We have investigated Li 4 SiO 4 scintillation crystals for their possible application in neutron detection due to high Li content and low density of 2.35 g/cm 3 . The micro-pulling-down method employing the Ir crucible and afterheater was optimized for crystal growth of Li 4 SiO 4 taking into account the Li evaporation. To grow high-quality crack-free single crystals, the heating power was increased to establish milder temperature gradient, thicker meniscus, smaller crystal diameter and resulting smaller stress in the as-grown crystals. The undoped, Ti-, Cr-, and Al- doped crystals were prepared and studied. Radioluminescence measurements under X-ray excitation showed quite high overall scintillation efficiency of the Ti-doped sample reaching as high as 250% of that of Bi 4 Ge 3 O 12 reference scintillator. The emission spectrum was dominated by one broad band peaking at 350 nm related to Ti 4+ impurity. Reasonable light yield of 10000 photons/neutron was found. However, its long decay time of 54 μs might be a limitation especially for high counting rate applications. The overall scintillation efficiency of the Cr 3+ sample was much lower and the spectrum shows one broad peak at 463 nm which does not correspond to Cr 3+ luminescence. The radioluminescence spectrum of the Al-doped sample resembled to that of the Ti-doped one, just its magnitude is considerably lower, which was explained by Ti contamination. Peculiarities and optimization of crystal growth and a preliminary sketch of luminescence mechanisms and dopant incorporation are discussed. [ABSTRACT FROM AUTHOR]

Ce-doped lutetium aluminum garnet Lu 3 Al 5 O 12 (LuAG) nanoceramics were fabricated at 1600 °C and 1700 °C by spark-plasma sintering (SPS) method from nano-powders prepared by radiation synthesis. Both undoped and Ce-doped LuAG ceramic samples were also prepared from the nano-powders at 1700 °C with significantly increased pre-heating rate. The backscattered electron images revealed large amount of pores in all the Ce-doped samples causing their significant opacity. On the other hand, very large grains and no pores were revealed in the undoped sample, which was the only transparent one. The radioluminescence measurements revealed superior overall scintillation efficiency of the samples sintered at the temperature 1700 °C, and their defect emission in the UV region was ascribed to oxygen-vacancy-related defects such as F + centers. The photoluminescence decay of the defect emission was characterized by an extremely fast decay time of a few nanoseconds. Influence of sintering procedure and subsequent annealing on the luminescence and scintillation properties is discussed. [ABSTRACT FROM AUTHOR]

Lutetium oxyorthosilicate Lu2SiO5 (LSO) and pyrosilicate Lu2Si2O7 (LPS) activated by Ce3+ or Pr3+ are known to be effective and fast scintillation materials for the detection of X-rays and γ-rays. Their performances can be further improved by co-doping with aliovalent ions. Herein, we investigate the Ce3+(Pr3+) → Ce4+(Pr4+) conversion and the formation of lattice defects stimulated by co-doping with Ca2+ and Al3+ in LSO and LPS powders prepared by the solid-state reaction process. The materials were studied by electron paramagnetic resonance (EPR), radioluminescence spectroscopy, and thermally stimulated luminescence (TSL), and scintillation decays were measured. EPR measurements of both LSO:Ce and LPS:Ce showed effective Ce3+ → Ce4+ conversions stimulated by Ca2+ co-doping, while the effect of Al3+ co-doping was less effective. In Pr-doped LSO and LPS, a similar Pr3+ → Pr4+ conversion was not detected by EPR, suggesting that the charge compensation of Al3+ and Ca2+ ions is realized via other impurities and/or lattice defects. X-ray irradiation of LPS creates hole centers attributed to a hole trapped in an oxygen ion in the neighborhood of Al3+ and Ca2+. These hole centers contribute to an intense TSL glow peak at 450–470 K. In contrast to LPS, only weak TSL peaks are detected in LSO and no hole centers are visible via EPR. The scintillation decay curves of both LSO and LPS show a bi-exponential decay with fast and slow component decay times of 10–13 ns and 30–36 ns, respectively. The decay time of the fast component shows a small (6–8%) decrease due to co-doping. [ABSTRACT FROM AUTHOR]

