Search

Impedance measurements are used to study the dielectric properties of nanocrystalline [Ni.sub.0.5][Zn.sub.0.5][Fe.sub.2][O.sub.4] spinel ferrite with various grain sizes, which is obtained by mechanical milling. The electrical modulus study has shown the presence of the non-Debye type of dielectric relaxation in the materials with the stretched exponent parameter [beta] decreasing with the reduction of grain size upon milling.

Li3Fe2(PO4)3 is interesting because of its technological application and environmentally benign nature. Nanocrystalline Li3Fe2(PO4)3 is synthesized by a solution combustion technique. The role of fuels/complexing agents in deciding the structural parameters and ac electrical behavior is investigated in this study. Antiferromagnetic nature and direct bandgap energy of 3.09 eV are recognized in the material. Enhanced conduction is established through mobility of Li+ ion in four co-ordination in the modified monoclinic symmetry and high temperature stability through orthorhombic symmetry. Quality of electrical data is confirmed through a Kramers-Kronig test and electrical relaxation parameters are obtained from modulus analysis. Scaling analysis of modulus data confirmed the time-temperature superposition principle. [ABSTRACT FROM AUTHOR]

The dielectric properties of nanocrystalline Ni0.5Zn0.5Fe2O4 spinel ferrite with various grain sizes, obtained by mechanically milling, have been studied using impedance measurements in the frequency range from 1 Hz to 10 MHz and in the temperature range from 300 to 823 K. The effect of milling, frequency, and temperature on the dielectric properties of nanocrystalline Ni-Zn ferrite is discussed. The real part of dielectric constant ([variant_greek_epsilon]′) for the 14 nm grain size sample is found to be about an order of magnitude smaller than that of the bulk nickel zinc ferrite. The anomalous frequency dependence of [variant_greek_epsilon]′ has been explained on the basis of hopping of both electrons and holes. The unusual increase in dielectric loss with milling is because of the increase in electrical conductivity due to oxygen vacancies introduced upon milling. The electrical modulus has been fitted to a stretched exponential function and the results clearly reveal the presence of the non-Debye type of dielectric relaxation in this material. The relaxation frequency is observed to decrease with milling due to increasing interaction between charge carriers arising out of oxygen vacancies introduced by milling. The mechanism for the electrical conduction is found to be the same as that for the dielectric polarization. [ABSTRACT FROM AUTHOR]

The dielectric properties of nanocrystalline Ni0.5Zn0.5Fe2O4 spinel ferrite with various grain sizes, obtained by mechanically milling, have been studied using impedance measurements in the frequency range from 1 Hz to 10 MHz and in the temperature range from 300 to 823 K. The effect of milling, frequency, and temperature on the dielectric properties of nanocrystalline Ni-Zn ferrite is discussed. The real part of dielectric constant ([variant_greek_epsilon]′) for the 14 nm grain size sample is found to be about an order of magnitude smaller than that of the bulk nickel zinc ferrite. The anomalous frequency dependence of [variant_greek_epsilon]′ has been explained on the basis of hopping of both electrons and holes. The unusual increase in dielectric loss with milling is because of the increase in electrical conductivity due to oxygen vacancies introduced upon milling. The electrical modulus has been fitted to a stretched exponential function and the results clearly reveal the presence of the non-Debye type of dielectric relaxation in this material. The relaxation frequency is observed to decrease with milling due to increasing interaction between charge carriers arising out of oxygen vacancies introduced by milling. The mechanism for the electrical conduction is found to be the same as that for the dielectric polarization. [ABSTRACT FROM AUTHOR]