Search

Growth of Au-catalysed ZnSe NWs has been successfully achieved on ZnSe peudo-substrates grown on GaAs substrate for the 1st time. Nucleation of the gold catalyst nanoparticles was studied in details. Au nanoparticles with homogeneous diameters are achieved. The nanowire diameter that results from these nanoparticles is in the range of the Bohr diameter of excitons in ZnSe and CdSe. Ultralow density achieved for Au nanoparticles makes it possible to grow nanowires in a non-competitive mode. Study of the influence of the growth parameters was done in details. A high Se:Zn~4 flux ratio and a growth temperature in the low 400C range are found to yield the straightest NWs. Homogeneous NWs with two main orientations are obtained on (001) ZnSe. The nanowire growth rate can be modeled by a kinetic mass-transport model of impinging adatoms flowing to the nanowire growth front. ZnSe NW growth was identified as taking place in the VSS mode, that is, with a solid catalyst, by in-situ RHEED observations. A growth of NWs by ALE yields only a single NW orientation. Incorporation of CdSe QDs was studied in details with numerous experimental techniques. It is possible to obtain CdZnSe QDs with a length of a few nanometers with compositionally sharp heterojunctions and a composition in Cd of about 50%. The optical study of such NWs shows sharp excitonic lines. Single photon emission on the biexciton was measured up to room temperature. A limitation comes from the fact that the NWs must be detached from the surface to be studied due to the presence of a discreet background emission originating from the substrate., Des nanofils de ZnSe catalysés avec de l'or ont été synthétisés pour la première fois sur pseudo-substrats de ZnSe déposé sur GaAs. La nucléation de l'or a été étuidiée en détails. Des nanoparticules d'or de diamètres homogènes ont été produites. Ces nanoparticules conduisent à la création de nanofils de diamètres de l'ordre des diamètres de Bohr des excitons dans le ZnSe et dans le CdSe. Les très basses densités de nanoparticules d'or obtenues permettent la croissance de nanofils de ZnSe dans un mode non-compétitif. La croissance a été étudiée en fonction de la variation de certains paramètres. Un rapport de flux élevé de Se:Zn~4, ainsi qu'une température aux alentours des 400C donnent lieu aux nanofils les plus droits. Les nanofils résultant de ces conditions sur ZnSe (001) s'orientent selon deux axes. La vitesse de croissance des nanofils peut être modélisée par la diffusion d'adatoms vers l'interface de croissance du nanofil. Il est démontré à l'aide d'observations RHEED que la croissance se déroule dans un mode vapeur-solide-solide (VSS), c'est à dire, avec un catalyseur à l'état solide. Une croissance dans le mode ALE produit des nanofils orientés selon un seul axe. L'incorporation de BQ de CdSe à été étudiée en détails par le biais de plusieurs techniques expérimentales. Il est possible d'obtenir des BQ de CdZnSe de quelques nanomètres de long, avec des hétérojonctions abruptes et contenant aux alentours de 50% de Cd. L'étude optique de ces BQ montre de fines raies excitoniques. L'émission de photons uniques a été mesurée sur la raie biexcitonique jusqu'à la température ambiante. À cause de la présence d'une émission discrète du substrat des nanofils, ceux-ci doivent être transférés sur un substrat non-luminescent pour les études optiques.

Growth of Au-catalysed ZnSe NWs has been successfully achieved on ZnSe peudo-substrates grown on GaAs substrate for the 1st time. Nucleation of the gold catalyst nanoparticles was studied in details. Au nanoparticles with homogeneous diameters are achieved. The nanowire diameter that results from these nanoparticles is in the range of the Bohr diameter of excitons in ZnSe and CdSe. Ultralow density achieved for Au nanoparticles makes it possible to grow nanowires in a non-competitive mode. Study of the influence of the growth parameters was done in details. A high Se:Zn~4 flux ratio and a growth temperature in the low 400C range are found to yield the straightest NWs. Homogeneous NWs with two main orientations are obtained on (001) ZnSe. The nanowire growth rate can be modeled by a kinetic mass-transport model of impinging adatoms flowing to the nanowire growth front. ZnSe NW growth was identified as taking place in the VSS mode, that is, with a solid catalyst, by in-situ RHEED observations. A growth of NWs by ALE yields only a single NW orientation. Incorporation of CdSe QDs was studied in details with numerous experimental techniques. It is possible to obtain CdZnSe QDs with a length of a few nanometers with compositionally sharp heterojunctions and a composition in Cd of about 50%. The optical study of such NWs shows sharp excitonic lines. Single photon emission on the biexciton was measured up to room temperature. A limitation comes from the fact that the NWs must be detached from the surface to be studied due to the presence of a discreet background emission originating from the substrate.; Des nanofils de ZnSe catalysés avec de l'or ont été synthétisés pour la première fois sur pseudo-substrats de ZnSe déposé sur GaAs. La nucléation de l'or a été étuidiée en détails. Des nanoparticules d'or de diamètres homogènes ont été produites. Ces nanoparticules conduisent à la création de nanofils de diamètres de l'ordre des diamètres de Bohr des excitons dans le ZnSe et dans le CdSe. Les très basses densités de nanoparticules d'or obtenues permettent la croissance de nanofils de ZnSe dans un mode non-compétitif. La croissance a été étudiée en fonction de la variation de certains paramètres. Un rapport de flux élevé de Se:Zn~4, ainsi qu'une température aux alentours des 400C donnent lieu aux nanofils les plus droits. Les nanofils résultant de ces conditions sur ZnSe (001) s'orientent selon deux axes. La vitesse de croissance des nanofils peut être modélisée par la diffusion d'adatoms vers l'interface de croissance du nanofil. Il est démontré à l'aide d'observations RHEED que la croissance se déroule dans un mode vapeur-solide-solide (VSS), c'est à dire, avec un catalyseur à l'état solide. Une croissance dans le mode ALE produit des nanofils orientés selon un seul axe. L'incorporation de BQ de CdSe à été étudiée en détails par le biais de plusieurs techniques expérimentales. Il est possible d'obtenir des BQ de CdZnSe de quelques nanomètres de long, avec des hétérojonctions abruptes et contenant aux alentours de 50% de Cd. L'étude optique de ces BQ montre de fines raies excitoniques. L'émission de photons uniques a été mesurée sur la raie biexcitonique jusqu'à la température ambiante. À cause de la présence d'une émission discrète du substrat des nanofils, ceux-ci doivent être transférés sur un substrat non-luminescent pour les études optiques.

Photothermal deflection spectroscopy (PDS) was used to measure the bandgap optical parameters and the Urbach energy of semi-insulating (SI) GaAs and a 238nm GaNAs epitaxial thin film in the energy range 800-1l00nm. To do so, a PDS apparatus was setup using a 0.lmW and l0nm bandwidth pump beam obtained with a f/3.8 monochromator and a 150W Tungsten Halogen lamp, a HeNe laser for the probe beam, CCI[superscript omitted] for the deflecting medium and a linear position sensitive detector. The spectra obtained for GaAs and GaNAs were compared with models based on the Rosencwaig-Gersho and the Fernelius theories of ID heat diffusion which consider absorption in respectively one and two sample layers, and also on a model of absorption based on literature results. Preliminary results indicate that more work will be needed on the apparatus/models to qualify the validity of the fitted optical parameters. The PDS apparatus demonstrated an absorbance sensitivity limit of ~10[superscript omitted] with the samples investigated.