Dy3+, Eu3+ co-doped glass ceramics (GCs) containing SrMoO 4 crystalline phase were prepared by melt-curing-crystallization method. The most favorable heat treatment conditions for the glass ceramics were found to be 610 °C/2 h by differential scanning calorimetry (DSC), ultraviolet spectrophotometer (UV–Vis), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The best doping concentrations of Dy3+ and Eu3+ in this glass ceramic were 0.8 % and 0.6 %, concentration quenching caused by dipole-dipole interactions occurs when the content of rare earth ions in GCs continues to increase. The chromaticity coordinates of the Dy3+- Eu3+ co-doped glass ceramics changed from cool white light to warm white light with the addition of Eu3+ concentration. At the optimal doping concentration (0.8 % Dy3+-0.6 % Eu3+), the chromaticity coordinate of glass ceramics is (0.3972, 0.3331), and the related color temperature is 3047 K. The luminescence intensity can still reach about 80 % of room temperature at 180 °C, and its thermal quenching activation energy is 0.233 eV. This suggests that glass ceramics have excellent thermal stability. After adding an appropriate amount of Li+, the crystalline phase of the glass ceramics remained unchanged and the luminous intensity of the glass ceramics increased by a factor of about 1.4 in the same environment. The thermal quenching activation energy of the glass ceramic doped with 0.2 % Li+-0.8 % Dy3+-0.6 % Eu3+ was 0.344 eV. The experimental results indicate that GCs has potential application prospects in the field of solid-state lighting. [ABSTRACT FROM AUTHOR]

This work addresses the problem of obtaining of Ca 3 Co 4 O 9+δ -based ceramics with enhanced thermoelectric performance. Phase-inhomogeneous layered calcium cobaltite ceramics with cationic nonstoichiometry were prepared by solid-state reactions method and a field assisted sintering technology (FAST). Comprehensive experimental characterizations were conducted on the prepared bulk samples, focusing on their phase composition, as well as thermal (including thermal expansion, thermal diffusivity, and thermal conductivity), electrical (encompassing electrical conductivity and the Seebeck coefficient), and functional properties (such as power factor and figure-of-merit). The FAST technique allowed to obtain ceramics with low porosity and high electrical conductivity, which increased as the Ca:Co ratio within the samples decreased, while sample phase inhomogeneity considerably increased the Seebeck coefficient. The best thermoelectric performance was demonstrated for cationic nonstoichiometric Ca 3 Co 4.4 O 9+δ , which power factor and figure-of-merit values at 825 °C reached 427 μW⋅m−1⋅K−2 and 0.146, respectively. • Ca 3 Co 4 O 9+δ -based ceramics prepared by field assisted sintering technology possessed low porosity and high conductivity. • Electrical conductivity of bulk samples increased at decreasing Ca:Co ratio. • Phase inhomogeneity of prepared ceramics increased the Seebeck coefficient. • Ca 3 Co 4.4 O 9+δ ceramics showed the best thermoelectric performance. [ABSTRACT FROM AUTHOR]

Low-cost amorphous nano-carbon (ANC) was employed as an absorbent to modify the microwave performance of AlN ceramics (AlN-4 wt% Y 2 O 3 - x wt% C, x = 0, 2.0, 3.8, 3.9, 4.0) via hot-pressing sintering, and the thermal and mechanical properties were also investigated. With the increase of ANC content from 0 to 4.0 wt%, the relative density of AlN composite decreases from 3.28 g cm−3 to 3.16 g cm−3 when sintered at 1800 °C for 2 h, and with the increase of sintering temperature from 1700 °C, the density of the 4.0 wt% ANC doped AlN composite presents trend of increase and reaches the maximum value of 3.16 g cm−3 at 1800 °C and then decreases. The XRD pattern shows that the composites are composed of AlN and Y–Al–O (YAG, YAP, YAM et al.) phases. SEM results indicate that average grain sizes for AlN and secondary phases gradually decrease with increasing carbon content, suggesting inhibited grain growth due to ANC addition. No obvious changes in phase constitution nor intensity changes were detected with the increase in carbon content and sintering temperature. As the carbon content increases from 0 to 4.0 wt%, the dielectric constant gradually increases from ∼9 to 13.89 at 10 GHz, the dielectric loss gradually increases from the vicinity of 10−3 to 0.38 at 10 GHz, and the reflective loss decreases from −27.92 dB to −49.40 dB, the thermal conductivity of the AlN-ANC composite decreases from 116.63 W m−1 K−1 to 50.13 W m−1 K−1. In addition, with 4.0 wt% ANC addition, the dielectric constant, dielectric loss, reflective loss, hardness, elastic modulus, bending strength, and fracture toughness are 13.89, 0.38, 49.40 dB, 6.4 ± 0.4 GPa, 262 GPa, 268.78 MPa, and 1.4 ± 0.1 MPa m1/2, respectively. Its ability to efficiently absorb microwave energy enhances the performance of devices including radar systems, communication equipment, and microwave heating systems, making it a promising candidate for microwave vacuum electronic applications. [ABSTRACT FROM AUTHOR]

To realize the high-brightness of yellow light-emitting diodes (LEDs), the yellow-emitting phosphor ceramics with high luminous efficiency (LE) are urgently explored. Based on the idea of spectrum regulation, the Lu 3 -x-y Gd y Al 5 O 12 : x Ce3+ (LuGdAG:Ce) phosphor ceramics were prepared via vacuum solid-state sintering. The effect of Gd3+ and Ce3+ content on the structure, luminescence and thermal properties of LuAG:Ce ceramics were investigated. The distortion ratio (D) of CeO 8 and bandgap were effectively modified via Gd3+ doping, resulting in massive red-shifting of Ce3+ emission (513→561 nm). The LEDs lighting encapsulated by LuGdAG:Ce ceramics changes from green to yellow. Importantly, the yellow LEDs with a LE up to 139.0 lm/W@180 W and a warm correlated color temperature (CCT) of 3620 K were achieved based ceramic Ce07Gd9. The LuGdAG:Ce phosphor ceramic has the best of luminescence performance in phosphor-converted yellow LEDs lighting so far, which is considered to be the highly promising color converter. [ABSTRACT FROM AUTHOR]

High-entropy ceramics have garnered significant attention in recent years owing to their exceptional properties and structural diversity. In this work, single-phase medium/high entropy ceramics, namely (Ca 0.2 Sr 0.4 Ba 0.4)(Zr 0.5 Ti 0.5)O 3 and (Ca 0.2 Sr 0.4 Ba 0.4)(Zr 0.1 Ti 0.9)O 3 , were successfully designed and prepared utilizing Spark Plasma Sintering (SPS). A comprehensive investigation was conducted into the phase structure, microscopic morphology, dielectric properties, and thermal behavior of these ceramics. It was observed that all ceramics maintained a cubic perovskite structure (space group: Pm 3 ‾ m), and the introduction of multi-element doping rendered them more stable across a wide frequency and temperature range. Notably, (Ca 0.2 Sr 0.4 Ba 0.4)(Zr 0.5 Ti 0.5)O 3 exhibited remarkably low dielectric loss (0.0001 at 1 kHz) at room temperature, along with excellent dielectric temperature stability (25–400 °C). By reducing the zirconium concentration in (Ca 0.2 Sr 0.4 Ba 0.4)(Zr 0.1 Ti 0.9)O 3 , a slight decrease in dielectric temperature stability was observed (25–350 °C); however, it demonstrated lower thermal conductivity (0.41 W/(m·K), 1200 °C) and maintained good high-temperature stability. The discovery highlights the promising practicality of both ceramics for high-temperature dielectric applications. [ABSTRACT FROM AUTHOR]

