Search

For many years, Si1−yGey alloys have been applied in the semiconductor industry due to the ability to adjust the performance of Si-based nanoelectronic devices. Following this alloying approach of group-IV semiconductors, adding tin (Sn) into the alloy appears as the obvious next step, which leads to additional possibilities for tailoring the material properties. Adding Sn enables effective bandgap and strain engineering and can improve the carrier mobilities, which makes Si1−x−yGeySnx alloys promising candidates for future opto- and nanoelectronics applications. The bottom-up approach for epitaxial growth of Si1−x−yGeySnx, e.g., by chemical vapor deposition and molecular beam epitaxy, allows tuning the material properties in the growth direction only; the realization of local material modifications to generate lateral heterostructures with such a bottom-up approach is extremely elaborate, since it would require the use of lithography, etching, and either selective epitaxy or epitaxy and chemical–mechanical polishing, giving rise to interface issues, non-planar substrates, etc. This article shows the possibility of fabricating Si1−x−yGeySnx alloys by Sn ion beam implantation into Si1−yGey layers followed by millisecond-range flash lamp annealing (FLA). The materials are investigated by Rutherford backscattering spectrometry, micro-Raman spectroscopy, x-ray diffraction, and transmission electron microscopy. The fabrication approach was adapted to ultra-thin Si1−yGey layers on silicon-on-insulator substrates. The results show the fabrication of single-crystalline Si1−x−yGeySnx with up to 2.3 at. % incorporated Sn without any indication of Sn segregation after recrystallization via FLA. Finally, we exhibit the possibility of implanting Sn locally in ultra-thin Si1−yGey films by masking unstructured regions on the chip, thus demonstrating the realization of vertical as well as lateral Si1−x−yGeySnx heterostructures by Sn ion implantation and flash lamp annealing. [ABSTRACT FROM AUTHOR]

Ge1−xSnx and Si1−x−yGeySnx alloys are promising materials for future opto- and nanoelectronics applications. These alloys enable effective bandgap engineering, broad adjustability of their lattice parameter, exhibit much higher carrier mobility than pure Si, and are compatible with the complementary metal-oxide-semiconductor technology. Unfortunately, the equilibrium solid solubility of Sn in Si1−xGex is less than 1% and the pseudomorphic growth of Si1−x−yGeySnx on Ge or Si can cause in-plane compressive strain in the grown layer, degrading the superior properties of these alloys. Therefore, post-growth strain engineering by ultrafast non-equilibrium thermal treatments like pulse laser annealing (PLA) is needed to improve the layer quality. In this article, Ge0.94Sn0.06 and Si0.14Ge0.8Sn0.06 thin films grown on silicon-on-insulator substrates by molecular beam epitaxy were post-growth thermally treated by PLA. The material is analyzed before and after the thermal treatments by transmission electron microscopy, x-ray diffraction (XRD), Rutherford backscattering spectrometry, secondary ion mass spectrometry, and Hall-effect measurements. It is shown that after annealing, the material is single-crystalline with improved crystallinity than the as-grown layer. This is reflected in a significantly increased XRD reflection intensity, well-ordered atomic pillars, and increased active carrier concentrations up to 4 × 1019 cm−3. [ABSTRACT FROM AUTHOR]

We grow AlN/4H-SiC and AlN/6H-SiC heterostructures by physical vapor deposition and characterize the heterointerface with micro-scale resolution. We investigate the spatial stress and strain distribution in these heterostructures using confocal Raman spectroscopy. We measure the spectral shifts of various vibrational Raman modes across the heterointerface and along the entire depth of the 4H- and 6H-SiC layers. Using the earlier experimental prediction for the phonon-deformation potential constants, we determine the stress tensor components in SiC as a function of the distance from the AlN/SiC heterointerface. Despite the fact that the lattice parameter of SiC is smaller than that of AlN, the SiC layers are compressively strained at the heterointerface. This counterintuitive behavior is explained by different coefficients of thermal expansion of SiC and AlN when the heterostructures are cooled from growth to room temperature. The compressive stress values are maximum at the heterointerface, approaching 1 GPa, and relax to the equilibrium value on the scale of several tens of micrometers from the heterointerface. [ABSTRACT FROM AUTHOR]

The flexibility of amorphous anodized alumina (AAO) in developing radiation dosimeter for hadron therapy is reported by controlled carbon ion implantation, followed by thermoluminescence (TL) measurements. The efficacy of amorphous AAO in controlling TL sensitivity is found to be governed by an increase in F+ defect centers as a function of carbon concentration, as revealed from the close resemblance of the trend in photoluminescence intensity. Moreover, its nanoporous structure is demonstrated to be advantageous for defect engineering due to the increase in the surface-to-volume ratio. Detailed X-ray photoelectron spectroscopy analysis suggests the formation of F+ centers by substituting Al3+ ions with C2+ in the vicinity of oxygen vacancies, where depth-dependent study showed the evolution of conducting channels owing to sp2 hybridized C–C bonding, leading to a differential charging effect. This work provides a direction to tune nanoporous AAO in its amorphous form for future ion beam dosimetry. [ABSTRACT FROM AUTHOR]