Luminescence of new irregular Ce3+-related centers: the unperturbed and perturbed Ce3+ ions located in Al3+ sites and the CeLu3+ ions perturbed by LuAl3+ ions was found. The systematic stuffy of these centers by means of the ESR and luminescence methods and their influence on scintillation characteristics was performed. The structure and symmetry of the irregular Ce3+ centers was established and their spectral characteristics were explained. [ABSTRACT FROM AUTHOR]

For the first time, hafnia (HfO2) nanoparticles have been produced by photochemical synthesis. The photochemical route has been proven to be scalable, affordable, and straightforward to create monoclinic HfO2 nanoparticles with a size of tens of nanometers. The exploitation of this route offers a chance to create large amounts of dense nanoparticles with reduced costs and time of production for future creation of large area composite scintillators for fast timing techniques. Specific annealing treatments from 450 °C to 1000 °C have been targeted to tune the structural and morphological properties and optimize the luminescence of the nanoparticles. Hafnia nanoparticles annealed at low temperature display an amorphous structure. After thermal treatment at 1000 °C, HfO2 nanoparticles crystallize into a monoclinic phase, as evidenced by thermal analyses and X-ray diffraction. Radioluminescence and photoluminescence of HfO2 have been investigated at room temperature and 77 K. The emission band of hafnia covers a range from 300 to 600 nm and it can be attributed to defects within the matrix. In particular, the highest radioluminescence intensity appears in the crystalline sample annealed at 1000 °C, thanks to the higher crystallinity degree and the reduction of non-radiative channels and quenching defects. Photoluminescence and scintillation decay have evidenced the presence of the fast decay in the nanosecond time range. Thus, due to their size, density, and spectroscopic and timing features, monoclinic hafnia nanoparticles obtained by photochemical synthesis are attractive for potential creation of large area scintillating composites. [ABSTRACT FROM AUTHOR]

Luminescence and scintillation properties of Lu 2 YAl 2.5 Ga 2.5 O 12 :Ce,Mg (0.02, 0.05 %) garnet crystals grown by the micro-pulling down method were investigated. The onset temperature for luminescence quenching at ∼365 K is determined from the temperature dependence of photoluminescence decay time. At room temperature, the Mg (0.05 %) sample exhibits high integral scintillation efficiency of ∼445 % of BGO crystal, light yield value of 23,500 photons/MeV, and fast scintillation decay times of 20 ns (15 %) + 54 ns (85 %). The higher radioluminescence intensity of the Mg (0.05 %) sample correlates with an appearance of its lower themally-stimulated luminescence intensity in 77–500 K range. • Luminescence and scintillation properties of Lu 2 YAl 2.5 Ga 2.5 O 12 :Ce,Mg (Mg = 0.02 %, 0.05 %) crystals are investigated. • Both crystals show onset of luminescence quenching at 365 K. • Lu 2 YAl 2.5 Ga 2.5 O 12 :Ce,0.05%Mg shows light yield of 23,500 photons/MeV. • Lu 2 YAl 2.5 Ga 2.5 O 12 :Ce,0.05%Mg shows scintillation decay time of 20 ns (14 %) + 54 ns (86 %). • Thermoluminescence characteristics are investigated. [ABSTRACT FROM AUTHOR]

The scintillation characteristics of Lu0.8Gd2.2 (Al5–xGax)O12:Ce,Mg (x = 2.6 and 3) single crystals grown by the micropulling down method are investigated. The light yield of 27600 photons/MeV obtained for Lu0.8Gd2.2Al2Ga3O12:Ce,Mg is higher than that of 25 400 photons/MeV obtained for Lu0.8Gd2.2Al2.4Ga2.6O12:Ce,Mg. The photoluminescence and scintillation decays measured at room temperature (RT) for Lu0.8Gd2.2Al2Ga3O12:Ce,Mg are faster than those for Lu0.8Gd2.2Al2.4Ga2.6O12:Ce,Mg. Temperature dependence of radioluminescence (RL) intensity indicates a lower quenching temperature for Lu0.8Gd2.2Al2Ga3O12:Ce,Mg. Coincidence time resolution of a Lu0.8Gd2.2Al2Ga3O12:Ce,Mg detector in coincidence experiment with a BaF2 detector was measured to be 410 ps. The afterglow and thermally stimulated luminescence (TSL) characteristics below RT are also measured. [ABSTRACT FROM AUTHOR]

