High-T(c) squid application in medicine and geophysics

In our laboratory of high-T(sub c), a one-hole squid was built from Y1Ba2Cu3O(7-x) ceramics obtained by a standard procedure of solid state reaction. The ceramics with critical current density J(sub c) is greater than 100 A/sq cm was selected. In the middle of a 10 x 10 x 2 mm ceramics pellet, a 0.8 mm hole was drilled in which the superconducting loop of the squid was located. Between the hole and the edge of the pellet, a cut was mechanically filed out with a bridge inside it connecting the superconducting ring. A scheme of the magnetometer is presented. The resonant frequency shift of the tank circuit, the connection of the squid with this circuit, and the squid inductance are evaluated. One of the most interesting fields of the squid-based magnetometer application is biomagnetism, particularly, the human heart magnetocardiogram measuring. The low-temperature squids were used in this area and many interesting and important scientific results have been obtained. The observations have shown that the main noise contribution was not due to the squid but to the Earth's magnetic field variations, industrial inductions, and mainly to the vibrations caused by liquid nitrogen boiling and by vibrations of the box. Further attempts are needed to reduce the magnetic noise inductions. Nevertheless, the estimations promise the maximum signal/noise relation of the high-T(sub c) squid-magnetocardiometer to be not less than 10:1 in a bandwidth of 60 Hz. Apparently, such resolution would be enough not only for steady cardiogram reading but even for thin structure investigation at average technique application.