We present a detailed analysis of the trap states in atomic layer deposition Al2O3/InAlN/GaN high electron mobility transistors grown by pulsed metal organic chemical vapor deposition. Trap densities, trap energies and time constants are determined by frequency-dependent conductance measurements. A high trap density of up to 1.6 × 1014 cm−2eV−1 is observed, which may be due to the lack of the cap layer causing the vulnerability to the subsequent high temperature annealing process. [ABSTRACT FROM AUTHOR]

GaN-based heterostructures with an InAlGaN/AlGaN composite barrier on sapphire (0001) substrates are grown by a low-pressure metal organic chemical vapor deposition system. Compositions of the InAlGaN layer are determined by x-ray photoelectron spectroscopy, structure and crystal quality of the heterostructures are identified by high resolution x-ray diffraction, surface morphology of the samples are examined by an atomic force microscope, and Hall effect and capacitance-voltage measurements are performed at room temperature to evaluate the electrical properties of heterostructures. The Al/In ratio of the InAlGaN layer is 4.43, which indicates that the InAlGaN quaternary layer is nearly lattice-matched to the GaN channel. Capacitance–voltage results show that there is no parasitic channel formed between the InAlGaN layer and the AlGaN layer. Compared with the InAlGaN/GaN heterostructure, the electrical properties of the InAlGaN/AlGaN/GaN heterostructure are improved obviously. Influences of the thickness of the AlGaN layer on the electrical properties of the heterostructures are studied. With the optimal thickness of the AlGaN layer to be 5 nm, the 2DEG mobility, sheet density and the sheet resistance of the sample is 1889.61 cm2/V · s, 1.44 × 1013 cm−2 and as low as 201.1 ω/sq, respectively. [ABSTRACT FROM AUTHOR]

Epitaxial growth of InAlGaN/GaN structures are performed on the c-plane sapphire by pulsed metal organic chemical vapor deposition with different triethylgallium (TEGa) flows in the growth process of InAlGaN quaternary alloys. X-ray photoelectron spectroscopy results show that the Al/In ratio of the samples increases as the TEGa flows increase in the InAlGaN quaternary growth process. High-resolution x-ray diffraction results show that the crystal quality is improved with increasing TEGa flows. Morphology of the InAlGaN/GaN heterostructures is characterized by an atomic force microscopy, and the growth mode of the InAlGaN quaternary shows a 2D island growth mode. The minimum surface roughness is 0.20 nm with the TEGa flows equaling to 3.6 μmol/min in rms. Hall effect measurement results show that the highest electron mobility μ is 1005.49 cm2 /Vs and the maximal two-dimensional electron gas is 1.63 × 1013 cm−2. [ABSTRACT FROM AUTHOR]