-Cu, Ag-Cu-Zn, and Ag-Cu-Zn-Sn alloys; and three series of Cu-based filler metals: the crystalline and amorphous Cu-P filler metals, as well as the Cu-Zn filler metals, were chosen as the representatives. The latest research progress on Sn-containing Ag-based and Cu-based brazing filler metals is summarized, and the influences of Sn on the melting characteristics, wettability, microstructure, and mechanical properties of the selected filler metals are analyzed. Based on these, the problems and corresponding solutions in the investigation and application of the Sn-containing Ag-based and Cu-based filler metals are put forward, and the research and development trends of these filler metals are proposed.