Characterization of Physical and Mechanical Properties of Bleaching Paper from Rice Straw

This paper aimed to determine the characteristics of physical and mechanical properties of rice straw hand sheet and investigated the optimal conditions for making rice straw paper. The chemical composition of rice straw determined with the TAPPI standards. The conditions of making paper hand sheet composed of pulping time: 2 hours, 4 hours, pulping temperature: 100°C, 130°C, pulping solvent: 2 wt% NaOH, 4 wt% NaOH and bleaching: unbleached pulp, bleached pulp with 2% H2O2. The paper hand sheet was tested based on TAPPI methods, basic weight TAPPI- T410-om-93, thickness TAPPI- T411-om-89, moisture content TAPPI- T412-om-93, brightness TAPPI T452 om-92, opacity TAPPI standard T 425 om-91, burst strength TAPPI T403 om-97, tensile strength TAPPI T494 om-01, and tear strength TAPPI-T414-om-88. The results showed that the optimal conditions of rice straw hand sheet including pulping time: 2 hours, pulping temperature: 100°C, pulping solvent: 2 wt% NaOH, and bleaching: unbleached pulp gave the highest the physical and mechanical properties form other conditions. This conditions showed as the basic weight 62.27 g/m2, thickness 259.30 µ, opacity 93.34 ISO%, burst strength 64.75 kPa.m2/g, tensile strength 95.33 N.m/g, and tear strength 473.55mN.m2/g. In this condition, the paper hand sheet used at the lowest concentration of pulping solvent and non-bleached, which reduces environmental pollution.