Enhancing thermal and dielectric properties of MgO–Al2O3–SiO2–B2O3 glass-ceramics through CuO doping.

In this work, (20- x)MgO–20Al 2 O 3 –56SiO 2 –4B 2 O 3 - x CuO (x = 0, 0.25, 0.5, 0.75, 1, 1.25 mol%) glass-ceramics were synthesized by solid-state reaction method. The crystallization, microstructure, thermal and dielectric properties of (20- x)MgO–20Al 2 O 3 –56SiO 2 –4B 2 O 3 - x CuO glass-ceramics was discussed in detail. It was demonstrated that the CuO lowers the crystallization temperature of α-cordierite and promotes the crystallization process of MgO–Al 2 O 3 –SiO–B 2 O 3 glass-ceramics. Thus, the crystallization showed a substantial influence on the dielectric properties, as evidenced by an elevation in dielectric constant and a decrease in dielectric loss. Specifically, with the addition of 0.5 mol% CuO, the MgO–Al 2 O 3 –SiO–B 2 O 3 glass-ceramics sintered at 1050 °C shows excellent properties of: ε r = 5.04, tan δ = 2.2 × 10-4, κ = 3.4 W/mK and α = 1.75 × 10-6/°C. These works provide valuable insights into the design and development of (20- x)MgO–20Al 2 O 3 –56SiO 2 –4B 2 O 3 - x CuO glass-ceramics with tailored properties for structure/function integration in the electronics industry. [ABSTRACT FROM AUTHOR]