Search

Thermochromic sensors provide an intuitive and real‐time solution for monitoring the local temperature with naked eyes. Conventional thermochromic sensors often utilize either solution‐type or dense film‐type platforms, which are suboptimal morphologies for exposing a large number of dye molecules to the surface, leading to low sensitivity and sluggish responding speeds. Herein, this article introduces rational synthetic routes to fabricate highly sensitive nanofiber (NF) sensor membranes loaded with thermochromic dyes (C3H6N6·CH2O)x‐loaded nanofibers (NFs) sensor membranes by alignment‐controllable electrospinning techniques (x–y perpendicular and rotary). The NF‐based porous sensor membranes exhibit two‐ to fivefold improved thermochromic sensitivity (ΔRGB) compared to those of dense film‐type sensors at 31.6–42.7 °C. This is attributed to the uniform distribution of dyes throughout the porous NF structure (≈95.7%), which exhibits excellent light transmittance that is 10–30‐fold higher than that of film‐type sensors. Based on the available shape‐conforming synthetic strategies, this article further demonstrates wearable thermochromic sensors in the forms of mask‐, patch‐, and bracelet‐type devices, which can accurately monitor body temperature in real time. [ABSTRACT FROM AUTHOR]

Electrospinning–etching strategy was employed to synthesize Pt-loaded SnO 2 hollow microbelts (Pt_SnO 2 HBLs) based chemiresistive-type sensor demonstrating high sensitivity and selectivity toward acetone gas. This strategy overcomes a major hurdle toward achieving ubiquitous gas diffusion in electrospun structures, and provides highly porous thin-walled HBLs with large surface area and small crystallites. [Display omitted] • In situ templating of SnO 2 with SiO 2 was employed to form Pt-loaded SiO 2 @SnO 2 core–shell microbelts. • Etching away of SiO 2 in the Pt-loaded SiO 2 @SnO 2 microbelts yielded Pt-loaded SnO 2 hollow microbelts. • The Pt-loaded SnO 2 hollow microbelts exhibited good response (R a /R g = 93.5) and selectivity toward 2 ppm acetone at 350 °C. Challenges for ubiquitous diffusion of gas analytes into semiconducting metal oxides (SMOs) based sensing layers have necessitated the introduction of unprecedented synthesis techniques for thin, porous and high-performance gas sensing materials. In this work, electrospinning and calcination were employed to prepare unprecedented SiO 2 –SnO 2 core–shell microbelts (hereinafter referred to as SiO 2 @SnO 2 BLs) followed by etching away of SiO 2 in NaOH solution (pH 12) to achieve hollow SnO 2 BLs (hereinafter referred to as SnO 2 HBLs) with mean crystal size of 14.01 nm, large BET surface area (143.5 m2‧g–1), high porosity (mean pore size of 5.7 nm), and shell thickness of 58.3 ± 11.4 nm. Sensitization of SnO 2 HBLs with apoferritin-templated platinum nanoparticles (Pt NPs) enhanced their detection capability toward acetone. Response (defined as R a /R g , where R a and R g are sensor resistances in air and target gas, respectively) of Pt(0.12 %)_SnO 2 HBLs toward 2 ppm acetone was up to 7.8 times higher compared to that of pristine SnO 2 HBLs, and exhibited faster response (9.2 s). The Pt(0.12 %)_SnO 2 HBLs based sensor indicated a promising long-term stability, and outstanding repeatability of response (R a /R g = 93.7 ± 0.89) toward 25 cycles of 2 ppm acetone exposure in a humid environment of 90 % relative humidity. This performance could be attributed to the unique morphology of HBLs, sensitization effects of catalytic Pt NPs, and enlargement of the electron-depleted layer resulting from a Schottky barrier between Pt NPs and SnO 2 grains. [ABSTRACT FROM AUTHOR]