Abstract: The Mg/Al laminated composite was fabricated by the accumulative roll bonding (ARB) using the pure magnesium and Al5052 alloy at 400°C. Tensile properties along rolling direction and the transverse direction and the microhardness were evaluated at the ambient temperature. The tensile strength of the laminated Mg/Al composite along both directions increased gradually till two ARB cycles, but then decreased after the third ARB cycles. Optical microscopy and scanning electron microscopy (SEM) were utilized to reveal the microstructure evolution and the failure mechanism. Grain refinement of Mg layers was not obvious during the ARB process due to the high temperature and interval reheating. The obvious crack at the coarse intermetallic compounds and rupture of the Al layer after the third cycle led to the premature failure of the sample along the rolling direction during the tensile test. [Copyright &y& Elsevier]

Abstract: The effect of Si content on low frequency damping capacities and mechanical properties of as-cast Mg–Si alloys were investigated. Both hypoeutectic alloys with 0.3wt.%Si, 0.8wt.%Si and hypereutectic alloy with 2.3wt.%Si exhibit high damping capacities since these Mg–Si alloys possess large size α-Mg phase with very small amount of soluble atoms in it. The amount of the in situ formed Mg2Si determines the dislocation density and then influences the damping capacity of these Mg–Si alloys. The Mg–0.3wt.%Si alloy exhibits the lowest damping value at small strain region but the highest damping value at large strain region among these Mg–Si alloys. Two damping peaks were found in Mg–Si alloys at 80 and 230°C, respectively. But the addition of Al in Mg–Si alloy impeded the appearance of these two damping peaks since the soluble Al atoms hindered the movement of dislocations and the slide of grain boundaries. The presence of large size, brittle primary Mg2Si particles decreases the tensile strength and ductility of the hypereutectic Mg–Si alloy. [Copyright &y& Elsevier]

Abstract: Mechanical properties of coated AZ91 Mg alloy, Al18B4O33w/AZ91 and SiCw/AZ91 composites by microarc oxidation (MAO) surface treatment technique were measured and effects of MAO treatment on the mechanical properties were investigated. Tensile test shows that MAO treatment just slightly decreases ultimate tensile strength (UTS) and elongation of the Mg-based materials, while enhances their elastic modulus to some extent. But the effects of MAO treatment on the mechanical properties will be influenced by the energy parameters applied during surface treatment. The three materials coated under the same process conditions have exhibited differential surface morphology and fracture after tensile test, which indirectly indicates that the qualities of MAO coatings are also related with the substrate materials. [Copyright &y& Elsevier]

The effect of high temperature exposure on the interface and tensile properties of Al18B4O33w/AZ91 magnesium matrix composite fabricated by squeeze casting was studied. The interfaces of the composites were examined using transmission electron microscopy, and the mechanical properties were evaluated by tensile tests. The interfacial region was composed of MgO which was formed by the reaction between the Al18B4O33 whisker and the Mg matrix. An thin and uniform interfacial reaction layer with a thickness of 10–20 nm formed during squeeze casting could act as a barrier to prevent the further reaction between Al18B4O33 whisker and Mg alloys. The interfacial reaction rate was very low during thermal exposure below the liquidus temperature of AZ91 matrix alloy. Only after exposure above the liquidus temperature of the AZ91 matrix alloy for a long period, the thickness of the interfacial layer increased obviously. However, the interfacial reaction rate was much slower than that in the Al18B4O33w/Al–Mg composites. The interfacial reaction kinetics was controlled by the seepage of Mg and release of Al and B along the narrow diffusion channels between the fine MgO particle. The composite did not show a degradation in the tensile properties after exposure below the solidus temperature of AZ91 for long periods, suggesting that the Al18B4O33w/AZ91 magnesium matrix composite could be subjected to long-term service at elevated temperature. [Copyright &y& Elsevier]

