The fly ash of class C for ceramic technology

The properties of different Czech fluidized fly ashes FFA (class C fly ash according to ASTM C618 12a with high content of CaO in the form of anhydrite primarily) and emisions of SO2 in flue gas during the firing of FFA are discussed. The decomposition of anhydrite CaSO4 was observed during the soaking time at 1200 °C during the firing of dry pressed bodies based on pure fluidized fly ash. The effect od fluidized fly ashes admixtures on the properties of ceramic bodies is as fluxing agent and the source of CaO for the creation of anorthite in the fired ceramic body. The properties of domestic fluidized fly ashes in connection with their utilization in ceramic technology are described.
V tomto příspěvku byly popsány vlastnosti různých fluidních popílků z České republiky (v americké normě ASTM C618 12a jsou označovány jako FFA class C, s vysokým obsahem CaO ve formě anhydritu). Také byly sledovány emise SO2 ve spalinách během výpalu popílků. Rozklad anhydritu CaSO4 byl pozorován během teplotní výdrže při 1200 °C při výpalu za sucha lisovaných zkušebních vzorků z fluidních popílků. Také byl sledován vliv fluidního popílku jako příměs do keramického střepu, kde se chová jako tavivo a zdroj CaO pro vytvoření minerálu anortitu ve vypáleném střepu. V příspěvku jsou také popsány vlastnosti fluidních popílků z ČR ve spojitosti s jejich využitím v keramické technologii.