Search

In‐plane biaxial fatigue tests of commercial pure titanium (CP‐Ti) were performed to investigate the effects of load ratio and phase shift on fatigue and ratcheting behavior. The results show that with the decrease of load ratio or the increase of phase shift, biaxial ratcheting strain effect is more significant, leading to the deterioration of fatigue resistance. Analysis of the crack morphology and fracture characteristic reveals that the crack propagation path becomes complex and the fracture morphology changes due to the enhanced non‐proportional hardening effect. Finally, current multiaxial life prediction models are evaluated to compare the applicability in the biaxial fatigue life prediction. Highlights: Effects of load ratio and phase shift on biaxial ratcheting behavior are discussed.Biaxial fatigue life is more sensitive to the variation of the phase shift.The crack morphology and fracture characteristics are analyzed.The applicability of different multiaxial life prediction models is evaluated. [ABSTRACT FROM AUTHOR]

• Influence of micronotch size on fatigue life is quantified by a new model. • Average crack arrest cycle decreases with the equivalent micronotch size. • Post-arrest behavior is characterized by crack coalescence and the alternation of slip system. • A high crack propagation rate is correlated with the dominate slip system of prismatic . • Micronotch size has little effect on the long crack propagation rate. The influence of the micronotch size on the small fatigue-crack behavior of CP-Ti was investigated in this study. With an increase in the equivalent micronotch size, the fatigue life and average crack-arrest cycle decreased. Microstructural analysis revealed that crack arrest results from high-angle grain boundaries, and the post-arrest behavior is mainly characterized by the connection of main and secondary cracks, or the alternation of the slip system. A high crack propagation rate is correlated with prismatic < a > slip. The activation of other slip modes may decrease the crack propagation rate. The micronotch size affected the distribution of the crack growth regions but had little influence on the long crack propagation rate. [ABSTRACT FROM AUTHOR]

Abstract Low cycle fatigue (LCF) behavior of CP-Ti along transverse direction under symmetrical strain and stress-controlled modes was compared systematically. For the strain-controlled tests, tension-compression asymmetry (TCA) has little effect on LCF behavior due to the negligible compressive mean stress. For the stress-controlled tests, TCA is detrimental to LCF resistance. The microstructure evolution during cycling deformation was characterized by EBSD and TEM to identify different deformation mechanisms. It was found that strain cycling deformation was dominated by dislocation slip and exhibited the transition from planar slip to wavy slip with the increase of strain amplitude. For the stress-controlled tests, tensile twinning together with dislocation slip accommodated the increased ratcheting deformation. The strain-life curve under stress-controlled tests is lower than that at strain-controlled tests due to the heterogeneous plastic deformation caused by ratcheting deformation. In order to obtain a unified fatigue life prediction model for different control modes, a novel effective strain range related model was proposed by introducing the TCA factor into the original Manson–Coffin relation. Furthermore, the application of this effective strain range related model was extended to the condition of asymmetrical stress cycling by correcting fatigue ductility coefficient and exponent. [ABSTRACT FROM AUTHOR]

Abstract In order to understand the effects of cyclic asymmetry and control mode on low cycle fatigue (LCF) behavior of CP-Ti along rolling direction (RD), symmetrical strain and stress-controlled fatigue tests were conducted in this paper. LCF behavior of CP-Ti along RD under different control modes was systematically compared from the aspects of cyclic response, microstructure evolution and fatigue life with the technique of electron backscatter diffraction (EBSD) and scanning electron microscope (SEM). It was found that cyclic softening resulted by dislocation slip dominates strain-controlled fatigue. On the contrary, cyclic hardening dominates stress-controlled fatigue at high stress amplitude, leading to a higher cyclic stress-strain curve. Owing to asymmetrical hysteresis loop, compressive ratcheting strain is accumulated in stress-controlled LCF test despite of the fully reversed stress cycling. EBSD results show there is a transition of deformation mechanism from dislocation slip to dislocation slip and twinning dominated cyclic deformation with the increase of compressive ratcheting strain. Meanwhile, GOS analysis and SEM observation indicate that the appearance of massive twins results in the heterogeneous plastic deformation and micro-cracks are favorable to be initiated in the twin abundant area. Besides, compressive ratcheting strain has significant effects on fatigue crack growth as the fracture surface presents the serious abrasion of cleavage facets and fatigue striations. Finally, strain-life curves under different control modes are identical, indicating that fatigue life along RD is insensitive to compressive ratcheting strain under the interaction of these factors. [ABSTRACT FROM AUTHOR]

Low cycle fatigue (LCF) behavior of commercially pure titanium (CP-Ti) was investigated under stress cycling and strain cycling along the rolling direction (RD), 30° to the rolling direction (RD-30°), 60° to the rolling direction (RD-60°) and the transverse direction (TD), respectively. The loading direction brings about eminent differences in the fatigue properties, which is summarized as follows; Cyclic strain hardening exponent: RD＞RD-30°＞RD-60°＞TD Cyclic stress amplitude: TD＞RD-60°＞RD-30°＞RD Ratcheting effect: TD＞RD-60°＞RD-30°＞RD Fatigue life: RD＞RD-30°＞RD-60°＞TD Based on the comprehensive analysis of Schmid factor, texture evolution, twinning activities, in-grain misorientation axis and geometrically necessary dislocation density, it is concluded that the anisotropic slip behavior characterizes the planar anisotropy of LCF behavior. The promotion of dislocation activities of non-prismatic slip with higher activation stress from the RD to the TD leads to the higher cyclic stress amplitude, lower cyclic strain hardening and more significant ratcheting effect, though prismatic slip always acts as the primary slip mode. The observation of fracture surfaces also confirms the critical role of dislocation activities on fatigue crack initiation. Introducing yield ratio parameter into the asymmetry coefficient related model, the fatigue lives in both the fatigue were accurately predicted. [ABSTRACT FROM AUTHOR]