Due to its service background, the thermal behavior of Ta films is substantially concerning to researchers, especially the heat-induced β-Ta to α-Ta phase transformation. In this work, the nanocrystalline Ta films with varying β/α phase ratios (0.85–0) were deposited and vacuum annealed at 200–800 °C to study the phase transformation behavior and mechanical properties. Partial phase transformation of β-Ta to α-Ta occurred at low temperature (200 °C) and complete transformation when the annealing temperature was raised to 800 °C. Moreover, an orientation relationship of β-<110>//α-<111> and β-{330}//α-{110} was concluded, and a hypothesis theory about the low-temperature phase transformation was proposed. Annealing hardening took place at 200–600 °C and softening at 800 °C in all the samples. The hardening is mostly due to the ordering of intergranular amorphous phases with the temperature increased, simultaneously bringing the increase of modulus. The annealing softening is governed by both grain coarsening and phase transformation, where the latter is dominated in high β fraction samples. • High-temperature induced grain boundary structure ordering promotes the hardening of Ta films at 200 °C–600 °C. • β-Ta to α-Ta phase transformation was found at a wide temperature range, which partially governs the softening of Ta at 800 °C. • A preferred orientation relationship of β-<110>{330}//α-<111>{110} was concluded • The influence of phase transformation on mechanical properties was independently quantified using a simple comparative method. [ABSTRACT FROM AUTHOR]

Abstract: The extruded Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr (wt%) alloy were subjected to large-strain hot rolling with different final rolling temperatures. The microstructural evolution and mechanical properties of the sheets were investigated. The microstructure became homogeneous after hot rolling process and long period stacking ordered (LPSO) phase distributed at grain boundaries along rolling direction. The sheet rolled at 300°C was composed of deformed grains, substructures and excessive dislocations. With increasing final rolling temperatures from 300°C to 400°C, the volume fraction of recrystallized grains with relatively random orientations increased significantly. The strength of the rolled sheets was improved while the ductility was deteriorated with decreasing final rolling temperatures. The tensile yield strength and ultimate tensile strength of the sheet rolled at 300°C reached 320MPa and 416MPa, respectively with the elongation to failure of 5.3%. The mechanical anisotropy of the rolling sheet became unity when rolled at higher temperature of 400°C due to the formation of weaker basal texture. [Copyright &y& Elsevier]

Abstract: Different cooling processes, such as quenching in warm water and cooling in furnace, were introduced to homogenize Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr (wt%) alloy. Microstructure evolution and mechanical properties of the homogenized alloy were investigated. The as-quenched sample was comprised of α-Mg matrix, Mg5RE phase and 18R LPSO phase distributed at the grain boundaries and a few of RE-rich particles distributed randomly. During the process of cooling in furnace, Mg5RE and 18R LPSO phases were transformed into block-shaped 14H LPSO phase and lamellar-shaped 14H LPSO phase, respectively, due to the diffusion of solute atoms into the α-Mg matrix. Furthermore, the lamellar-shaped 14H LPSO phase grew and ran through the whole grains. The as-quenched sample exhibits tensile yield strength of 130MPa, ultimate tensile strength of 206MPa and elongation to failure of 5.5%, while the sample cooled in the furnace exhibits higher tensile yield strength but lower ultimate tensile strength and ductility due to the coarse grains and formation of block-shaped 14H LPSO phase. [Copyright &y& Elsevier]

Abstract: The Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr (wt.%) alloy was hot rolled with different final rolling reductions at 400°C. The microstructure evolution and texture of the sheets were analyzed, and their effect on the mechanical properties was discussed. All of the rolled sheets consist of fine dynamically recrystallized grains with almost random orientation, large deformed grains with strong basal texture. In addition, bent lamellar-shaped long period stacking ordered (LPSO) phases due to kink deformation were observed in the deformed grains. The volume fraction of the dynamic recrystallization increased with increasing final rolling reduction and the basal texture weakened gradually. The strength of the alloy sheets changed a little with increasing final rolling reduction, while the yield anisotropy and the ductility were significantly improved. The sheet final-rolled with thickness reduction of 60% exhibits tensile yield strength of 306MPa, ultimate tensile strength of 393MPa and elongation to failure of 14.6% at ambient temperature, and tensile yield strength of 264MPa, ultimate tensile strength of 345MPa and elongation to failure of 19.4% at 250°C. [Copyright &y& Elsevier]

