Search

For the first time, hafnia (HfO2) nanoparticles have been produced by photochemical synthesis. The photochemical route has been proven to be scalable, affordable, and straightforward to create monoclinic HfO2 nanoparticles with a size of tens of nanometers. The exploitation of this route offers a chance to create large amounts of dense nanoparticles with reduced costs and time of production for future creation of large area composite scintillators for fast timing techniques. Specific annealing treatments from 450 °C to 1000 °C have been targeted to tune the structural and morphological properties and optimize the luminescence of the nanoparticles. Hafnia nanoparticles annealed at low temperature display an amorphous structure. After thermal treatment at 1000 °C, HfO2 nanoparticles crystallize into a monoclinic phase, as evidenced by thermal analyses and X-ray diffraction. Radioluminescence and photoluminescence of HfO2 have been investigated at room temperature and 77 K. The emission band of hafnia covers a range from 300 to 600 nm and it can be attributed to defects within the matrix. In particular, the highest radioluminescence intensity appears in the crystalline sample annealed at 1000 °C, thanks to the higher crystallinity degree and the reduction of non-radiative channels and quenching defects. Photoluminescence and scintillation decay have evidenced the presence of the fast decay in the nanosecond time range. Thus, due to their size, density, and spectroscopic and timing features, monoclinic hafnia nanoparticles obtained by photochemical synthesis are attractive for potential creation of large area scintillating composites. [ABSTRACT FROM AUTHOR]

Lutetium oxyorthosilicate Lu2SiO5 (LSO) and pyrosilicate Lu2Si2O7 (LPS) activated by Ce3+ or Pr3+ are known to be effective and fast scintillation materials for the detection of X-rays and γ-rays. Their performances can be further improved by co-doping with aliovalent ions. Herein, we investigate the Ce3+(Pr3+) → Ce4+(Pr4+) conversion and the formation of lattice defects stimulated by co-doping with Ca2+ and Al3+ in LSO and LPS powders prepared by the solid-state reaction process. The materials were studied by electron paramagnetic resonance (EPR), radioluminescence spectroscopy, and thermally stimulated luminescence (TSL), and scintillation decays were measured. EPR measurements of both LSO:Ce and LPS:Ce showed effective Ce3+ → Ce4+ conversions stimulated by Ca2+ co-doping, while the effect of Al3+ co-doping was less effective. In Pr-doped LSO and LPS, a similar Pr3+ → Pr4+ conversion was not detected by EPR, suggesting that the charge compensation of Al3+ and Ca2+ ions is realized via other impurities and/or lattice defects. X-ray irradiation of LPS creates hole centers attributed to a hole trapped in an oxygen ion in the neighborhood of Al3+ and Ca2+. These hole centers contribute to an intense TSL glow peak at 450–470 K. In contrast to LPS, only weak TSL peaks are detected in LSO and no hole centers are visible via EPR. The scintillation decay curves of both LSO and LPS show a bi-exponential decay with fast and slow component decay times of 10–13 ns and 30–36 ns, respectively. The decay time of the fast component shows a small (6–8%) decrease due to co-doping. [ABSTRACT FROM AUTHOR]

Driven by the pursuit of optimizing the luminescent properties of garnet-based single crystals for X-ray imaging applications, this work reports on the successful synthesis and in-depth characterization of GYAGG crystals doped with Ce³⁺ or Tb³⁺ ions, and doubly-doped with both of them. Micro-pulling down synthesis yielded crystals with a single cubic phase confirmed by X-ray diffraction. Photoluminescence (PL) and radioluminescence (RL) measurements on Ce³⁺,Tb³⁺ co-doped GYAGG revealed bidirectional energy transfer processes. Characteristic broadband 5d 1 →4f emission of Ce³⁺ centers peaking at 530 nm and narrow 4f→4f emission lines of Tb³⁺ ions starting from 5D 4 level within 480–630 nm were observed. At higher doping levels, cross-relaxation in Tb³⁺ pairs resulted depleted 5D 3 state and only the emission from 5D 4 one was observed in the spectra. Analysis of PL decay characteristics corroborated the spectral observations, confirming progressively decreasing Ce³⁺ decay time (down to 40 ns at 15 % Tb3+) due to enhanced Ce³⁺→Tb³⁺ energy transfer. Similarly, the Tb³⁺ decay time accelerated by more than 60 % after the Ce³⁺ co-doping. Notably, co-doping with 0.5 % Ce³⁺ and 10–15 % Tb³⁺ doubled the luminescence intensity of RL spectra compared to 0.5 % Ce³⁺-doping alone, attributed to the increased density of emitting centers. • High-quality and crack-free GYAGG:Ce,Tb single crystals were successfully grown. • The photoluminescence spectra revealed Ce³⁺↔Tb³⁺ bidirectional energy transfer. • At lower Tb³⁺ doping (0.5 %), the bidirectional energy transfer was inefficient. • High Tb³⁺ doping (15 %) significantly enhanced energy transfer. • Co-doping yielded a two-fold radioluminescence intensity compared to sole doping. [ABSTRACT FROM AUTHOR]

