Search

High-purity cubic silicon carbide possesses the second-highest thermal conductivity among large-scale crystals, surpassed only by diamond, making it crucial for practical applications of thermal management. Recent theoretical studies predict that heavy doping reduces the thermal conductivity of 3C-SiC via phonon-defect and phonon-electron scattering. However, experimental evidence has been limited. In this work, we report the thermal conductivity of heavily nitrogen doped 3C SiC single crystals, grown using the top-seeded solution growth method, measured via time domain thermoreflectance. Our results show that a significant reduction (up to 30%) in thermal conductivity is observed with nitrogen doping concentrations around 1020 cm-3. A comparison with theoretical calculations indicates less intensive scatterings are observed in the measured thermal conductivity. We speculate that the electron-phonon scattering may have a smaller impact than previously anticipated or the distribution of defects are nonuniform which leads to less intensive scatterings. These findings shed light on understanding the doping effects on thermal transport in semiconductors and support further exploration of 3C SiC for thermal management in electronics.

Overheating has emerged as a primary challenge constraining the reliability and performance of next-generation high-performance electronics, such as chiplets and (ultra)wide bandgap electronics. Advanced heterogeneous integration not only constitutes a pivotal technique for fabricating these electronics but also offers potential solutions for thermal management. This study presents the integration of high thermal conductivity semiconductors, specifically, 3C-SiC thin films and diamond substrates, through a room-temperature surface-activated bonding technique. Notably, the thermal conductivity of the 3C-SiC films is among the highest for all semiconductor films which can be integrated near room temperature with similar thicknesses. Furthermore, following annealing, the interfaces between 3C-SiC and diamond demonstrate a remarkable enhancement in thermal boundary conductance (TBC), reaching up to approximately 300%, surpassing all other grown and bonded heterointerfaces. This enhancement is attributed to interfacial reactions, specifically the transformation of amorphous silicon into SiC upon interaction with diamond, which is further corroborated by picosecond ultrasonics measurements. Subsequent to annealing at 1100 C, the achieved TBC (150 MW/m2-K) is record-high among all bonded diamond interfaces. Additionally, the visualization of large-area TBC, facilitated by femtosecond laser-based time-domain thermoreflectance measurements, shows the uniformity of the interfaces which are capable of withstanding temperatures as high as 1100 C. Our research marks a significant advancement in the realm of thermally conductive heterogeneous integration, which is promising for enhanced cooling of next-generation electronics.

The coupled transport of charge and heat provide fundamental insights into the microscopic thermodynamics and kinetics of materials. We describe a sensitive ac differential resistance bridge that enables measurements of the temperature difference on two sides of a coin cell with a resolution of better than 10 uK. We use this temperature difference metrology to determine the ionic Peltier coefficients of symmetric Li-ion electrochemical cells as a function of Li salt concentration, solvent composition, electrode material, and temperature. The Peltier coefficients {\Pi} are negative, i.e., heat flows in the direction opposite to the drift of Li ions in the applied electric field, large, 30 kJ mol-1, and increase with increasing temperature at T > 300 K. The Peltier coefficient is approximately constant on time scales that span the characteristic time for mass diffusion across the thickness of the electrolyte, suggesting that heat of transport plays a minor role in comparison to the changes in partial molar entropy of Li at the interface between the electrode and electrolyte. Our work demonstrates a new platform for studying the non-equilibrium thermodynamics of electrochemical cells and provides a window into the transport properties of electrochemical materials through measurements of temperature differences and heat currents that complement traditional measurements of voltages and charge currents.

Iron-based superconductors have great potential for high-power applications due to their prominent high-field properties. One of the central issues in enhancing the critical current density of iron-based superconducting wires is to reveal the roles and limitations of grain boundaries in supercurrent transport. Here, we finely tuned the electronic properties of grain boundaries by doping Ba1-xKxFe2As2 superconductors in a wide range (0.25