Abstract: Magnesium matrix nanocomposites reinforced by SiC nanoparticles were fabricated by ultrasonic vibration with SiC nanoparticle size of 60nm and volume fractions of 0.5%, 1% and 2%, respectively. With increasing the volume fraction of the SiC nanoparticles, grain size of matrix in the SiCp/AZ91 nanocomposites was gradually decreased and morphology of the phase Mg17Al12 was refined compared with as-cast AZ91 alloy. Most of the SiC nanoparticles exhibited a homogeneous distribution in the 0.5 and 1vol.% SiCp/AZ91 nanocomposites. The ultimate tensile strength, yield strength and elongation to fracture of the 0.5 and 1vol.% SiCp/AZ91 nanocomposites were simultaneously improved. However, agglomerates of SiC nanoparticles along the grain boundaries were evidently increased when the volume fraction of nanoparticles was increased to 2, which caused the decrease of ultimate tensile strength and elongation to fracture. [Copyright &y& Elsevier]

Abstract: The pure Mg sheets were processed by ARB at 400°C and 300°C up to 8 cycles and 4 cycles, respectively. The microstructure was refined during the first cycle and only homogenized during the following ARB process due to the high deformation temperature, intermediate reheating and air-cooling. The ARB process did not show an obvious effect on the tensile properties of the as-ARBed pure Mg sheet due to the stable grain size and dominant basal plane texture during ARB. Further deformation should be introduced to improve the bonding quality of the as-ARBed sheet. [ABSTRACT FROM AUTHOR]

This study investigates the precipitation behavior in the graphene nanoplatelets (GNPs) reinforced bimodal structural Mg-6Zn (wt%) matrix composite. The GNPs with an increasing content progressively accelerate the age-hardening response in the local regions of the composite. The composite takes only half the time that the Mg-6Zn alloy needs to reach the peak strength when aging at 200 °C. The observation reveals that the planar and wrinkled GNPs in the composite act as the effective trigger of dislocations and collector of solute atoms to accelerate the precipitation. It is concluded that GNPs have a pronounced effect on the development of matrix microstructure. Moreover, the orientation relationship between the aligned GNPs towards the extrusion direction and the matrix grains with a fiber type texture makes the GNPs and [0001] Mg precipitate rods constitute a hybrid strengthening architecture in the composite. As a result, the synergistic strengthening effect of the GNPs and the precipitates is realized. [ABSTRACT FROM AUTHOR]

Pure molybdenum (PM) and La 2 O 3 dispersion strengthened Mo alloy (ODS-Mo) were prepared by powder metallurgy through two different mixing method (solid-solid or SS mixing and solid-liquid or SL mixing). After annealed at 1050 °C for 1 h, the PM, SS-Mo and SL-Mo were compared in microstructure and mechanical properties. The microstructural examinations showed that the PM was mostly recrystallized with rather coarse grains, but the ODS-Mo alloys remained fine elongated grains. This discrepancy is due to a higher recrystallization temperature held in the ODS-Mo alloys. The uniaxial testing results showed that the ODS-Mo had higher tensile mechanical properties compared to the PM, which are attributed to the remarkable strengthening and ductilizing effect induced by the La 2 O 3 particles. The low cycle fatigue (LCF) testing results revealed that the PM experienced cyclic hardening behaviors, while the ODS-Mo alloys exhibited cyclic softening behaviors. The Basquin-Manson-Coffin analyses results demonstrated that the ODS-Mo possessed a higher fatigue ductility and longer fatigue life than the PM. Two kinds of cracks, i.e., cleavage cracks and intergranular cracks, were experimentally observed to coexist on the fracture surface. In particular in the SL-Mo alloy, the two crack interacted and propagated forward until final fracture, leading to a step-like crack growth path and concomitantly enhanced fatigue ductility. In addition, different cycling dislocation structures were revealed between the PM and ODS-Mo alloys. Cycle fatigue mechanisms responsible for the fatigue behaviors and microstructure evolution during LCF testing were discussed. The best LCF resistance combined with superior uniaxial tensile mechanical properties found in the SL-Mo alloy were rationalized. [ABSTRACT FROM AUTHOR]

High quality WE43 magnesium alloy ingots with diameter of 500 mm are successfully fabricated by direct-chill (DC) casting. The alloying elements distributed almost homogeneously across the large ingot. With the average grain size decreasing from the center to the edge of the ingot, the mechanical properties are improved gradually. After solution treatment at 525 °C for 8 h, the Mg 14 Nd 2 Y phases distributing along the grain boundaries are well dissolved into matrix. The direct-chill (DC) casting ingot exhibits remarkable age-hardening response from 85 Hv to 117 Hv after T6 treatment at 250 °C. The T6 peak-aged sample exhibits ultimate tensile strength of 274 MPa, yield strength of 215 MPa and elongation to failure of 3.4%, which are higher than those of sand-cast and permanent mold cast WE43 alloys. The large amount of nano prismatic β ′ and β 1 phases precipitated during T6 treatment contribute to improved strength of the WE43 alloy. [ABSTRACT FROM AUTHOR]