Aluminum nitride (AlN), prized for its high thermal conductivity and electronic insulating properties, finds widespread use in electronic applications, particularly as a substrate material. However, its relatively low fracture toughness limits its application. In this study, to enhance both the thermal and mechanical properties of AlN ceramics, we thoroughly investigate the microstructure, thermal, and mechanical properties of self-reinforced AlN ceramics fabricated by spark plasma sintering, with self-reinforcement achieved through the integration of AlN whiskers within the AlN matrix. Unlike previous studies utilizing conventional pressureless sintering with limited sintering conditions, this work employs spark plasma sintering with a wide range of temperatures (1600–1900 °C) and holding times (10–30 min), providing a comprehensive understanding of the sintering behavior. Microstructural features, observed through optical and scanning electron microscopy, reveal distinct toughening mechanisms via crack deflection and branching, with a maximum 20% enhancement. The self-reinforced AlN ceramics exhibit remarkable improvements in thermal conductivity, reaching up to 150 W m−1 K−1, surpassing reported values for spark plasma-sintered AlN ceramics. Adding AlN whiskers enhances the thermal and mechanical properties of AlN simultaneously, particularly at 1800 °C for 10 min with controlled grain size and nicely integrated AlN whiskers. This work not only contributes valuable insights into the complex relationship between processing parameters, microstructure, and resulting thermal and mechanical properties but also highlights the enhanced thermal and mechanical properties of self-reinforced AlN ceramics. [ABSTRACT FROM AUTHOR]

Addressing the issue of carbon contamination during the smelting of specialty metals or alloys, utilizing graphite crucibles, has attracted considerable research attention, prompting the exploration of novel ceramic crucible materials. AlN ceramic, renowned for their exceptional high-temperature stability and resistance to corrosion, have emerged as promising candidates to mitigate this concern. Nonetheless, the limited mechanical properties and thermal shock resistance of AlN curtail its widespread application. In this study, Y 2 Zr 2 O 7 was introduced as an additive to enhance AlN's properties, and AlN-based composite ceramics were fabricated by employing pressureless sintering. The effects of Y 2 Zr 2 O 7 addition (3–10 wt%) on the mechanical properties and thermal shock resistance of the resulting composites were examined. The findings revealed that the incorporation of 5 wt% Y 2 Zr 2 O 7 (AlN-5YZO) led to the highest relative density and a refined grain structure, resulting in superior mechanical properties. Notably, the flexural strength, fracture toughness, and Vickers hardness of AlN-5YZO reached 322 MPa, 3.70 MPa m1/2, and 13.34 GPa, respectively. Furthermore, the presence of crack branching and crack deflection within the composite ceramics impeded crack propagation, effectively augmenting their thermal shock resistance. AlN-5YZO samples exhibited residual strength retention rates of 91.0 %, 84.2 %, and 76.7 % after 10, 20, and 50 thermal shocks between 1000 and 1600 °C, surpassing those of pure AlN. The findings of this study present promising avenues for advancing crucible materials tailored for high-temperature applications. [ABSTRACT FROM AUTHOR]

Thermal camouflage technology can effectively hide an object by lowering its infrared emissivity and reducing its surface temperature. So far, it has been a challenge to realize thermal camouflage at high-temperatures with a single material. Here, we report a Ti 3 AlC 2 MAX phase material that exhibits excellent thermal camouflage properties from room temperature to 500 °C, and maintains a low emissivity of 0.25 at 500 °C, which is difficult to achieve for most metals due to the rapid increase in emissivity caused by oxidation. The thermal camouflage mechanism of Ti 3 AlC 2 was analyzed on the basis of experimental results and first-principles calculations, providing a feasible approach to select other MAX phases (such as Ti 3 SiC 2 , Cr 2 AlC, and Ti 2 AlC) with attractive thermal camouflage performance. Ti 3 AlC 2 and other MAX phases are promising candidates for thermal camouflage applications due to their low emissivity, high-temperature stability, good oxidation resistance and ease of fabrication. [ABSTRACT FROM AUTHOR]

Exploring new applications of negative thermal expansion (NTE) materials is a recent research hotspot. In this work, the IV A element Sn was used to tailor the thermal expansion and dielectric properties of NTE material ZrMgMo 3 O 12 , and the samples Zr 1–x Sn x MgMo 3 O 12 (x = 0.05, 0.10, 0.15, 0.20, 0.25) can be used in the field of high-frequency dielectric ceramics. Both the substitution amount of Sn and sintering temperature have a certain effect on the properties of Zr 1-x Sn x MgMo 3 O 12. The coefficients of thermal expansion (CTE) can be adjusted between near zero thermal expansion (ZTE) (−0.24 × 10−6/K−1) and NTE (−8.16 × 10−6/K−1) and become larger toward negative as the amount of Sn increased under the same sintering temperature. The dielectric constants of Zr 1-x Sn x MgMo 3 O 12 can be adjusted in the range of 130∼155, which are about 25 times than ZrMgMo 3 O 12. The dissipation factors of Zr 1-x Sn x MgMo 3 O 12 were adjustable between 4.37 × 10−4 and 5.54 × 10−4, meeting the application requirements of high-frequency dielectric ceramics. This research shows that Sn can adjust the thermal expansion properties and significantly improves the dielectric properties of ZrMgMo 3 O 12 , so that Zr 1-x Sn x MgMo 3 O 12 materials have high value in the field of high-frequency dielectric ceramics. [ABSTRACT FROM AUTHOR]

The concurrent enhancement of toughness, electrical conductivity, and thermal stability in polycrystalline diamond composites represents a formidable challenge. Here, a novel diamond-TiC composites (referred to as DTC) with high fracture toughness and conductivity were synthesized through a high-temperature and high-pressure reaction sintering process utilizing two precursors: diamond mixtures containing TiH 2 and Ti-coated diamonds. On the one hand, the inherent bonding and encasing of TiC onto the diamond matrix form a heterogeneous structure, providing high strength and excellent fracture toughness up to 11.6 MPa·m1/2. On the other hand, the established oxygen barrier and current pathway offer a thermal stability of 765 °C and high conductivity up to 837 S·m−1. Remarkably, this rare combination of mechanical, electrical, and thermal properties has been realized within a single material under relatively moderate sintering conditions, thus positioning diamond-TiC composites as a promising ceramic for electrical applications in high-stress environments. [ABSTRACT FROM AUTHOR]

This work investigates the behavior and properties of corundum and mullite ceramics at high temperatures and during very long exposures in a controlled atmosphere. The motivation of the work lies primarily in advanced applications in nuclear energy technology, specifically in the search for materials for helium-cooled reactors of the 4th generation. The studied ceramic samples Al63, Al70, Al76, Al96, Al100, where the number indicates the mass percentage of Al 2 O 3 , were exposed for 1000 h at a temperature of 900 °C in gaseous atmospheres of helium, nitrogen and air. The properties of the exposed and unexposed samples were evaluated by measuring the bending strength at room temperature (CMOR), hot modulus of rupture at high temperature (HMOR), and isothermal creep, BET method, and using electron microscopy. The color changes induced by the reducing atmosphere and temperature were also interpreted using a simple thermochemical model. The CMOR measurement results show that all ceramic samples do not significantly change their properties due to long-term exposure. The detected deviations in the exposed samples from the unexposed ones can be considered random caused by the inherent heterogeneous structure. A similar conclusion also applies in the case of the HMOR measurement results, except for the results for the Al63 sample, where the drop in the strength of the exposed samples by approx. 37 MPa (20 %) may be related with the highest proportion of polyvalent oxide admixtures of all studied ceramics, i.e. 1.01 wt % Fe 2 O 3 and 0.52 wt % TiO 2. The change in color indicates that the iron and titanium present are being reduced. However, none of the conducted experiments indicate that changes in the redox state associated with the formation of oxygen vacancies would significantly reduce strength at high temperatures or increase creep in mullite ceramics. [ABSTRACT FROM AUTHOR]