beta-Ga2O3 is a wide bandgap semiconductor with electrical properties better than SiC and GaN which makes it promising for applications of next-generation power devices. However, the thermal conductivity of \b{eta}-Ga2O3 is more than one order of magnitude lower than that of SiC and GaN, resulting in serious thermal management problems that limit device performance and reliability. This work reports selectively transferring of high thermal conductivity 3C-SiC thin film grown on Si to beta-Ga2O3 (001) substrate using surface activated bonding (SAB) technique at room temperature, to attempt extracting the heat from the surface of the devices. A 4.5-nm-thick interfacial crystal defect layer is formed at the as-bonded 3C-SiC/beta-Ga2O3 interface. The thickness of the interfacial crystal defect layer decreases with increasing annealing temperature, which decreases to 1.5 nm after annealing at 1000 C. No voids and unbonded area are observed at the interfaces, even after annealing at temperature as high as 1000 C. The thermal boundary conductance (TBC) of the 1000 C-annealed 3C-SiC/beta-Ga2O3 interface and thermal conductivity of the beta-Ga2O3 substrate was measured by time-domain thermoreflectance (TDTR). The 3C-SiC/beta-Ga2O3 TBC value was determined to be 244 MW/m2-K, which is the highest value ever reported for SiC/Ga2O3 interfaces, due to the high-quality heterointerface. Our works demonstrate that selective transferring of 3C-SiC film to the beta-Ga2O3 substrate is an efficient path to improve heat dissipation of the \b{eta}-Ga2O3 power devices.

High thermal conductivity electronic materials are critical components for high-performance electronic and photonic devices as either active functional materials or thermal management materials. We report an isotropic high thermal conductivity over 500 W m-1K-1 at room temperature in high-quality wafer-scale cubic silicon carbide (3C-SiC) crystals, which is the second highest among large crystals (only surpassed by diamond). Furthermore, the corresponding 3C-SiC thin films are found to have record-high in-plane and cross-plane thermal conductivity, even higher than diamond thin films with equivalent thicknesses. Our results resolve a long-lasting puzzle that the literature values of thermal conductivity for 3C-SiC are perplexingly lower than the structurally more complex 6H-SiC. Further analysis reveals that the observed high thermal conductivity in this work arises from the high purity and high crystal quality of 3C-SiC crystals which excludes the exceptionally strong defect-phonon scatterings in 3C-SiC. Moreover, by integrating 3C-SiC with other semiconductors by epitaxial growth, we show that the measured 3C-SiC-Si TBC is among the highest for semiconductor interfaces. These findings not only provide insights for fundamental phonon transport mechanisms, also suggest that 3C-SiC may constitute an excellent wide-bandgap semiconductor for applications of power electronics as either active components or substrates.

Coherent conversion of microwave and optical photons can significantly expand the ability to control the information processing and communication systems. Here, we experimentally demonstrate the microwave-to-optical frequency conversion in a magneto-optical whispering gallery mode microcavity. By applying a magnetic field parallel to the microsphere equator, the intra-cavity optical field will be modulated when the magnon is excited by the microwave drive, leading to microwave-to-optical conversion via the magnetic Stokes and anti-Stokes scattering processes. The observed single sideband conversion phenomenon indicates a non-trivial optical photon-magnon interaction mechanism, which is derived from the magnon induced both the frequency shift and modulated coupling rate of optical modes. In addition, we demonstrate the single-sideband frequency conversion with an ultrawide tuning range up to 2.5GHz, showing its great potential in microwave-to-optical conversion., Comment: 6 pages, 4 figures

The reversible heat in lithium-ion batteries (LIBs) due to entropy change is fundamentally important for understanding the chemical reactions in LIBs and developing proper thermal management strategies. However, the direct measurements of reversible heat are challenging due to the limited temperature resolution of applied thermometry. In this work, by developing an ultra-sensitive thermometry with a differential AC bridge using two thermistors, the noise-equivalent temperature resolution we achieve (10 uK) is several orders of magnitude higher than previous thermometry applied on LIBs. We directly observe reversible heat absorption of a LIR2032 coin cell during charging with negligible irreversible heat generation and a linear relation between heat generations and discharging currents. The cell entropy changes determined from the reversible heat agree excellently with those measured from temperature dependent open circuit voltage. Moreover, it is found that the large reversible entropy change can cancel out the irreversible entropy generation at a charging rate as large as C/3.7 and produce a zero-heat-dissipation LIB during charging. Our work significantly contributes to fundamental understanding of the entropy changes and heat generations of the chemical reactions in LIBs, and reveals that reversible heat absorption can be an effective way to cool LIBs during charging.