Search

Purpose: To evaluate the effect of simulated gastric acid solution (SGAS) and resin cement composition on the shear bond strength (SBS) of zirconia-based materials with different levels of translucency to composite resin. Materials and Methods: A total of 40 medium-opacity (MO; 3Y-TZP) and 40 medium-translucency (MT; 4Y-PSZ) zirconia slabs were distributed into four groups according to the composition of the resin luting system (MDP free or with MDP [primer + Panavia V5]) and storage method (distilled water or SGAS [5% hydrochloric acid]). Composite resin cylinders were cemented on the zirconia surface and stored for 91 hours. SBS, failure mode, and surface characterization analyses via scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS) were performed. SBS data were analyzed using three-way ANOVA and Tukey tests, and failure mode was assessed using one-way ANOVA (P < .05). Results: Storage media (P = .180), resin cement (P = .110), zirconia (P = .404), and their interactions did not affect SBS values. Bond strength ranged from 21.41 to 26.11 MPa. SEM images showed that SGAS modified the surface topography of zirconia and resin cement. The presence of chlorine and silicon (wt%) were higher after SGAS storage than after water storage in both cements used, while barium was higher only for the MDP cement. There was a prevalence of mixed failures for most of the groups. Conclusions: The SBS between both types of zirconia and resin cement was not affected by SGAS, although changes in zirconia topography were observed after SGAS exposure. The presence of MDP in the cement layer had no effect on the SBS challenged by SGAS. [ABSTRACT FROM AUTHOR]

Titanium-based dental prostheses are essential for prosthodontics and can now be 3D printed using powder bed fusion (PBF) technology with different densities by controlling the process parameters. This study aimed to assess the surface topography and bonding strength of dental resins made of 3D-printed titanium alloys with varying densities and growth directions. Three groups of titanium alloy (Ti6Al4V) specimens differentiated by density (low, medium, and high) were produced using laser-melting 3D printing technology (N = 8). Each group included specimen surfaces with vertical and horizontal growths. Vickers microhardness, surface profilometry, wettability, and shear bond strength (SBS) of the titanium samples were measured for all groups. Scanning electron microscopy (SEM) was performed. Statistical analyses were conducted using a two-way ANOVA and Fisher's multiple test. Higher-density specimens exhibited greater microhardness (p < 0.05), and those with horizontal growth directions were harder (p < 0.05) than their vertical counterparts within the same density category. Additionally, low-density specimens in both growth directions had the highest surface roughness values (p < 0.05) compared to the other groups. The wettability values were similar (p > 0.05) among the groups in the vertical direction, but not in the horizontal direction (p < 0.05). However, the density type did not significantly (p > 0.05) influence the bonding strength of 3D-printed titanium. This study revealed significant variations in surface roughness, contact angle, and microhardness based on density and growth direction. [ABSTRACT FROM AUTHOR]

Purpose: To evaluate the effect of simulated gastric acid solution (SGAS) and resin cement composition on the shear bond strength (SBS) of zirconia-based materials with different levels of translucency to composite resin., Materials and Methods: A total of 40 medium-opacity (MO; 3Y-TZP) and 40 medium-translucency (MT; 4Y-PSZ) zirconia slabs were distributed into four groups according to the composition of the resin luting system (MDP free or with MDP [primer + Panavia V5]) and storage method (distilled water or SGAS [5% hydrochloric acid]). Composite resin cylinders were cemented on the zirconia surface and stored for 91 hours. SBS, failure mode, and surface characterization analyses via scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS) were performed. SBS data were analyzed using three-way ANOVA and Tukey tests, and failure mode was assessed using one-way ANOVA (P < .05)., Results: Storage media (P = .180), resin cement (P = .110), zirconia (P = .404), and their interactions did not affect SBS values. Bond strength ranged from 21.41 to 26.11 MPa. SEM images showed that SGAS modified the surface topography of zirconia and resin cement. The presence of chlorine and silicon (wt%) were higher after SGAS storage than after water storage in both cements used, while barium was higher only for the MDP cement. There was a prevalence of mixed failures for most of the groups., Conclusions: The SBS between both types of zirconia and resin cement was not affected by SGAS, although changes in zirconia topography were observed after SGAS exposure. The presence of MDP in the cement layer had no effect on the SBS challenged by SGAS.