In the thermal protection system of spacecraft, the bolts connecting the ceramic to the internal superalloy need to have low thermal conductivity and high strength. Two dense high entropy fluorite oxides (Zr 1/7 Hf 1/7 Ce 1/7 Y 2/7 La 2/7)O 2-δ (ZHCYL) and (Zr 1/8 Hf 1/8 Ce 1/8 Y 1/4 La 1/4 Pr 1/8)O 2-δ (ZHCYLP) were designed and synthesized by using the synergistic effect of plasma-assisted ball milling and spark plasma sintering(SPS). Through the synergistic effect of lattice distortion and oxygen vacancy guided by entropy regulation, ZHCYLP synthesized in this study has lower thermal conductivity(1.13 W·m−1·K−1), higher high temperature strength(192 MPa at 1000 °C) and high temperature phase stability up to 1600 °C than 8YSZ ceramics. The thermo-mechanical coupling finite element analysis results of high temperature bending test show that the variation trend of the maximum stress value of the sample is consistent with the experimental results. This shows that the mechanical and thermal properties of high entropy oxides can predict the variation trend of the maximum stress value in high temperature bending tests. It opens up a new way for designing and synthesizing high entropy oxide materials with low thermal conductivity and high strength which can be applied in the field of heat protection and load bearing. [ABSTRACT FROM AUTHOR]

Ceramic aerogels are promising candidates for high-temperature thermal resistance and thermal insulation materials. However, their application can be restricted by their brittleness when exposed to harsh conditions. Herein, this study has developed a novel synthesis process based on a sol-gel method and carbothermal reduction-nitridation to produce a porous TiN composite aerogel from an organic/inorganic hybrid. The resulting TiN displays a polyhedral particle size of around 30–60 nm with nanoscale pores. In addition, the TiN aerogel demonstrates a high BET-specific surface area of 653.42 m2/g and a very low thermal conductivity of 0.046 W/(m·K). Furthermore, the TiN aerogel composite displays a good thermal difference with no shrinkage and cracks of the morphology during the butane blazing torch at 1300 °C for 10 min under air environment, demonstrating its excellent thermal insulation property and anti-oxidation characteristics. The gas-solid reaction mechanism of TiN aerogel based on the Gibbs free energy calculations is also proposed. [ABSTRACT FROM AUTHOR]

Ceramic fibers are an important thermal insulation material that are not only widely used in extreme conditions, but also play an important role in energy conservation and energy efficiency for sustainable development. However, the practical application of conventional ceramic fibers has a high thermal conductivity in high-temperature environments, which hinders their widespread application. Here, a novel lamellar structured porous SiTiOC/C composite ceramic materials was designed and prepared with excellent thermal insulating properties. The unique microstructure endowed the porous SiTiOC/C composite ceramic materials with a high IR refractive index (93.81%) and an ultra-low thermal conductivity (0.0562 W·m−1 K−1 at 600 ℃). In addition, the porous SiTiOC/C composite ceramic materials not only exhibited excellent mechanical properties (4.46 MPa at 800 ℃), but also demonstrated impressive oxidation resistance and thermal stability. In summary, the proposed porous SiTiOC/C composite ceramic materials provide a reference for the development of high-temperature insulation with good mechanical properties. [ABSTRACT FROM AUTHOR]

(KMg)3+ co-doped Sc 2 W 3 O 12 ceramics have been prepared via co-precipitation method. Effects of (KMg)3+ co-doping amount and sintering temperature on the phase constitution, microstructure, morphology, and negative thermal expansion (NTE) performance of K x Mg x Sc 2- x W 3 O 12 (0 ≤ x ≤ 1.25) ceramics were studied. Results indicate that: Sc3+ cations can be substituted by (KMg)3+ dual-cations and a composition-induced structural phase transition was observed in K x Mg x Sc 2- x W 3 O 12. For x ≤ 0.25, orthorhombic Sc 2 W 3 O 12 gradually changed into hexagonal K x Mg x Sc 2- x W 3 O 12 and coexisted. Single phase K x Mg x Sc 2- x W 3 O 12 with hexagonal symmetry can be prepared for 0.25 < x ≤ 1. When x ≥ 1.25, (KMg)3+ substitution reaches its solid solution limit in Sc 2 W 3 O 12 , and impurity MgWO 4 formed in the samples. As co-doping amount x increased, the NTE performance of the K x Mg x Sc 2- x W 3 O 12 (0 ≤ x ≤ 1) ceramics gradually enhanced. The coefficient of thermal expansion (CTE) of K x Mg x Sc 2- x W 3 O 12 (0 ≤ x ≤ 1) ceramics enhanced from −2.14 × 10−6 °C−1 to −19.68 × 10−6 °C−1 in 30–700 °C. With the increase of sintering temperature from 800 to 1100 °C, the grains grew up and the density of the K 0.75 Mg 0.75 Sc 1.25 W 3 O 12 ceramics increased as well, and the NTE performance was also improved. The linear CTE of K 0.75 Mg 0.75 Sc 1.25 W 3 O 12 ceramics enhances from −2.15 × 10−6 °C−1 to −14.70 × 10−6 °C−1 in 30–700 °C. [ABSTRACT FROM AUTHOR]

Lightweight phenolic matrix composites are highly potential in ablative thermal protective materials for future aerospace vehicles, and hybrid modification is considered as one of effective ways to improve the oxidation and ablation resistance of phenolic matrix. Herein, the co-continuous silica zirconium hybrid phenolic resin (SZRx) was synthesized, which can be used to prepare lightweight ablation resistant aerogel composites by the sol-gel method. The SZRx aerogel showed stable porous structure and excellent hydrophobicity, and the silicon zirconium hybrid greatly improved the high temperature carbon residue and oxidation resistance of phenolic resin. The SZRx aerogel composites also possessed excellent integrated characteristics of heat protection and insulation, with a linear ablation rate as low as 0.032 mm/s and a back temperature below 200 °C. The synergistic effect of silicon and zirconium formed the multiphase ceramic layer (C, SiO 2 , SiC and ZrO 2) with the sea-island-like structure on the surface of the composite material, which can effectively resist high-temperature ablation and aerodynamic exfoliation. This can indicate that silicon zirconium dual element hybrid phenolic resin is the highly competitive matrix for lightweight and ablation resistant composite materials. [Display omitted] [ABSTRACT FROM AUTHOR]

In this study, a highly dense GdB 6 bulk ceramic material was fabricated using one-step in-situ reaction spark plasma sintering technology. The sample with a relative density of 96.7 % and a purity of 96.9 wt% was successfully obtained by sintering at 1800 °C for 30 min under a uniaxial pressure of 50 MPa. The Vickers hardness, elastic modulus and fracture toughness of the as-obtained GdB 6 bulk ceramics were 18.9 GPa, 209 GPa and 1.6 MPa·m1/2, respectively. The thermal conductivity of GdB 6 at room temperature was 28.68 W·m−1·K−1, 70 % of which was mainly attributed to phonon vibration, while the remaining 30 % to the electrical thermal conductivity. In addition, the as-obtained GdB 6 ceramics showed no phase transformation after heat treatment at a relatively high temperature of 2100 °C for 20 min in Ar atmosphere. The highly covalent octahedral boron framework played a critical role in maintaining the phase stability of the GdB 6 crystal lattice. This suggested that GdB 6 ceramics could be used as potential ultra-high temperature ceramics for aerospace applications and high-power vacuum electronic devices operated at high temperatures. [ABSTRACT FROM AUTHOR]

