Search

Thermally modified wood is becoming an increasingly popular material for different applications in buildings. Laboratory tests indicated a positive effect of thermal modification on durability, dimensional stability and thermal conductivity of wood. Therefore, windows and facade elements made of thermally modified Norway spruce and non-modified Norway spruce were tested in the field and installed in different test objects which were exposed at five locations in Europe (Slovenia, Germany, Sweden, and Spain). Results from monitoring showed that elements and windows made of thermally modified spruce (TMS) had considerably lower wood moisture content compared to the ones made of non-modified spruce and that wax further positively influenced moisture performance. Colour changes of TMS were more intensive compared to non-modified spruce but were successfully retarded by adding pigments to the wax. Mould and stain growth was largely dependent on the location, amount of precipitation and relative humidity. [ABSTRACT FROM AUTHOR]

In this study, we modified melamine-formaldehyde (MF) resin adhesive with liquefied wood (LW) and determined the properties of MF–LW adhesive mixtures. Furthermore, we produced particleboards using prepared MF–LW mixtures and evaluated their mechanical and physical properties. Results showed that with increasing content of LW in the adhesive mixture gel time and peak temperature increased while reaction enthalpy decreased. With increasing substitution of MF resin adhesive with LW the thermal stability of adhesive mixture reduced, namely thermal degradation started at lower temperature and weight loss increased. Properties of particleboards improved with increasing amount of LW in the adhesive mixture up to 20% and then deteriorated. Nevertheless, the properties of particleboard with 30% LW in the adhesive mixture were comparable to the properties of particleboard without LW while they worsen at greater portion of LW. Consequently, MF resin adhesive with 30% LW substitution could be used to produce particleboards with suitable mechanical properties and reduced formaldehyde release content. [ABSTRACT FROM PUBLISHER]

The bonding of beech (Fagus sylvaticaL.) with liquefied wood (LW) causes deterioration of the wood surface, resulting in a high percentage of wood failure at a relatively low bond shear strength. Light microscopy, scanning electron microscopy, FT-IR micro-spectroscopy and elemental carbon, nitrogen and sulphur (CNS) analysis techniques were used to investigate the formation of such bonds. It was assumed that the degradation of lignin, hemicelluloses and parts of the cellulose occurred in the cells of the wood surface where the LW had been applied. At the elevated temperatures occurring during the bonding process, the deteriorated cells were carbonised to some extent. The weak boundary layer of the bond was determined to be a layer of delignified cells located between the zone of partly carbonised cells on the one side and the cells of the undamaged wood of the adherend on the other side. The bonds which formed during the bonding of wood with LW were found to be very untypical compared to bonds formed by synthetic wood adhesives. No adhesive film was formed, the adhesive-adherend interface was not clear and the cells of the adherend subsurface were damaged. [ABSTRACT FROM AUTHOR]