Search

This paper contains results of tests performed in order to determine mechanical properties of steel P460NL1, used as filler material during the execution of welded joints. Arc welding of samples from which the specimens were taken was carried out through the application of welding process 111, because it is one of the processes for the execution of pipelines for pressure equipment. Microspecimens with diameter of 1,5 mm were tested in order to determine tensile properties of material taken from the heat-affected zone and weld metal, while specimens with diameter of 6 mm were tested in order to determine tensile properties of parent material. Standard Charpy V-notch specimens were used in order to determine impact energy. Results of metallographic tests which refer to the structure of a pipe welded joint are also presented.

Turbine and generator rotors and shafts undergo high stresses during regular working life and, from a safety and operational aspect, are the most significant components of a power generation system. Depending on the appropriate operating conditions, like temperature and/or corrosion the, shafts can be fabricated out of low/high alloy heat resistance material or of low alloyed, highly toughened material for different application. Despite known good practice and developed operation procedures, the failures of shafts sometimes occur. The right and well-defined failure analysis is the basis for feasibility analysis of repair method in the power generating industry. The analysis of direct and indirect costs of repair after the failure analysis as well as the analysis of the repair and post-repair conditions of the repaired element is the vital for decision on the key question. Is it possible to repair this element and what is the optimal repair strategy? This paper compares and analyses two approaches, by weldability analysis and weld cycle simulation, in order to determine welding feasibility analysis of cracked hydro turbine shafts.

The steels fracture toughness was measured at two different temperature T= - 60°C and T = -90°C, at v=0.02 mm/min and v=0.5 mm/min. The following steels: CrMoV, 20MnMoNi55, A533B and A508 were tested with three different sizes of CT specimens 50 and 100 and 200. Those steels are weldable, although the authors investigated the fracture behaviour of base material. In order to satisfy statistical analyses, a large number of specimens were tested. Fracture behaviour has turned out to be typical, S-shaped curve for transitional fracture at low temperatures. Apart from the other variables, specimen’s width significantly affects measured toughness. Smaller specimens, CT50, might be considered of upper bound reliability while the CT200 specimens were shown to be the most conservative. In this way it has been shown that wider specimens are more reliable in a fracture assessment of the examined steels. In this paper, the fracture probabilities of specimens in function of fracture toughness were determined as well, and it could be concluded that the widest specimens are the most likely to be broken for the same values of the fracture toughness.

Technical diagnostics of hydromechanical equipment, is based on testing procedures including the history of the exploitation with expert knowledge of structures and operating conditions, as well as, on the analysis of results performed by experts with appropriate experience and knowledge in design, exploitation, maintenance, reliability, fracture mechanics etc. Degradation of properties of the material and/or welded joints of hydro-mechanical equipment is being caused by the simultaneous influence of a large number of factors. First of all, it is thought of technological, metallurgical, structural and conditions of exploitation. In this paper, the selection of methodology for the rehabilitation of hydro-mechanical equipment is presented based on the previously conducted assessment of state of equipment using the nondestructive testing methods. Repair welding, repair of damaged surfaces by cold metallization, corrections of existing structural solutions of metallic components in order to improve their technical characteristics and extend the service life are presented.

Vertical Kaplan turbines, manufactured in Russia and with nominal power of 200 MW, have been installed in 6 hydroelectric generating units at hydro power plant Djerdap 1. Hydroelectric generating sets have been designed for the service life of 40 years due to structural solutions and limited possibilities of performing periodic inspections and state analyses. During the rehabilitation of the hydroelectric generating sets, non-destructive tests were performed on all components and structures in order to complete state analysis. In this paper the damages and methodology of repair welding for damaged glasses, which are the integral part of the kinematic system of runner blades, are presented.