Rare earth compounds (RE 2 O 3), typically Eu 2 O 3 and Gd 2 O 3 , are considered as absorbing materials due to their long chain neutron absorbing ability and high efficiency of neutron absorption. In this paper, a specifically designed x Eu 2 O 3 -(1-x)Gd 2 Zr 2 O 7 (x = 0.6, 0.7, 0.8, 0.85) composite ceramics with excellent thermal properties were synthesized through direct thermal decomposition reactions followed a high-temperature sintering method under vacuum conditions. X-ray diffraction (XRD) and Raman spectroscopy analysis indicated that the obtained ceramics consisted of monoclinic Eu 2 O 3 and fluorite Gd 2 Zr 2 O 7 phases. The hardness of x Eu 2 O 3 -(1-x)Gd 2 Zr 2 O 7 ceramics (x = 0.8, 0.85) have no significantly changes in the test temperature range (25–350 °C). The thermal expansion coefficients (TECs) (7.3–10 ×10-6 K-1) are lower than Dy 2 TiO 5 (9.3–10.4 ×10-6 K-1), and the thermal expansion rate changes linearly with the increase of temperature, which indicates that the x Eu 2 O 3 -(1-x)Gd 2 Zr 2 O 7 ceramics exhibit excellent high temperature phase stability. Furthermore, the range of thermal conductivities is from 0.96 W·m-1·K-1 to 2.02 W·m-1·K-1 (25–800 °C), which is higher than Dy 2 TiO 5 (0.27–0.55 W/m·K, 220–650 °C). Compared with the state-of-art Dy 2 TiO 5 ceramics, x Eu 2 O 3 -(1-x)Gd 2 Zr 2 O 7 have superior thermal properties and are therefore expected to be the next generational of neutron absorbent materials used in ash rod. [ABSTRACT FROM AUTHOR]

This study utilizes modulation of ionic disorder and electronegativity differences for targeted component design of high-entropy ceramic compositions. A series of novel multicomponent ceramics with the general formula (LaGdYSm) x 2 Yb x 1 Zr 2 O 7 (x 1 +4x 2 = 2, x 1 = 0.6,0.4,0.2,0) were prepared by solid-state reaction. The evolution patterns of their microstructures were analyzed using XRD and TEM, and the anti-sintering ability and thermophysical properties were evaluated. The results confirm that the multicomponent ceramics gradually transform from the coexistence of pyrochlore/fluorite dual-phase structure to pyrochlore structure with the tuning of the size disorder degree. After 50h of exposure to air at 1500 °C, the ceramics retained excellent phase stability. Segregation of La and Yb elements with large differences in radius size occurs, forming a mixture of the La-rich pyrochlore and the Yb-rich fluorite phases. The specimen with the maximum size disorder exhibits the lowest grain growth rate and the greatest thermal insulation properties. Large lattice distortions and sluggish diffusion effects are responsible for the mutual inhibition of grain growth in the two-phase coexistence zone. The thermal insulation properties of the ceramics show well correlated with the degree of the size disorder, further validating the effectiveness of the component design. Meanwhile, the thermal expansion coefficients of prepared ceramic can reach 11.49 × ∼11.58 × 10−6 K−1 at 1000–1100 °C. The customization principles used in this work fill a gap in the compositional design methodology for multicomponent lanthanum zirconate-based high-entropy ceramics. It is essential for developing rare-earth zirconates with tunable thermophysical properties in the area of thermal barrier coatings. [ABSTRACT FROM AUTHOR]

High-entropy carbide ceramic materials exhibited excellent thermal and mechanical properties, making them highly sought after in high-temperature applications. However, the oxidation resistance of high-entropy carbide ceramic needed to be further improved. This work unraveled the oxidation behavior and mechanism of high-entropy carbide ceramic by introducing the Cr 3 C 2. The results indicated that the oxidation rate of (TiZrTaNbCr)C initially decreased with temperature up to 900 °C, followed by an increased with further temperature rise up to 1100 °C. At 800 and 900 °C, the parabolic oxidation rate constants were 0.70 and 0.17 mg2cm−4min−1, respectively. And the minimum thickness of oxidized layer was 60 µm at 900 °C for 120 min. This unusual phenomenon suggested the formation of different oxidation products. Specifically, the CrNbO 4 and Nb 2 Zr 6 O 17 oxide layer were formed at 900 °C, leading to an increased resistance to oxygen diffusion. Subsequently, loose oxidation products of Nb 2 O 5 were formed after 1000 °C, hindering the oxidation resistance. In the current study on oxidation resistance of high entropy carbides, this work showed a competitive performance. Overall, this study illustrated the oxidation mechanism and behavior of (TiZrTaNbCr)C and proposed a new avenue for the design of high-entropy ceramic components. [ABSTRACT FROM AUTHOR]

Al 2 O 3 /B 2 O 3 powder mixtures prepared at various ratios from 10.7 to 54.1 wt% B 2 O 3 were used to synthesize Al 18 B 4 O 33 powders by solid state calcination at 1300 °C for 1 h. Al 18 B 4 O 33 formation was completed at 44 wt% B 2 O 3 instead of stoichiometric ratio of 13.17 wt% B 2 O 3. In other words, B 2 O 3 -rich liquid phase accelerated Al 18 B 4 O 33 crystallization. Al 18 B 4 O 33 particles were not acicular in shape when first formed, but they were fully acicular for the 44 wt% and the 54.1 wt% B 2 O 3 mixtures. Anorthite-based glass and CaO were selected to induce liquid phase sintering. CaO considerably improved densification to 95.4 % relative density at 1350 °C. Both glass and mullite also enhanced densification to 94.8 %. Epitaxial nucleation of mullite on Al 18 B 4 O 33 particles resulted in a solid solution as well. Dielectric, mechanical and thermal properties of the samples were investigated and evaluated for possible applications. [ABSTRACT FROM AUTHOR]

The mechanical and thermal properties of ZrC x are strongly dependent on the composition and microstructure. In the present study, densified ZrC x (x = 0.5, 0.7 and 1.0) with relative density in the range of 99.2–99.7% have been prepared by a combination of spark plasma sintering (SPS) and vacuum arc melting (VAM). Both the Young's modulus and Vickers hardness monotonically increase with increasing C/Zr ratio. The maximum Young's modulus and Vickers hardness values of 488.1 ± 13.4 GPa and 28.8 ± 1.7 GPa, respectively, for dense ZrC have been obtained. With increasing the C/Zr ratio, the thermal conductivity of ZrC x increases. The thermal conductivity ZrC ranged from 25.17 W/m/K to 43.85 W/m/K from ambient to 1200 °C. Owing to the higher density of ZrC x , the present thermal conductivities and Young's modulus of ZrC x are higher than those of the previous studies. The present results are beneficial to design and preparation of ZrC x ceramics. [ABSTRACT FROM AUTHOR]

A novel NbSi 2 /Nb 2 O 5 -SiO 2 /MoSi 2 multilayer thermal protection ceramic coating is designed and fabricated via halide-activated pack cementation and liquid-plasma-assisted particle deposition and sintering technology, endowing the coating with multiple high-temperature protective properties. The incorporation of MoSi 2 nanoparticles not only gives superior high-temperature oxidation resistance/hot corrosion resistance of coating by forming a dense SiO 2 barrier layer, but also promotes passive radiative heat dissipation. When NbSi 2 /Nb 2 O 5 -SiO 2 /MoSi 2 coating was prolonged exposure to air at 1250 °C for 50 h of oxidation and at 900 °C for 100 h of corrosion, the mass gains are only 0.37 mg/cm2 and − 0.52 mg/cm2, respectively. The multilayer coating exhibits enhanced emissivity (>0.88) over the thermal infrared range of 3–20 µm, due to the lattice vibrational absorption-matching synergy of Nb 2 O 5 , SiO 2 , and MoSi 2 , as well as the mutual doping of SiO 2 /Nb 2 O 5 , mismatch of atoms at the interface, and a high degree of lattice distortion within the coating. [ABSTRACT FROM AUTHOR]