The effect of Ca/Al ratio on microstructure and mechanical properties of the as-cast and as-extruded Mg-Al-Ca-Mn alloys were investigated. The as-cast Mg-Al-Ca-Mn alloys with Ca/Al mass ratios less than 0.50 contain divorced and lamellar eutectic (Mg,Al) 2 Ca. When Ca/Al ratio is greater than 0.90, fine lamellar Mg 2 Ca phase is formed in the as-cast Mg-Al-Ca-Mn alloys. After extrusion, the second phases are broken and dispersed along the extrusion direction. The area fraction of DRXed regions decrease with increasing Ca/Al ratio, the microstructure changes from an almost fully recrystallized structure to a bimodal structure consisting of fine dynamically recrystallized (DRXed) grains and coarse deformed regions. With increasing Ca/Al ratio, the DRXed grains and dispersed second phases are refined. The as-extruded alloys exhibit a strong basal fiber texture, the intensity of which is increased with increasing Ca/Al ratio. With increasing Ca/Al ratio, the {0002}<11-20> texture component in the DRXed regions is suppressed, and shifted to a {0002}<10-10> texture component. The strength of the as-extruded Mg-Al-Ca-Mn alloys increases significantly with increasing Ca/Al ratio. The as-extruded Mg-2.7Al-3.5Ca-0.4Mn (wt%) alloy exhibits a tensile proof strength of 438 MPa and an ultimate tensile strength of 457 MPa. The extraordinary high strengths are attributed to the ultrafine DRXed grains pinned by fragmented secondary phases, strong basal texture and dense nano-scale precipitates. The present research indicates that the Mg-Al-Ca-Mn alloys have a great potential as next generation low-cost ultrahigh-strength wrought Mg alloys. [ABSTRACT FROM AUTHOR]

AZ91 alloy was subjected to multidirectional forging (MDF) and the relationship between microstructures and mechanical properties generated by MDF were investigated. The results showed that after 1 MDF pass grain size of the alloy decreased compared with as-cast alloy, and the amount of recrystallization grains increased when the MDF temperature increased from 250 °C to 400 °C. With increasing the MDF passes at 350 °C, grains of the alloy were gradually refined. A typical basal texture was obtained after 1 MDF pass, and then the basal pole scattered with the increase of MDF passes. Mg 17 Al 12 phases were precipitated along grain boundaries during MDF, which could hinder the growth of recrystallization grains. Both tensile strength and elongation to failure of the alloy were significantly enhanced till 3 MDF passes with increasing the MDF passes. [ABSTRACT FROM AUTHOR]

Abstract: Bimodal sized (Micro-particles: m and Nano-particles: n) SiC particulates (SiCp) reinforced magnesium matrix composites with different volume fractions of micro-particles (1n+4p, 1n+9p and 1n+14p) were prepared by a semisolid stirring assisted ultrasonic vibration method. Both the as-cast SiCp/AZ31B composites and the AZ31B alloy were extruded at 350°C with the extrusion ratio of 12:1 at a constant ram speed of 15mm/s. The microstructure investigation was carried out by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscopy (TEM). The results show that the distribution of bimodal size SiCp and the mechanical properties of the AZ31B alloy were significantly improved after hot extrusion. When the volume fraction of nano SiCp is 1vol%, both the yield strength and ultimate tensile strength of the AZ31B/SiC/1n+14p composite are stronger than that of the AZ31B/SiC/1n+4p and AZ31B/SiC/1n+9p composites, while the elongation to fracture was decreased comparing with the AZ31B/SiC/1n+4p and AZ31B/SiC/1n+9p composites. [Copyright &y& Elsevier]

Abstract: Carbon nanotube (CNTs) reinforced Mg matrix composites were successfully fabricated by a novel approach. After hot extrusion, the influence of CNTs on microstructure and mechanical properties of Mg–6Zn matrix was investigated. The results showed that most CNTs distributed uniformly and individually in the composites, and good interfacial bonding was achieved. CNTs significantly refined the grains of Mg–6Zn matrix, and the CNTs evidently improved the ultimate tensile strength (UTS), yield strength (YS) and Young's modulus. Grain refinement, load transfer mechanism and Orowan strengthening mechanism play important roles on the increase of the yield strength. [Copyright &y& Elsevier]