Luminescence and scintillation properties of Lu 2 YAl 2.5 Ga 2.5 O 12 :Ce,Mg (0.02, 0.05 %) garnet crystals grown by the micro-pulling down method were investigated. The onset temperature for luminescence quenching at ∼365 K is determined from the temperature dependence of photoluminescence decay time. At room temperature, the Mg (0.05 %) sample exhibits high integral scintillation efficiency of ∼445 % of BGO crystal, light yield value of 23,500 photons/MeV, and fast scintillation decay times of 20 ns (15 %) + 54 ns (85 %). The higher radioluminescence intensity of the Mg (0.05 %) sample correlates with an appearance of its lower themally-stimulated luminescence intensity in 77–500 K range. • Luminescence and scintillation properties of Lu 2 YAl 2.5 Ga 2.5 O 12 :Ce,Mg (Mg = 0.02 %, 0.05 %) crystals are investigated. • Both crystals show onset of luminescence quenching at 365 K. • Lu 2 YAl 2.5 Ga 2.5 O 12 :Ce,0.05%Mg shows light yield of 23,500 photons/MeV. • Lu 2 YAl 2.5 Ga 2.5 O 12 :Ce,0.05%Mg shows scintillation decay time of 20 ns (14 %) + 54 ns (86 %). • Thermoluminescence characteristics are investigated. [ABSTRACT FROM AUTHOR]

Optical and scintillation characteristics of Mg2+-codoped Lu 2 Y(Al 5-x Ga x)O 12 :Ce (x = 2, 3) multicomponent garnet crystals grown by the micro-pulling down method were investigated. At RT, the shortening of scintillation decay time and a decrease of light yield (LY) value measured for a higher Ga containing samples can be explained by thermal ionization of the Ce3+ 5d 1 excited state. At 662 keV γ-rays, Lu 2 YAl 3 Ga 2 O 12 : Ce, 0.05%Mg exhibits high LY value of 29,000 ph/MeV along with scintillation decay times of 50 ns (86%) + 73 ns (14%). Co-doping with larger Mg2+ content leads to a decrease of LY value, scintillation decay time, and afterglow level. Radioluminescence quenching observed at low temperature region in correlation with large thermoluminescence peaks can be caused by trapping of electrons at intrinsic shallow traps. • Luminescence and scintillation properties of Lu 2 Y(Al 5-x Ga x)O 12 :Ce,Mg (x = 2, 3) crystals are investigated. • Temperature dependencies of photo-and radioluminescence are presented. • Lu 2 YAl 3 Ga 2 O 12 :Ce,0.05%Mg shows high light yield of 29,000 photons/MeV. • Lu 2 YAl 3 Ga 2 O 12 :Ce,0.05%Mg shows quenching temperature at 435 K due to thermal ionization. • Afterglow and thermoluminescence characteristics are investigated. [ABSTRACT FROM AUTHOR]

Mg2+-codoped Y 0.6 Gd 2.4 Al 2 Ga 3 O 12 :Ce (YGAGG:Ce,Mg) single crystal was grown by the Czochralski method and its luminescence and scintillation properties were investigated. Temperature dependence of radioluminescence (RL) yield and photoluminescence (PL) decay time was measured, and activation energy of thermal ionization process was determined from temperature-dependent PL decay time measurement. YGAGG:Ce,Mg exhibited high X-ray excited RL yield almost 5 times higher than BGO reference scintillator. Its light yield of 41,500 ph/MeV and scintillation decay times of 12 ns (2%) + 52 ns (65%) + 207 ns (33%) were measured under excitation with 662 keV γ rays from 137Cs source. Afterglow and thermally stimulated luminescence characteristics are also investigated. • Luminescence and scintillation properties of Y 0.6 Gd 2.4 Al 2 Ga 3 O 12 :Ce,Mg crystal are investigated. • Temperature dependence of photo-and radioluminescence are presented. • Y 0.6 Gd 2.4 Al 2 Ga 3 O 12 :Ce,Mg shows high light yield of 41,500 photons/MeV. • Luminescence quenching above RT can be caused by thermal ionization. • Afterglow and thermoluminescence characteristics are investigated. [ABSTRACT FROM AUTHOR]