Polycrystalline samples of (1-x)K 0.5 Bi 0.5 TiO 3 - xBaTiO 3 [(1-x)KBT - xBT] were synthesized using a solid-state reaction pathway. X-ray diffraction analysis confirmed the presence of a single-phase perovskite structure. To explore relaxation and conduction mechanisms, complex impedance spectroscopy was employed. Reduction in Curie temperature was observed as BT content increased. The grain and grain boundary contributions to relaxation was examined through complex impedance and modulus plots and quantified via fitting experimental data to an equivalent circuit model. Examination of the Complex impedance spectra uncovered the existence of dielectric relaxation characteristic of a non-Debye nature. Furthermore, the activation energy determined suggests commonalities in governing the conduction and relaxation processes in relation to temperature-dependent conductivity and relaxation time. A negative temperature coefficient of resistance behaviour was obtained from the temperature-dependent conductive study. Dielectric spectra revealed that these ceramic capacitors are useful in reduction of signal interference, signal attenuation and impedance matching circuits applications. [ABSTRACT FROM AUTHOR]

Mullite fiber-based porous ceramics is one of the most commonly used high-temperature insulation materials. However, how to further reduce the thermal conductivity and improve the strength of such materials has been a challenge in the field of high-temperature insulation. In this paper, mullite micro/nano fiber-based porous ceramic was prepared by introducing mullite nanofibers into mullite microfiber-based porous ceramics and the effect of microfiber/nanofiber weight ratio on the samples properties were characterized and analyzed. Results showed that the compressive strength and high-temperature thermal insulation properties of the porous ceramics increased significantly with an increase in the nanofiber content. For the porous ceramics with similar density (about 0.50 g/cm3), the compressive strength of the sample with a microfibers/nanofibers weight ratio of 1:2 was 1.43 MPa, which was much higher than that of the porous ceramics prepared with only microfibers (0.26 MPa). Meanwhile, the backside thermal equilibrium temperature of the sample with a microfiber/nanofiber weight ratio of 1:2 at 900 °C environment was 355.8 °C, which was much lower than that of the porous ceramic prepared with only microfibers (476.5 °C). In addition, in order to investigate the temperature resistance of mullite micro/nano fiber-based porous ceramics, the sintering temperatures was increased from 1400 °C to 1500 °C. Results shows that the high-temperature thermal insulation performance of mullite micro/nano fiber-based porous ceramics with high mullite nanofiber content decays more seriously. The back-temperature test showed that the thermal equilibrium temperature of the samples with a mullite micron/nanofiber weight ratio of 1:1 in 900 °C environment increased rapidly from 386.3 °C to 454.2 °C when the sintering temperature was increased from 1400 °C to 1500 °C. The preparation of mullite micro/nanofiber-based porous ceramics provides a new strategy to improve the performance of fiber-based porous ceramics. [ABSTRACT FROM AUTHOR]

Ni-containing SiOC bulk ceramics have been prepared by spark plasma sintering at 1300 °C from polysiloxane at Ar atmosphere in the present work. The microstructure and properties of SiOC ceramics with different Ni content were studied. The resultant Ni-containing SiOC ceramics consists of in situ formed turbostractic layer carbon, CNTs (C nanotubes) and SiC crystals which dispersed in the SiOC matrix. With increasing content of Ni, the Ni-containing SiOC ceramics displayed less porosity. And the increasing Ni improved the mechanical, thermal and friction properties of SiOC ceramics. Ni-containing SiOC ceramics developed a carbon friction layer, which enhanced abrasion resistance to provide friction materials with stable friction coefficients and low abrasion values. A decrease in wear mass, from 2.06 to 0.18 mg was observed as the Ni content increasing from 0 to 2 wt%. The primary wear mechanisms of SiOC ceramics were recognized as abrasive wear, fatigue wear, and adhesion wear. [ABSTRACT FROM AUTHOR]

Entropy plays a crucial role in designing new functional materials or enhancing material performance. The design of high entropy ceramics (HECs) introduces a larger composition space, thus the understanding of the correlation between the composition, entropy effect, and the performance of HECs is becoming increasingly important. In this work, to pursue superior properties, a series of CeNbO 4 -based solid solution ceramics with a maximum of 9 species cations in a single sublattice were synthesized by using high entropy configuration strategy. The interaction of composition, size disorder, and configurational entropy on the properties of HECs was emphasized. The potential conflict between high resistivity and low material constant of thermosensitive ceramics was overcome and thus achieving excellent thermal sensitivity properties having an extremely wide temperature range from room temperature to 1623 K and long-term high-temperature stability. This will bring innovative prospects for the design and application of high-temperature functional ceramics. [ABSTRACT FROM AUTHOR]

Mullite fiber-based porous ceramics is one of the most commonly used high-temperature insulation materials. However, how to further reduce the thermal conductivity and improve the strength of such materials has been a challenge in the field of high-temperature insulation. In this paper, mullite micro/nano fiber-based porous ceramic was prepared by introducing mullite nanofibers into mullite microfiber-based porous ceramics and the effect of microfiber/nanofiber weight ratio on the samples properties were characterized and analyzed. Results showed that the compressive strength and high-temperature thermal insulation properties of the porous ceramics increased significantly with an increase in the nanofiber content. For the porous ceramics with similar density (about 0.50 g/cm3), the compressive strength of the sample with a microfibers/nanofibers weight ratio of 1:2 was 1.43 MPa, which was much higher than that of the porous ceramics prepared with only microfibers (0.26 MPa). Meanwhile, the backside thermal equilibrium temperature of the sample with a microfiber/nanofiber weight ratio of 1:2 at 900 °C environment was 355.8 °C, which was much lower than that of the porous ceramic prepared with only microfibers (476.5 °C). In addition, in order to investigate the temperature resistance of mullite micro/nano fiber-based porous ceramics, the sintering temperatures was increased from 1400 °C to 1500 °C. Results shows that the high-temperature thermal insulation performance of mullite micro/nano fiber-based porous ceramics with high mullite nanofiber content decays more seriously. The back-temperature test showed that the thermal equilibrium temperature of the samples with a mullite micron/nanofiber weight ratio of 1:1 in 900 °C environment increased rapidly from 386.3 °C to 454.2 °C when the sintering temperature was increased from 1400 °C to 1500 °C. The preparation of mullite micro/nanofiber-based porous ceramics provides a new strategy to improve the performance of fiber-based porous ceramics. [ABSTRACT FROM AUTHOR]

Ni-containing SiOC bulk ceramics have been prepared by spark plasma sintering at 1300 °C from polysiloxane at Ar atmosphere in the present work. The microstructure and properties of SiOC ceramics with different Ni content were studied. The resultant Ni-containing SiOC ceramics consists of in situ formed turbostractic layer carbon, CNTs (C nanotubes) and SiC crystals which dispersed in the SiOC matrix. With increasing content of Ni, the Ni-containing SiOC ceramics displayed less porosity. And the increasing Ni improved the mechanical, thermal and friction properties of SiOC ceramics. Ni-containing SiOC ceramics developed a carbon friction layer, which enhanced abrasion resistance to provide friction materials with stable friction coefficients and low abrasion values. A decrease in wear mass, from 2.06 to 0.18 mg was observed as the Ni content increasing from 0 to 2 wt%. The primary wear mechanisms of SiOC ceramics were recognized as abrasive wear, fatigue wear, and adhesion wear. [ABSTRACT FROM AUTHOR]