The Mg–4.50Zn–1.13Ca (wt%) alloy was subjected to double extrusion, and the microstructure and mechanical properties of the extruded alloys were investigated. Double extrusion refined the microstructure significantly, resulting in the enhancement of mechanical properties of the double-extruded alloys compared with the single-extruded alloy. The yield strength of the single-extruded alloy was 173MPa, while the value was increased to 320MPa and 370MPa after subsequent second extrusion at 300°C and 250°C, respectively. The second extrusion ratio had little effect on the microstructure and mechanical properties of the double-extruded alloys, while grain size was decreased and strength was increased with the decrease of double extrusion temperature. The double-extruded Mg–Zn–Ca alloy exhibited superior elevated temperature mechanical properties, which was attributed to the fine stable Ca2Mg6Zn3 intermetallic compound particles dispersed in the alloy. [ABSTRACT FROM AUTHOR]

Abstract: The microstructures and mechanical properties of Mg–5.3Zn–0.2Ca–0.5Ce (wt%) alloy fabricated by semi-continuous casting were investigated. The as-cast alloy consists of α-Mg, Ca2Mg6Zn3 and T′1 phase with orthorhombic structure (a=0.57nm, b=0.75nm and c=1.00nm). T′1 phase mainly distributes at the triple conjunctions while the Ca2Mg6Zn3 at the grain boundaries. The as-cast alloy exhibits high strength retention due to the stable Ca2Mg6Zn3 and T′1 phase at the grain boundaries. [Copyright &y& Elsevier]

Abstract: A large Mg-4.50Zn-1.13Ca (wt%) alloy ingot 350mm in diameter and 1730mm long was successfully fabricated by semi-continuous casting. The microstructures and mechanical properties of the as-cast and as-extruded alloys were investigated. The as-cast alloy exhibits uniform chemical composition and microstructure from the centre to the surface of the ingot and mainly consists of α-Mg and Ca2Mg6Zn3. The coarse grains and network-like second phases that are distributed at the grain boundaries result in poor mechanical properties for the as-cast alloy. The mechanical properties of the as-extruded alloys are significantly enhanced. The high yield strengths of the as-extruded alloys mainly result from the fine DRXed grain and the stronger basal texture. [Copyright &y& Elsevier]

Abstract: Extruded Mg–8.2Gd–3.8Y–1Zn–0.4Zr (wt%) alloy was subjected to ageing treatment at 200°C. The microstructures, textures and mechanical properties of the as-extruded and peak-aged alloys were investigated. Recrystallization occurred during ageing treatment. A large number of β′ phases were observed in the peak-aged alloy, accompanied with the decrease of the volume fraction of LPSO phases. A basal fiber texture and an unusual texture component with basal planes perpendicular to the extrusion direction were found in the as-extruded alloy, and the basal fiber texture was strengthened after ageing treatment. The peak-aged alloy exhibited a tensile yield strength (TYS), an ultimate tensile strength (UTS) and an elongation to failure of 395MPa, 470MPa and 8%, respectively, at ambient temperature, and 271MPa, 311MPa and 19%, respectively, at 300°C. The superior strength of the peak-aged alloy was mainly attributed to the precipitation of fine β′ phases, the remaining LPSO phases and the texture modification. [Copyright &y& Elsevier]

Abstract: In this paper, 0.2μm SiCp/AZ91 composite was fabricated by stir casting technology. The influence of fine (<1μm) particles on the dynamic recrystallization (DRX) behavior of AZ91 matrix was investigated by researching the microstructure evolution of 0.2μm 1vol% SiCp/AZ91 composite during the hot extrusion process. Results showed that the DRXed ratio of AZ91 matrix increased as well as the average size of DRXed grains reduced due to the addition of fine particles. The SiCp could not only pin dislocation, but also was helpful to generate dislocations owing to the deformation mismatch between matrix and particles, thus causing the increase of dislocation density around SiCp, which was benefit to stimulate DRX nucleation. Meanwhile, the growth of DRXed grains was suppressed in the following deformation process due to the pinning effect of fine particles on grain boundaries. Thus, the fine particles had significant effect on stimulating DRXed nucleation and refining grain size. The yield strength and ultimate tensile strength of the as-deformed 0.2μm 1vol% SiCp/AZ91 composite are 275 and 335MPa, respectively, which are mainly attributed to the grain refinement, basal plane texture and uniform particle distribution induced by hot deformation. [Copyright &y& Elsevier]

