Search

In this study, stirred and column bioleaching methods were used for colemanite taken from Eti Maden Emet Boron Work. Pure Aspergillus Niger, used in bioleaching, obtained from Biology Department of Cukurova University. The dissolution yields of different solid rates were examined in the stirred bioleaching experiments and the column bioleaching experiments were made at 5% solids rate for 39 weeks. B2O3 dissolution yields, obtained from the results of experiments, were compared. According to the results of the experimental work, the stirred bioleaching dissolution yield was 90.18% and the column bioleaching dissolution yield was 70.02%., Bu çalışmada, Eti Maden Emet Bor İşletmesinden temin edilen kolemanit numunesine karıştırmalı ve kolon biyoliçi yöntemleri uygulanmıştır. Biyoliç deneylerinde Çukurova Üniversitesi Biyoloji Bölümünden saf olarak temin edilen Aspergillus Niger kullanılmıştır. Karıştırmalı biyoliç deneylerinde farklı katı oranlarındaki çözünme verimleri irdelenmiş, Kolon biyoliçi deneylerinde ise %5 katı oranında 39 haftalık kolon liçi yapılmıştır. Yapılan deneyler sonucunda elde edilen B2O3 çözünme verimleri karşılaştırılmıştır. Buna göre karıştırmalı biyoliçi çözünme verimi %90,18 iken kolon biyoliçi çözünme verimi ise %70,02 olarak tespit edilmiştir.

In this study, bioleaching method was used for kaolin sample taken from Kale Maden A.Ş.(Çan/ Çanakkale). Acidithiobacillus ferrooxidans bacteria, used in bioleaching experiments, were obtained from Deutsche Sammlung von Mikroorganismen und Zellkulturen (DSMZ). The effect of solids ratio on iron removal from the kaolin sample was investigated. pH, bacteria quantity and Fe concentration were measured in the experiments. Dissolution rates of Fe decreased with increasing solids ratio. The best iron removal was obtained as 59.44% Fe2O3 at 1% solids ratio., Bu çalışmada, Kale Maden A.Ş. (Çan/Çanakkale)’den temin edilen kaolen numunesine biyoliç yöntemi uygulanmıştır. Biyoliç deneylerinde Deutsche Sammlung von Mikroorganismen und Zellkulturen (DSMZ) kültür koleksiyonundan temin edilen Acidithiobacillus ferrooxidans kullanılmıştır. Deneysel çalışmalarda katı-sıvı oranının demir giderimi işlemi üzerindeki etkileri araştırılmıştır. Deneyler sırasında; pH, bakteri sayısı ve çözeltiye geçen Fe derişimi ölçülmüştür. Biyoliç deneylerinde katı oranı arttıkça demir giderimi düşmektedir. En iyi demir giderimi %1 katı oranında %59,44 olarak elde edilmiştir

In this study, optimum conditions of oxalic acid leaching to reduce iron content of the feldspar supplied by Kaltun Mining (Cine-Aydın) were investigated. For this purpose, two-stage oxalic acid leaching experiments were carried out. In the first stage, the leaching experiments were conducted according to Yates’ experimental design. Then, optimization tests were applied taking into consideration effective parameter in the second stage. Optimum conditions were 5% solids, 0.2 M of oxalic acid concentration, 80 oC temperature and 120 minutes of leaching (reaction) time. The iron removal from feldspar was 72.59% and the Fe2O3 content of the feldspar concentrate was 0.032% after the optimization tests., Bu çalışmada Kaltun Madencilik’ten (Çine-Aydın) alınan feldspat numunesindeki demir içeriğinin azaltılması için oksalik asit liçi optimum koşulları araştırılmıştır. Bu amaçla iki aşamalı oksalik asit liçi deneyleri yapılmıştır. İlk aşamada, liç deneyleri Yates tekniğine göre yapılmış buradan tespit edilen etkili parametre dikkate alınarak ikinci aşamada optimizasyon deneyleri yapılmıştır. Deneyler sonucunda optimum koşullar; katı oranı: %5, oksalik asit derişimi: 0,2 M, sıcaklık: 80 oC, liç süresi: 120 dk. olarak tespit edilmiştir. Optimizasyon deneyleri sonucunda feldspattaki demirin %72,59’u giderilmiş ve liç sonrası elde edilen konsantrenin Fe2O3 içeriği %0,032 olarak belirlenmiştir

In this study; coagulation/flocculation tests were carried out using solid tailings taken from flotation plant of Trakya Glass Industry (Mersin-Tarsus). Alum and fly ash were used as coagulants and the pulp was mixed in Jar-Test apparatus for 30 minutes. Then, sedimentation behavior of the particles was investigated at 5, 10, 15, 20, 25 and 30 minutes periods. After the experiments, it was determined that fly ash can be used instead of alum in the plant as a coagulant, Bu çalışmada; Trakya Cam Sanayi (Mersin-Tarsus) flotasyon tesisinden alınan atık üzerinde koagülasyon/flokülasyon deneyleri yapılmıştır. Koagülant olarak Afşin-Elbistan uçucu külü ve alüm kullanılmış ve süspansiyon Jar-Test deney aletinde 30 dakika süreyle karıştırılmıştır. Daha sonra 5, 10, 15, 20, 25 ve 30 dakikalık zaman aralıklarındaki çökme davranışları araştırılmıştır. Yapılan çalışmalar sonucunda koagülant olarak uçucu külün alümün yerine kullanılabileceği tespit edilmiştir.