Novel high-entropy (TiTaNbZrMo X)(CN) (x = 0, 5, 10, 15, and 20 at%) carbonitride ceramics were synthesised using the carbothermal reduction-nitridation and spark plasma sintering methods. The effects of Mo doping on the microstructure, mechanical properties, and thermal characteristics of these high-entropy ceramics were investigated. The increase in Mo contents caused increased grain size, uniform distribution of elements, improved Vickers hardness and fracture toughness, and reduced thermal conductivity at the same temperature. High-entropy (TiTaNbZrMo 0.2)(CN) ceramic displayed superior Vickers hardness of 21.41 GPa and fracture toughness of 4.34 MPa·m1/2, compared with 20.51 GPa and 3.94 MPa·m1/2 for (TiTaNbZr)(CN) ceramic, respectively. Density functional theory calculations indicated that adding Mo atoms promoted the hybridisation of metal and carbon elements, thereby preferentially enhancing electron filling in the bonding orbital due to high valence electrons. This, in turn, improved the mechanical properties of (TiTaNbZrMo x)(CN) ceramics. Additionally, the increased Mo contents strengthened covalent bonding and induced lattice distortion, reducing the thermal conductivity of high-entropy ceramics. [ABSTRACT FROM AUTHOR]

In this study, according to the Dinger model, aqueous Si 3 N 4 slurries with a solid loading of 63 vol% and a viscosity lower than 1.0 Pa s were successfully prepared using two-grade Si 3 N 4 powders with D 50 = 7.2 μm and 9.4 μm as starting materials. These resulting slurries exhibited good rheological properties and suspension stability. Notably, the presence of β-Si 3 N 4 seeds existed in the starting materials effectively reduced the nucleation barrier by transforming homogeneous nucleation into heterogeneous nucleation. Consequently, it facilitated the reconstructive phase transformation of α-Si 3 N 4 to β-Si 3 N 4 , promoted the anisotropic growth of β-Si 3 N 4 nucleation, and resulted in the final formation of the bimodal microstructure. This unique microstructure significantly enhanced the mechanical properties of Si 3 N 4 ceramics, resulting in a high flexural strength of 1011.4 MPa and a fracture toughness of 14.8 MPa m1/2. These excellent properties were achieved through the combination of gelcasting and gas pressure sintering. Simultaneously, the Si 3 N 4 ceramics exhibited a low thermal conductivity of 47.7 W m−1 K−1, mainly owing to the low density of 95.3 %, the presence of low-thermal-conductivity silicate-based noncrystalline substances, and the possible existence of lattice oxygen in Si 3 N 4 crystals. [ABSTRACT FROM AUTHOR]

Lightweight ablative materials owing to their low density, high efficiency heat insulation and excellent designability, which are considered as the most promising candidate materials in the field of aerospace ablative thermal protection. In this work, a polycarbosilane (PCS) in-situ reinforced carbon felt/phenolic (PR/C f) aerogel composite is reported. The surface of aerogel and carbon fiber was coated with PCS protective layer by sol gel method and secondary vacuum impregnation process. The aerogel composite material possesses low density (0.264–0.307 g/cm3), hydrophobic, low thermal conductivity (0.121–0.178 W/(m·K)) and significant high compressive strength (12.89 MPa). When the oxygen acetylene flame with high heat flow density ablates for 20 s, it shows high efficiency in heat protection and insulation, and the linear ablation rate is as low as 0.089 mm/s. The PL/PR/C f aerogel composite shows competitive and broad application prospects in the field of ablation heat protection in the future. [ABSTRACT FROM AUTHOR]

To investigate the mechanism of the influence of the sintering additive ratio on the microstructure evolution of silicon nitride (Si 3 N 4) ceramics, Si 3 N 4 ceramics were prepared by gas pressure sintering using different ratios of Y 2 O 3 /MgSiN 2 as additives. Varying the ratio of Y 2 O 3 /MgSiN 2 changed the composition of the liquid phase, thereby affecting the densification process and phase transformation rate of Si 3 N 4 ceramics, and ultimately changing their microstructure. The reduction in the Y 2 O 3 /MgSiN 2 ratio raised the N/O and Si/O ratios in the system, which increased the liquid phase viscosity. The Si 3 N 4 grain distribution varied from "normal to bimodal". In the case of increasing the proportion of MgSiN 2 and prolonging the sintering time, more of the glass phase evaporated, which reduced the content of the low thermal conductivity phase and increased the continuity of Si 3 N 4 /Si 3 N 4. Therefore, Si 3 N 4 ceramics with 1 wt% Y 2 O 3 and 5 wt% MgSiN 2 exhibited excellent properties after sintering at 1900 °C for 12 h, with thermal conductivity, bending strength, and fracture toughness of 106.7 Wm−1K−1, 776 MPa, and 11.66 MPa m1/2, respectively. [ABSTRACT FROM AUTHOR]

In recent years, the MgO-Nd 2 Zr 2 O 7 composite ceramics inert matrix (IM) was proposed as a candidate for the transmutation of Pu and minor actinides (MA) in light water reactors (LWR) or accelerator driven sub-critical system (ADS). To take full advantage of the pyrochlore structure of Nd 2 Zr 2 O 7 to accommodate different types of MA and Pu, in this work, Y and Ce co-doped ω MgO-(1- ω)(Nd 1- x Y x) 2 (Zr 1- x Ce x) 2 O 7 (M-NYZC) composite ceramics used as a candidate IM for inert matrix fuel were prepared by solid-state one-step sintering method at 1500 °C for 3 h. The phase structure and microstructure of M-NYZC composite ceramics were characterized by XRD and SEM-EDS. Also, the thermal physical properties of M-NYZC composite ceramics including the thermal expansion coefficient and thermal conductivity were investigated systematically. Results from XRD and SEM-EDS showed that the magnesium oxide and NYZC pyrochlore solid solution are intermixed well with each other, and the M-NYZC samples present uniform element distribution with a grain size of about 1 μm. Also, the as-prepared samples possessed well densified microstructure, and the average relative density of all samples could exceed 95 %. Moreover, the thermal expansion coefficient and thermal conductivity of 0.5M-0.5NYZC (x = 0, 0.15, 0.2, 0.5, 0.9) samples were located in the range of 13.4 × 10-6–14.4 × 10-6 K-1 and 16.34–3.70 W·m-1·K-1 respectively. By comparison, the thermal physical properties of 0.5M-0.5NYZC samples are superior to that of traditional UO 2 and MOX fuels. It is suggested that the M-NYZC composite ceramics prepared in this study can meet the thermal physical performances of inert matrix fuel. [ABSTRACT FROM AUTHOR]

High-performance ceramics with low thermal conductivity, high mechanical properties, and idea thermal expansion coefficients have important applications in fields such as turbine blades and automotive engines. Currently, the thermal conductivity of ceramics has been significantly reduced by local doping/substitution or further high-entropy reconfiguration of the composition, but the mechanical properties, especially the fracture toughness, are insufficient and still need to be improved. In this work, based on the high-entropy titanate pyrochlore, TiO 2 was introduced for composite toughening and the high-entropy (Ho 0.2 Y 0.2 Dy 0.2 Gd 0.2 Eu 0.2) 2 Ti 2 O 7 -xTiO 2 (x = 0, 0.2, 0.4, 1.0 and 2.0) composites with high hardness (16.17 GPa), Young's modulus (289.3 GPa) and fracture toughness (3.612 MPa·m0.5), low thermal conductivity (1.22 W·m−1·K−1), and thermal expansion coefficients close to the substrate material (9.5 ×10−6/K) were successfully prepared by the solidification method. The fracture toughness of the composite toughened sample is 2.25 times higher than that before toughening, which exceeds most of the current low-thermal conductivity ceramics. • Preparation of high-entropy pyrochlore/TiO 2 composites by rapid melt solidification. • The composite toughened samples have ultrahigh fracture toughness (3.612 MPa·m0.5). • The solidified composites exhibit excellent mechanical and thermal properties. [ABSTRACT FROM AUTHOR]

