Search

This paper aimed to determine the characteristics of physical and mechanical properties of rice straw hand sheet and investigated the optimal conditions for making rice straw paper. The chemical composition of rice straw determined with the TAPPI standards. The conditions of making paper hand sheet composed of pulping time: 2 hours, 4 hours, pulping temperature: 100°C, 130°C, pulping solvent: 2 wt% NaOH, 4 wt% NaOH and bleaching: unbleached pulp, bleached pulp with 2% H2O2. The paper hand sheet was tested based on TAPPI methods, basic weight TAPPI- T410-om-93, thickness TAPPI- T411-om-89, moisture content TAPPI- T412-om-93, brightness TAPPI T452 om-92, opacity TAPPI standard T 425 om-91, burst strength TAPPI T403 om-97, tensile strength TAPPI T494 om-01, and tear strength TAPPI-T414-om-88. The results showed that the optimal conditions of rice straw hand sheet including pulping time: 2 hours, pulping temperature: 100°C, pulping solvent: 2 wt% NaOH, and bleaching: unbleached pulp gave the highest the physical and mechanical properties form other conditions. This conditions showed as the basic weight 62.27 g/m2, thickness 259.30 µ, opacity 93.34 ISO%, burst strength 64.75 kPa.m2/g, tensile strength 95.33 N.m/g, and tear strength 473.55mN.m2/g. In this condition, the paper hand sheet used at the lowest concentration of pulping solvent and non-bleached, which reduces environmental pollution.

Anode surface plays important role for extracellular electron transfer (EET) of exoelectrogenic microbes in microbial fuel cell (MFC). In this report, the electrochemical performance of a TiO2nanorod array modified carbon paper electrode (TiO2NRs/CP) is greatly improved by controlled chemical etching process. The etching process keeps the array morphology but yields obvious hollows on tops of TiO2nanorods. The etched electrode (TiO2NRs-HOT/CP) exhibits better hydrophilicity than carbon paper (CP) and TiO2NRs/CP electrode as seen from smaller contact angle (CA) and more attached microbes S.loihica PV-4. Meanwhile, the hollows allow higher local concentration of microbial self-secreted flavins that can act as electron mediators for interfacial electron transfer of PV-4 through in-direct pathway. Accordingly, PV-4 produces larger current density at TiO2NRs-HOT/CP electrode with maximum current density of 0.038 mA cm–2, which was much higher than that at CP electrode, and almost five times higher than that at un-etched TiO2NRs/CP electrode.

In this study, 12 commercially available paper towels were collected from the local market. Their tensile properties were investigated by Kawabata Evaluation System for Fabric (KES-F). Four tensile properties namely: (i) extensibility (EMT), (ii) tensile energy (WT), (iii) tensile resilience (RT) and (iv) linearity of WT (LT) were evaluated. Experimental results revealed that the tensile properties varied within the products. EMT was used as the key property for discussing the tensile properties of paper towels. However, when the different tensile properties were correlated, it was found that WT/RT, WT/EMT and RT/EMT had strong Pearson correlation. In addition, there was no significant statistically relationship between weight and thickness to EMT. Based on this study, it can provide some information about the tensile properties of paper towels in local market which may help the industry for further improving the product quality.

12 commercially available paper towels were collected from the local market and studied in this paper. Kawabata Evaluation System for Fabric (KES-F) was used for evaluating their bending properties. Two bending properties namely: (i) bending rigidity (B) and (ii) bending moment (2HB) were evaluated. Experimental results indciated that the bending properties varied within the products. B was used as the key property for discussing the bending properties of paper towels. When the correlations of different bending properties were investigated, it was found that no significant was found between B and 2HB. However, there was significant statistically relationship between weight and B but no relationship between thickness and B. With the use of the results, the product developer could improve the bending properties of the paper towels.

In this study, 12 commercially available paper towels were collected from the market. Their shearing properties were evaluated by Kawabata Evaluation System for Fabric (KES-F). Three properties namely: (i) coefficient of friction (MIU), (ii) deviation of MIU (MMD) and (iii) geometric roughness (SMD). Experimental results revealed that the surface properties varied within the products. When different properties were correlated, it was found that there was not significantly relationship between MIU, MMD and SMD. However, weight and thickness had well statistically relationship to SMD.

