Microstructure, Mechanical, and Tribological Behaviour of Spark Plasma Sintered TiN, TiC, TiCN, TaN, and NbN Ceramic Coatings on Titanium Substrate

Titanium (Ti) is widely used in structural, maritime, aerospace, and biomedical applications because of its outstanding strength-to-weight ratio, superior corrosion resistance, and excellent biocompatibility. However, the lower surface hardness and inferior wear resistance of the Ti and Ti alloys limit their industrial applications. Coating Ti surfaces can initiate new possibilities to give unique characteristics with significant improvement in the Ti component’s functionality. The current research designed and synthesized titanium nitride (TiN), titanium carbide (TiC), titanium carbonitride (TiCN), tantalum nitride (TaN), and niobium nitride (NbN) ceramic coating layers (400 µm) over a Ti substrate using a spark plasma sintering process (SPS). The coatings on the Ti substrate were compact and consolidated at an SPS temperature of 1500 °C, pressure of 50 MPa, and 5 min of holding time in a controlled argon atmosphere. Microstructure investigation revealed a defect-less coating-substrate interface formation with a transition/diffusion zone ranging from 10 µm to 20 µm. Among all of the ceramic coatings, titanium carbide showed the highest improvement in surface hardness, equal to 1817 ± 25 HV, and the lowest coefficient of friction, equal to 0.28 for NbN.