The porous SiC-Mullite porous ceramics with different pore size were prepared by SiC particles, kaolin, Al(OH) 3 , and flake graphite, V 2 O 5 and AlF 3 were used as mineralizers, the pore size was controllable by adjusting the size of flake graphite. Then the improved empirical formula and grey theory were used to study the effect of the change in pore size on the material properties. The results showed that with the increase of mean pore size from 1.1 μm to 8.5 μm, the cold modulus of rupture and cold crushing strength decreased by 20.8 MPa and 13.7 MPa, respectively. And the thermal conductivity increased from 1.213 W⋅m−1⋅K−1 to 1.721 W⋅m−1⋅K−1 at 800 °C. The <5 μm pores were helped enhance the strength and decreased the thermal conductivity. [ABSTRACT FROM AUTHOR]

Reaction-bonded SiC is a ceramic with excellent thermal properties, good corrosion resistance and the characteristic of near-net-shape manufacturing. However, the poor fracture toughness of free Si limits the applications of reaction-bonded SiC. In this study, TiC was added to reaction-bonded SiC and reacted with free Si to form Ti 3 SiC 2. The effects of TiC and carbon black on the mechanical properties of reaction-bonded SiC were investigated. The results demonstrated that the in-situ formation of Ti 3 SiC 2 and decrease in the content and size of free Si improved the mechanical properties of reaction-bonded SiC ceramics. The mechanical properties of TiC-added reaction-bonded SiC with 17.5 wt% carbon black were superior to those of TiC-added reaction-bonded SiC with 15 wt% carbon black. Moreover, increasing the TiC content of reaction-bonded SiC with 17.5 wt% carbon black from 0 to 7.5 wt% caused an increase in its bending strength from 183.92 to 424.43 MPa and an increase in fracture toughness from 3.7 to 5.24 MPa m1/2. [ABSTRACT FROM AUTHOR]

In Part 1 of this study, we investigated the macrokinetic parameters and phase formation mechanism in the combustion front of Zr–Nb–B mixtures. In the second part, we produced consolidated samples of solid solutions NbB 2 -(0.100%)ZrB 2 by hot pressing the combustion-derived powders at 1900 °C. By measuring the crystallographic parameters, mechanical and thermophysical properties of the produced bulk samples, we obtained valuable insights into the behavior of the solid solutions. Our results pave the way for the application-specific fine-tuning of the mechanical properties and thermal conductivity of diboride solid solutions in the Zr–Nb–B system for ultra-high temperature applications. Our findings have significant implications for the development of advanced materials with outstanding performance in extreme environments. [ABSTRACT FROM AUTHOR]

Anisotropic layered porous ceramics are crucial to satisfy the demand for devices with directional functions. However, challenges, such as complicated preparation processes and difficulties in regulating the oriented structure, severely limit their application. Here, multilayered mullite ceramics (MLMCs) with specific porosities and strongly anisotropy properties, were prepared by designing porous thin-layered units and an interlayer layout, in combination with a simple gel-casting. Benefiting from the suitable slurry properties, the samples did not show obvious defects, and a perfect bonding was observed between the layers. The optimized MLMCs exhibited a porosity of 65.12%, the differences in compressive and flexural strengths of 14 (± 0.7) and 5 (± 0.2) MPa in different pressure directions respectively, and the anisotropy factor of thermal conductivity up to 0.98, as well as exhibited good high temperature thermal insulation properties. Ultimately, the MLMCs formed transverse heat conductor and longitudinal heat insulation heat-transfer patterns, with promising applications in thermal insulation. [ABSTRACT FROM AUTHOR]

In this work, (20- x)MgO–20Al 2 O 3 –56SiO 2 –4B 2 O 3 - x CuO (x = 0, 0.25, 0.5, 0.75, 1, 1.25 mol%) glass-ceramics were synthesized by solid-state reaction method. The crystallization, microstructure, thermal and dielectric properties of (20- x)MgO–20Al 2 O 3 –56SiO 2 –4B 2 O 3 - x CuO glass-ceramics was discussed in detail. It was demonstrated that the CuO lowers the crystallization temperature of α-cordierite and promotes the crystallization process of MgO–Al 2 O 3 –SiO–B 2 O 3 glass-ceramics. Thus, the crystallization showed a substantial influence on the dielectric properties, as evidenced by an elevation in dielectric constant and a decrease in dielectric loss. Specifically, with the addition of 0.5 mol% CuO, the MgO–Al 2 O 3 –SiO–B 2 O 3 glass-ceramics sintered at 1050 °C shows excellent properties of: ε r = 5.04, tan δ = 2.2 × 10-4, κ = 3.4 W/mK and α = 1.75 × 10-6/°C. These works provide valuable insights into the design and development of (20- x)MgO–20Al 2 O 3 –56SiO 2 –4B 2 O 3 - x CuO glass-ceramics with tailored properties for structure/function integration in the electronics industry. [ABSTRACT FROM AUTHOR]

Herein, Nd 2 O 3 -doped 0.11PIN-0.89PHT (PIN-PHT) single-phase tetragonal piezoelectric ceramics are prepared by traditional solid-phase method. In addition, impacts of Nd-doping on crystal structure and electrical performance for 0.11PIN-0.89PHT ceramics are systematically investigated. Based on Landau theory, we propose a novel strategy for obtaining high-performance ceramics by combining tetragonal phase and relaxor ferroelectrics. Results reveal that the introduction of polar nano-regions in tetragonal phase ceramics by doping with rare-earth ions to convert normal ferroelectrics into relaxed ferroelectrics is responsible for excellent properties of 0.11PIN-0.89PHT- x Nd ceramics. The optimized comprehensive performance is obtained at x = 0.9 mol%, where d 33 = 670 pC/N, S max = 0.29% (45 kV/cm), strain hysteresis = 8.68% (45 kV/cm), d 33 * = 736 p.m./V (30 kV/cm), T C = 312.6 °C, ε r = 3234, k p = 0.62, tan δ = 0.014, and excellent high-temperature stability in temperature range of 20–240 °C. After 106 cycles, electrical properties and strain remain unchanged, showing excellent anti-fatigue behavior. This work provides a novel approach for the development of ceramics with outstanding piezoelectric response, high strain, low strain hysteresis, excellent anti-fatigue resistance and thermal stability, and is expected to realize practical applications of piezoelectric ceramics. [ABSTRACT FROM AUTHOR]

In this work, the cold sintering assisted process was utilized to fabricate dense 0–3 type (1- x)BaTiO 3 - x CaTiO 3 :Pr3+ ((1- x)BT- x CT:Pr3+, x = 0.1, 0.2 and 0.3) binary composite ceramics. Under the combined action of uniaxial pressure and temperature, CT:Pr3+ has been successfully integrated with BT to form the preliminary BT-CT:Pr3+ composites during cold sintering. It is found that the cold sintering could increase the grain size a little, and annealing at 900 °C significantly promotes the grain size. The prepared (1- x)BT- x CT:Pr3+ composite ceramics have a pure phase of CT:Pr3+, which is difficult to prepare using high temperature solid reaction method when x < 0.23. It is found that all the composite ceramics exhibit excellent ferroelectric properties. Furthermore, a strong photoluminescence, photo-stimulated luminescence and thermal luminescence properties have been obtained. Present study illustrates a potential approach to combine luminescent and piezoelectric properties into the ferroelectric-based composite ceramics by the cold sintering assisted sintering. [ABSTRACT FROM AUTHOR]