Abstract: The microstructure and mechanical properties of Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr (wt%) alloy sheets produced by combined processes of extrusion, large-strain hot rolling and ageing treatment were investigated. The sheet rolled at 300°C was mainly composed of deformed grains while that rolled at 400°C was fully recrystallized, and the LPSO phase distributed at the grain boundaries in both sheets. The sheet rolled at 300°C and then peak-aged at 200°C exhibits 0.2% proof stress (PS) of 454MPa, ultimate tensile strength (UTS) of 469MPa and elongation to failure of 1.3% at ambient temperature, and 0.2% PS of 413MPa, UTS of 457MPa and elongation to failure of 6.8% at 200°C, respectively. While the sheet rolled at 400°C and peak aged at 200°C had lower 0.2% PS and superior ductility. The improvement of strength is ascribed to the fine β′ phase precipitated within the grains, the LPSO phase and dispersed cuboid Mg–Gd–Y containing phase located at the grain boundaries. [Copyright &y& Elsevier]

Abstract: Mg-8.2Gd-3.8Y-1.0Zn-0.4Zr alloy ingot with diameter of 280mm and length of 2940mm was successfully fabricated by semi-continuous casting. The microstructure and mechanical properties of the large ingot at different locations were investigated. The concentration of the RE and Zn elements distributed almost homogeneously through the whole alloy ingot. The average grain size decreased from the center to the surface of the alloy ingot, while the strength and ductility were improved gradually. The main eutectic compounds located at the grain boundaries were (Mg,Zn)3(Gd,Y) phase, adjacent to these eutectic compounds the 14H-type long period stacking ordered (LPSO) phase formed. Furthermore, some block-shaped Mg24(Gd,Y)5 phase and isolated Zr cores can be recognized in the interior of the grains. [Copyright &y& Elsevier]

Abstract: Ultra high-strength Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr alloy sheet was prepared by large-strain hot rolling and subsequent ageing process. The sheet exhibits excellent tensile properties at ambient temperature with ultimate tensile strength of 517MPa, 0.2% proof stress of 426MPa and elongation to failure of 4.5%. The notable improvement in strength is attributed to the dense distribution of the fine precipitates inside the grains, scattered precipitates at the grain boundaries, bimodal grain size distribution with fine recrystallized grains and large deformed grains with intense basal texture. [Copyright &y& Elsevier]

sAbstract: The Mg/Al laminated composites were fabricated by the accumulative roll bonding (ARB) at ambient temperature using the pure magnesium and commercial pure Al sheets. Mg grains were refined after the primary sandwich preparation and then homogenized during the following ARB process while the grain size of Al layer decreased with increasing of the accumulated strains. Both the yield strength and ultimate strength along rolling direction and transverse direction increased gradually while the elongation to failure along both directions decreased with increasing of the ARB cycles. Formation of the Mg17Al12 phase indicated that the ARB process at ambient temperature could lead to a metallurgic bonding of the Mg/Al interface. [Copyright &y& Elsevier]

Abstract: In this paper, three kinds of magnesium matrix composites reinforced by SiCp with the sizes of 0.2, 5 and 10μm, respectively, were fabricated by stir casting technology. Then the as-cast ingots were deformed by the combination of forging and extrusion process. Typical microstructures were obtained in the composites reinforced by different particle sizes. For the composites with lower volume fraction of particles (2%), submicron SiCp had significant influence on grain refinement and strengthening effect, which resulted in better mechanical properties of submicron SiCp/AZ91 composite. However, mechanical properties reduced owing to the obvious agglomerated submicron SiC particles as the volume fraction increased to 5% and 10%. On the contrary, for micron SiCp/AZ91 composite, the grain size was refined and the strengthening effect was enhanced with the increasing of volume fraction. Although particle size has no influence on the texture type, it has different effects on weakening the intensity of texture. [Copyright &y& Elsevier]

