Effect of Methyl Methacrylate on the Properties of Transparent Flame Retardant Unsaturated Phosphate Ester Copolymer

The effect of methyl methacrylate (MMA) on the properties of transparent flame retardant unsaturated phosphate ester copolymer (poly[UPE-co-MMA]) prepared by bulk polymerization technique was investigated. Fourier transform infrared spectra, gel fraction (G) test, and dynamic mechanical analysis revealed the structure and crosslinking density of poly(UPE-co-MMA) copolymers. The thermal degradation and flame retardancy of copolymers were indicated by thermogravimetric analysis, limiting oxygen index (LOI), and microscale combustion calorimeter (MCC) test. Besides, the mechanical properties and transparency were tested with testing machines and solid ultraviolet absorption spectra. As the MMA content increased to 50%, the copolymer contained 50 wt% MMA showed the maximal G (88.93%) and transmittance was up to 91.72%. From the poly(UPE-co-MMA) copolymers, the tensile strength increased from 14.62 to 26.95 MPa, assigned to the increase of crosslinking density of copolymers. The char yield of poly(UPE-co-MMA) was up to 21.18 wt%, which was a result of decomposition of phosphate groups, producing a phosphorus-rich layer that increased the thermal stability of the residues. LOI and MCC results confirm that the introduction of MMA can retain the flame retardancy of copolymer remarkably.
INTRODUCTION Polymer materials have been widely used as advanced composite matrices in various areas such as building construction, automobiles to space vehicles, shipping, and electronic/electrical industries for their outstanding properties, [...]