The fabrication of high-entropy ceramics has recently expanded the pool of ultra-high temperature ceramics (UHTCs). To properly assess the suitability of these new types of ceramics for advanced aerospace applications, it is of vital interest to extend the characterizations beyond ambient conditions. Here, we have studied the thermal and ablation properties of a high-entropy diboride (HEB): (Hf 0.2 Zr 0.2 Ti 0.2 Ta 0.2 Nb 0.2)B 2. The thermal conductivity of the HEB increases as a function of temperature and becomes comparable to that of other UHTCs at high temperatures. The electron dominated thermal conductivity of HEB is also nearly isotropic along different crystallographic orientations. The temperature-dependent volumetric heat capacity of HEB is measured and found to remain in agreement with that of ZrB 2. Additionally, both material systems possess nearly the same ablation resistance. The multitudes of characterizations performed in this study establishes the suitability of HEB for high thermal load applications in extreme environments. [ABSTRACT FROM AUTHOR]

The effects of B 4 C content on the specific stiffness and mechanical and thermal properties of pressureless-sintered SiC ceramics were investigated. SiC ceramics containing 2.5 wt% C and 0.7–20 wt% B 4 C as sintering aids could be sintered to ≥ 99.4% of the theoretical density at 2150 °C for 1 h in Ar. The specific stiffness of SiC ceramics increased from 136.1 × 106 to 144.4 × 106 m2‧s−2 when the B 4 C content was increased from 0.7 to 20 wt%. The flexural strength and fracture toughness of the SiC ceramics were maximal with the incorporation of 10 wt% B 4 C (558 MPa and 3.69 MPa‧m1/2, respectively), while the thermal conductivity decreased from ∼154 to ∼83 W‧m−1‧K−1 when the B 4 C content was increased from 0.7 to 30 wt%. The flexural strength and thermal conductivity of the developed SiC ceramic containing 20 wt% B 4 C were ∼346 MPa and ∼105 W‧m−1‧K−1, respectively. [ABSTRACT FROM AUTHOR]

Double ceramic layer (DCL) TBCs consisting of a top 20 wt.% Al 2 O 3 -7YSZ layer and a bottom 7YSZ layer were desirably designed to achieve preferable performance while the thermal, mechanical and thermal cyclic properties were comprehensively investigated. Compared to the conventional 7YSZ TBCs, the thermal insulation properties of the DCL coating were significantly improved due to the increased oxygen vacancy concentration induced by Al 2 O 3 addition while the thickness of the thermally grown oxides was diminished by the decreased oxygen diffusion rate. Furthermore, the improved fracture toughness of the DCL coating also prolonged the thermal cyclic life. [ABSTRACT FROM AUTHOR]

The hierarchically porous La 2 Zr 2 O 7 (LZO) microsphere fabricated by the electro-spraying assisted phase inversion (ESP) method is a promising feedstock for thermal barrier coatings (TBCs), due to its low thermal conductivity, quite high near-infrared reflectivity and high temperature structure stability. However, the thermal properties of hierarchically porous LZO ceramics above 1000 K are still unclear, limiting its application in TBCs. The effect of hierarchical structure on thermal conduction and thermal radiation was investigated in comparison with mono-sized pores, using the ESP microspheres (LZO-ESP) and other two carbon fillers to modulate the pores. The results showed that LZO-ESP samples exhibited ultra-low thermal conductivity (1.28 W m−1 K−1 at 1173 K), which was 30% lower than that of the reference samples of similar porosity. Heat flux simulation revealed that hierarchical structure can induce more disorder domains than the randomly distributed mono-sized pores. The disorder domains with high tortuosity of heat flux played a predominant role in the reduction of thermal conductivity. Additionally, the hierarchical structure significantly reduced thermal radiation by 36% compared with dense sample due to the decrease in transmissivity. [ABSTRACT FROM AUTHOR]

The phase composition, microstructure, electrical and thermal properties of hot-pressed AlN-2 wt% Yb 2 O 3 -4 wt% Sm 2 O 3 - x wt% TiN (x = 0, 0.4, 0.8, 1, 2, 3, 4) ceramics were systematically investigated. Yb 2 O 3 and Sm 2 O 3 were used to react with Al 2 O 3 in AlN to form Yb 3 Al 5 O 12 , SmAlO 3 and SmAl 11 O 18 , which made the samples densely sintered. When sintered at higher than 1700 °C, the electrical resistivity of AlN ceramics with 2 wt% Yb 2 O 3 -4 wt% Sm 2 O 3 decreased significantly to 1010 Ω·cm. This decrease in resistivity was probably caused by the continuity of the secondary phase, which encasing the AlN grains and deteriorating the thermal conductivity. When sintered at 1650 °C, the addition of 0.4–4.0 wt% TiN reduces the electrical resistivity from 8.9 × 1012 to 2 × 1010 Ω·cm while maintaining thermal conductivity at around 90 W/m·K with high compactness. Finally, a series of high performance AlN ceramics, with adjustable electrical/thermal properties, could be obtained for modern semiconductor industry. [ABSTRACT FROM AUTHOR]

Rare-earth (RE) oxide-doped La 2 (Zr 0.7 Ce 0.3) 2 O 7 (LZC) has attracted great interest in thermal barrier coatings (TBCs) because of its lower thermal conductivity. However, studies on the laws governing the effect of different types of RE oxide doping on the performance of LZC ceramics are limited. Therefore, in this study, different types of RE (Sc, Y, Gd and Eu) doped LZC ceramic bulks have been prepared using solid phase reaction method. The effects of RE doping on the crystal structure, mechanical properties and thermal properties of the LZC ceramics were investigated. The results indicated that all five ceramics exhibited a single pyrochlore phase structure, whereas their lattice constants were reduced after doping, with (La 0.85 Sc 0.15) 2 (Zr 0.7 Ce 0.3) 2 O 7 having the lowest lattice constant. The effect of rare earth doping on the grain growth of LZC was not evident; however, it could significantly improve the hardness of LZC. In addition, doping with all four RE ions significantly reduced the thermal conductivity of the LZC ceramics, and the most significant reduction was observed for Gd3+ doping. [ABSTRACT FROM AUTHOR]

Dy 2 TiO 5 ceramics with small grain size range of 1.5–3 μm were successfully prepared by microwave sintering method. The phase composition, microstructure, thermal expansion, stability, corrosion resistance and neutron absorption properties of Dy 2 TiO 5 ceramics were investigated. The results show that Dy 2 TiO 5 ceramics possess high mechanical properties due to the small grain size, with a microhardness of 12.26 GPa. The addition of Mo significantly reduces the thermal expansion phenomenon of the sample. The oxide film formed on the surface of the Dy 2 TiO 5 ceramic enhances its excellent corrosion resistance. In addition, the Dy 2 TiO 5 ceramic shows excellent neutron absorption with 87.34% neutron absorption and over 94% thermal neutron absorption in 8 cm thick particles. [ABSTRACT FROM AUTHOR]

In this study, we investigated the tunable porous structure of SiCN(O)-derived ceramic aerogels by changing the molecular structure of the polysilazanes from linear to branched. We also studied the effect of molecular structure on the thermal insulation properties of ceramic aerogels. As the percentage of branched molecular structure in the polysilazane precursor increased, the internal microscopic pore structure of the aerogels changed from macroporous to mesoporous. The specific surface areas and pore volumes of the ceramic aerogels prepared with different precursors increased after pyrolysis at 1000 °C, ranging from 3.7 to 255.9 m2/g and 0.01–0.36 cm3/g, respectively. The corresponding thermal conductivities increased slightly as the aerogels contracted after pyrolysis. The low thermal conductivity (0.046 W/(m·K) at minimum) can be attributed to the decrease in pore size caused by adjusting the precursor structure, which limits the thermal conduction of gas in the porous aerogel materials. [ABSTRACT FROM AUTHOR]