Impact of Alumina Particles on the Morphology and Mechanics of Hybrid Wood Plastic Composite Materials

Hybrid composite panels of Wood-Plastic Composites (WPC) consisting of wood and poly (methyl methacrylate) (PMMA) were reinforced with alumina particles and made by “hot pressing” method. Alumina-based particles were made by sol-gel technique. The particles were characterized by the X-ray diffraction (XRD). The resulting alumina particles were modified with (3mercaptopropyl) trimethoxysilane (MPTMS), in order to obtain better mechanical properties of the composite relative to the composite with unmodified alumina particles. The aim of this work was to study the influence of composite structure and the moisture absorption on bending and the impact properties of the hybrid composite. The bending and impact tests revealed that modulus of elasticity and absorbed energy of deformation increased with modification of alumina and slightly decrease after moisture absorption.
Хибридни композитни панели дрво-пластика композит (ДПК) који се састоје од дрвета и поли(метил метакрилата) (ПММА) ојачани честицама алуминијум оксида прецесирани методом „врућег пресовања“. Честице засноване на алуминијум оксиду направљене су сол – гел техником. Карактеризација честица вршена је рендгенском анализом. Добијене честице алуминијум оксида модификоване су помоћу (меркаптопропил)триметоксисилана, како би се постигла боља механичка својства композита у односу на композит са немодификованим честицама алуминијум оксида. Циљ овог рада је проучавање утицаја структуре хибридног композита и апсорбоване влаге на механичка својства, савијање и контролисани удар. Тестови савијања и удара показали су да се модул еластичности и апсорбована енергија деформације повећава модификацијом алуминијум оксидних честица, а незнатно самањује након апсорпције влаге.