As a kind of environmentally friendly material, microfibrillated cellulose (MFC) has the following advantages: renewable raw materials, easy recycling, biodegradable, safety and so on. It can be combined with antibacterial agents to prepare the antibacterial packing materials for food. In this paper, the nano-ZnO was modified by titanate coupling agent TM-38s at first,determines the best dosage of TM-38 is 3% in the modification process,the dosage of the isopropyl alcohol for 40ml,improving its dispersibility. And then added in the MFC suspension to formulate the antibacterial coating for antibacterial coated paper preparation. The changes of antibacterial properties of the paper before and after coating were investigated in this study. The results showed that the paper had a significant antibacterial activity to e. coli and staphylococcus aureus (the antibacterial circle was bigger than 15 mm).When the nano-ZnO dosage was 2.5wt%, the antibacterial properties of the coated paper could reach the best situation. Application of the antibacterial caoated paper to the food packaging could restrain and kill the microorganisms on the food surface effectively, prolong the shelf life of food, and improve the food safety.

Noise pollution is a workplace hazard which causes loss of hearing, depending on the sound pressure level and duration of exposure. Because duration of exposure is usually uncontrollable, sound absorbers are used to reduce the value of sound pressure level. A common method to reduce noise is to use porous sound absorbers made out of mineral wools or glass fibres. However, these materials pose health risks and are non-recyclable. This project aimed to fabricate a sound absorber using recycled paper which is in the form of egg cartons as an alternative to the abovementioned fibres. Paper fibres posses high fibre porosity and can be manufactured in a manner which the properties can be easily controlled, making them ideal to be made into sound absorbers. Furthermore, they are biodegradable, do not pose health risks and can be manufactured into different shapes easily. Recycled paper was first turned into pulp, blended and poured into moulds. Different amounts of pulp was compressed until the sample size was approximately 20 mm thick and then dried in a furnace dryer at 600C for 12 hours. The samples were tested using a two-microphone, transfer function impedance tubes according to the ISO 10534-2 standard. Its porosity was determined using a modified wash basin method. The results indicate that the optimum panel has an average noise reduction coefficient, (NRC) of 0.50, which qualifies it to be used as a sound absorbing material. It also encounters its maximum value of 0.98 which occurred at the 1575-1675 Hz range. When compared to other materials, recycled paper has similar properties as coir fibre and is quite comparable to other commercial sound absorbers at the same thickness.

In this paper, the stiffness and folding endurance of the paper were investigated with three kinds of pulp, such as the mechanical wood pulp, chemical pulp and composite pulp, after using common additives and cleaning additives. The results indicated that the stiffness of the paper can be increased by 20% ~ 30% and folding endurance can improve 20% ~ 60% after using new kind of cleaning additives no matter what kind of filler. New cleaning additives can not only improve the physical properties of paper, but also change "acidic papermaking" of the traditional paper industry into clean neutral papermaking environment. Especially, it is suitable for the production of food card paper.

Microfibrillated cellulose (MFC) was prepared from the bleached kraft hardwood pulp using TEMPO/NaClO/NaBr oxidation system and high pressure homogenization. By changing dosages of the TEMPO, NaClO and NaBr, the pressure and times of homogenization, pretreatment and homogenization process were optimized. Experimental investigation indicated that for making MFC of high quality, 0.25%TEMPO, 2.5%NaBr, 60%NaClO (based on oven dry pulp), 20 times of homogenization, pressure of 60MPa in the process of treatment were required. At last, the mechanical and barrier properties were tested after the base paper was coated by homemade MFC. The study suggested that mechanical properties (especially 5 times increase of the folding strength) increased substantially and air permeability decreased by 100times.

The influence of coating layer structure on both physical and printing quality of the paper was studied. Different coating layers were obtained by changing the ratio of polyvinyl alcohol adhesives and silicon dioxide pigments in the coating formula. Then the structure, physical properties and ink-jet printing performance of the coated paper were measured. The influences of coating structure on physical properties and ink-jet printing performance were evaluated. The results showed that as the ratio of adhesive increased, the coating porosity decreased; the average pore diameter increased at first and then decreased, but in general tended to decrease; the initial drop contact angle increased, which testified the stronger hydrophobicity of the coated surface with higher adhesive ratio. The average pore diameter has a negative linear correlation with paper roughness while has a positive linear correlation with air permeability. The larger the average pore diameter, the greater the density values, as well as the better tone reproduction and the larger color gamut range. Average pore diameter also has a weak correlation with dot area and dot roundness.