Enhancement of Impact Abrasion Resistance Performances of White Cast Iron Utilizing Ti3AlC2

Al-Ti-C master alloy agent is currently the most promising grain refiner. This work investigates the influence of Ti3AlC2 addition (1.0–3.0 wt.%) on the microstructure of a hypoeutectic cast iron (4.7 wt.% Cr, 2.3 wt.% C). Microstructures of the samples were examined by SEM (scanning electron microscope). It was demonstrated that the added Ti3AlC2 did reduce the size of coarse primary carbides. The XRD (X-ray diffraction) pattern shows that Ti3AlC2 is decomposed into TiC in the alloy substrate. The EDS (energy dispersive spectrometer) interfacial element analysis shows that TiC combines well with the matrix interface. As the Ti3AlC2 amount was increased, the finest microstructure was achieved. When 2 wt.% Ti3AlC2 was added, the wear-resistance property of the material improved and became two times harder than the former. However, when 3% Ti3AlC2 was added, TiC gathered at the crystal boundary, which caused a decrease in the wear resistance of the material.