Superionic behavior in the xAgI-(1-x)CsAg2I3 polycrystalline system

A superionic phase behavior (with DC ionic conductivities higher than 0.01 S/cm) has been observed in xAgI-(1-x)CsAgI (x≈0.67) polycrystalline system grown by slow evaporation using AgI and CsI powders (molar ratio Cs/Ag=0.25) as starting salts and an aqueous solution of HI as solvent. The transition from the normal-to- the superionic state is first-order with a hysteretic behavior in temperature centered at about 116 °C as reflected by thermal (DSC) and electrical conductivity measurements. This mixture is composed of CsAgI and AgI crystalline phases and an additional amorphous AgI phase that explains the glassy-type behavior observed in the superionic phase transition.