Search

Various commercial zeolites, including FER, MOR, ZSM‐5, BEA, and FAU frameworks, were treated with NH4F aqueous solutions to study the effects of fluoride etching on different zeolite frameworks. NH4F‐treated small‐medium pore FER, MOR, and ZSM‐5 samples showed much higher mesoporosities than the untreated ones without alteration of the structural compositions and acidic properties. On the other hand, the 12‐membered ring zeolites BEA and FAU showed severe dissolution of the framework aluminosilicate structure after NH4F etching due to the high accessibility of fluoride species into the framework structures. The effect of NH4F concentration on the fluoride treatment of H‐ZSM‐5 zeolite was specifically studied. From the results, we observed that structural etching with 20 wt % NH4F was optimal for fabricating open‐pore H‐ZSM‐5 zeolite and resulted in a high mesoporosity with comparable relative crystallinity and acidity with respect to the untreated H‐ZSM‐5. The catalytic activities of the open‐pore H‐ZSM‐5 were evaluated with acid‐catalyzed methanol and bioethanol conversions. Remarkably, the hierarchical open‐pore H‐ZSM‐5 zeolite fabricated via fluoride etching exhibited an enhanced catalytic performance in bioethanol conversion with >85 % conversion over 34 h TOS and a higher catalytic stability in methanol conversion than the parent H‐ZSM‐5 (~50 % of bioethanol conversion at 34 h TOS). [ABSTRACT FROM AUTHOR]

Hydrogels with or without chemical cross-linking have been studied and used for biomedical applications, such as tissue repair, surgical sealants, and three dimensional biofabrication. These materials often undergo a physical sol–gel or gel–sol transition between room and body temperatures and can also be chemically cross-linked at these temperatures to give dimensional stability. However, few studies have clearly shown the effect of heating/cooling rates on such transitions. Moreover, only a little is known about the effect of cross-linking temperature or the state on the modulus after cross-linking. We have established rheological methods to study these effects, an approach to determine transition temperatures, and a method to prevent sample drying during measurements. All the rheological measurements were performed minimizing the normal stress build-up to compensate for the shrinking and expansion due to temperature and phase changes. We chemically modified gelatin to give gelatin methacryloyl and determined the degree of methacryloylation by proton nuclear magnetic resonance. Using the gelatin methacryloyl as an example, we have found that the gel state or lower temperature can give more rigid gelatin-based polymers by cross-linking under visible light than the sol state or higher temperature. These methods and results can guide researchers to perform appropriate studies on material design and map applications, such as the optimal operating temperature of hydrogels for biomedical applications. We have also found that gelation temperatures strongly depend on the cooling rate, while solation temperatures are independent of the heating rate. [ABSTRACT FROM AUTHOR]

We studied polymer-polymer interfacial slip in bilayer films of highly immiscible (interaction parameter, χ≅0.1) polyethylene and fluoropolymer from medium to higher shear stresses (10-200 kPa) using both visualization and stress reduction. We found good agreement between results from the two methods as well as with previous studies using multilayers by Lee et al. [J. Rheol. 53, 893-915 (2009)] and visualization of flow in a transparent capillary by Migler et al. [J. Rheol. 45, 565-581 (2001)]. We observed two power-law regions: Vslip∝τ6.2 with a transition to Vslip∝τ1.8 at 50 kPa. This is in contrast to the theory of Brochard-Wyart and de Gennes [C. R. Acad. Sci., Ser. II: Mec., Phys., Chim., Sci. Terre Univers 317, 13-17 (1993)], which predicts a transition from infinite slope to a slope of one at a critical stress. [ABSTRACT FROM AUTHOR]

Strain hardening has important roles in understanding material structures and polymer processing methods, such as foaming, film forming, and fiber extruding. A common method to improve strain hardening behavior is to chemically branch polymer structures, which is costly, thus preventing users from controlling the degree of behavior. A smart microfiber blending technology, however, would allow cost-efficient tuning of the degree of strain hardening. In this study, we investigated the effects of compounding polymers with microfibers for both shear and extensional rheological behaviors and characteristics and thus for the final foam morphologies formed by batch physical foaming with carbon dioxide. Extensional rheometry showed that compounding of in situ shrinking microfibers significantly enhanced strain hardening compared to compounding of nonshrinking microfibers. Shear rheometry with linear viscoelastic data showed a greater increase in both the loss and storage modulus in composites with shrinking microfibers than in those with nonshrinking microfibers at low frequencies. The batch physical foaming results demonstrated a greater increase in the cell population density and expansion ratio with in situ shrinking microfibers than with nonshrinking microfibers. The enhancement due to the shrinkage of compounded microfibers decreasing with temperature implies that the strain hardening can be tailored by changing processing conditions. [ABSTRACT FROM AUTHOR]

I Coatings i was able to uphold its high standards for published papers due to the outstanding efforts of our reviewers. Thanks to the efforts of our reviewers in 2022, the median time to first decision was 14 days and the median time to publication was 36 days. Regardless of whether the articles they examined were ultimately published, the editors would like to express their appreciation and thank the following reviewers for the time and dedication that they have shown I Coatings i : olely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). [Extracted from the article]