The relationship between the magnetic interaction and photoinduced dynamics in antiferromagnetic perovskites is investigated in this study. In La${}_{1/3}$Sr${}_{2/3}$FeO${}_{3}$ thin films, commensurate spin ordering is accompanied by charge disproportionation, whereas SrFeO${}_{3}$ thin films show incommensurate helical antiferromagnetic spin ordering due to increased ferromagnetic coupling compared to La${}_{1/3}$Sr${}_{2/3}$FeO${}_{3}$. To understand the photoinduced spin dynamics in these materials, we investigate the spin ordering through time-resolved resonant soft X-ray scattering. In La${}_{1/3}$Sr${}_{2/3}$FeO${}_{3}$, ultrafast quenching of the magnetic ordering within 130 fs through a nonthermal process is observed, triggered by charge transfer between the Fe atoms. We compare this to the photoinduced dynamics of the helical magnetic ordering of SrFeO${}_{3}$. We find that the change in the magnetic coupling through optically induced charge transfer can offer an even more efficient channel for spin-order manipulation., 7 pages, 5 figures

Nanostructure-induced L10-ordering of twinned single-crystals in CoPt ferromagnetic nanowires on Si/SiO2 substrates is demonstrated, where nanostructure-induced L10-ordering is driven by ultrasmall 10 nm-scale curvature radii of the nanowires.

L10-ordered CoPt with a large coercivity (H c) of 13 kOe was demonstrated on Si/SiO2 substrates by hydrogen annealing. Equiatomic 11.2 nm thick (Co/Pt)4 multilayer thin films were fabricated by electron-beam evaporation and were annealed at 500 °C–900 °C for 10–90 min under an Ar/H2 mixed gas atmosphere. The annealing temperature and time dependences of the crystal structures, magnetic properties, and surface morphologies of the films were systematically analyzed based on the experimental results obtained from grazing incidence X-ray diffraction (GI-XRD), vibrating sample magnetometer, and scanning electron microscope, respectively. Hydrogen annealing effectively promoted the out-of-plane c-axis orientation of L10-ordered CoPt compared to the vacuum annealing according to the GI-XRD patterns. A maximum H c of 13.3 kOe was obtained in L10-ordered CoPt with angular-outlined isolated grains by hydrogen annealing at 800 °C for 60 min, where the c-axis of L10-ordered CoPt was randomly distributed.

We report a synchrotron radiation X-ray diffraction study of the BiS2-layered superconductor LaO0.5F0.5BiS2. We observed superlattice reflections with the propagation vector \(\boldsymbol{q}_{\text...