The scintillation characteristics of Gd 3 Al 2 Ga 3 O 12 :Ce, Li (GAGG:Ce,Li) and Gd 3 Al 2 Ga 3 O 12 :Ce, Mg (GAGG:Ce,Mg) single crystals were compared. Radioluminescence spectra and photoluminescence decay curves were measured at various temperatures between 77 and 500 K to investigate the thermal luminescence quenching. At 662 keV γ rays, the LY value of 35,400 photons/MeV and energy resolution of 6.9% obtained for GAGG:Ce, Li are superior to those of 24,200 photons/MeV and 9.5% for GAGG:Ce,Mg. Scintillation decays are approximated by a double exponentials with a fast principal decay component of 47 ns (83%) for GAGG:Ce, Mg and 90 ns (86%) for GAGG:Ce,Li. Coincidence time resolution of 282 ps obtained for GAGG:Ce, Mg is better than that of 389 ps for GAGG:Ce,Li. GAGG:Ce, Mg shows a much lower afterglow and thermally stimulated luminescence intensity with respect to GAGG:Ce,Li. • Scintillation properties of Li+ and Mg2+ -codoped Gd 3 Al 2 Ga 3 O 12 :Ce are compared. • Gd 3 Al 2 Ga 3 O 12 :Ce, Mg exhibits better timing performance. • Gd 3 Al 2 Ga 3 O 12 :Ce, Mg shows lower afterglow and TSL intensity. • Gd 3 Al 2 Ga 3 O 12 :Ce, Li exhibits high light yield and good energy resolution. [ABSTRACT FROM AUTHOR]

Ce3+,Pr3+-codoped SiO2-Al2O3-B2O3-Gd2O3 glasses (SABG:Ce,Pr) were prepared by melt quenching under a CO reducing atmosphere. Luminescence properties were investigated under UV and X-ray excitations. A dominant emission band at 430 nm belonging to the Ce3+:5d1 → 4f transition was observed in the photo- and radio-luminescence spectra. The energy transfer occurs from this Ce3+ band toward the 3PJ levels of Pr3+ with an efficiency of up to 24%, followed by the reduction of integrated luminescence intensity with an increasing Pr3+ concentration. This result is attributed to the increase in the reabsorption of Ce3+ luminescence and the non-radiative energy transfer toward the 3PJ levels of Pr3+. The cross-relaxation process within the Pr3+ pairs can further diminish the total luminescence yield at high Pr3+ concentrations. The integral scintillation efficiency and light yield measurements were carried out and compared to the reference Bi4Ge3O12 (BGO) crystal. [ABSTRACT FROM AUTHOR]

Optical and scintillation characteristics of Mg2+-codoped Lu 2 Y(Al 5-x Ga x)O 12 :Ce (x = 2, 3) multicomponent garnet crystals grown by the micro-pulling down method were investigated. At RT, the shortening of scintillation decay time and a decrease of light yield (LY) value measured for a higher Ga containing samples can be explained by thermal ionization of the Ce3+ 5d 1 excited state. At 662 keV γ-rays, Lu 2 YAl 3 Ga 2 O 12 : Ce, 0.05%Mg exhibits high LY value of 29,000 ph/MeV along with scintillation decay times of 50 ns (86%) + 73 ns (14%). Co-doping with larger Mg2+ content leads to a decrease of LY value, scintillation decay time, and afterglow level. Radioluminescence quenching observed at low temperature region in correlation with large thermoluminescence peaks can be caused by trapping of electrons at intrinsic shallow traps. • Luminescence and scintillation properties of Lu 2 Y(Al 5-x Ga x)O 12 :Ce,Mg (x = 2, 3) crystals are investigated. • Temperature dependencies of photo-and radioluminescence are presented. • Lu 2 YAl 3 Ga 2 O 12 :Ce,0.05%Mg shows high light yield of 29,000 photons/MeV. • Lu 2 YAl 3 Ga 2 O 12 :Ce,0.05%Mg shows quenching temperature at 435 K due to thermal ionization. • Afterglow and thermoluminescence characteristics are investigated. [ABSTRACT FROM AUTHOR]