Abstract: In this study, firstly, dynamic microstructural changes of an as-cast Mg–5.0 Zn–0.9 Y–0.16 Zr (wt.%) alloy (designated ZWK510) during hot extrusion at 350°C and a ram speed of 3.33mms−1 was systematically investigated by electron backscattering diffraction (EBSD) analysis. The dynamic recrystallization (DRX) mechanism during hot extrusion was discussed. Then, the effect of microstructure and texture on the mechanical properties of the as-extruded alloy specimens at room temperature was discussed. The as-cast ZWK510 alloy consists of a-Mg and quasicrystalline I-phase. During hot extrusion at 350°C, the main DRX mechanism is the continuous DRX near the original grain boundaries. The I-phase can accelerate the DRX behavior near these areas by obstructing the slip of dislocations. The deformation twins and massive blocky substructures formed in original grains can coordinate the DRX process near the original grain boundaries, however the DRX seldom occurs inside of these area. After further deformation, these deformation twins and massive blocky substructures are elongated along the material flow and become so-called unDRXed area, then a bimodal “necklace structure” composed of fine DRXed grains of about 2.1μm and unrecrystallized coarse area is formed. The extruded ZWK510 alloy shows a DRX ratio of about 58% and a typical basal fiber texture of extrusion direction (ED). In the DRXed area around the crushed eutectic I-phase a large number of fine I-phase precipitates are observed pinning at the newly formed DRXed grain boundaries. The 0.2% proof strength and the ultimate tensile strength of the extruded ZWK510 alloy specimen are 317 and 363MPa, respectively, with an elongation to failure of 12%, which have been attributed to strong basal fiber texture, refined grain size as well as the existence of fine precipitates formed during the hot extrusion. [Copyright &y& Elsevier]

Abstract: The effect of trace Mn addition on the microstructure, texture and mechanical properties of the as-cast and as-extruded Mg–5.25wt.% Zn–0.6wt.% Ca (ZX51) alloys was investigated in this study. Mn addition had a negligible effect on the grain size of the as-cast ZX51 alloy. However, the addition of Mn led to the obvious decrease of grain size in the as-extruded Mg–5.25wt.% Zn–0.6wt.% Ca–0.3wt.% Mn (ZXM510) alloy, because the Mn addition restricted the grain growth during the hot extrusion process. After the addition of Mn, the basal fiber texture with most of {0002} planes parallel to the extrusion direction (ED) was significantly enhanced in the as-extruded ZXM510 alloy. Both tensile yield strength (TYS) and ultimate tensile strength (UTS) were increased in the as-extruded ZXM510 alloy, while the ductility was slightly decreased, which was ascribed to the grain refinement and texture strengthening. [Copyright &y& Elsevier]

Abstract: Mg–5.25wt.% Zn–0.6wt.% Ca alloy was subjected to equal channel angular pressing (ECAP) at 250°C using route A, Bc and C, respectively, in order to investigate the effect of shearing strain path on microstructure, texture and mechanical properties. Route Bc was the most effective in grain refinement and generating high angle grain boundaries, while route A was the least effective. Different textures were developed when a different ECAP route was applied. After ECAP using route A, the tensile yield strength (TYS) got much higher than those of the as-extruded alloy, which was primarily resulted from the strengthening due to the grain refinement. Because the Schmid factor for basal slip system was changed only a little, the texture soften effect was not obvious. After ECAP using route C, TYS of the Mg alloy was significantly decreased although the grain size was significantly refined, because the texture softening effect was dominant over the strengthening due to the grain refinement. [Copyright &y& Elsevier]

Abstract: An ultrafine-grained (UFG) Mg–5.12wt.% Zn–0.32wt.% Ca alloy with an average grain size of 0.7μm was produced by subjecting the as-extruded alloy to equal channel angular pressing (ECAP) for 4 passes at 250°C. The fine secondary phase restricted the dynamic recrystallized (DRXed) grain growth during the ECAP processing, resulting in a remarkable grain refinement. A new texture was formed in the ECAPed Mg alloy with the {0002} plane inclined at an angle of 58° relative to the extrusion direction. The yield stress (YS) was decreased in the as-ECAPed alloy with finer grains, indicating that the texture softening effect was dominant over the strengthening from grain refinement. The ductility of the as-ECAPed alloy was increased to 18.2%. The grain refinement caused an obvious decrease in work hardening rate in the as-ECAPed alloy during tensile deformation at room temperature. [Copyright &y& Elsevier]