The properties and microstructure of friction stir processed AA 7075-T651 (Al-Zn-Mg-Cu) Aluminium alloy were studied using various tool designs. Trials were conducted on AA 5005-H34 with the aim of determining the most suitable FSP tool design out of the considered three different pin designs. Fully recrystallised fine microstructure and a defect free processed zone was achieved through the use of some of the FSP pin designs. For FSP 5005-H34 aluminium alloy substantial grain refinement was detected. The initial 192 µm pancake-like microstructure in the AA 5005-H34 base material was refined to 10–20 µm in the processed regions. Similarly, the grain size of around 50 µm in the base material was decreased to 4–10 µm in the processed regions of the FSP of 7075-T651 aluminium alloy. The traverse speed has a greater influence on the microhardness and mechanical properties, compared to the tool rotational speed. Microhardness and mechanical properties were improved as the traverse speed increased, due to the reduction in the precipitate-free zones at the grain boundaries.

Local material properties of the cladding layer, heat affected zone and substrate of laser cladded hypereutectoid steel rails were evaluated by uniaxial tensile tests on miniature specimens. Three laser cladding materials, i.e. 410 L, SS420 and Stellite 6, and two different heat treatment conditions were considered. To examine any possible anisotropic behaviour, specimens machined along the longitudinal and transverse laser cladding directions were tested. All the cladding layers showed similar or higher yield and ultimate tensile strengths, but lower elongation than the non-clad rail. Application of post-heat treatment significantly improved the elongation of all the cladding layer specimens. Elongation increments of 70%, 192% and 90% were respectively obtained from the 410 L, SS420 and Stellite 6 post-heat treated cladding layers. The post-heat treatment also marginally increased the yield and ultimate tensile strengths in this region. The improvement in tensile properties was associated with a more favourable microstructure, which resulted in a more dimpled morphology as depicted in the SEM images of the fractographic analysis of the tested specimens. While other properties are similar, both cladding layer and HAZ specimens showed significant different elongation values between the longitudinal and transverse directions in some cases, which indicates certain anisotropy in those materials’ ductility.