Mg2+-codoped Y 0.6 Gd 2.4 Al 2 Ga 3 O 12 :Ce (YGAGG:Ce,Mg) single crystal was grown by the Czochralski method and its luminescence and scintillation properties were investigated. Temperature dependence of radioluminescence (RL) yield and photoluminescence (PL) decay time was measured, and activation energy of thermal ionization process was determined from temperature-dependent PL decay time measurement. YGAGG:Ce,Mg exhibited high X-ray excited RL yield almost 5 times higher than BGO reference scintillator. Its light yield of 41,500 ph/MeV and scintillation decay times of 12 ns (2%) + 52 ns (65%) + 207 ns (33%) were measured under excitation with 662 keV γ rays from 137Cs source. Afterglow and thermally stimulated luminescence characteristics are also investigated. • Luminescence and scintillation properties of Y 0.6 Gd 2.4 Al 2 Ga 3 O 12 :Ce,Mg crystal are investigated. • Temperature dependence of photo-and radioluminescence are presented. • Y 0.6 Gd 2.4 Al 2 Ga 3 O 12 :Ce,Mg shows high light yield of 41,500 photons/MeV. • Luminescence quenching above RT can be caused by thermal ionization. • Afterglow and thermoluminescence characteristics are investigated. [ABSTRACT FROM AUTHOR]

The optical and scintillation properties of Ce 3+ -doped YGd 2 Al 5− x Ga x O 12 ( x =2,3,4) single crystals were investigated. With increasing Ga content in the garnet host, the 5d 1 absorption and emission bands shift toward higher energy due to the decrease in the crystal field splitting of the 5d levels. Temperature dependences of absorption and emission spectra and of photoluminescence decays of both prompt and delayed components were measured. Light yield (LY) and its dependence on an amplifier shaping time were measured under excitation with γ-rays. High LY value of 38,000 photons/MeV was obtained for a YGd 2 Al 2 Ga 3 O 12 :Ce sample. Scintillation decay was measured with an extended dynamical and temporal scale under the nanosecond-pulsed soft X-ray excitation. The relative content of the fastest component in the scintillation response increases with increasing Ga content. [ABSTRACT FROM AUTHOR]

Doubly doped LaF3:Er, Nd scintillation crystals were grown by modified micropulling-down method. The Er codoping was chosen to enhance the energy transfer from the host lattice to the Nd3+ luminescence center via the 5d-levels of Er3+, which can be enabled by the overlap of Er3+ 5d-4f emission spectrum with the Nd3+ 4f-5d absorption. However, no relevant energy transfer was found by photo- and radioluminescence spectra measurements. The reasons of no significant positive effect of Er codoping are discussed. [ABSTRACT FROM AUTHOR]

Abstract: Nd3+ 1%, 5% and 10% doped BaF2 single crystals were grown by the micro-pulling down method. Photoluminescence properties, including excitation and emission spectra and luminescence decay were measured under synchrotron radiation excitation at the Superlumi station in HASYLAB at DESY (Hamburg, Germany). The Nd3+ related 5d-4f emission lines peaking around 180 nm, 230 nm, and 260 nm, identified as the 5d–4Ij, 5d–4Fj, and 5d–2Gj transitions, were observed under 140–168 nm excitation. In photoluminescence decay under the 160 nm excitation, the dominant component decay time is about 12, 2.5 and 1.2 ns for Nd3+ 1%, 5% and 10% concentration, respectively. The decay time shortening is explained by the concentration quenching effect. Transmittance of Nd1% sample is about 80% for wavelengths above 185 nm. Finally, gamma-ray responses, non-proportionality and energy resolution of Nd1% sample were compared with the undoped BaF2 scintillator. The light yield of the Nd1%:BaF2 is about 93% of that of undoped BaF2. ©2009 Elsevier Ltd. All rights reserved. [Copyright &y& Elsevier]

Abstract: Doubly doped BaY2F8:Er,Nd scintillation crystals were grown by modified micro-pulling-down method. The Er co-doping was chosen to enhance the energy transfer from the host lattice to the Nd3+ luminescence center via the 5d-levels of Er3+, which can be enabled by the overlap of Er3+ 5d-4f emission spectrum with the Nd3+ 4f-5d absorption. The energy transfer was clearly evidenced in the BaY2F8:Er,Nd. The processes are complicated by energy migration to killer centres and/or cross-relaxation processes. The luminescence and energy transfer mechanism are discussed. [Copyright &y& Elsevier]