The organic thin film solar cells (OTFSCs) have been successfully fabricated using PCDTBT : PC71BM with different mixing ratios (1 : 1 to 1 : 8) and the influence of hole transport layer thickness (PEDOT : PSS). The active layers with different mixing ratios of PCDTBT : PC71BM have been fabricated using o-dichlorobenzene (o-DCB). The surface morphology of the active layers and PEDOT : PSS layer with different thicknesses were characterized by AFM analysis. Here, we report that the OTFSCs with high performance have been optimized with 1 : 4 ratios of PCDTBT : PC71BM. The power conversion efficiency (PCE = 5.17%) of the solar cells was significantly improved by changing thickness of PEDOT : PSS layer. The thickness of the PEDOT : PSS layer was found to be of significant importance; the thickness of the PEDOT : PSS layer at 45 nm (higher spin speed 5000 rpm) shows higher short circuit current density (Jsc) and lower series resistance (Rs) and higher PCE.

Organic thin film solar cells (OTFSCs) were fabricated with blended active layers of poly[[4,8-bis[(2-ethylhexyl)oxy]benzo[1,2-b:4,5-b′]dithiophene-2,6-diyl][3-fluoro-2-[(2-ethylhexyl)carbonyl]thieno[3,4-b]thiophenediyl]] (PTB7)/[6,6]-phenyl-C71-butyric (PC71BM). The performances of active layers are prepared in chlorobenzene (CB) with different additives of 1-chloronaphthalene (CN) and 1,8-Diiodooctane (DIO) by a wet process with spin coating technique. The effects of different solvent additives on photovoltaic parameters such as fill factor, short circuit current density, and power conversion efficiency of active layers are reported. The absorption and surface morphology of the active layers are investigated using UV-visible spectroscopy and atomic force microscopy, respectively. The results indicate that structural and morphological changes were induced by the additives with solvent. The current density-voltage (J-V) characteristics of photovoltaic cells were measured under the illumination of simulated solar light with 100 mW/cm2 (AM 1.5 G) by an Oriel 1000 W solar simulator. The OTFSCs of PTB7/PC71BM prepared with organic solvent additives of DIO+CN show more improved PCE of 4.96% by spin coating method.